CN105543911A - 氯化1-庚基-3-甲基咪唑/氯化镍体系电镀液 - Google Patents

氯化1-庚基-3-甲基咪唑/氯化镍体系电镀液 Download PDF

Info

Publication number
CN105543911A
CN105543911A CN201511009332.7A CN201511009332A CN105543911A CN 105543911 A CN105543911 A CN 105543911A CN 201511009332 A CN201511009332 A CN 201511009332A CN 105543911 A CN105543911 A CN 105543911A
Authority
CN
China
Prior art keywords
methylimidazole
heptyl
chlorination
chloride
nickelous chloride
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201511009332.7A
Other languages
English (en)
Inventor
田鹏
黄涛
康艳红
刘丽艳
曾敬
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shenyang Normal University
Original Assignee
Shenyang Normal University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shenyang Normal University filed Critical Shenyang Normal University
Priority to CN201511009332.7A priority Critical patent/CN105543911A/zh
Publication of CN105543911A publication Critical patent/CN105543911A/zh
Pending legal-status Critical Current

Abstract

氯化1-庚基-3-甲基咪唑/氯化镍体系电镀液(g·kg-1)，其由以下成份组成：氯化1-庚基-3-甲基咪唑:620～625，氯化镍：310～314，氯化铁：31～34，乙二醇：5～8，明胶：1～3，氯化钠(NaCl):20～25。氯化1-庚基-3-甲基咪唑/氯化镍体系电镀液，其电化学窗口较宽，电沉积过程中副反应较少，因此得到的金属质量更高；电镀液的操作温度范围相对较宽，有利于研究电沉积工艺的影响。此电镀液不存在水化、水解、析氢等问题，具有腐蚀小、污染小等绿色溶剂应具备的性质。

