CN104630634B - 冷锻性优异的渗碳用钢及其制造方法 - Google Patents
冷锻性优异的渗碳用钢及其制造方法 Download PDFInfo
- Publication number
- CN104630634B CN104630634B CN201510028676.6A CN201510028676A CN104630634B CN 104630634 B CN104630634 B CN 104630634B CN 201510028676 A CN201510028676 A CN 201510028676A CN 104630634 B CN104630634 B CN 104630634B
- Authority
- CN
- China
- Prior art keywords
- less
- steel
- carburizing
- spheroidizing
- ferrite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
- C21D1/06—Surface hardening
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
- C21D1/26—Methods of annealing
- C21D1/32—Soft annealing, e.g. spheroidising
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
- C21D9/32—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for gear wheels, worm wheels, or the like
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C1/00—Making non-ferrous alloys
- C22C1/02—Making non-ferrous alloys by melting
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/001—Ferrous alloys, e.g. steel alloys containing N
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/20—Ferrous alloys, e.g. steel alloys containing chromium with copper
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/24—Ferrous alloys, e.g. steel alloys containing chromium with vanadium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C8/00—Solid state diffusion of only non-metal elements into metallic material surfaces; Chemical surface treatment of metallic material by reaction of the surface with a reactive gas, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals
- C23C8/02—Pretreatment of the material to be coated
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C8/00—Solid state diffusion of only non-metal elements into metallic material surfaces; Chemical surface treatment of metallic material by reaction of the surface with a reactive gas, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals
- C23C8/06—Solid state diffusion of only non-metal elements into metallic material surfaces; Chemical surface treatment of metallic material by reaction of the surface with a reactive gas, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using gases
- C23C8/08—Solid state diffusion of only non-metal elements into metallic material surfaces; Chemical surface treatment of metallic material by reaction of the surface with a reactive gas, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using gases only one element being applied
- C23C8/20—Carburising
- C23C8/22—Carburising of ferrous surfaces
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C8/00—Solid state diffusion of only non-metal elements into metallic material surfaces; Chemical surface treatment of metallic material by reaction of the surface with a reactive gas, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals
- C23C8/80—After-treatment
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D2211/00—Microstructure comprising significant phases
- C21D2211/005—Ferrite
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D2211/00—Microstructure comprising significant phases
- C21D2211/009—Pearlite
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Mechanical Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Physics & Mathematics (AREA)
