CN105363060A - 具有止血镇痛功效的医用凝胶 - Google Patents

具有止血镇痛功效的医用凝胶 Download PDF

Info

Publication number
CN105363060A
CN105363060A CN201510773079.6A CN201510773079A CN105363060A CN 105363060 A CN105363060 A CN 105363060A CN 201510773079 A CN201510773079 A CN 201510773079A CN 105363060 A CN105363060 A CN 105363060A
Authority
CN
China
Prior art keywords
parts
water
add
medical gel
borax
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510773079.6A
Other languages
English (en)
Inventor
不公告发明人
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201510773079.6A priority Critical patent/CN105363060A/zh
Publication of CN105363060A publication Critical patent/CN105363060A/zh
Pending legal-status Critical Current

Abstract

本发明公开了具有止血镇痛功效的医用凝胶，主要由下列原料制备而成，均为质量份：硼砂6-10，薏苡仁9-16，蒲黄8-12，白及10-13，半夏8-11，干姜11-14，紫花地丁12-16，附子9-16，百灵草7-10，补血草5-9，冬瓜皮7-10，羧甲基纤维素25-45，聚乙稀醇20-30，明胶5-10，三乙醇胺适量。本发明所得产品抗菌效果好，伤口愈合快，柔软弹性好，安全无毒副作用。

Description

具有止血镇痛功效的医用凝胶
技术领域
本发明涉及医用材料领域，特别是涉及具有止血镇痛功效的医用凝胶。
背景技术
日常生活和工作中，我们的皮肤常会在外界致伤因子（如外科手术、外力、热、电流、化学物质、低温）以及机体内在因素（如局部血液供应障碍等）的作用下受到损害。常伴有皮肤完整性的破坏以及一定量正常组织的丢失，同时，皮肤的正常功能受损。造成组织缺失后，局部组织通过再生、修复、重建，进行修补。在创面愈合的过程中会出现肉芽组织的增生以及瘢痕组织的形成，且过程中还会有致病微生物的存在，使皮肤出现感染，创面难以愈合，一旦创面愈合不良会给患者造成较大的伤害。
公布号CN104353104A（申请号201410626620.6）的中国专利文献公开了一种透气、无副作用的医用凝胶材料及其制备方法，所述的透气、无副作用的医用凝胶材料包括大豆低聚糖、聚己内酯、β-葡聚糖、果胶和水，制备方法包括以下步骤：（1）取水，将水温度升高至75-80℃，向水中加入大豆低聚糖为15-30份，搅拌至大豆低聚糖完全溶解；（2）保持温度不变，再向步骤（1）的溶液中加入聚己内酯、β-葡聚糖、果胶，再进行机械搅拌；（3）保持温度不变，将步骤（2）的凝胶材料再进行剪切处理；（4）将凝胶材料冷却至室温，制备得到透气、无副作用的医用凝胶材料。公布号CN102302797A（申请号201110271650.6）的中国专利文献公开了一种医用胶体敷料及其应用，该敷料主要包括水溶性甲壳素和氯己定。公布号CN103623457A（申请号201310664339.7）的中国专利文献公开了一种异形水凝胶功能敷料及其制备方法，将质量百分含量为5%～70%的亲水性高分子聚合物水溶液注入模具中，通过物理交联方法和/或化学交联方法制成所述异形水凝胶功能敷料。