Description

氯化1-庚基-3-甲基咪唑/氯化镍体系电镀液
技术领域
本发明涉及一种电镀液，尤其是一种氯化1-庚基-3-甲基咪唑/氯化镍体系电镀液。
背景技术
镍铁等磁性合金镀层的研发历来受到重视，并已有大量的研究报告和应用报告。磁性的镍钴镀层包括软磁与开发定向和垂直记忆等已发展至五元合金镀层。利用不同的添加剂、采用脉冲或换向电流以及交直流的叠加等不同的馈电方案，可以有效的调节镀层的结构和取向。所以用电镀方法来制备磁性元件并不困难。例如其异常共沉积的机理、各种添加剂和电极上吸附的特性和影响、电流波形和参数包括脉冲和换向及脉动的作用，及至极薄的镍铁薄膜的制备等等。
为实现上述目的，本发明采用的技术方案是：氯化1-庚基-3-甲基咪唑/氯化镍体系电镀液的配方：
氯化1-庚基-3-甲基咪唑:620～625g·kg-1
氯化镍：310～314g·kg-1
氯化铁：31～34g·kg-1
乙二醇：5～8g·kg-1
明胶：1～3g·kg-1
氯化钠(NaCl):20～25g·kg-1
含铁12％～40％的镍铁合金镀层外观亮白，而且比纯镍镀层硬和韧，其防腐蚀性能与纯镍相当。用镍铁代替纯镍层来打底，不仅成本降低而且外观也更好。但这种镀层不能加太多的铁，否则表面在遭到腐蚀后便会出现铁的特征性黄色腐蚀产物。所以在生产中用镍铁来代镍时往往先镀上一层占2/3厚度的含铁多的合金，然后覆盖上低铁的合金，这样不仅成本低、效果好而且不会出现黄锈。
氯化1-庚基-3-甲基咪唑/氯化镍体系电镀液，其电化学窗口较宽，电沉积过程中副反应较少，因此得到的金属质量更高；电镀液的操作温度范围相对较宽，有利于研究电沉积工艺的影响。此电镀液不存在水化、水解、析氢等问题，具有腐蚀小、污染小等绿色溶剂应具备的性质。
具体实施方式
使用原料：氯化1-庚基-3-甲基咪唑，氯化镍，氯化铁，乙二醇，明胶，氯化钠。
实施例1：
氯化1-庚基-3-甲基咪唑:620
氯化镍：314
氯化铁：34
乙二醇：8
明胶：1
氯化钠(NaCl):23
取上述组分，混合成1000克的氯化1-庚基-3-甲基咪唑/氯化镍体系电镀液。
实施例2：
氯化1-庚基-3-甲基咪唑:622
氯化镍：312
氯化铁：33
乙二醇：7
明胶：1
氯化钠(NaCl):25
取上述组分，混合成1000克的氯化1-庚基-3-甲基咪唑/氯化镍体系电镀液。
实施例3：
氯化1-庚基-3-甲基咪唑:622
氯化镍：314
氯化铁：31
乙二醇：6
明胶：3
氯化钠(NaCl):24
取上述组分，混合成1000克的氯化1-庚基-3-甲基咪唑/氯化镍体系电镀液。
实施例4：
氯化1-庚基-3-甲基咪唑:623
氯化镍：313
氯化铁：32
乙二醇：7
明胶：2
氯化钠(NaCl):23
取上述组分，混合成1000克的氯化1-庚基-3-甲基咪唑/氯化镍体系电镀液。
实施例5：
氯化1-庚基-3-甲基咪唑:623
氯化镍：314
氯化铁：31
乙二醇：8
明胶：3
氯化钠(NaCl):21
取上述组分，混合成1000克的氯化1-庚基-3-甲基咪唑/氯化镍体系电镀液。
实施例6：
氯化1-庚基-3-甲基咪唑:624
氯化镍：313
氯化铁：32
乙二醇：6
明胶：1
氯化钠(NaCl):24
取上述组分，混合成1000克的氯化1-庚基-3-甲基咪唑/氯化镍体系电镀液。
实施例7：
氯化1-庚基-3-甲基咪唑:624
氯化镍：312
氯化铁：34
乙二醇：5
明胶：3
氯化钠(NaCl):22
取上述组分，混合成1000克的氯化1-庚基-3-甲基咪唑/氯化镍体系电镀液。
实施例8：
氯化1-庚基-3-甲基咪唑:625
氯化镍：313
氯化铁：33
乙二醇：7
明胶：2
氯化钠(NaCl):20
取上述组分，混合成1000克的氯化1-庚基-3-甲基咪唑/氯化镍体系电镀液。
实施例9：
氯化1-庚基-3-甲基咪唑:625
氯化镍：310
氯化铁：33
乙二醇：7
明胶：3
氯化钠(NaCl):22
取上述组分，混合成1000克的氯化1-庚基-3-甲基咪唑/氯化镍体系电镀液。
用本发明电镀时，要求溶液pH:4.0～4.4，溶液温度(℃)：110～119，电流密度(A/dm2):3.0～3.6。

Claims (10)