- Thermal Sciences (AREA)
- Crystallography & Structural Chemistry (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Heat Treatment Of Steel (AREA)
- Solid-Phase Diffusion Into Metallic Material Surfaces (AREA)
Applications Claiming Priority (5)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2010-267779 | 2010-11-30 | ||
JP2010267779 | 2010-11-30 | ||
JP2011218340 | 2011-09-30 | ||
JP2011-218340 | 2011-09-30 | ||
CN201180048735.6A CN103154293B (zh) | 2010-11-30 | 2011-11-29 | 冷锻性优异的渗碳用钢及其制造方法 |
Related Parent Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
CN201180048735.6A Division CN103154293B (zh) | 2010-11-30 | 2011-11-29 | 冷锻性优异的渗碳用钢及其制造方法 |
Publications (2)
Publication Number | Publication Date |
---|---|
CN104630634A CN104630634A (zh) | 2015-05-20 |
CN104630634B true CN104630634B (zh) | 2017-09-08 |
Family
ID=46171457
Family Applications (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
CN201510028676.6A Active CN104630634B (zh) | 2010-11-30 | 2011-11-29 | 冷锻性优异的渗碳用钢及其制造方法 |
CN201180048735.6A Active CN103154293B (zh) | 2010-11-30 | 2011-11-29 | 冷锻性优异的渗碳用钢及其制造方法 |
Family Applications After (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
CN201180048735.6A Active CN103154293B (zh) | 2010-11-30 | 2011-11-29 | 冷锻性优异的渗碳用钢及其制造方法 |
Country Status (5)
Country | Link |
---|---|
US (1) | US20130186522A1 (ja) |
JP (1) | JP5927868B2 (ja) |
KR (1) | KR101631521B1 (ja) |
CN (2) | CN104630634B (ja) |
WO (1) | WO2012073485A1 (ja) |
Families Citing this family (19)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP6057626B2 (ja) * | 2012-09-04 | 2017-01-11 | 山陽特殊製鋼株式会社 | 熱処理変形の小さい機械構造用鋼材 |
JP6241136B2 (ja) * | 2013-08-26 | 2017-12-06 | 新日鐵住金株式会社 | 肌焼鋼鋼材 |
JP6225613B2 (ja) * | 2013-09-30 | 2017-11-08 | 新日鐵住金株式会社 | 肌焼鋼鋼材 |
JP6143355B2 (ja) * | 2013-10-22 | 2017-06-07 | 株式会社神戸製鋼所 | 絞り加工性と浸炭熱処理後の表面硬さに優れる熱延鋼板 |
JP6197761B2 (ja) * | 2014-07-24 | 2017-09-20 | Jfeスチール株式会社 | 冷間加工品の製造方法 |
JP2016098426A (ja) * | 2014-11-26 | 2016-05-30 | 山陽特殊製鋼株式会社 | 浸炭肌で使用する耐ピッチング特性に優れた機械構造用肌焼鋼 |
JP2016169433A (ja) * | 2015-03-13 | 2016-09-23 | 株式会社神戸製鋼所 | 冷間加工性と浸炭熱処理後の靱性に優れる浸炭用鋼板 |
JP6558016B2 (ja) * | 2015-03-26 | 2019-08-14 | 日本製鉄株式会社 | 浸炭機械構造部品 |
KR101705168B1 (ko) * | 2015-04-20 | 2017-02-10 | 현대자동차주식회사 | 내구성이 향상된 침탄 합금강 및 이의 제조방법 |
JP6319212B2 (ja) * | 2015-07-09 | 2018-05-09 | Jfeスチール株式会社 | 歯車部品および歯車部品の製造方法 |
JP6794012B2 (ja) * | 2015-12-10 | 2020-12-02 | 山陽特殊製鋼株式会社 | 耐結晶粒粗大化特性、耐曲げ疲労強度および耐衝撃強度に優れた機械構造用鋼 |
EP3584340B1 (en) | 2017-02-20 | 2024-01-10 | Nippon Steel Corporation | Steel sheet |
CN107217210A (zh) * | 2017-07-27 | 2017-09-29 | 陈海燕 | 一种齿轮钢 |
CN108165883A (zh) * | 2018-01-22 | 2018-06-15 | 弗兰德传动系统有限公司 | 20CrMnMo钢及其加工方法 |
JP7152832B2 (ja) * | 2018-06-18 | 2022-10-13 | 株式会社小松製作所 | 機械部品 |
JP2019011510A (ja) * | 2018-08-20 | 2019-01-24 | 株式会社神戸製鋼所 | 冷間加工性と浸炭熱処理後の靱性に優れる浸炭用鋼板 |
CN110846580B (zh) * | 2019-12-05 | 2021-09-07 | 马鞍山钢铁股份有限公司 | 一种高Mo高性能Mn-Cr系风电输出齿轮用钢及其生产方法 |
CN113430461B (zh) * | 2021-06-24 | 2022-05-17 | 马鞍山钢铁股份有限公司 | 一种Nb、V微合金化齿轮钢及其制备方法、热处理方法、渗碳处理方法和渗碳齿轮钢 |
CN114574768A (zh) * | 2022-03-15 | 2022-06-03 | 中新(重庆)超高强材料研究院有限公司 | 一种汽车用铌钒复合微合金化、高接触疲劳性能齿轮用钢及齿轮的制造方法 |
Family Cites Families (10)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2945714B2 (ja) | 1990-05-15 | 1999-09-06 | 日産自動車株式会社 | 高面圧歯車 |
