CN102418125A - 一种锌镍合金电镀 - Google Patents

一种锌镍合金电镀 Download PDF

Info

Publication number
CN102418125A
CN102418125A CN2011104249166A CN201110424916A CN102418125A CN 102418125 A CN102418125 A CN 102418125A CN 2011104249166 A CN2011104249166 A CN 2011104249166A CN 201110424916 A CN201110424916 A CN 201110424916A CN 102418125 A CN102418125 A CN 102418125A
Authority
CN
China
Prior art keywords
zinc
nickel
nickel alloy
plating liquid
alloy plating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011104249166A
Other languages
English (en)
Inventor
蒋惠良
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GALVANIZING BRANCH OF ZHANGJIAGANG SCHUMACHER ELEVATOR INSTALLATION MAINTENANCE SERVICE CO Ltd
Original Assignee
GALVANIZING BRANCH OF ZHANGJIAGANG SCHUMACHER ELEVATOR INSTALLATION MAINTENANCE SERVICE CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GALVANIZING BRANCH OF ZHANGJIAGANG SCHUMACHER ELEVATOR INSTALLATION MAINTENANCE SERVICE CO Ltd filed Critical GALVANIZING BRANCH OF ZHANGJIAGANG SCHUMACHER ELEVATOR INSTALLATION MAINTENANCE SERVICE CO Ltd
Priority to CN2011104249166A priority Critical patent/CN102418125A/zh
Publication of CN102418125A publication Critical patent/CN102418125A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种锌镍合金电镀，其物料及含量组成如下：氧化锌10～15g/L，六水硫酸镍10～15g/L，苛性碱75～100g/L，乙亚胺15～25mL/L，三乙醇胺23～30mL/L，乌洛托品0.5～3g/L，香兰素0.05～0.5g/L，糖精1.0～5.0g/L，二乙基己基硫酸钠0.1～0.6mL/L。采用本发明公开的锌镍合金电镀电镀后，获得的镀层银白色光亮,光滑,致密,含镍量在11~14%,具有较好的耐蚀性。

Description

一种锌镍合金电镀
技术领域
本发明属于电镀液领域，具体涉及一种锌镍合金电镀。
背景技术
在锌基合金中 ,锌镍合金镀层是一种新型的优良的防护性镀层 ,适合于恶劣的工业大气和严酷的海洋环境中使用。含镍11~14%的锌镍合金具有较好的耐蚀性。
锌镍合金镀液主要分为2种类型:弱酸性体系和碱性锌酸盐体系。弱酸性体系具有镀液成分简单、电流效率高、沉积速度快等优点,但其分散能力差,对镀件腐蚀性强。碱性锌酸盐体系镀液分散能力好,在电流密度范围内镀层成分、厚度较均匀,对设备和工件腐蚀性小,工艺稳定,成本较低。在碱性镀液中获得光亮镀层的关键在于采用合适的添加剂。目前,碱性镀锌镍电镀液效果不是很理想，无法满足高标准电镀需求。
发明内容
本发明所要解决的技术问题在于提供一种稳定性好，镀膜表面镀层具有较好的光亮性、 整平性和耐蚀性,且成本较低的锌镍合金电镀。
为解决上述技术问题，本发明所采用的技术方案为：一种锌镍合金电镀，其物料组成如下： 
氧化锌                10～15g/L 
六水硫酸镍            10～15g/L 
苛性碱                75～100g/L 
乙亚胺                15～25mL/L 
三乙醇胺              23～30mL/L
乌洛托品              0.5～3g/L
香兰素                0.05～0.5 g/L
糖精                  1.0～5.0g/L
二乙基己基硫酸钠      0.1～0.6 mL/L。
所述苛性碱为选自下述中的至少一种：氢氧化锂、氢氧化钠和氢氧化钾。
所述镍铁合金电镀液电流密度为2～4 A/dm2。
所述镍铁合金电镀液温度为20～25℃。
本发明的有益效果：本发明所提供的镍铁合金电镀液在存放和使用过程中稳定性好，采用本发明公开的锌镍合金电镀电镀后，获得的镀层银白色光亮,光滑,致密,含镍量在11~14%,具有较好的耐蚀性。
具体实施方式
实施例1
一种锌镍合金电镀液，其物料按照重量份数组成如下： 
氧化锌                10g/L 
六水硫酸镍            15g/L 
氢氧化钠              85g/L 
乙亚胺                15mL/L 
三乙醇胺              25mL/L
乌洛托品              0.8g/L
香兰素                0.1 g/L
糖精                  2.8g/L
二乙基己基硫酸钠      0.2 mL/L。
在20～25℃、电流密度 2A/dm2、搅拌速率 700r/min下电镀 1h。采用市售 B12垫圈作为试样。施镀工艺流程:打磨→碱洗液除油→水洗→酸洗液除锈→水洗→抛光 →水洗→施镀。
阴极与阳极的面积比为 2∶1,试验采用分立电源,控制I Zn∶I Ni = 4∶1。
获得镀层银白色光亮,光滑,致密,含镍量在13% ,具有较好的耐蚀性。
实施例2
一种锌镍合金电镀液，其物料按照重量份数组成如下： 
氧化锌                12g/L 
六水硫酸镍            14g/L 
氢氧化钾              78g/L 
乙亚胺                20mL/L 
三乙醇胺              30mL/L
乌洛托品              3g/L
香兰素                0.5 g/L
糖精                  5.0g/L
二乙基己基硫酸钠      0.5 mL/L。
在20～25℃、电流密度 3A/dm2、搅拌速率 700r/min下电镀 1h。采用市售 B12垫圈作为试样。施镀工艺流程:打磨→碱洗液除油→水洗→酸洗液除锈→水洗→抛光 →水洗→施镀。
阴极与阳极的面积比为 2∶1,试验采用分立电源,控制I Zn∶I Ni = 4∶1。
获得镀层银白色光亮,光滑,致密,含镍量在14% ,具有较好的耐蚀性。 

Claims (4)

1.一种锌镍合金电镀，其物料及含量组成如下：
Figure FDA0000121500610000011
2.根据权利要求1所述的一种锌镍合金电镀液，其特征在于：苛性碱为选自下述中的至少一种：氢氧化锂、氢氧化钠和氢氧化钾。
3.根据权利要求1所述的一种锌镍合金电镀液剂，其特征在于：所述镍铁合金电镀液电流密度为2～4A/dm2。
4.根据权利要求1所述的一种锌镍合金电镀液，其特征在于：所述镍铁合金电镀液温度为20～25℃。
CN2011104249166A 2011-12-17 2011-12-17 一种锌镍合金电镀 Pending CN102418125A (zh)