CN1061100C - 能够稳定得到优良磁特性的晶粒取向硅钢薄板的制造方法 - Google Patents

能够稳定得到优良磁特性的晶粒取向硅钢薄板的制造方法 Download PDF

Info

Publication number
CN1061100C
CN1061100C CN95118685A CN95118685A CN1061100C CN 1061100 C CN1061100 C CN 1061100C CN 95118685 A CN95118685 A CN 95118685A CN 95118685 A CN95118685 A CN 95118685A CN 1061100 C CN1061100 C CN 1061100C
Authority
CN
China
Prior art keywords
silicon steel
atmosphere
steel plate
annealing
annealing step
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
CN95118685A
Other languages
English (en)
Chinese (zh)
Other versions
CN1139154A (zh
Inventor
小谷桂介
黑泽光正
河野正树
石飞宏威
坂口雅之
铃木隆史
西池氏裕
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JFE Steel Corp
Original Assignee
Kawasaki Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP16195595A external-priority patent/JP3463417B2/ja
Application filed by Kawasaki Steel Corp filed Critical Kawasaki Steel Corp
Publication of CN1139154A publication Critical patent/CN1139154A/zh
Application granted granted Critical
Publication of CN1061100C publication Critical patent/CN1061100C/zh
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/12—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D3/00—Diffusion processes for extraction of non-metals; Furnaces therefor
    • C21D3/02—Extraction of non-metals
    • C21D3/04—Decarburising
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/12—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties
    • C21D8/1244—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties characterised by the heat treatment
    • C21D8/1255—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of articles with special electromagnetic properties characterised by the heat treatment with diffusion of elements, e.g. decarburising, nitriding
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Physics & Mathematics (AREA)
  • Materials Engineering (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Mechanical Engineering (AREA)
  • Thermal Sciences (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Electromagnetism (AREA)
  • Manufacturing & Machinery (AREA)
  • Manufacturing Of Steel Electrode Plates (AREA)
  • Soft Magnetic Materials (AREA)
CN95118685A 1995-06-28 1995-09-30 能够稳定得到优良磁特性的晶粒取向硅钢薄板的制造方法 Expired - Lifetime CN1061100C (zh)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP16195595A JP3463417B2 (ja) 1994-09-30 1995-06-28 優れた磁気特性が安定して得られる方向性珪素鋼板の製造方法
JP161955/1995 1995-06-28
JP161955/95 1995-06-28

Publications (2)

Publication Number Publication Date
CN1139154A CN1139154A (zh) 1997-01-01
CN1061100C true CN1061100C (zh) 2001-01-24

Family

ID=15745243

Family Applications (1)

Application Number Title Priority Date Filing Date
CN95118685A Expired - Lifetime CN1061100C (zh) 1995-06-28 1995-09-30 能够稳定得到优良磁特性的晶粒取向硅钢薄板的制造方法

Country Status (6)

Country Link
US (1) US5620533A (enExample)
EP (1) EP0752480B9 (enExample)
KR (1) KR100259401B1 (enExample)
CN (1) CN1061100C (enExample)
DE (1) DE69527778T2 (enExample)
TW (1) TW299354B (enExample)

Families Citing this family (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3220362B2 (ja) * 1995-09-07 2001-10-22 川崎製鉄株式会社 方向性けい素鋼板の製造方法
KR100293141B1 (ko) 1997-04-16 2001-06-15 아사무라 타카싯 피막특성과 자기특성이 우수한 일방향성 전자강판과 그 제조방법및그제조방법에사용되는탈탄소둔설비
JP4673937B2 (ja) * 2009-04-06 2011-04-20 新日本製鐵株式会社 方向性電磁鋼板用鋼の処理方法及び方向性電磁鋼板の製造方法
CN103305745B (zh) * 2012-03-09 2016-04-27 宝山钢铁股份有限公司 一种高质量硅钢常化基板的生产方法
CN103525999A (zh) * 2013-09-13 2014-01-22 任振州 一种高磁感取向硅钢片的制备方法
CN110283981B (zh) * 2019-07-24 2020-12-11 武汉钢铁有限公司 一种能提高低温高磁感取向硅钢氧含量的生产方法

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0452122A2 (en) * 1990-04-13 1991-10-16 Kawasaki Steel Corporation Method of producing grain oriented silicon steel sheets having less iron loss
EP0488726A2 (en) * 1990-11-30 1992-06-03 Kawasaki Steel Corporation Thin decarburized grain oriented silicon steel sheet having improved coating and magnetic characteristics