现有创面敷料各有优缺点，其性能仍有待提高，因此需要加强对此方面的研究，满足患者的需要。
发明内容
针对现有技术的问题，本发明的目的是提供一种生物相容性好、使用安全无刺激的具有止血镇痛功效的医用凝胶。
本发明的技术方案是：
具有止血镇痛功效的医用凝胶，主要由下列原料制备而成，均为质量份：硼砂6-10，薏苡仁9-16，蒲黄8-12，白及10-13，半夏8-11，干姜11-14，紫花地丁12-16，附子9-16，百灵草7-10，补血草5-9，冬瓜皮7-10，羧甲基纤维素25-45，聚乙稀醇20-30，明胶5-10，三乙醇胺适量。
优选方案为，硼砂7-9，薏苡仁11-14，蒲黄9-11，白及11-12，半夏9-10，干姜12-13，紫花地丁13-15，附子11-14，百灵草8-9，补血草6-8，冬瓜皮8-9，羧甲基纤维素30-40，聚乙稀醇22-28，明胶6-9，三乙醇胺适量。
更加优选的是，硼砂8，薏苡仁12.5，蒲黄10，白及11.5，半夏9.5，干姜12.5，紫花地丁14，附子12.5，百灵草8.5，补血草7，冬瓜皮8.5，羧甲基纤维素35，聚乙稀醇25，明胶7.5，三乙醇胺适量。
所述的具有止血镇痛功效的医用凝胶的制备方法，步骤如下：
（1）将硼砂除去杂质，砸碎成块，置于砂锅内，加入粳米没过硼砂1cm，淋入醋水浸泡，中火加热至沸腾，改小火继续加热至有糊味逸出，取出，除去粳米，放凉捣碎；
（2）取半夏和附子洗净除杂，切成厚片，用豆腐块包裹，置于容器内，加水煮40-60分钟（优选的：加水煮45-55分钟；更加优选的：加水煮50分钟），取出晾干，放入炒锅内，加入麻油，文火翻炒至原料表面变黄，取出放凉；
（3）将薏苡仁和冬瓜皮洗净除杂，加入白酒浸润10-22分钟（优选的：浸润14-18分钟；更加优选的：浸润16分钟），取出切碎，与洗净的蒲黄一起置于炒锅内，文火翻炒至表面变黑，关火后淋入盐水继续闷，取出放凉；
（4）将白及、干姜、紫花地丁、百灵草和补血草捡净杂质，置于非铁质容器内，加水煎煮至沸腾，再加入步骤（1）（2）（3）所制原料，转小火继续煎煮24-36分钟（优选的：继续煎煮28-32分钟；更加优选的：继续煎煮30分钟），关火后过滤，收集滤液，滤渣加水再次煎煮20分钟，过滤后合并两次所得滤液；
（5）取明胶置于容器内，加入明胶质量3-5倍的水（优选的：加入明胶质量4倍的水），水浴加热震荡至完全溶解，得到明胶溶液，将羧甲基纤维素和聚乙稀醇分别溶解于蒸馏水中，制成2%的羧甲基纤维素溶液和1%的聚乙稀醇溶液；
（6）在水浴加热的条件下，将步骤（5）所得三种溶液混合，机械搅拌均匀，再加入步骤（4）所得滤液，继续搅拌60-120分钟，加入三乙醇胺调节pH至中性，静置并冷却至室温，无菌封装，即可得到医用凝胶。
所述的具有止血镇痛功效的医用凝胶的制备方法，步骤（1）淋入醋水量为硼砂质量的8-12倍（优选的：淋入醋水量为硼砂质量的9-11倍；更加优选的：淋入醋水量为硼砂质量的10倍）。