1.氯化1-庚基-3-甲基咪唑/氯化镍体系电镀液，其特征在于：氯化1-庚基-3-甲基咪唑/氯化镍体系电镀液的配方由以下组成：
氯化1-庚基-3-甲基咪唑:620～625g·kg-1
氯化镍：310～314g·kg-1
氯化铁：31～34g·kg-1
乙二醇：5～8g·kg-1
明胶：1～3g·kg-1
氯化钠:20～25g·kg-1。
2.如权利要求1所述的氯化1-庚基-3-甲基咪唑/氯化镍体系电镀液，其特征在于：氯化1-庚基-3-甲基咪唑/氯化镍体系电镀液的配方由以下组成：
氯化1-庚基-3-甲基咪唑:620g·kg-1
氯化镍：314g·kg-1
氯化铁：34g·kg-1
乙二醇：8g·kg-1
明胶：1g·kg-1
氯化钠:23g·kg-1。
3.如权利要求1所述的氯化1-庚基-3-甲基咪唑/氯化镍体系电镀液，其特征在于：氯化1-庚基-3-甲基咪唑/氯化镍体系电镀液的配方由以下组成：
氯化1-庚基-3-甲基咪唑:622g·kg-1
氯化镍：312g·kg-1
氯化铁：33g·kg-1
乙二醇：7g·kg-1
明胶：1g·kg-1
氯化钠:25g·kg-1。
4.如权利要求1所述的氯化1-庚基-3-甲基咪唑/氯化镍体系电镀液，其特征在于：氯化1-庚基-3-甲基咪唑/氯化镍体系电镀液的配方由以下组成：
氯化1-庚基-3-甲基咪唑:622g·kg-1
氯化镍：314g·kg-1
氯化铁：31g·kg-1
乙二醇：6g·kg-1
明胶：3g·kg-1
氯化钠:24g·kg-1。
5.如权利要求1所述的氯化1-庚基-3-甲基咪唑/氯化镍体系电镀液，其特征在于：氯化1-庚基-3-甲基咪唑/氯化镍体系电镀液的配方由以下组成：
氯化1-庚基-3-甲基咪唑:623g·kg-1
氯化镍：313g·kg-1
氯化铁：32g·kg-1
乙二醇：7g·kg-1
明胶：2g·kg-1
氯化钠:23g·kg-1。
6.如权利要求1所述的氯化1-庚基-3-甲基咪唑/氯化镍体系电镀液，其特征在于：氯化1-庚基-3-甲基咪唑/氯化镍体系电镀液的配方由以下组成：
氯化1-庚基-3-甲基咪唑:623g·kg-1
氯化镍：314g·kg-1
氯化铁：31g·kg-1
乙二醇：8g·kg-1
明胶：3g·kg-1
氯化钠:21g·kg-1。
7.如权利要求1所述的氯化1-庚基-3-甲基咪唑/氯化镍体系电镀液，其特征在于：氯化1-庚基-3-甲基咪唑/氯化镍体系电镀液的配方由以下组成：
氯化1-庚基-3-甲基咪唑:624g·kg-1
氯化镍：313g·kg-1
氯化铁：32g·kg-1
乙二醇：6g·kg-1
明胶：1g·kg-1
氯化钠:24g·kg-1。
8.如权利要求1所述的氯化1-庚基-3-甲基咪唑/氯化镍体系电镀液，其特征在于：氯化1-庚基-3-甲基咪唑/氯化镍体系电镀液的配方由以下组成：
氯化1-庚基-3-甲基咪唑:624g·kg-1
氯化镍：312g·kg-1
氯化铁：34g·kg-1
乙二醇：5g·kg-1
明胶：3g·kg-1
氯化钠:22g·kg-1。
9.如权利要求1所述的氯化1-庚基-3-甲基咪唑/氯化镍体系电镀液，其特征在于：氯化1-庚基-3-甲基咪唑/氯化镍体系电镀液的配方由以下组成：
氯化1-庚基-3-甲基咪唑:625g·kg-1
氯化镍：313g·kg-1
氯化铁：33g·kg-1
乙二醇：7g·kg-1
明胶：2g·kg-1
氯化钠:20g·kg-1。
10.如权利要求1所述的氯化1-庚基-3-甲基咪唑/氯化镍体系电镀液，其特征在于：氯化1-庚基-3-甲基咪唑/氯化镍体系电镀液的配方由以下组成：
氯化1-庚基-3-甲基咪唑:625g·kg-1
氯化镍：310g·kg-1
氯化铁：33g·kg-1
乙二醇：7g·kg-1
明胶：3g·kg-1
氯化钠:22g·kg-1。
CN201511009332.7A 2015-12-29 2015-12-29 氯化1-庚基-3-甲基咪唑/氯化镍体系电镀液 Pending CN105543911A (zh)