CN105038515B - 一种仿红铜防腐粉末涂料 - Google Patents

一种仿红铜防腐粉末涂料 Download PDF

Info

Publication number
CN105038515B
CN105038515B CN201510562236.9A CN201510562236A CN105038515B CN 105038515 B CN105038515 B CN 105038515B CN 201510562236 A CN201510562236 A CN 201510562236A CN 105038515 B CN105038515 B CN 105038515B
Authority
CN
China
Prior art keywords
parts
powder
slag
red
nickel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201510562236.9A
Other languages
English (en)
Other versions
CN105038515A (zh
Inventor
邹良木
黄文�
黄溪福
陈家兴
陈冠军
杨杰龙
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang Jie Yu new materials Polytron Technologies Inc
Original Assignee
FUJIAN WANAN INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by FUJIAN WANAN INDUSTRY Co Ltd filed Critical FUJIAN WANAN INDUSTRY Co Ltd
Priority to CN201510562236.9A priority Critical patent/CN105038515B/zh
Publication of CN105038515A publication Critical patent/CN105038515A/zh
Application granted granted Critical
Publication of CN105038515B publication Critical patent/CN105038515B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明属于粉末涂料的制备领域,具体涉及一种仿红铜防腐粉末涂料,按重量份数计,原料组成为:环氧树脂35‑40份,端羧基饱和聚酯树脂35‑40份,流平剂1‑1.2份,沉淀硫酸钡10‑19份,珠光粉4‑5份,红金粉3‑4份,安息香0.5‑0.8份,聚乙烯蜡1.5‑2份,镍渣粉5‑6份。通过将珠光粉、红金粉邦定加入,将金属颜料颗粒粘结在粉末涂料颗粒上,制造出具有金属效果的涂层,能够很好地解决粉末涂料很难达到油漆效果的问题;而在粉末中加入镍渣,镍渣中富含Al2O3、Fe2O3两性氧化物,可与酸碱反应,起到很好耐酸耐碱作用。