所述的具有止血镇痛功效的医用凝胶的制备方法，步骤（2）加入麻油量为原料质量的0.1-0.3倍（优选的：加入麻油量为原料质量的0.2倍）。
所述的具有止血镇痛功效的医用凝胶的制备方法，步骤（3）淋入盐水继续闷6-10分钟（优选的：继续闷7-9分钟；更加优选的：继续闷8分钟）。
所述的具有止血镇痛功效的医用凝胶的制备方法，步骤（4）加水量为总原料质量的6-9倍（优选的：加水量为总原料质量的7-8倍；更加优选的：加水量为总原料质量的7.5倍）。
所述的具有止血镇痛功效的医用凝胶的制备方法，步骤（6）机械搅拌的转速为50-100转/分钟（优选的：转速为60-90转/分钟；更加优选的：转速为75转/分钟）。
所述的具有止血镇痛功效的医用凝胶的制备方法，步骤（6）继续搅拌80-100分钟（优选的：继续搅拌90分钟）。
本发明提供的具有止血镇痛功效的医用凝胶生物相容性好，制备方法简单。除此之外，它的优良之处还表现在：
1、本发明所得产品，抗菌消炎效果好，伤口愈合快；
2、本发明所得产品柔软弹性好，透视透气，安全无毒副作用；
3、本发明所得产品不易与皮肤粘连，更换简单，可减少患者痛苦。
具体实施方式
下面结合实施例和实验例详细说明本发明的技术方案，但保护范围不限于此。
本发明所用主要原料的药理如下：
硼砂：基原：天然矿物硼砂的矿石，经提炼精制而成的结晶体。药理作用：硼砂对多种革兰氏阳性与阴性菌、浅部皮肤真菌及白色念珠菌有不同程度抑制作用，并略有防腐作用。对皮肤和粘膜还有收敛和保护作用。实验表明，硼砂能抗电惊厥和戊四氮阵挛性惊厥；减轻机体氟负荷，调整体内微量元素平衡，增加尿氟排出，但不能动员骨氟的移出。性味与归经：甘，咸，凉。归肺、胃经。有清热，消痰，解毒，防腐的功效。用于急性扁桃体炎，咽喉炎，口腔炎，齿龈炎，中耳炎，目赤肿痛，汗斑。
薏苡仁：基原：为禾本科植物薏苡的种仁。化学成份：种仁含蛋白质16.2％，脂肪4.65％，碳水化物79.17％，少量维生素B1（330微克％）。种子含氨基酸（为亮氨酸、赖氨酸、精氨酸、酪氨酸等）、薏苡素、薏苡酯、三萜化合物。性味：甘淡，凉。归经：入脾、肺、肾经。功能主治：健脾，补肺，清热，利湿。治泄泻，湿痹，筋脉拘挛，屈伸不利，水肿，脚气，肺痿，肺痈，肠痈，淋浊，白带。
蒲黄：基原：为香蒲科植物长苞香蒲、狭叶香蒲、宽叶香蒲或其同属多种植物的花粉。性味：甘辛，凉。归经：入肝、心经。功能主治：凉血止血，活血消瘀。生用治经闭腹痛，产后瘀阻作痛，跌扑血闷，疮疖肿毒；炒黑止吐血，衄血，崩漏，泻血，尿血，血痢，带下；外治重舌，口疮，聤耳流脓，耳中出血，阴下湿痒。
白及：基原：为兰科植物白及的块茎。化学成份：新鲜块茎含水分14.6％、淀粉30.48％，葡萄糖1.5％。又含挥发油、粘液质。根含白及甘露聚糖，是由4份甘露糖和1份葡萄糖组成的葡配甘露聚糖。性味：苦甘，凉。归经：入肺经。功能主治：补肺，止血，消肿，生肌，敛疮。治肺伤咳血，衄血，金疮出血，痈疽肿毒，溃疡疼痛，汤火灼伤，手足皲裂。
半夏：基原：为天南星科植物半夏的块茎。性味与归经：辛、温；有毒。归脾、胃、肺经。有燥湿化痰，降逆止呕，消痞散结的功效。用于湿痰寒痰，咳喘痰多，痰饮眩悸，风痰眩晕，痰厥头痛，呕吐反胃，胸脘痞闷，梅核气；外治痈肿痰核。
干姜：基原：为姜科植物姜根茎的干燥品。性味：味辛；性热。归经：脾；胃；心；肺经。功能主治：温中散寒；回阳通脉；温肺化饮。主脘腹冷痛；呕吐；泄泻，亡阳厥逆；寒饮喘咳；寒湿痹痛。
