CN104556686A - 一种铁锰着色低硼硅药用玻璃管及其制备方法 - Google Patents

一种铁锰着色低硼硅药用玻璃管及其制备方法 Download PDF

Info

Publication number
CN104556686A
CN104556686A CN201510031281.1A CN201510031281A CN104556686A CN 104556686 A CN104556686 A CN 104556686A CN 201510031281 A CN201510031281 A CN 201510031281A CN 104556686 A CN104556686 A CN 104556686A
Authority
CN
China
Prior art keywords
parts
glass
muffle furnace
pipe
glass tube
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510031281.1A
Other languages
English (en)
Inventor
孙世增
韩银刚
孙新奉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Puyang New Harmony Industrial Development Co Ltd
Original Assignee
Puyang New Harmony Industrial Development Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Puyang New Harmony Industrial Development Co Ltd filed Critical Puyang New Harmony Industrial Development Co Ltd
Priority to CN201510031281.1A priority Critical patent/CN104556686A/zh
Publication of CN104556686A publication Critical patent/CN104556686A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种铁锰着色低硼硅药用玻璃管，所述药用玻璃管由下述重量份数比的原料制备而成：SiO2＝67-70份，Al2O3＝4.5-6份，B2O3＝6-8份，CaO＝1-3份，BaO＝1.5-2.2份，Na2O＝8-10份，K2O＝1.6-2.4份，Fe2O3＝0.3-3份，MnO2＝3-10份，本发明的药用玻璃管颜色为深棕色，避光性能好，满足药品包装的要求，最大特点是玻璃管上无气泡线，解决了一直采用的硫、碳着色或铁、钛、铈着色而产生的产品气泡线问题。

