CN105062259A - 一种单组份低成本抗划伤水性木器漆 - Google Patents
一种单组份低成本抗划伤水性木器漆 Download PDFInfo
- Publication number
- CN105062259A CN105062259A CN201510286712.9A CN201510286712A CN105062259A CN 105062259 A CN105062259 A CN 105062259A CN 201510286712 A CN201510286712 A CN 201510286712A CN 105062259 A CN105062259 A CN 105062259A
- Authority
- CN
- China
- Prior art keywords
- water
- component
- thickening material
- agent
- defoamer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于木器漆领域,具体说是涉及一种水性木器漆,该水性木器漆为单组份水性木器漆。本发明提供一种单组份低成本抗划伤水性木器漆,由水性丙烯酸树脂乳液、面漆粉料浆和各种助剂配制而成。该水性木器漆施工简单、成本低,漆膜保光保色性好,干燥时间短,硬度上升速度快,抗划伤,成膜助剂加量少,VOC排放量低,对各种基材和底漆均有更高更可靠的附着力。
Description
技术领域
本发明属于木器漆领域,具体说是涉及一种水性木器漆,该水性木器漆为单组份水性木器漆。本发明提供一种单组份低成本抗划伤水性木器漆。
技术背景
相对于溶剂型木器漆产品,水性木器漆具有低危害、低污染特性。水性木器漆的推广对于资源的合理利用和环境卫生的改善,都十分有利。随着人们环保健康意识的增强,国家环保法规的日趋严格,水性木器漆的市场需求正逐步由潜在需求向刚性需求过渡,并呈现出快速上升的趋势。
中国专利CN101575474B提供了一种水性木器漆及其制备方法,包括以下物质组分:水性丙烯酸树脂、抑泡剂、消泡剂、成膜助剂、纳米二氧化硅浆料、防腐杀菌剂和水。该发明专利提供的水性木器漆具有高固含量、高透明性的特点,对板材有良好的填充性,可以防止板材出现发白的现象,提高了产品的施工宽容性。
中国专利CN102676085B提供了一种高光泽抗划耐磨环保水性木器清漆及其制备方法,其由以下组分组成:芳香族聚氨醋分散体,丙烯酸改性聚氨醋乳液,分散剂,抗划耐磨助剂,竹炭粉,抗划伤蜡助剂,消泡剂,润湿剂,水与其它组分。该发明专利提供的高光泽抗划耐磨环保水性木器清漆大大降低了产品VOC的含量,光泽度高,耐磨抗划性能好。
由于生产工艺和配方上的一系列问题,因此导致水性木器漆的成本较溶剂型木器漆要高,严重制约水性木器涂料发展。在国内木器涂料市场上,占绝对主导地位是溶剂型双组分聚氨酯涂料。与溶剂型双组分聚氨酯涂料相比,水性木器涂料在涂膜光泽度、丰满度、硬度、抗划伤性和耐磨性等方面均具有一定的差距。
现阶段用来制备水性木器涂料的乳液主要有水性聚氨酯(PU)乳液、水性丙烯酸酯酷(PA)乳液及丙烯酸酯改性水性聚氨酯乳液(PUA)。PU乳液制备的水性木器涂料硬度不高、耐化学性差。PA乳液由于玻璃化温度较高,一般在常温下不能成膜,在配制水性木器涂料时需加入成膜助剂。PUA乳液结合了PU与PA乳液的优点,但其配制的水性木器涂料在硬度及漆膜综合性能上还是不能完全满足我国家具行业的需求。
发明内容
为克服上述缺点,本发明提供一种单组份低成本抗划伤水性木器漆。该水性木器漆施工简单、成本低,漆膜保光保色性好,干燥时间短,硬度上升速度快,抗划伤,成膜助剂加量少,VOC排放量低,对各种基材和底漆均有更高更可靠的附着力。
本发明提供的一种单组份低成本抗划伤水性木器漆,由水性丙烯酸树脂乳液、面漆粉料浆和各种助剂配制而成。各组份的质量百分比如下:水性丙烯酸树脂60~65%,消泡剂0.05~0.2%,面漆粉料浆23.0~28.0%,乙二醇丁醚2~3%,二乙二醇丁醚2~3%,增稠剂0.05~0.2%,增稠剂B0.05~0.2%,水性流平剂0.1~0.3%,润湿剂0.1~0.3%,抗划伤剂2.0~4.0%,水4.0~6.0%。所述单组份低成本抗划伤水性木器漆按水性木器漆常规工艺配制,喷涂时按粘度需要加10~20%水喷涂。