紫花地丁：基原：为堇菜科堇菜属植物紫花地丁的全草。药性：苦，辛，寒。归心、肝经。功用主治：清热解毒，燥湿凉血。主治疔疮痈疽，丹毒，痄腮，肠痈，湿热泻痢，黄疸，目赤肿痛，毒蛇咬伤。
附子：基原：为毛茛科植物乌头（栽培品）的旁生块根（子根）。性味：辛甘，热，有毒。归经：入心、脾、肾经。功能主治：回阳救逆，补火助阳，散寒除湿。治阴盛格阳，大汗亡阳，吐利厥逆，心腹冷痛，脾泄冷痢，脚气水肿小儿慢惊，风寒湿痹，踒躄拘挛，阳萎，宫冷阴，疽疮漏及一切沉寒痼冷之疾。
百灵草：基原：为双子叶植物药萝藦科植物百灵草的全株。性味：味甘、微苦、性温、有毒。归经：肝；肾经。功能主治：祛风除湿；平喘；活血通络。主风湿痹痛；风湿性心脏病；支气管哮喘；跌打损任；骨折。
补血草：基原：为白花丹科植物补血草的根。性味：苦；微咸；性凉。功能主治：清热；利湿；止血；解毒。主湿热便血；脱肛；血淋；月经过多，白带；痈肿疮毒。
冬瓜皮：基原：为葫芦科植物冬瓜的外层果皮。性味：味甘；性微寒。归经：归肺；脾；小肠经。功能主治：清热利水；消肿。主水肿；小便不利；泄泻；疮肿。
羧甲基纤维素：是当今世界上使用范围最广、用量最大的纤维素种类。属表面活性胶体的高分子化合物，是一种无臭、无味、无毒的水溶性纤维素衍生物，为白色或微黄色纤维颗粒状粉末，易溶于水，并形成透明粘稠胶体，溶液呈中性或微碱性，在医药工业中可作针剂的乳化稳定剂，片剂的粘结剂和成膜剂该膜防止创面感染，与纱布敷料无明显差异，在控制创面组织液渗出与创面快速愈合上，此膜明显优于纱布敷料，并有减轻术后水肿和创面刺激作用。
聚乙烯醇：乳白色粉末，用于制造聚乙烯醇缩醛、耐汽油管道和维尼纶合成纤维、织物处理剂、乳化剂、纸张涂层、粘合剂、胶水等。医药级聚乙烯醇，不同于化工级别聚乙烯醇，它是一种极安全的高分子有机物，对人体无毒，无副作用，具有良好的生物相容性，尤其在医疗中的如其水性凝胶在眼科、伤口敷料和人工关节方面的有广泛应用，同时在聚乙烯醇薄膜在药用膜，人工肾膜等方面也有使用。
明胶：由动物皮肤、骨、肌膜、肌魅等结缔组织中的胶原部分降解而成为白色或淡黄色、半透明、微带光泽的薄片或粉粒；是一种无唤无味，无挥发性、透明坚硬的非晶体物质，可溶于热水，不溶于冷水，但可以缓慢吸水膨胀软化，广泛应用于食品、医药及化工产业。
三乙醇胺：分子式：C6H15NO3，无色至淡黄色透明粘稠液体，微有氨味，低温时成为无色至淡黄色立方晶系晶体，易溶于水、乙醇、丙酮、甘油及乙二醇等，微溶于苯、乙醚及四氯化碳等，可用作乳化剂、保湿剂、增湿剂、增稠剂、PH平衡剂等。
实施例1具有止血镇痛功效的医用凝胶，主要由下列原料制备而成（每份10g）：硼砂6份，薏苡仁9份，蒲黄8份，白及10份，半夏8份，干姜11份，紫花地丁12份，附子9份，百灵草7份，补血草5份，冬瓜皮7份，羧甲基纤维素25份，聚乙稀醇20份，明胶5份，三乙醇胺适量。上述具有止血镇痛功效的医用凝胶的制备方法是：
（1）将硼砂除去杂质，砸碎成块，置于砂锅内，加入粳米没过硼砂1cm，淋入硼砂质量8倍的醋水浸泡，中火加热至沸腾，改小火继续加热至有糊味逸出，取出，除去粳米，放凉捣碎；
（2）取半夏和附子洗净除杂，切成厚片，用豆腐块包裹，置于容器内，加水煮40分钟，取出晾干，放入炒锅内，加入原料质量0.1倍的麻油，文火翻炒至原料表面变黄，取出放凉；
（3）将薏苡仁和冬瓜皮洗净除杂，加入白酒浸润10分钟，取出切碎，与洗净的蒲黄一起置于炒锅内，文火翻炒至表面变黑，关火后淋入盐水继续闷6分钟，取出放凉；
