CN105776862A - 高性能陶瓷容器用窑变高粱红花釉及其制备方法 - Google Patents

高性能陶瓷容器用窑变高粱红花釉及其制备方法 Download PDF

Info

Publication number
CN105776862A
CN105776862A CN201610174692.0A CN201610174692A CN105776862A CN 105776862 A CN105776862 A CN 105776862A CN 201610174692 A CN201610174692 A CN 201610174692A CN 105776862 A CN105776862 A CN 105776862A
Authority
CN
China
Prior art keywords
parts
glaze
preparation
sorghum
safflower
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610174692.0A
Other languages
English (en)
Inventor
葛宜翔
何畏
孙素强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Yixiang Ceramic Technology Co Ltd
Original Assignee
Jiangsu Yixiang Ceramic Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Yixiang Ceramic Technology Co Ltd filed Critical Jiangsu Yixiang Ceramic Technology Co Ltd
Priority to CN201610174692.0A priority Critical patent/CN105776862A/zh
Publication of CN105776862A publication Critical patent/CN105776862A/zh
Pending legal-status Critical Current

Abstract

本发明涉一种陶瓷釉料及其制备方法，具体为高性能陶瓷容器用窑变高粱红花釉及其制备方法。高性能陶瓷容器用窑变高粱红花釉及其制备方法，包括以下步骤：以下釉料按照重量份数组成：长石30份，石英5份，高岭土5份，滑石20份，玻璃粉10份，白云石15份，氧化铬2份，氧化钴5份，氧化铁5份，钛白粉7份；釉料分别进行球磨，过筛后调制成釉浆；在胚体上施釉后，在1220～1250℃煅烧坯体20～23小时。本发明提供的高性能陶瓷容器用窑变高粱红花釉及其制备方法，生产陶瓷制品的成品率高，并且工艺简单，降低了生产成本。

Description

高性能陶瓷容器用窑变高粱红花釉及其制备方法
技术领域
本发明涉一种陶瓷釉料及其制备方法，具体为高性能陶瓷容器用窑变高粱红花釉及其制备方法。
背景技术
花釉是指瓷器釉面上同时出现两种或两种以上颜色，色彩自然交汇融合，显现各种各样的色调和质感的复色釉，是一种具有特殊装饰效果的釉。传统的生产工艺是在瓷器坯体上施以两种或两种以上不同熔点的釉，在釉烧过程中由于不同釉料熔点不同而相对流动，使釉面产生丰富多彩的流纹和底面釉之间的过渡颜色。但是这种施釉的工艺方法烦琐复杂，存在着生产成本高，成品率低等问题，难以适应大批量生产。
发明内容
针对上述技术问题，本发明提供一种成品率高、工艺简单，生产成本低的红花釉制备方法。
本发明的技术方案如下：
高性能陶瓷容器用窑变高粱红花釉及其制备方法，包括以下步骤：
由以下釉料按照重量份数组成：长石30份，石英5份，高岭土5份，滑石20份，玻璃粉10份，白云石15份，氧化铬2份，氧化钴5份，氧化铁5份，钛白粉7份；釉料分别进行球磨，过筛后调制成釉浆；在胚体上施釉后，在1220～1250℃煅烧坯体20～23小时。
本发明提供的高性能陶瓷容器用窑变高粱红花釉及其制备方法，生产陶瓷制品的成品率高，并且工艺简单，降低了生产成本。
具体实施方式
结合具体实施例说明本发明的具体实施方式：
高性能陶瓷容器用窑变高粱红花釉及其制备方法，包括以下步骤：
以下釉料按照重量份数组成：长石30份，石英5份，高岭土5份，滑石20份，玻璃粉10份，白云石15份，氧化铬2份，氧化钴5份，氧化铁5份，钛白粉7份；釉料分别进行球磨，过筛后调制成釉浆；在胚体上施釉后，在1220～1250℃煅烧坯体20～23小时。

Claims (1)

1.高性能陶瓷容器用窑变高粱红花釉及其制备方法，其特征在于：包括以下步骤由以下釉料按照重量份数组成：长石30份，石英5份，高岭土5份，滑石20份，玻璃粉10份，白云石15份，氧化铬2份，氧化钴5份，氧化铁5份，钛白粉7份；釉料分别进行球磨，过筛后调制成釉浆；在胚体上施釉后，在1220～1250℃煅烧坯体20～23小时。
CN201610174692.0A 2016-03-25 2016-03-25 高性能陶瓷容器用窑变高粱红花釉及其制备方法 Pending CN105776862A (zh)