CN105985712A - 一种耐水性较好的聚酯漆包线漆的制备方法 - Google Patents

一种耐水性较好的聚酯漆包线漆的制备方法 Download PDF

Info

Publication number
CN105985712A
CN105985712A CN201510060506.6A CN201510060506A CN105985712A CN 105985712 A CN105985712 A CN 105985712A CN 201510060506 A CN201510060506 A CN 201510060506A CN 105985712 A CN105985712 A CN 105985712A
Authority
CN
China
Prior art keywords
preparation
polyester
wire enamel
acid
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510060506.6A
Other languages
English (en)
Inventor
张建清
姚扎西
张杏荣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DANYANG STAR CHEMICAL Co Ltd
Original Assignee
DANYANG STAR CHEMICAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DANYANG STAR CHEMICAL Co Ltd filed Critical DANYANG STAR CHEMICAL Co Ltd
Priority to CN201510060506.6A priority Critical patent/CN105985712A/zh
Publication of CN105985712A publication Critical patent/CN105985712A/zh
Pending legal-status Critical Current

Abstract

一种耐水性较好的聚酯漆包线漆的制备方法，包括：1）在搅拌状态下依次加入0.51份二聚酸、1.52份对苯二甲酸、1份低聚聚酯二元醇，1份乙二醇，1.22份甘油，投料完毕后升温至140℃；2）然后以每小时10.5℃的速度升温至225℃，保温2.2小时，抽真空；3）加入若干甲酚溶剂降温至180℃，保温3.2小时；4）取上述制备好的树脂，加入甲酚和二甲苯搅拌，稀释至所需固含量。