（4）将白及、干姜、紫花地丁、百灵草和补血草捡净杂质，置于非铁质容器内，加入总原料质量6倍的水煎煮至沸腾，再加入步骤（1）（2）（3）所制原料，转小火继续煎煮24分钟，关火后过滤，收集滤液，滤渣加水再次煎煮20分钟，过滤后合并两次所得滤液；
（5）取明胶置于容器内，加入明胶质量3倍的水，水浴加热震荡至完全溶解，得到明胶溶液，将羧甲基纤维素和聚乙稀醇分别溶解于蒸馏水中，制成2%的羧甲基纤维素溶液和1%的聚乙稀醇溶液；
（6）在水浴加热的条件下，将步骤（5）所得三种溶液混合，机械搅拌均匀（转速为50转/分钟），再加入步骤（4）所得滤液，继续搅拌60分钟，加入三乙醇胺调节pH至中性，静置并冷却至室温，无菌封装，即可得到医用凝胶。
实施例2具有止血镇痛功效的医用凝胶，主要由下列原料制备而成（每份10g）：硼砂10份，薏苡仁16份，蒲黄12份，白及13份，半夏11份，干姜14份，紫花地丁16份，附子16份，百灵草10份，补血草9份，冬瓜皮10份，羧甲基纤维素45份，聚乙稀醇30份，明胶10份，三乙醇胺适量。上述具有止血镇痛功效的医用凝胶的制备方法是：
（1）将硼砂除去杂质，砸碎成块，置于砂锅内，加入粳米没过硼砂1cm，淋入硼砂质量12倍的醋水浸泡，中火加热至沸腾，改小火继续加热至有糊味逸出，取出，除去粳米，放凉捣碎；
（2）取半夏和附子洗净除杂，切成厚片，用豆腐块包裹，置于容器内，加水煮60分钟，取出晾干，放入炒锅内，加入原料质量0.3倍的麻油，文火翻炒至原料表面变黄，取出放凉；
（3）将薏苡仁和冬瓜皮洗净除杂，加入白酒浸润22分钟，取出切碎，与洗净的蒲黄一起置于炒锅内，文火翻炒至表面变黑，关火后淋入盐水继续闷10分钟，取出放凉；
（4）将白及、干姜、紫花地丁、百灵草和补血草捡净杂质，置于非铁质容器内，加入总原料质量9倍的水煎煮至沸腾，再加入步骤（1）（2）（3）所制原料，转小火继续煎煮36分钟，关火后过滤，收集滤液，滤渣加水再次煎煮20分钟，过滤后合并两次所得滤液；
（5）取明胶置于容器内，加入明胶质量5倍的水，水浴加热震荡至完全溶解，得到明胶溶液，将羧甲基纤维素和聚乙稀醇分别溶解于蒸馏水中，制成2%的羧甲基纤维素溶液和1%的聚乙稀醇溶液；
（6）在水浴加热的条件下，将步骤（5）所得三种溶液混合，机械搅拌均匀（转速为100转/分钟），再加入步骤（4）所得滤液，继续搅拌120分钟，加入三乙醇胺调节pH至中性，静置并冷却至室温，无菌封装，即可得到医用凝胶。
实施例3具有止血镇痛功效的医用凝胶，主要由下列原料制备而成（每份10g)：硼砂7份，薏苡仁11份，蒲黄9份，白及11份，半夏9份，干姜12份，紫花地丁13份，附子11份，百灵草8份，补血草6份，冬瓜皮8份，羧甲基纤维素30份，聚乙稀醇22份，明胶6份，三乙醇胺适量。上述具有止血镇痛功效的医用凝胶的制备方法是：
（1）将硼砂除去杂质，砸碎成块，置于砂锅内，加入粳米没过硼砂1cm，淋入硼砂质量9倍的醋水浸泡，中火加热至沸腾，改小火继续加热至有糊味逸出，取出，除去粳米，放凉捣碎；
（2）取半夏和附子洗净除杂，切成厚片，用豆腐块包裹，置于容器内，加水煮45分钟，取出晾干，放入炒锅内，加入原料质量0.1倍的麻油，文火翻炒至原料表面变黄，取出放凉；
（3）将薏苡仁和冬瓜皮洗净除杂，加入白酒浸润14分钟，取出切碎，与洗净的蒲黄一起置于炒锅内，文火翻炒至表面变黑，关火后淋入盐水继续闷7分钟，取出放凉；
