CN106048239B - 一种含六价铬废渣的资源循环再利用的处理方法 - Google Patents
一种含六价铬废渣的资源循环再利用的处理方法 Download PDFInfo
- Publication number
- CN106048239B CN106048239B CN201610502468.XA CN201610502468A CN106048239B CN 106048239 B CN106048239 B CN 106048239B CN 201610502468 A CN201610502468 A CN 201610502468A CN 106048239 B CN106048239 B CN 106048239B
- Authority
- CN
- China
- Prior art keywords
- waste residue
- chromium
- recycles
- processing method
- processing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种含六价铬废渣的资源循环再利用的处理方法,属于铬渣的清洁处理及资源的循环再利用领域。该方法的具体步骤为:1)向含六价铬的废渣中加入水,混合均匀;2)向步骤1)所得溶液中加入矿化剂,充分搅拌,得混合液;所述矿化剂为氯酸钠、高氯酸钠和盐酸;3)采用水热法或直接加热处理混合液;4)加热处理后,使固液混合物自然冷却至室温,静置;5)将固体渣与含铬上清液分离,并将滤渣用水洗涤再干燥;6)将含铬溶液回收并返回工段中,或者进行回收铬处理。本方法工艺简单、成本低、见效快、处理量大、解毒彻底,可以实现全渣利用,具有较高的社会效益和经济效益。
Description
技术领域
本发明属于铬渣的清洁处理及资源的循环再利用领域,具体涉及一种含六价铬废渣的资源循环再利用的处理方法。
背景技术
铬盐生产及应用行业在生产过程中会产生大量的含六价铬废渣。在含铬废渣的转运和储存过程中,若长时间受到风化和雨水浸泡,大量六价铬会缓慢释放到环境当中,不仅对周边环境造成严重污染,而且也浪费了大量的金属铬资源。
目前针对含六价铬废渣的处理方法,核心思路还是将六价铬还原固定后堆存或填埋,主要包括湿法解毒、干法解毒和生物法。湿法解毒是通过碱或酸浸出将铬渣中的六价铬转移至水相,然后加入还原剂将六价铬还原为三价铬,以达到解毒作用;但是还原后的三价铬随环境的变化又会氧化成六价铬,不能彻底解毒,并且处理后的废渣难以得到应用还需占用大量的土地进行堆放。干法解毒是在高温还原性气氛下焙烧,将六价铬还原成三价铬并固封于烧结矿中以达到解毒的目的,但是该方法需要较高的解毒温度(一般在800度以上),而且锻烧产生的烟气将造成二次污染,需要增加除烟除尘设备,使得成本上升。生物法因其无污染、成本低等优点受到越来越多的关注,但生物法也存在一些缺点,如启动时间长、处理速度慢、有机物耗量大等。
上述这些方法都只是将六价铬还原并固定,铬仍然排放在环境中,不仅铬资源得不到回收和利用,而且存在“返黄”等二次污染。因此,较理想的方法是将铬渣中的铬提取并回用到工业中,从源头上减少铬的排放,变废为宝、化害为利,在减少污染的同时收获资源。