JPH07122118A (ja) | 1993-10-27 | 1995-05-12 | Akira Suzuki | 電導性有機超薄膜 |
JPH1112684A (ja) * | 1997-06-19 | 1999-01-19 | Kobe Steel Ltd | 冷間鍛造用肌焼鋼 |
DE69811200T2 (de) * | 1997-07-22 | 2003-10-09 | Nippon Steel Corp | Einsatzstahl mit hervorragender verhinderung der sekundärrekristallisation während der aufkohlung, verfahren zu dessen herstellung, halbzeug für aufzukohlende teile |
US6264759B1 (en) * | 1998-10-16 | 2001-07-24 | Pohang Iron & Steel Co., Ltd. | Wire rods with superior drawability and manufacturing method therefor |
JP3954772B2 (ja) * | 2000-04-26 | 2007-08-08 | 新日本製鐵株式会社 | 結晶粒粗大化防止特性に優れた高温浸炭部品用素形材とその製造方法 |
JP4392324B2 (ja) | 2004-10-28 | 2009-12-24 | 株式会社神戸製鋼所 | 冷間鍛造用肌焼鋼の製造方法 |
JP4709944B2 (ja) * | 2009-01-16 | 2011-06-29 | 新日本製鐵株式会社 | 肌焼鋼、浸炭部品、及び肌焼鋼の製造方法 |
JP5332646B2 (ja) * | 2009-01-23 | 2013-11-06 | Jfeスチール株式会社 | 冷間鍛造性に優れた浸炭用鋼の製造方法 |
JP5495648B2 (ja) * | 2009-03-17 | 2014-05-21 | 山陽特殊製鋼株式会社 | 耐結晶粒粗大化特性に優れた機械構造用鋼及びその製造方法 |
-
2011
- 2011-11-29 JP JP2011260725A patent/JP5927868B2/ja active Active
- 2011-11-29 WO PCT/JP2011/006655 patent/WO2012073485A1/ja active Application Filing
- 2011-11-29 CN CN201510028676.6A patent/CN104630634B/zh active Active
- 2011-11-29 CN CN201180048735.6A patent/CN103154293B/zh active Active
- 2011-11-29 US US13/821,763 patent/US20130186522A1/en not_active Abandoned
- 2011-11-29 KR KR1020137010303A patent/KR101631521B1/ko active IP Right Grant
Also Published As
Publication number | Publication date |
---|---|
KR101631521B1 (ko) | 2016-06-24 |
KR20130058069A (ko) | 2013-06-03 |
WO2012073485A1 (ja) | 2012-06-07 |
JP2013082988A (ja) | 2013-05-09 |
CN103154293A (zh) | 2013-06-12 |
US20130186522A1 (en) | 2013-07-25 |
CN103154293B (zh) | 2015-09-16 |
CN104630634A (zh) | 2015-05-20 |
JP5927868B2 (ja) | 2016-06-01 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
CN104630634B (zh) | 冷锻性优异的渗碳用钢及其制造方法 | |
CN103119189B (zh) | 渗碳用钢、渗碳钢部件及其制造方法 | |
JP4435954B2 (ja) | 冷間鍛造用棒線材とその製造方法 | |
CN103119188B (zh) | 渗碳用钢、渗碳钢部件及其制造方法 | |
JP6098732B2 (ja) | 浸炭鋼部品の製造方法及び浸炭鋼部品 | |
JP5332646B2 (ja) | 冷間鍛造性に優れた浸炭用鋼の製造方法 | |
JP4435953B2 (ja) | 冷間鍛造用棒線材とその製造方法 | |
CN104024444B (zh) | 钢制部件的制造方法 | |
CN107002193A (zh) | 冷锻部件用轧制棒钢或轧制线材 | |
JP4941252B2 (ja) | 動力伝達部品用肌焼鋼 | |
KR20130108403A (ko) | 열간 단조용 압연 봉강 또는 선재 | |
JP3738004B2 (ja) | 冷間加工性と浸炭時の粗大粒防止特性に優れた肌焼用鋼材とその製造方法 | |
JP3738003B2 (ja) | 冷間加工性と浸炭時の粗大粒防止特性に優れた肌焼用鋼材およびその製造方法 | |
WO2019102584A1 (ja) | はだ焼鋼の鍛造熱処理品 | |
US11952668B2 (en) | Carburized part and method for manufacturing same | |
CN109196134A (zh) | 表面硬化钢及其制造方法以及齿轮部件的制造方法 | |
WO2019244504A1 (ja) | 機械部品の製造方法 | |
TW200538559A (en) | The crank shaft excellent in bending fatigue strength | |
JP3551573B2 (ja) | 歯切り性に優れた浸炭歯車用鋼 | |
JP5206911B1 (ja) | 熱間鍛造用非調質鋼および熱間鍛造非調質品、ならびにその製造方法 | |
JP6390685B2 (ja) | 非調質鋼およびその製造方法 | |
JP5969204B2 (ja) | 耐摩耗性と面疲労特性に優れた高周波焼入歯車およびその製造方法 | |
CN106133174A (zh) | 疲劳特性优异的高强度钢材 | |
JP4411096B2 (ja) | 球状化後の冷間鍛造性に優れた肌焼用鋼線材・棒鋼 | |
JP2020094236A (ja) | 浸炭部品、浸炭部品用の素形材、及び、それらの製造方法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
C06 | Publication | ||
PB01 | Publication | ||
C10 | Entry into substantive examination | ||
SE01 | Entry into force of request for substantive examination | ||
GR01 | Patent grant | ||
GR01 | Patent grant |