（4）将白及、干姜、紫花地丁、百灵草和补血草捡净杂质，置于非铁质容器内，加入总原料质量7倍的水煎煮至沸腾，再加入步骤（1）（2）（3）所制原料，转小火继续煎煮28分钟，关火后过滤，收集滤液，滤渣加水再次煎煮20分钟，过滤后合并两次所得滤液；
（5）取明胶置于容器内，加入明胶质量3倍的水，水浴加热震荡至完全溶解，得到明胶溶液，将羧甲基纤维素和聚乙稀醇分别溶解于蒸馏水中，制成2%的羧甲基纤维素溶液和1%的聚乙稀醇溶液；
（6）在水浴加热的条件下，将步骤（5）所得三种溶液混合，机械搅拌均匀（转速为60转/分钟），再加入步骤（4）所得滤液，继续搅拌80分钟，加入三乙醇胺调节pH至中性，静置并冷却至室温，无菌封装，即可得到医用凝胶。
典型案例：xxx，男性，16岁。患者不小心被热水烫伤，到医院检查，部分皮肤需进行植皮，手术结束后使用本实例所得具有止血镇痛功效的医用凝胶，敷在皮肤表面，用薄膜固定，三天后不适症减轻，伤口无恶化，愈合状况良好，皮肤与凝胶无粘连，一个月后，伤口基本愈合，无结痂，皮肤表面光滑，疤痕不明显。
实施例4具有止血镇痛功效的医用凝胶，主要由下列原料制备而成（每份10g）：硼砂9份，薏苡仁14份，蒲黄11份，白及12份，半夏10份，干姜13份，紫花地丁15份，附子14份，百灵草9份，补血草8份，冬瓜皮9份，羧甲基纤维素40份，聚乙稀醇28份，明胶9份，三乙醇胺适量。上述具有止血镇痛功效的医用凝胶的制备方法是：
（1）将硼砂除去杂质，砸碎成块，置于砂锅内，加入粳米没过硼砂1cm，淋入硼砂质量11倍的醋水浸泡，中火加热至沸腾，改小火继续加热至有糊味逸出，取出，除去粳米，放凉捣碎；
（2）取半夏和附子洗净除杂，切成厚片，用豆腐块包裹，置于容器内，加水煮55分钟，取出晾干，放入炒锅内，加入原料质量0.3倍的麻油，文火翻炒至原料表面变黄，取出放凉；
（3）将薏苡仁和冬瓜皮洗净除杂，加入白酒浸润18分钟，取出切碎，与洗净的蒲黄一起置于炒锅内，文火翻炒至表面变黑，关火后淋入盐水继续闷9分钟，取出放凉；
（4）将白及、干姜、紫花地丁、百灵草和补血草捡净杂质，置于非铁质容器内，加入总原料质量8倍的水煎煮至沸腾，再加入步骤（1）（2）（3）所制原料，转小火继续煎煮32分钟，关火后过滤，收集滤液，滤渣加水再次煎煮20分钟，过滤后合并两次所得滤液；
（5）取明胶置于容器内，加入明胶质量5倍的水，水浴加热震荡至完全溶解，得到明胶溶液，将羧甲基纤维素和聚乙稀醇分别溶解于蒸馏水中，制成2%的羧甲基纤维素溶液和1%的聚乙稀醇溶液；
（6）在水浴加热的条件下，将步骤（5）所得三种溶液混合，机械搅拌均匀（转速为90转/分钟），再加入步骤（4）所得滤液，继续搅拌100分钟，加入三乙醇胺调节pH至中性，静置并冷却至室温，无菌封装，即可得到医用凝胶。
典型案例：xxx，女性，36岁。患者干活时不小心被砸伤，到医院检查，需对伤口进行处理，医生使用本实例所得具有止血镇痛功效的医用凝胶，敷在伤口表面，用胶带固定，恢复期间，伤口无发炎或恶化，疼痛明显减轻，十天后伤口基本愈合，皮肤表面平滑，基本无疤痕。
实施例5具有止血镇痛功效的医用凝胶，主要由下列原料制备而成（每份10g）：硼砂8份，薏苡仁12.5份，蒲黄10份，白及11.5份，半夏9.5份，干姜12.5份，紫花地丁14份，附子12.5份，百灵草8.5份，补血草7份，冬瓜皮8.5份，羧甲基纤维素35份，聚乙稀醇25份，明胶7.5份，三乙醇胺适量。上述具有止血镇痛功效的医用凝胶的制备方法是：