中国专利“一种从铬渣中回收六价铬资源的方法”(CN102191390A)采用常温下硫酸或盐酸浸出水溶性和酸溶性的六价铬,然后经过还原和沉淀收集浸出的铬资源。虽然该方法铬渣中铬的回收率可以达到60%-80%,但是处理后渣中仍残留部分六价铬,铬渣解毒不彻底,处理后渣难以综合利用,而且仍存在环境隐患。中国专利“循环再利用处理铬渣及废水工艺”(CN102699006A),在常温条件下先用酸将铬渣几乎完全溶解,然后分别加入不同的沉淀剂,将溶液中的混合离子沉淀和分离。这种方法需要消耗大量的酸和沉淀剂等化学试剂,而且工艺流程繁杂,处理成本较高。
发明内容
本发明的目的是针对现有含六价铬废渣处理技术的不足,提供一种含六价铬废渣的资源循环再利用的处理方法。该方法工艺简单、投资小、见效快、解毒彻底,可以充分提取六价铬、有效治理铬污染又不造成二次污染。采用该方法提取的铬,可以重新回用到生产中,如涂料、颜料、造纸等,实现变废为宝。采用该方法得到的滤渣可用于橡胶、塑料、肥料、油漆、纺织、造纸等行业。
本发明的目的通过以下技术方案实现。
一种含六价铬废渣的资源循环再利用的处理方法,步骤如下:
1)向含六价铬的废渣中加入水,混合均匀;
2)向步骤1)所得溶液中加入矿化剂,充分搅拌,得混合液;所述矿化剂为氯酸钠、高氯酸钠和盐酸;
3)采用水热法或直接加热处理步骤2)所得混合液;
4)将步骤3)所得固液混合物自然冷却至室温,静置;
5)将固体渣与含铬上清液分离,并将滤渣用水洗涤再干燥;
6)将含铬溶液回收并返回工段中,或者进行回收铬处理。
进一步地,步骤1)所述含六价铬的废渣中加入水后固液质量比为1:0.5 ~ 1:10(w/w)。
进一步地,步骤2)所述氯酸钠在混合液中的浓度为0.1 mol/L ~ 1 mol/L。
进一步地,步骤2)所述高氯酸钠在混合液中的浓度为0.1 mol/L ~ 1 mol/L。
进一步地,步骤2)所述混合液的pH为0.5 ~ 5。
进一步地,步骤3)所述水热法或直接加热的温度均控制在30℃ ~ 250℃。
进一步地,步骤3)中保温时间为2 ~ 12小时 。
进一步地,步骤4)所述静置的时间为0.5 ~ 48小时。
进一步地,步骤6)所述回收铬处理具体步骤为:向含铬溶液中加入还原剂,将溶液中六价铬还原为三价铬,再加入沉淀剂NaOH生产Cr(OH)3沉淀,最后把Cr(OH)3沉淀煅烧成Cr2O3。
一种含六价铬废渣的资源循环再利用的处理方法,步骤如下:
(1)将含六价铬的废渣和水按固液比1:0.5 ~ 1:10(w/w)混合均匀后,加入氯酸钠、高氯酸钠、盐酸,调节pH到0.5 ~ 5。
(2)充分搅拌,使废渣和溶液充分混合。
(3)设定温度为30℃ ~ 250℃,保温时间为2 ~ 12小时。
(4)停止加热,让其自然冷却,静置时间为0.5 ~ 48小时。
(5)水热处理或者加热处理结束后,废渣固体沉淀在底部,上层清液含浓度较高的六价铬。
(6)将固体渣与含铬上清液过滤分离,并将固体渣渣进行洗涤、脱水和干燥。
(7)分离出的上层清液和洗涤滤渣的水可回用到生产中或者进行回收铬处理。
本发明提供一种含六价铬废渣的循环再利用处理方法原理如下:
原渣中主要含有细小的二水硫酸钙颗粒,吸附有氯化钠、铬酸钠等。本发明加入矿化剂在进行水热处理或加热处理时,酸性条件下的铬渣中的六价铬更容易溶解到水相中,而硫酸钙在矿化剂溶液中重新结晶再生长,固体颗粒长大、比表面积减小,实现六价铬从颗粒表面脱附并分离。
