CN105985718A - 一种聚酯漆包线漆及其制备方法 - Google Patents
一种聚酯漆包线漆及其制备方法 Download PDFInfo
- Publication number
- CN105985718A CN105985718A CN201510060944.2A CN201510060944A CN105985718A CN 105985718 A CN105985718 A CN 105985718A CN 201510060944 A CN201510060944 A CN 201510060944A CN 105985718 A CN105985718 A CN 105985718A
- Authority
- CN
- China
- Prior art keywords
- polyester
- acid
- wire enamel
- ethylene glycol
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种聚酯漆包线漆及其制备方法,其包括的各组分及其配比为:二聚酸和对苯二甲酸摩尔比为1∶1~1∶20;低聚聚酯二元醇和乙二醇的摩尔比为1∶1~1∶20;二聚酸和对苯二甲酸总摩尔量与低聚聚酯二元醇和乙二醇总摩尔量的比为1∶1,二聚酸和对苯二甲酸总摩尔量与甘油摩尔量的比为1∶0.6。本发明通过在制备聚酯时引入带疏水侧链的二聚酸和低聚聚酯二元醇,从而大大提升漆包线漆的耐水性,不需要做额外处理即可达到良好的耐水效果。
Description
技术领域
本发明为一种聚酯漆包线漆及其制备方法,涉及到一种耐水性聚酯漆包线漆及其制备方法。
背景技术
在一些特殊的场合需要用到耐水性较好的漆包线漆,而目前耐水性漆是以环氧树脂为主体,其它如聚酰胺酰亚胺、缩醛、聚海因等也是耐水性比较好的漆,而聚酯、聚酰亚胺,聚氨酯,非THEIC聚酯亚胺等易被水解,耐水性较差 , 然而即使是耐水性的漆料,作为漆包线,由于漆层较薄,单独使用也有一定限度,因此在一些特殊场合,如在水中工作的马达使用时还需在漆包线外层覆盖一层聚乙烯后再将整个线圈用环氧树脂处理后使用。这样涂制漆包线过程较为复杂,降低了生产效率。我们通过在制备聚酯时引入带疏水侧链的二聚酸和低聚聚酯二元醇,从而大大提升漆包线漆的耐水性,不需要做额外处理即可达到良好的耐水效果。
发明内容
本发明的目的在于提供一种耐水性聚酯漆包线漆及其制备方法。
本发明通过在制备聚酯时引入带疏水侧链的二聚酸和低聚聚酯二元醇,从而提升漆包线漆的耐水性,达到良好的耐水效果。
本发明涉及的聚酯漆包线漆组分及其配比如下:
带疏水侧链的二聚酸和对苯二甲酸摩尔比为1∶1~1∶20;低聚聚酯二元醇和乙二醇的摩尔比为1∶1~1∶20;带疏水侧链的二聚酸和对苯二甲酸总摩尔量与低聚聚酯二元醇和乙二醇总摩尔量的比为1:1至1:1.1,带疏水侧链的二聚酸和对苯二甲酸总摩尔量与甘油摩尔量的比为1∶0.6至1∶0.7。
本发明所述聚酯漆包线漆的制备方法包括:
首先采用带疏水侧链的二聚酸、低聚聚酯二元醇、对苯二甲酸、乙二醇、甘油来合成耐水性聚酯树脂。该制备过程包括,在搅拌状态下依次加入乙二醇、低聚聚酯二元醇、甘油、带疏水侧链的二聚酸和对苯二甲酸,投料完毕后升温至120-160℃。然后以每小时8-10℃的速度升温至200-240℃,保温2-3小时,抽真空至理论出液量。加入若干甲酚溶剂降温至160-180℃,保温2-3小时。取上述制备好的树脂,加入若干甲酚和二甲苯搅拌稀释至所需固含量。
进一步优选的方案是:所述带疏水侧链的二聚酸由十八碳不饱和脂肪酸通过白土催化二聚法制得。
进一步优选的方案是:所述低聚聚酯二元醇由己二酸与乙二醇缩合制得。
与现有技术相比,用本发明的耐水性聚酯漆包线漆具有以下优点:
1, 在涂制耐水漆包线时无需其他步骤,不用另外进行防水处理,一步完成涂制,大大提高生产效率。
2,
制成的漆包线耐水性大大提升,常温下耐水时间大于等于150小时,远大于现有技术50H以下的耐水时间。
3,