（1）将硼砂除去杂质，砸碎成块，置于砂锅内，加入粳米没过硼砂1cm，淋入硼砂质量10倍的醋水浸泡，中火加热至沸腾，改小火继续加热至有糊味逸出，取出，除去粳米，放凉捣碎；
（2）取半夏和附子洗净除杂，切成厚片，用豆腐块包裹，置于容器内，加水煮50分钟，取出晾干，放入炒锅内，加入原料质量0.2倍的麻油，文火翻炒至原料表面变黄，取出放凉；
（3）将薏苡仁和冬瓜皮洗净除杂，加入白酒浸润16分钟，取出切碎，与洗净的蒲黄一起置于炒锅内，文火翻炒至表面变黑，关火后淋入盐水继续闷8分钟，取出放凉；
（4）将白及、干姜、紫花地丁、百灵草和补血草捡净杂质，置于非铁质容器内，加入总原料质量7.5倍的水煎煮至沸腾，再加入步骤（1）（2）（3）所制原料，转小火继续煎煮30分钟，关火后过滤，收集滤液，滤渣加水再次煎煮20分钟，过滤后合并两次所得滤液；
（5）取明胶置于容器内，加入明胶质量4倍的水，水浴加热震荡至完全溶解，得到明胶溶液，将羧甲基纤维素和聚乙稀醇分别溶解于蒸馏水中，制成2%的羧甲基纤维素溶液和1%的聚乙稀醇溶液；
（6）在水浴加热的条件下，将步骤（5）所得三种溶液混合，机械搅拌均匀（转速为75转/分钟），再加入步骤（4）所得滤液，继续搅拌90分钟，加入三乙醇胺调节pH至中性，静置并冷却至室温，无菌封装，即可得到医用凝胶。
试验例1本发明所得具有止血镇痛功效的医用凝胶（实施例5）的临床应用：
选取对象：筛选试验用小白鼠60只，体重250-300g，雄性30只，雌性30只。
试验方法：将小白鼠随机分为两组，实验组30只和对照组30只，两组小白鼠在性别、体重指数、饲养时间等方面无显著差异。分别对两组小白鼠进行麻醉，除去腹部的毛，无菌剔除腹部皮肤并形成直径2cm的全层皮肤缺损创面，两组小白鼠均按常规方法消毒创伤面，待表面干燥后，实验组患者使用本发明所得医用凝胶，敷在伤口处，并用胶带固定，对照组采用普通伤口辅料，并用胶带固定。治疗后观察两组小白鼠的伤口愈合情况及将伤口分泌物涂片进行细菌学检查。
试验结果：两组小白鼠的试验结果如表1所示：
由此可知，实验组中小白鼠的伤口愈合时间及感染例明显少于对照组，且出血量少，伤口不易结痂，因此本发明所得产品可有效促进伤口愈合，具有抗菌消炎、止血定痛的功效。
本发明中所使用的中药，硼砂清热解毒，薏苡仁健脾补肺，蒲黄凉血止血，白及止血消肿，半夏消痞散结，干姜温中散寒，紫花地丁燥湿凉血，附子回阳救逆，百灵草活血通络，补血草止血解毒，冬瓜皮清热消肿，多种药材共同发挥出清热解毒、活血止血的功效，将中药材与羧甲基纤维素、聚乙稀醇和明胶三种原料有机结合，制成医用凝胶，可有效促进伤口愈合，减少患者痛苦。
应当指出的是，具体实施方式只是本发明比较有代表性的例子，显然本发明的技术方案不限于上述实施例，还可以有很多变形。本领域的普通技术人员，以本发明所明确公开的或根据文件的书面描述毫无异议的得到的，均应认为是本专利所要保护的范围。

Claims (10)

1.具有止血镇痛功效的医用凝胶，其特征在于，主要由下列原料制备而成，均为质量份：硼砂6-10，薏苡仁9-16，蒲黄8-12，白及10-13，半夏8-11，干姜11-14，紫花地丁12-16，附子9-16，百灵草7-10，补血草5-9，冬瓜皮7-10，羧甲基纤维素25-45，聚乙稀醇20-30，明胶5-10，三乙醇胺适量。
2.如权利要求1所述的具有止血镇痛功效的医用凝胶，其特征在于，硼砂7-9，薏苡仁11-14，蒲黄9-11，白及11-12，半夏9-10，干姜12-13，紫花地丁13-15，附子11-14，百灵草8-9，补血草6-8，冬瓜皮8-9，羧甲基纤维素30-40，聚乙稀醇22-28，明胶6-9，三乙醇胺适量。