原渣在经过上述方法处理之后,得到的脱毒滤渣,其主要成分为二水硫酸钙。加热处理后,先不立即分离固体渣和含铬上清液,而是让处理后的反应体系自然冷却,并陈化一段时间。自然冷却是因为若通过骤冷,冷却速度太快,高温条件下稳定的半水硫酸钙会迅速转变成低温条件下稳定的二水硫酸钙,从而造成浆体硬化和结块,给处理工艺带来困难。控制陈化时间可以调控废渣中硫酸钙晶粒生长程度,颗粒尺寸较大时,可以减小硫酸钙对六价铬的吸附能力,使洗涤分离六价铬时更加简单,洗脱用水量更少。
经水热法或加热法处理、陈化处理过后,废渣中硫酸钙粒径有所增大,废渣性状也随之改变:颗粒表面吸附作用减小,铬酸根离子也更容易脱附并溶于水中;同时颗粒比重增大,固液分离容易。经上述方法处理后,脱毒渣按国家标准(HJ/T 299-2007固体废物浸出毒性方法硫酸硝酸法)进行铬浸出测试,浸出六价铬含量<3mg/L,总铬含量<9 mg/L,低于国家标准(HJ/T 301-2007)一般工业固体废渣的限制。处理后的含六价铬上清液中的离子主要是钠离子、氯离子、氯酸根和铬酸根离子,有利于回收利用到生产工段。
与现有技术相比,本发明具有如下优点与技术效果:
本发明解决了含六价铬废渣浸出处理难、成本高、铬回收难等问题,而且废渣处理后的上层清液经过处理后回用到工业生产中或制成铬盐产品。处理后的滤渣浸出六价铬的含量低于国家标准(HJ/T 301-2007)一般工业固体废渣的限制,而且纯度高,可用于橡胶、塑料、肥料、油漆、纺织、造纸等行业。本方法工艺简单、成本低、见效快、处理量大、解毒彻底,可能实现全渣利用,具有较高的社会效益和经济效益。
具体实施方式
以下结合实施例对本发明作进一步地说明,但本发明的实施方式不限于此。
实施例1
1)取0.5 吨含六价铬的废渣放入水热釜中,再加入水使固液比为1:1(w/w),充分搅拌,加入氯酸钠、高氯酸钠、盐酸,并调节体系中氯酸钠的浓度为0.5 mol/L,高氯酸钠的浓度为1 mol/L,pH=0.5,设定温度为100℃,保温2 h。
2)2h后,停止加热,自然缓慢冷却至室温,静置24 h。
3)静置结束后,倒出上层含六价铬的溶液。对水热处理静置后的渣进行离心洗涤脱水,将滤渣干燥,得白色或白色偏黄固体。
4)将含铬溶液回用到生产中,或者汇集于废水处理站,进行还原、回收、净化处理,加入还原剂(如硫化钠、亚硫酸氢钠)和沉淀剂(NaOH),将溶液六价铬还原为三价铬,并生成Cr(OH)3沉淀,经处理后水可以达到国家排水标准。整个过程中,水在系统中可以循环利用。
5)最后产物分别是主要含硫酸钙的渣和主要含Cr(OH)3的铬泥,硫酸钙渣可以作为原料用于橡胶、塑料、肥料、农药、油漆、纺织、造纸等行业。铬泥可以煅烧成Cr2O3,实现铬的回收。
本实施例的原始铬渣浸出六价铬浓度为265 mg/L,处理后浸出六价铬浓度为1.31mg/L。
实施例2
取1吨含六价铬废渣放入水热釜中,再加入水使固液比为1:2(w/w),充分搅拌,加入氯酸钠、高氯酸钠、盐酸,并调节体系中氯酸钠的浓度为1 mol/L,高氯酸钠的浓度为0.5mol/L,加入盐酸至pH=5,充分搅拌,关闭水热釜,设定温度为140℃,保温5 h,停止加热后静置48 h。其他工艺过程与实施例1相同。
本实施例的原始铬渣浸出六价铬浓度为252 mg/L,处理后浸出六价铬浓度为0.92mg/L。
实施例3
取1吨含六价铬废渣放入水热釜中,再加入水使固液比为1:5(w/w),充分搅拌,加入氯酸钠、高氯酸钠、盐酸,并调节体系中氯酸钠的浓度为1 mol/L,高氯酸钠的浓度为1mol/L,加入盐酸至pH=0.5,充分搅拌,关闭水热釜,设定温度为30℃,保温12 h,停止加热后静置0.5 h。其他工艺过程与实施例1相同。