所述的面漆粉料浆由如下质量百分比的组分配制而成:金红石型钛白粉34~38%,消光粉1.5~2.5%,润湿分散剂1.0~2.0%,消泡剂0.5~1.5%,pH调节剂0.2~0.4%,二乙二醇丁醚1.0~2.5%,增稠剂0.05~0.2%,流变助剂0.6~1.0%,水54~60%。所述的面漆粉料浆制浆工艺按水性漆常规工艺进行制备。其中润湿分散剂是带颜料亲和基团的共聚物,不含VOC和溶剂;消泡剂是分子级消泡物质,消泡机理特殊,与其它通用的矿物油、硅油基消泡物质不同,该消泡剂还具有传统消泡剂所不具备的润湿作用,其添加量比传统消泡剂低1/3~1/2,能降低至少20%的消泡剂成本;流变助剂加入后能形成三维网络,这样形成的触变流动性可有效防止沉降和改善流挂性,同时对涂层的耐水性影响很小。
本发明提供的一种单组份低成本抗划伤水性木器漆,通过原料的选择和工艺的改进,有效地简化了施工、降低了生产成本。
本发明通过有机-无机杂化,利用无机成分的高硬度、耐磨性、优异的耐候性,结合有机成分的柔韧性,并加入耐划伤助剂,进而使水性木器涂料兼具有机无机特性,提升水性木器涂料的硬度和抗划伤性能。
具体实施方式:
实施例1:
一种单组份低成本抗划伤水性木器漆,包括如下质量百分比的组分:
组分质量百分比%
水性丙烯酸树脂60.0
消泡剂0.2
面漆粉料浆26.0
乙二醇丁醚2.7
二乙二醇丁醚2.7
增稠剂0.1
水性流平剂0.3
润湿剂0.3
抗划伤剂2.8
水4.9
所述面漆粉料浆包括如下质量百分比的组分:
组分质量百分比%
金红石型钛白粉34.0
消光粉2.5
润湿分散剂1.0
消泡剂1.5
pH调节剂0.2
二乙二醇丁醚1.4
增稠剂0.4
流变助剂1.0
水58.0
实施例2:
一种单组份低成本抗划伤水性木器漆,包括如下质量百分比的组分:
组分质量百分比%
水性丙烯酸树脂61.3
消泡剂0.1
面漆粉料浆25.0
乙二醇丁醚2.5
二乙二醇丁醚2.5
增稠剂0.2
水性流平剂0.2
润湿剂0.2
抗划伤剂3.0
水5.0
所述面漆粉料浆包括如下质量百分比的组分:
组分质量百分比%
金红石型钛白粉36.0
消光粉2.0
润湿分散剂1.5
消泡剂1.0
pH调节剂0.3
二乙二醇丁醚1.7
增稠剂0.2
流变助剂0.8
水56.5
实施例3:
一种单组份低成本抗划伤水性木器漆,包括如下质量百分比的组分:
组分质量百分比%
水性丙烯酸树脂63.0
消泡剂0.05
面漆粉料浆24.0
乙二醇丁醚2.3
二乙二醇丁醚2.3
增稠剂0.3
水性流平剂0.1
润湿剂0.1
抗划伤剂3.15
水4.7
所述面漆粉料浆包括如下质量百分比的组分:
组分质量百分比%
金红石型钛白粉38.0
消光粉1.5
润湿分散剂2.0
消泡剂1.0
pH调节剂0.4
二乙二醇丁醚2.0
增稠剂0.1
流变助剂0.6
水54.4
依据上述实施例制备的水性木器漆,保光保色性好,干燥时间短,硬度上升速度快,成膜助剂加量少,成本低,同时VOC排放量低。制造和应用较简单,成本低,光泽度稳定性易于控制。
本发明所述的实施例仅仅是对本发明的优选实施方式进行的描述,并非对本发明构思和范围进行限定,在不脱离本发明设计思想的前提下,本领域中工程技术人员对本发明的技术方案作出的各种变型和改进,均应落入本发明的保护范围,本发明请求保护的技术内容,已经全部记载在权利要求书中。
Claims (4)
1.一种单组份低成本抗划伤水性木器漆,其特征在于,包括如下质量百分比的组分:
组分质量百分比%
水性丙烯酸树脂60~65
消泡剂0.05~0.2
面漆粉料浆23.0~28.0
乙二醇丁醚2~3
二乙二醇丁醚2~3
增稠剂0.1~0.4
水性流平剂0.1~0.3
润湿剂0.1~0.3
抗划伤剂2.0~4.0
水4.0~6.0
以上各组分百分比之和为100%。
2.根据1所述的一种单组份低成本抗划伤水性木器漆,其特征在于,面漆粉料浆包括如下质量百分比的组分:
组分质量百分比%
金红石型钛白粉34~38
消光粉1.5~2.5
润湿分散剂1.0~2.0
消泡剂0.5~1.5
pH调节剂0.2~0.4
二乙二醇丁醚1.0~2.5
增稠剂0.1~0.4
流变助剂0.6~1.0
水54~60
以上各组分百分比之和为100%。
3.根据权利要求1所述的一种单组份低成本抗划伤水性木器漆,其特征在于:水性丙烯酸树脂最低成膜温度为35℃,固含量为(42±1)%;增稠剂为水性聚氨酯类增稠剂;水性流平剂为聚醚改性有机硅;润湿剂是TEGO245润湿剂;抗划伤剂为水蜡浆。
4.根据权利要求2所述的面漆粉料浆,其特征在于:消光粉是德固赛消光粉OK607,其是经过有机处理的消泡剂,粒径大小为2微米;pH调节剂是氨水(28%);增稠剂与1中所使用的增稠剂一样。