3.如权利要求1所述的具有止血镇痛功效的医用凝胶，其特征在于，硼砂8，薏苡仁12.5，蒲黄10，白及11.5，半夏9.5，干姜12.5，紫花地丁14，附子12.5，百灵草8.5，补血草7，冬瓜皮8.5，羧甲基纤维素35，聚乙稀醇25，明胶7.5，三乙醇胺适量。
4.如权利要求1-3任一所述的具有止血镇痛功效的医用凝胶的制备方法，其特征在于，步骤如下：
（1）将硼砂除去杂质，砸碎成块，置于砂锅内，加入粳米没过硼砂1cm，淋入醋水浸泡，中火加热至沸腾，改小火继续加热至有糊味逸出，取出，除去粳米，放凉捣碎；
（2）取半夏和附子洗净除杂，切成厚片，用豆腐块包裹，置于容器内，加水煮40-60分钟（优选的：加水煮45-55分钟；更加优选的：加水煮50分钟），取出晾干，放入炒锅内，加入麻油，文火翻炒至原料表面变黄，取出放凉；
（3）将薏苡仁和冬瓜皮洗净除杂，加入白酒浸润10-22分钟（优选的：浸润14-18分钟；更加优选的：浸润16分钟），取出切碎，与洗净的蒲黄一起置于炒锅内，文火翻炒至表面变黑，关火后淋入盐水继续闷，取出放凉；
（4）将白及、干姜、紫花地丁、百灵草和补血草捡净杂质，置于非铁质容器内，加水煎煮至沸腾，再加入步骤（1）（2）（3）所制原料，转小火继续煎煮24-36分钟（优选的：继续煎煮28-32分钟；更加优选的：继续煎煮30分钟），关火后过滤，收集滤液，滤渣加水再次煎煮20分钟，过滤后合并两次所得滤液；
（5）取明胶置于容器内，加入明胶质量3-5倍的水（优选的：加入明胶质量4倍的水），水浴加热震荡至完全溶解，得到明胶溶液，将羧甲基纤维素和聚乙稀醇分别溶解于蒸馏水中，制成2%的羧甲基纤维素溶液和1%的聚乙稀醇溶液；
（6）在水浴加热的条件下，将步骤（5）所得三种溶液混合，机械搅拌均匀，再加入步骤（4）所得滤液，继续搅拌60-120分钟，加入三乙醇胺调节pH至中性，静置并冷却至室温，无菌封装，即可得到医用凝胶。
5.如权利要求4所述的具有止血镇痛功效的医用凝胶的制备方法，其特征在于，步骤（1）淋入醋水量为硼砂质量的8-12倍（优选的：淋入醋水量为硼砂质量的9-11倍；更加优选的：淋入醋水量为硼砂质量的10倍）。
6.如权利要求4所述的具有止血镇痛功效的医用凝胶的制备方法，其特征在于，步骤（2）加入麻油量为原料质量的0.1-0.3倍（优选的：加入麻油量为原料质量的0.2倍）。
7.如权利要求4所述的具有止血镇痛功效的医用凝胶的制备方法，其特征在于，步骤（3）淋入盐水继续闷6-10分钟（优选的：继续闷7-9分钟；更加优选的：继续闷8分钟）。
8.如权利要求4所述的具有止血镇痛功效的医用凝胶的制备方法，其特征在于，步骤（4）加水量为总原料质量的6-9倍（优选的：加水量为总原料质量的7-8倍；更加优选的：加水量为总原料质量的7.5倍）。
9.如权利要求4所述的具有止血镇痛功效的医用凝胶的制备方法，其特征在于，步骤（6）机械搅拌的转速为50-100转/分钟（优选的：转速为60-90转/分钟；更加优选的：转速为75转/分钟）。
10.如权利要求4所述的具有止血镇痛功效的医用凝胶的制备方法，其特征在于，步骤（6）继续搅拌80-100分钟（优选的：继续搅拌90分钟）。
CN201510773079.6A 2015-11-13 2015-11-13 具有止血镇痛功效的医用凝胶 Pending CN105363060A (zh)