CN107586094A - A kind of nano composite diatom ooze paint - Google Patents
A kind of nano composite diatom ooze paint Download PDFInfo
- Publication number
- CN107586094A CN107586094A CN201610521793.0A CN201610521793A CN107586094A CN 107586094 A CN107586094 A CN 107586094A CN 201610521793 A CN201610521793 A CN 201610521793A CN 107586094 A CN107586094 A CN 107586094A
- Authority
- CN
- China
- Prior art keywords
- parts
- nano
- diatom ooze
- titanium oxide
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention belongs to building material field, proposes a kind of nano composite diatom ooze paint, is made up of the raw material of following weight part ratio:30 40 parts of calcined diatomite, 10 15 parts of dicalcium powder, 15 parts of nano titanium oxide dispersion, 15 parts of starch ether, 15 parts of rock wool fibers;Described calcined diatomite particle diameter is not more than 200 mesh sieves;Described nano titanium oxide dispersion, it is made up of the raw material of following weight part ratio:60 80 parts of nano TiO 2 material, 10 15 parts of styrene-acrylic emulsion, 5 10 parts of amino propylamine dioleate;Product cost is not high;Properties of product are stable, do not lump, do not solidify, good weatherability.
Description
Technical field
The invention belongs to building material field, and in particular to a kind of nano composite diatom ooze paint.
Background technology
Diatom ooze coating, a kind of novel wall surface ornament materials without formaldehyde, benzene, TVOC and heavy metal material is not only,
The suction-operated to pernicious gas can be more played, so as to play the effect of purification indoor environment.But the diatom ooze that current city is discussed face to face
Product, the problems such as cost of manufacture is higher, and product easily lumps, and painting brushing effects are uneven still be present, need further to be improved.
The content of the invention
In view of the above-mentioned deficiencies in the prior art, it is an object of the present invention to provide a kind of nano composite diatom ooze paint.
Technical scheme
1. a kind of nano composite diatom ooze paint, it is made up of the raw material of following weight part ratio:Calcined diatomite 30-40 parts, weight
Calcium powder 10-15 parts, nano titanium oxide dispersion 1-5 parts, starch ether 1-5 parts, rock wool fibers 1-5 parts.
2. calcined diatomite particle diameter described in is not more than 200 mesh sieves.
3. nano titanium oxide dispersion described in, it is made up of the raw material of following weight part ratio:Nano TiO 2 material 60-
80 parts, styrene-acrylic emulsion 10-15 parts, amino propylamine dioleate 5-10 parts.
The beneficial effects of the present invention are:
Easily sought 1. raw material are inexpensive, product cost is not high.
2. properties of product are stable, do not lump, do not solidify, good weatherability.
Embodiment
In order that the technical means, the inventive features, the objects and the advantages of the present invention are readily apparent from understandable, tie below
Closing specific embodiment, the present invention is described in more detail, but present disclosure is not limited to this completely.
Embodiment 1:
1. a kind of nano composite diatom ooze paint, by following weight than raw material be made:Calcined diatomite 30Kg, dicalcium powder 10
Kg, the Kg of nano titanium oxide dispersion 3, the Kg of starch ether 3, the Kg of rock wool fibers 2.
2. calcined diatomite particle diameter described in is 200 mesh sieves.
3. described nano titanium oxide dispersion, by following weight than raw material be made:Nano TiO 2 material 60
Kg, the Kg of styrene-acrylic emulsion 10, the Kg of amino propylamine dioleate 7.
Embodiment 2
1. a kind of nano composite diatom ooze paint, by following weight than raw material be made:The Kg of calcined diatomite 35, dicalcium powder
12 Kg, the Kg of nano titanium oxide dispersion 5, the Kg of starch ether 5, the Kg of rock wool fibers 5.
2. calcined diatomite particle diameter described in is 150 mesh sieves.
3. described nano titanium oxide dispersion, by following weight than raw material be made:Nano TiO 2 material 75
Kg, the Kg of styrene-acrylic emulsion 10, the Kg of amino propylamine dioleate 8.
Embodiment 3
1. a kind of nano composite diatom ooze paint, by following weight than raw material be made:The Kg of calcined diatomite 40, dicalcium powder
13 Kg, the Kg of nano titanium oxide dispersion 2, the Kg of starch ether 2, the Kg of rock wool fibers 3.
2. calcined diatomite particle diameter described in is 100 mesh sieves.
Nano titanium oxide dispersion described in 3., by following weight than raw material be made:Nano TiO 2 material 80
Kg, the Kg of styrene-acrylic emulsion 14, amino propylamine dioleate 9Kg.
Embodiments of the invention are the foregoing is only, are not intended to limit the scope of the invention, it is every to utilize this hair
The equivalent structure or equivalent flow conversion that bright description is made, or directly or indirectly it is used in other related technology necks
Domain, it is included within the scope of the present invention.
Claims (3)
1. a kind of nano composite diatom ooze paint, it is characterised in that be made up of the raw material of following weight part ratio:Calcined diatomite
30-40 parts, dicalcium powder 10-15 parts, nano titanium oxide dispersion 1-5 parts, starch ether 1-5 parts, rock wool fibers 1-5 parts.
A kind of 2. nano composite diatom ooze paint according to claim 1, it is characterised in that described calcined diatomite grain
Footpath is not more than 200 mesh sieves.
A kind of 3. nano composite diatom ooze paint according to claim 1, it is characterised in that described nano titanium oxide
Dispersion liquid, it is made up of the raw material of following weight part ratio:Nano TiO 2 material 60-80 parts, styrene-acrylic emulsion 10-15 parts, aminopropan
Amine dioleate 5-10 parts.