Description

一种耐水性较好的聚酯漆包线漆的制备方法
技术领域
本发明为一种聚酯漆包线漆及其制备方法，涉及到一种耐水性聚酯漆包线漆及其制备方法。
背景技术
在一些特殊的场合需要用到耐水性较好的漆包线漆，而目前耐水性漆是以环氧树脂为主体，其它如聚酰胺酰亚胺、缩醛、聚海因等也是耐水性比较好的漆，而聚酯、聚酰亚胺，聚氨酯，非THEIC聚酯亚胺等易被水解，耐水性较差 , 然而即使是耐水性的漆料，作为漆包线，由于漆层较薄，单独使用也有一定限度，因此在一些特殊场合，如在水中工作的马达使用时还需在漆包线外层覆盖一层聚乙烯后再将整个线圈用环氧树脂处理后使用。这样涂制漆包线过程较为复杂，降低了生产效率。我们通过在制备聚酯时引入带疏水侧链的二聚酸和低聚聚酯二元醇，从而大大提升漆包线漆的耐水性，不需要做额外处理即可达到良好的耐水效果。
发明内容
本发明的目的在于提供一种耐水性聚酯漆包线漆及其制备方法。
本发明通过在制备聚酯时引入带疏水侧链的二聚酸和低聚聚酯二元醇，从而提升漆包线漆的耐水性，达到良好的耐水效果。
本发明涉及的耐水性聚酯漆包线漆组分及其配比如下：
带疏水侧链的二聚酸和对苯二甲酸摩尔比为1∶1～1∶22；低聚聚酯二元醇和乙二醇的摩尔比为1∶1～1∶22；带疏水侧链的二聚酸和对苯二甲酸总摩尔量与低聚聚酯二元醇和乙二醇总摩尔量的比为1：1至1：1.2，带疏水侧链的二聚酸和对苯二甲酸总摩尔量与甘油摩尔量的比为1∶0.5至1∶0.7。
上述耐水性聚酯漆包线漆的制备方法包括：
首先采用带疏水侧链的二聚酸、低聚聚酯二元醇、对苯二甲酸、乙二醇、甘油来合成耐水性聚酯树脂。该制备过程包括，在搅拌状态下依次加入乙二醇、低聚聚酯二元醇、甘油、带疏水侧链的二聚酸和对苯二甲酸，投料完毕后升温至118-158℃。然后以每小时8-12℃的速度升温至205-245℃，保温1.5-3小时，抽真空（优选抽真空至理论出液量）。加入若干甲酚溶剂降温至170-190℃，保温2.5-3.5小时。取上述制备好的树脂，加入若干甲酚和二甲苯搅拌稀释至所需固含量。
进一步优选的方案是：聚酯漆包线漆的制备方法，其特征在于包括：
1）在搅拌状态下依次加入1份二聚酸、1份对苯二甲酸、1份低聚聚酯二元醇，2份乙二醇，1.2份甘油，投料完毕后升温至145℃；
2）然后以每小时9℃的速度升温至206℃，保温2小时，抽真空；
3）加入若干甲酚溶剂降温至185℃，保温3.2小时；
4）取上述制备好的树脂，加入甲酚和二甲苯搅拌，稀释至所需固含量。
所述带疏水侧链的二聚酸由十八碳不饱和脂肪酸通过白土催化二聚法制得。
进一步优选的方案是：所述低聚聚酯二元醇由己二酸与乙二醇缩合制得。
与现有技术相比，用本发明的耐水性聚酯漆包线漆具有以下优点：
1， 在涂制耐水漆包线时无需其他步骤，不用另外进行防水处理，一步完成涂制，大大提高生产效率。
2， 制成的漆包线耐水性大大提升,常温下耐水时间大于等于150小时，远大于现有技术50H以下的耐水时间。
3， 制成的漆包线漆没有相容性问题，适应性广，工艺余度宽。
具体实施方式
比较例
采用现有技术聚酯漆包线漆（如丹阳四达化工有限公司的STE 30L产品），高速涂制漆包线。
实施例1
首先采用妥尔油脂肪酸通过白土催化二聚法制得二聚酸，通过己二酸与乙二醇的缩合获得低聚聚酯二元醇。
在搅拌状态下按下述配比依次加入0.51份二聚酸、1.52份对苯二甲酸、1份低聚聚酯二元醇，1份乙二醇，1.22份甘油，投料完毕后升温至140℃。然后以每小时10.5℃的速度升温至225℃，保温2.2小时，抽真空至出液量。加入甲酚溶剂降温至180℃，保温3.2小时。
取上述制备好的树脂，加入甲酚和二甲苯搅拌稀释至所需固含量。
使用按上述步骤制备的耐水性聚酯漆包线漆涂制漆包线。
实施例2
首先采用妥尔油脂肪酸通过白土催化二聚法制得二聚酸，通过己二酸与乙二醇的缩合获得低聚聚酯二元醇。
在搅拌状态下按下述配比依次加入1份二聚酸、1份对苯二甲酸、1份低聚聚酯二元醇，2份乙二醇，1.2份甘油，投料完毕后升温至145℃。然后以每小时9℃的速度升温至206℃，保温2小时，抽真空至出液量。加入甲酚溶剂降温至185℃，保温3.2小时。
取上述制备好的树脂，加入甲酚和二甲苯搅拌稀释至所需固含量。
使用按上述步骤制备的耐水性聚酯漆包线漆涂制漆包线。
实施例3
首先采用亚油酸通过白土催化二聚法制得二聚酸，通过己二酸与乙二醇的缩合获得低聚聚酯二元醇。
在搅拌状态下按下述配比依次加入1份二聚酸、2份对苯二甲酸、1份低聚聚酯二元醇，1份乙二醇，1.8份甘油，投料完毕后升温至120℃。然后以每小时8.5℃的速度升温至240℃，保温2.4小时，抽真空至出液量。加入甲酚溶剂降温至186℃，保温2.3小时。
取上述制备好的树脂，加入甲酚和二甲苯搅拌稀释至所需固含量。
使用按上述步骤制备的耐水性聚酯漆包线漆涂制漆包线。
实施例4
首先采用亚油酸通过白土催化二聚法制得二聚酸，通过己二酸与乙二醇的缩合获得低聚聚酯二元醇。
在搅拌状态下按下述配比依次加入1份二聚酸、3份对苯二甲酸、1份低聚聚酯二元醇，3份乙二醇，2.4份甘油，投料完毕后升温至148℃。然后以每小时11℃的速度升温至230℃，保温2.7小时，抽真空至出液量。加入甲酚溶剂降温至181℃，保温2.3小时。
取上述制备好的树脂，加入甲酚和二甲苯搅拌稀释至所需固含量。
使用按上述步骤制备的耐水性聚酯漆包线漆涂制漆包线。
比较例与实施例性能测试列表：
比较例 实施例1 实施例2 实施例3 实施例4
圆铜线直径/mm 0.600 0.600 0.600 0.600 0.600
漆包线外径/mm 0.623 0.622 0.621 0.622 0.621
外观 光滑 光滑 光滑 光滑 光滑
耐水时间（h，25℃） 30 180 200 230 225

Claims (3)

1.一种聚酯漆包线漆的制备方法，其特征在于包括：
1）在搅拌状态下依次加入1份二聚酸、1份对苯二甲酸、1份低聚聚酯二元醇，2份乙二醇，1.2份甘油，投料完毕后升温至145℃；
2）然后以每小时9℃的速度升温至206℃，保温2小时，抽真空；
3）加入若干甲酚溶剂降温至185℃，保温3.2小时；
4）取上述制备好的树脂，加入甲酚和二甲苯搅拌，稀释至所需固含量。
2. 按照权利要求2所述的聚酯漆包线漆的制备方法，其特征在于：所述的带疏水侧链的二聚酸由十八碳不饱和脂肪酸通过白土催化二聚法制得。
3. 按照权利要求2所述的聚酯漆包线漆的制备方法，其特征在于：所述低聚聚酯二元醇由己二酸与乙二醇缩合制得。
CN201510060506.6A 2015-02-05 2015-02-05 一种耐水性较好的聚酯漆包线漆的制备方法 Pending CN105985712A (zh)