制成的漆包线漆没有相容性问题,适应性广,工艺余度宽。
具体实施方式
比较例
采用现有技术聚酯漆包线漆(如丹阳四达化工有限公司的STE 30L产品),高速涂制漆包线。
实施例1
首先采用妥尔油脂肪酸通过白土催化二聚法制得二聚酸,通过己二酸与乙二醇的缩合获得低聚聚酯二元醇。
在搅拌状态下按下述配比依次加入0.5份二聚酸、1.5份对苯二甲酸、1份低聚聚酯二元醇,1份乙二醇,1.2份甘油,投料完毕后升温至140℃。然后以每小时10℃的速度升温至220℃,保温2小时,抽真空至出液量。加入甲酚溶剂降温至180℃,保温3小时。
取上述制备好的树脂,加入甲酚和二甲苯搅拌稀释至所需固含量。
使用按上述步骤制备的耐水性聚酯漆包线漆涂制漆包线。
实施例2
首先采用妥尔油脂肪酸通过白土催化二聚法制得二聚酸,通过己二酸与乙二醇的缩合获得低聚聚酯二元醇。
在搅拌状态下按下述配比依次加入1份二聚酸、1份对苯二甲酸、1份低聚聚酯二元醇,2份乙二醇,1.2份甘油,投料完毕后升温至140℃。然后以每小时10℃的速度升温至220℃,保温2小时,抽真空至出液量。加入甲酚溶剂降温至180℃,保温3小时。
取上述制备好的树脂,加入甲酚和二甲苯搅拌稀释至所需固含量。
使用按上述步骤制备的耐水性聚酯漆包线漆涂制漆包线。
实施例3
首先采用亚油酸通过白土催化二聚法制得二聚酸,通过己二酸与乙二醇的缩合获得低聚聚酯二元醇。
在搅拌状态下按下述配比依次加入1份二聚酸、2份对苯二甲酸、1份低聚聚酯二元醇,1份乙二醇,1.8份甘油,投料完毕后升温至140℃。然后以每小时10℃的速度升温至220℃,保温2小时,抽真空至出液量。加入甲酚溶剂降温至180℃,保温3小时。
取上述制备好的树脂,加入甲酚和二甲苯搅拌稀释至所需固含量。
使用按上述步骤制备的耐水性聚酯漆包线漆涂制漆包线。
实施例4
首先采用亚油酸通过白土催化二聚法制得二聚酸,通过己二酸与乙二醇的缩合获得低聚聚酯二元醇。
在搅拌状态下按下述配比依次加入1份二聚酸、3份对苯二甲酸、1份低聚聚酯二元醇,3份乙二醇,2.4份甘油,投料完毕后升温至140℃。然后以每小时10℃的速度升温至220℃,保温2小时,抽真空至出液量。加入甲酚溶剂降温至180℃,保温3小时。
取上述制备好的树脂,加入甲酚和二甲苯搅拌稀释至所需固含量。
使用按上述步骤制备的耐水性聚酯漆包线漆涂制漆包线。
比较例与实施例性能测试列表:
比较例 | 实施例1 | 实施例2 | 实施例3 | 实施例4 | |
圆铜线直径/mm | 0.600 | 0.600 | 0.600 | 0.600 | 0.600 |
漆包线外径/mm | 0.623 | 0.622 | 0.621 | 0.622 | 0.621 |
外观 | 光滑 | 光滑 | 光滑 | 光滑 | 光滑 |
耐水时间(h,25℃) | 30 | 180 | 200 | 230 | 225 |
Claims (4)
1.一种聚酯漆包线漆,其特征在于:其包括的各组分及其配比:带疏水侧链的二聚酸和对苯二甲酸摩尔比为1∶1~1∶20;低聚聚酯二元醇和乙二醇的摩尔比为1∶1~1∶20;带疏水侧链的二聚酸和对苯二甲酸总摩尔量与低聚聚酯二元醇和乙二醇总摩尔量的比为1:1至1:1.1,带疏水侧链的二聚酸和对苯二甲酸总摩尔量与甘油摩尔量的比为1∶0.6至1∶0.7。
2. 一种权利要求1所述的聚酯漆包线漆的制备方法,包括:
1)在搅拌状态下依次加入乙二醇、低聚聚酯二元醇、甘油、带疏水侧链的二聚酸和对苯二甲酸,投料完毕后升温至120-160℃;
2)然后以每小时8-10℃的速度升温至200-240℃,保温2-3小时,抽真空;
3)加入若干甲酚溶剂降温至160-180℃,保温2-3小时;
4)取上述制备好的树脂,加入甲酚和二甲苯搅拌,稀释至所需固含量。
3.按照权利要求2所述的聚酯漆包线漆的制备方法,其特征在于:所述的带疏水侧链的二聚酸由十八碳不饱和脂肪酸通过白土催化二聚法制得。
4.按照权利要求2或3所述的聚酯漆包线漆的制备方法,其特征在于:所述低聚聚酯二元醇由己二酸与乙二醇缩合制得。