Family Cites Families (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5250529A (en) 1975-10-20 1977-04-22 Seiko Instr & Electronics Silver oxide battery
GB1558257A (en) * 1978-01-09 1979-12-19 Korotkova L F Method of heat treating magnetic circuit sheets in relativvely high-carbon steel
US4200477A (en) * 1978-03-16 1980-04-29 Allegheny Ludlum Industries, Inc. Processing for electromagnetic silicon steel
US4213804A (en) * 1979-03-19 1980-07-22 Allegheny Ludlum Industries, Inc. Processing for cube-on-edge oriented silicon steel
US4897131A (en) * 1985-12-06 1990-01-30 Nippon Steel Corporation Grain-oriented electrical steel sheet having improved glass film properties and low watt loss
JPH0663033B2 (ja) * 1986-12-26 1994-08-17 川崎製鉄株式会社 鉄損劣化の少ない薄手方向性けい素鋼板の製造方法
EP0305966B1 (en) * 1987-08-31 1992-11-04 Nippon Steel Corporation Method for producing grain-oriented electrical steel sheet having metallic luster and excellent punching property
JPH01119622A (ja) * 1987-10-30 1989-05-11 Nippon Steel Corp 磁気特性およびグラス皮膜特性に優れた一方向性電磁鋼板の製造方法
JPH04350124A (ja) * 1991-05-28 1992-12-04 Kawasaki Steel Corp 薄板厚の一方向性珪素鋼板の製造方法
JP3301629B2 (ja) * 1992-03-16 2002-07-15 川崎製鉄株式会社 金属光沢を有しかつ磁気特性の優れた方向性けい素鋼板の製造方法

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0452122A2 (en) * 1990-04-13 1991-10-16 Kawasaki Steel Corporation Method of producing grain oriented silicon steel sheets having less iron loss
EP0488726A2 (en) * 1990-11-30 1992-06-03 Kawasaki Steel Corporation Thin decarburized grain oriented silicon steel sheet having improved coating and magnetic characteristics

Also Published As

Publication number Publication date
EP0752480B9 (en) 2003-04-09
CN1139154A (zh) 1997-01-01
DE69527778T2 (de) 2002-12-05
EP0752480A1 (en) 1997-01-08
US5620533A (en) 1997-04-15
DE69527778D1 (de) 2002-09-19
KR970001568A (ko) 1997-01-24
EP0752480B1 (en) 2002-08-14
KR100259401B1 (ko) 2000-06-15
TW299354B (enExample) 1997-03-01

Similar Documents

Publication Publication Date Title
US7833360B2 (en) Method of producing grain-oriented electrical steel sheet very excellent in magnetic properties
KR101294624B1 (ko) 구리를 포함하는 입자 방향성 실리콘 강철을 제조하기 위한 방법
CN102803521B (zh) 方向性电磁钢板的制造方法
JP2000355717A (ja) 被膜特性と磁気特性に優れた方向性けい素鋼板およびその製造方法
JPWO2019131853A1 (ja) 低鉄損方向性電磁鋼板とその製造方法
CN1061100C (zh) 能够稳定得到优良磁特性的晶粒取向硅钢薄板的制造方法
CN101573458B (zh) 高产率地生产具有优异磁特性的晶粒定向电工钢板的方法
JP5920387B2 (ja) 方向性電磁鋼板の製造方法
JP7582455B2 (ja) 方向性電磁鋼板およびその製造方法
JPH059666A (ja) 方向性電磁鋼板およびその製造方法
JP7623636B2 (ja) 方向性電磁鋼板の製造方法
JP3329641B2 (ja) 磁気特性及び鋼板端部形状に優れるＡｌ含有方向性電磁鋼板の製造方法
WO2022210503A1 (ja) 方向性電磁鋼板の製造方法
JP2002241906A (ja) 被膜特性および磁気特性に優れた方向性電磁鋼板
JP3061491B2 (ja) 磁気特性の優れた厚い板厚のグラス被膜の少ない一方向性電磁鋼板の製造方法
JPH11256242A (ja) グラス皮膜と磁気特性に極めて優れた方向性電磁鋼板の製造方法
JP3011609B2 (ja) 磁気特性の優れたグラス被膜の少ない一方向性電磁鋼板の製造方法
JPH11199939A (ja) 磁束密度が高く被膜特性に優れた方向性電磁鋼板の製造方法
JP4292804B2 (ja) 方向性電磁鋼板の製造方法
JP4604827B2 (ja) 一方向性電磁鋼板の製造方法
JP3463417B2 (ja) 優れた磁気特性が安定して得られる方向性珪素鋼板の製造方法
JPH05295441A (ja) グラス被膜特性が優れ、磁気特性の良好な高磁束密度方向性電磁鋼板の製造方法
JP2735929B2 (ja) 磁気特性および被膜特性に優れた方向性けい素鋼板の製造方法
JPH04350124A (ja) 薄板厚の一方向性珪素鋼板の製造方法
JP3885257B2 (ja) 方向性電磁鋼板の製造方法

Legal Events

Date Code Title Description
C06 Publication
PB01 Publication
C10 Entry into substantive examination
SE01 Entry into force of request for substantive examination
C14 Grant of patent or utility model
GR01 Patent grant
CX01 Expiry of patent term

Granted publication date: 20010124

EXPY Termination of patent right or utility model