Description

一种仿红铜防腐粉末涂料
技术领域
本发明属于粉末涂料的制备领域,具体涉及一种仿红铜防腐粉末涂料。
背景技术
粉末涂料不同于油漆等溶剂型涂料,将干粉喷涂烘烤熔融流平固化后,金属物质混于其中,很难达到油漆的那种金属效果,只能做到颜色接近。金属粉末的颜色主要有银白、香槟、红铜、黄铜色。而目前市场上很少有仿红铜颜色的粉末涂料。而且即使在粉末涂料中加入紫铜粉,也很难达到油漆的那种仿红铜的金属效果。
发明内容
本发明的目的在于针对现有技术的不足,提供一种仿红铜防腐粉末涂料。通过对配方进行改进,将珠光粉、红金粉邦定加入,将金属颜料颗粒粘结在粉末涂料颗粒上,制造出具有金属效果的涂层,能够很好地解决粉末涂料很难达到油漆效果的问题;镍渣粉的加入,镍渣中富含Al2O3、Fe2O3两性氧化物,可与酸碱反应,起到很好耐酸耐碱作用,能起到防腐作用。
为实现上述目的,本发明采用如下技术方案:
一种仿红铜防腐粉末涂料,按重量份数计,包括以下原料:环氧树脂35-40份,端羧基饱和聚酯树脂35-40份,流平剂1-1.2份,沉淀硫酸钡10-19份,安息香0.5-0.8份,聚乙烯蜡1.5-2份。
一种制备如上所述的仿红铜防腐粉末涂料的方法,称取环氧树脂、端羧基饱和聚酯树脂、流平剂、沉淀硫酸钡、安息香、聚乙烯蜡,将这些组分依次投入高速搅拌机均匀混合,再通过双螺杆挤出机挤出、压片、冷却、破碎、过筛制成粉末涂料底粉;再将底粉、珠光粉、红金粉投入邦定机中,通入保护气体,在60~70℃以500-900rpm邦定3-6min,得到邦定粉末。
一种仿红铜防腐粉末涂料,按重量份数计,由以下原料组成:环氧树脂35-40份,端羧基饱和聚酯树脂35-40份,流平剂1-1.2份,沉淀硫酸钡10-19份,珠光粉4-5份,红金粉3-4份,安息香0.5-0.8份,聚乙烯蜡1.5-2份,镍渣粉5-6份。
一种制备如上所述的仿红铜防腐粉末涂料的方法,称取环氧树脂、端羧基饱和聚酯树脂、流平剂、沉淀硫酸钡、安息香、聚乙烯蜡,将这些组分依次投入高速搅拌机均匀混合,再通过双螺杆挤出机挤出、压片、冷却、破碎、过筛制成粉末涂料底粉;再将底粉、珠光粉、红金粉、镍渣粉投入邦定机中,通入保护气体,在60~70℃以500-900rpm邦定3-6min,得到邦定粉末。
镍渣的化学成分为:SiO2含量30% -50%,Fe2O3含量30%-60%,CaO含量1.5%-5%,MgO含量1% -15%,Al2O3含2.5%-6%。
镍渣粉的制备方法为:将镍渣置于球磨机中湿法球磨18~25小时,研磨的浆料取出后置于电热鼓风恒温干燥箱中80~120℃烘干10~12h,然后过100目筛得到统料。
所述的环氧树脂为分子量在1000~4000,软化点在90℃左右的双酚A型树脂,环氧值为0.12,国内牌号为E-12或604型环氧树脂。
本发明的有益效果在于:
1)通过对配方进行改进,将珠光粉、红金粉邦定加入,将金属颜料颗粒粘结在粉末涂料颗粒上,制造出具有金属效果的涂层,能够很好地解决粉末涂料很难达到油漆效果的问题;
2)镍渣与粒化高炉矿渣相比,SiO2、Fe2O3和Al2O3含量高,能与酸碱反应,起到防腐的作用;镍渣的加入,使得本发明的粉末涂料耐酸、耐碱性好,具有优异的防腐性能。
具体实施方式
本发明用下列实施例来进一步说明本发明,但本发明的保护范围并不限于下列实施例。
实施例1
一种仿红铜防腐粉末涂料,按重量份数计,原料组成为:环氧树脂40份,端羧基饱和聚酯树脂44份,流平剂1份,沉淀硫酸钡13份,安息香0.5份,聚乙烯蜡1.5份。
将各组分依次投入高速搅拌机均匀混合,再通过双螺杆挤出机挤出、压片、冷却、破碎、过筛制成粉末涂料底粉,再将92份底粉,4份珠光粉,4份红金粉投入邦定机中,通入保护气体,在65℃以600rpm邦定4min,得到邦定粉末。
实施例2
一种仿红铜防腐粉末涂料,按重量份数计,原料组成为:环氧树脂44.4份,端羧基饱和聚酯树脂43份,流平剂1.2份,沉淀硫酸钡10份,安息香0.6份,聚乙烯蜡1.8份,镍渣粉5份;
一种制备如上所述的仿红铜防腐粉末涂料的方法,将各组分依次投入高速搅拌机均匀混合,再通过双螺杆挤出机挤出、压片、冷却、破碎、过筛制成粉末涂料底粉,再将92份底粉,5份珠光粉,3份红金粉,5份镍渣粉投入邦定机中,通入保护气体,在70℃以500rpm邦定3min,得到邦定粉末。
实施例3
一种仿红铜防腐粉末涂料,按重量份数计,原料组成为:环氧树脂40份,端羧基饱和聚酯树脂37.1份,流平剂1.1份,沉淀硫酸钡19份,安息香0.8份,聚乙烯蜡2份,镍渣粉6份;
一种制备如上所述的仿红铜防腐粉末涂料的方法,将各组分依次投入高速搅拌机均匀混合,再通过双螺杆挤出机挤出、压片、冷却、破碎、过筛制成粉末涂料底粉,再将91份底粉,5份珠光粉,4份红金粉,6份镍渣粉投入邦定机中,通入保护气体,在60℃以900rpm邦定6min,得到邦定粉末。
对比例1
一种仿红铜防腐粉末涂料,按重量份数计,原料组成为:环氧树脂40份,端羧基饱和聚酯树脂44份,流平剂1份,沉淀硫酸钡13份,安息香0.5份,聚乙烯蜡1.5份。
粉末涂料按配方比例均匀混合,再通过双螺杆挤出机挤出、压片、冷却、破碎、过筛,制成粉末涂料底粉,再将底粉92份,珠光粉4份,红金粉4份投入混合机中搅拌均匀,用静电喷涂的方式喷于样板上,进行性能检测。固化条件为 180℃/15min。
对比例2
一种仿红铜防腐粉末涂料,按重量份数计,原料组成为:环氧树脂40份,端羧基饱和聚酯树脂44份,流平剂1份,沉淀硫酸钡13份,安息香0.5份,聚乙烯蜡1.5份,镍渣粉5份。
粉末涂料按配方比例均匀混合,再通过双螺杆挤出机挤出、压片、冷却、破碎、过筛,制成粉末涂料底粉,再将底粉92份,珠光粉4份,红金粉4份,镍渣粉5份,投入混合机中搅拌均匀,用静电喷涂的方式喷于样板上,进行性能检测。固化条件为 180℃/15min。
检测结果如表1所示:
表1 性能测试
以上所述仅为本发明的较佳实施例,凡依本发明申请专利范围所做的均等变化与修饰,皆应属本发明的涵盖范围。

Claims (1)

1. 一种仿红铜防腐粉末涂料,其特征在于:所述的仿红铜防腐粉末涂料,按重量份数计,由以下原料组成:环氧树脂35-40 份,端羧基饱和聚酯树脂35-40 份,流平剂1-1.2 份,沉淀硫酸钡10-19 份,珠光粉4-5 份,红金粉3-4 份,安息香0.5-0.8 份,聚乙烯蜡1.5-2份,镍渣粉5-6份;镍渣含有以下重量百分比的化学成分:SiO2含量30%-50%,Fe2O3含量30%-60%,CaO含量1.5%-5%,MgO含量1% -15%,Al2O3含量2.5%-6%。
CN201510562236.9A 2015-09-07 2015-09-07 一种仿红铜防腐粉末涂料 Active CN105038515B (zh)