本实施例的原始铬渣浸出六价铬浓度为269 mg/L,处理后浸出六价铬浓度为0.72mg/L。
实施例4
取1.5吨含六价铬废渣放入水热釜中,再加入水使固液比为1:10(w/w),充分搅拌,加入氯酸钠、高氯酸钠、盐酸,并调节体系中氯酸钠的浓度为0.5 mol/L,高氯酸钠的浓度为0.1 mol/L,pH=4,充分搅拌,关闭水热釜,设定温度为240℃,保温2 h,停止加热后静置24h。其他工艺过程与实施例1相同。
本实施例的原始铬渣浸出六价铬浓度为274 mg/L,处理后浸出六价铬浓度为0.86mg/L。
实施例5
取2吨含六价铬废渣放入水热釜中,再加入水使固液比为1:0.5(w/w),充分搅拌,加入氯酸钠、高氯酸钠、盐酸,并调节体系中氯酸钠的浓度为0.1 mol/L,高氯酸钠的浓度为0.5 mol/L,pH=2,充分搅拌,关闭水热釜,设定温度为80℃,保温12 h,停止加热后静置24h。其他工艺过程与实施例1相同。
本实施例的原始铬渣浸出六价铬浓度为278 mg/L,处理后浸出六价铬浓度为0.91mg/L。
水热处理或加热处理后静置时间越短,处理后的渣的颗粒就越小,重新吸附六价铬的能力越强,故洗涤需要用的水更多,回收会更难。反之,静置时间越长,处理后的渣颗粒度会更大,洗涤用水更少,回收渣更方便,但静置时间过长,所得处理后废渣颜色会偏黄,影响废渣处理效果。
同理,根据权利要求限定的保护范围和本说明书给出的技术解决方案,还能给出多个实施案例,都属于本发明保护范围。
Claims (8)
1.一种含六价铬废渣的资源循环再利用的处理方法,所述废渣主要含有二水硫酸钙颗粒,吸附有氯化钠和铬酸钠;其特征在于,所述方法步骤如下:
1)向含六价铬的废渣中加入水,混合均匀;
2)向步骤1)所得浆液中加入氯酸钠、高氯酸钠、盐酸三种矿化剂,调节pH到0.5~5,充分搅拌,得混合液;
3)采用水热法或直接加热处理步骤2)所得混合液;
4)将步骤3)所得固液混合物自然冷却至室温,静置,控制废渣中硫酸钙晶粒生长程度;
5)将固体渣与含铬上清液分离,并将滤渣用水洗涤再干燥;
6)对步骤5)所得的含铬溶液进行回收铬处理。
2.根据权利要求1所述的一种含六价铬废渣的资源循环再利用的处理方法,其特征在于,步骤1)所述含六价铬的废渣中加入水后固液比w/w为1:0.5 ~ 1:10。
3.根据权利要求1所述的一种含六价铬废渣的资源循环再利用的处理方法,其特征在于,步骤2)所述氯酸钠在混合液中的浓度为0.1 mol/L ~ 1 mol/L。
4.根据权利要求1所述的一种含六价铬废渣的资源循环再利用的处理方法,其特征在于,步骤2)所述高氯酸钠在混合液中的浓度为0.1 mol/L ~ 1 mol/L。
5.根据权利要求1所述的一种含六价铬废渣的资源循环再利用的处理方法,其特征在于,步骤3)所述水热法或直接加热的温度均控制在30℃ ~ 250℃。
6.根据权利要求1所述的一种含六价铬废渣的资源循环再利用的处理方法,其特征在于,步骤3)中保温时间为2 ~ 12小时。
7.根据权利要求1所述的一种含六价铬废渣的资源循环再利用的处理方法,其特征在于,步骤4)所述静置的时间为0.5 ~ 48小时。
8.根据权利要求1所述的一种含六价铬废渣的资源循环再利用的处理方法,其特征在于,步骤6)所述回收铬处理具体步骤为:向含铬溶液中加入还原剂,将溶液中六价铬还原为三价铬,再加入沉淀剂NaOH生产Cr(OH)3沉淀,最后把Cr(OH)3沉淀煅烧成Cr2O3。