Description

一种铁锰着色低硼硅药用玻璃管及其制备方法
技术领域
本发明属于玻璃管制备领域，主要涉及一种铁锰着色低硼硅药用玻璃管及其制备方法。
背景技术
低硼硅玻璃药用管(棕色)，是制造低硼硅玻璃管制注射剂瓶(棕色)和低硼硅玻璃安瓿(棕色)的原材料。低硼硅玻璃药用管(棕色)的质量直接决定着低硼硅玻璃管制注射剂瓶(棕色)和低硼硅玻璃安瓿(棕色)的质量，目前生产低硼硅玻璃药用管(棕色)，采用硫碳着色原理，颜色较浅，避光性能较差，更为严重是一直存在较严重气泡线，属质量缺陷，出瓶率较低，此瓶盛装药品特别是水剂存在药品安全隐患，制瓶公司投入大量检验人员进行人工检验，人工检验很难将带气泡线的药用瓶检验干净，这样就造成药品的安全隐患，目前一直无法解决棕色药用玻璃管的气线问题。
发明内容
本发明的目的正是为了解决上述现有技术所存在的问题，而提供一种铁锰着色低硼硅药用玻璃管及其制备方法。
本发明实现上述目的所采取的技术方案是：一种铁锰着色低硼硅药用玻璃管，所述药用玻璃管由下述重量份数比的原料制备而成：SiO2＝67-70份，Al2O3＝4.5-6份，B2O3＝6-8份，CaO＝1-3份，BaO＝1.5-2.2份，Na2O＝8-10份，K2O＝1.6-2.4份，Fe2O3＝0.3-3份，MnO2＝3-10份。
一种制备上述铁锰着色低硼硅药用玻璃管的方法，所述制备方法如下：首先，将各种原料按设计成分配制成均匀度≥96％的合格粉料；然后，将合格粉料投入玻璃池炉内，熔化80小时左右，得到均匀一致的完全澄清的玻璃液；接着，将均匀的玻璃液经过控制温度为1250-1270℃的料道，进入到马氟炉内由驱动机带动的旋转管表面上，马氟炉I区温度900-950℃，马氟炉II区温度960-1000℃，马氟炉III区温度1050-1100℃；然后，经过牵引机牵引，通过长40-50m的跑道，由激光测径仪控制玻璃管的直径，并由精切圆口机将玻璃管两端进行精切和圆口，最后包装装箱。
本发明的原理是：由于物体对光的吸收和对光的散射，不同物质吸收光的波长各异，所以呈现不同的颜色。Fe2+吸收200nm附近的波长，通过470-480nm波长，显蓝绿色。Mn3+吸收470-520nm的波长，通过300-450nm的波长，显示紫色。根据颜色的叠加原理，两颜色在一起显示深棕色。在实际生产中必须掌握Fe2+/Fe3+与Mn2+/Mn3+的平衡关系，通过大量实验Fe2O3＝0.3-3％，MnO2＝3-10％时产生理想的深棕色，此料方没有硫和碳，在玻璃熔化过程中只产生微量气泡，但在氟硅酸钠、澄清剂的作用下，将玻璃液本身的微量气泡排出玻璃液，所以产品无任何气泡线，是理想的医药用避光材料。
本发明的有益效果如下：
1、原料容易获的，都是玻璃的常用原料，各地均有。
2、工艺简单，容易成型。
3、铁、锰着色(Fe2+/Fe3+、Mn2+/Mn3+)颜色为深棕色，避光性能好，满足药品包装的要求，最大特点是玻璃管上无气泡线，解决了一直采用的硫、碳着色或铁、钛、铈着色而产生的产品气泡线问题。
具体实施方式
实施例1
本发明的铁锰着色低硼硅药用玻璃管由下述重量百分比的原料制备而成：SiO2＝67.6份，Al2Oa＝5.5份，B2O3＝6.5份，CaO＝3份，BaO＝2份，Na2O＝10份，K2O＝2.1份，Fe2O3＝O.3份，MnO2＝3份。
上述铁锰着色低硼硅药用玻璃管的制备方法如下：首先，将各种原料按设计成分配制成均匀度≥96％的合格粉料；然后，将合格粉料投入玻璃池炉内，熔化80小时左右，得到均匀一致的完全澄清的玻璃液；接着，将均匀的玻璃液经过控制温度为1250-1270℃的料道，进入到马氟炉内由驱动机带动的旋转管表面上，马氟炉I区温度900-950℃，马氟炉II区温度960-1000℃，马氟炉III区温度1050-1100℃；然后，经过牵引机牵引，通过长40-50m的跑道，由激光测径仪控制玻璃管的直径，并由精切圆口机将玻璃管两端进行精切和圆口，最后包装装箱。
实施例2
本发明的铁锰着色低硼硅药用玻璃管由下述重量百分比的原料制备而成：SiO2＝67.5份，Al2O3＝4.5份，B2O3＝6.5份，CaO＝2.5份，BaO＝1.5份，Na2O＝9份，K2O＝2份，Fe2O3＝O.5份，MnO2＝6份。
上述铁锰着色低硼硅药用玻璃管的制备方法同实施例1.
实施例3
本发明的铁锰着色低硼硅药用玻璃管由下述重量百分比的原料制备而成：SiO2＝68份，Al2O3＝5份，B2O3＝7份，CaO＝1.5份，BaO＝2份，Na2O＝8.6份，K2O＝2.4份，Fe2O3＝1.5份，MnO2＝4份。
上述铁锰着色低硼硅药用玻璃管的制备方法同实施例1.
实施例1-3的化学组成及性能比较见下表：

Claims (2)

1.一种铁锰着色低硼硅药用玻璃管，其特征在于：所述药用玻璃管由下述重量份数比的原料制备而成：SiO2＝67-70份，Al2O3＝4.5-6份，B2O3＝6-8份，CaO＝1-3份，BaO＝1.5-2.2份，Na2O＝8-10份，K2O＝1.6-2.4份，Fe2O3＝0.3-3份，MnO2＝3-10份。
2.一种制备权利要求1所述铁锰着色低硼硅药用玻璃管的方法，其特征在于：所述制备方法如下：首先，将各种原料按设计成分配制成均匀度≥96％的合格粉料；然后，将合格粉料投入玻璃池炉内，熔化80小时左右，得到均匀一致的完全澄清的玻璃液；接着，将均匀的玻璃液经过控制温度为1250-1270℃的料道，进入到马氟炉内由驱动机带动的旋转管表面上，马氟炉I区温度900-950℃，马氟炉II区温度960-1000℃，马氟炉III区温度1050-1100℃；然后，经过牵引机牵引，通过长40-50m的跑道，由激光测径仪控制玻璃管的直径，并由精切圆口机将玻璃管两端进行精切和圆口，最后包装装箱。
CN201510031281.1A 2015-01-19 2015-01-19 一种铁锰着色低硼硅药用玻璃管及其制备方法 Pending CN104556686A (zh)