CN105293895A - 一种高品质琉璃 - Google Patents
一种高品质琉璃 Download PDFInfo
- Publication number
- CN105293895A CN105293895A CN201510719943.4A CN201510719943A CN105293895A CN 105293895 A CN105293895 A CN 105293895A CN 201510719943 A CN201510719943 A CN 201510719943A CN 105293895 A CN105293895 A CN 105293895A
- Authority
- CN
- China
- Prior art keywords
- oxide
- hydrogen peroxide
- sesquioxide
- quartz sand
- coloured glaze
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高品质琉璃,其组成成分及其重量份比例为:粒径范围是0.2mm-0.5mm的石英砂40%-50%;助熔剂:氧化钙10%-15%和氧化镁2%-5%;澄清剂:硝酸铵6%-12%和、氯化钠5%-10%和氯化铵2%-5%;氧化剂:过氧化氢2%-5%;着色剂:氧化铜3%-5%,氧化镉3%-8%,三氧化二钴2%-6%和三氧化二镍3%-8%;其他助剂:脂肪醇苯磺酸钠2%-5%,双氧水1%-4%和过硫酸盐1%-3%。通过相应的配方使生产的品质更佳。
Description
技术领域
本发明涉及了一种高品质琉璃,属于琉璃加工技术领域。
背景技术
琉璃是一种硅酸盐制品,具有悠久的历史,其品质晶莹剔透,光彩夺目,变幻瑰丽,充分体现出东方人的精致、细腻和含蓄,是一种重要的装饰构件。
琉璃成分以软化点低、料性长为有优良特性,如此便于工艺制造,适合琉璃成形,琉璃制品的品质体现在光泽好,气泡、条纹、结石少。琉璃的软化点、料性主要取决于琉璃配方中成分的种类及其比例,而在琉璃基础成分中加入澄清剂可以使琉璃熔化温度降低、熔化质量得到提高,避免产生气泡、条纹、结石等缺陷。澄清剂能够在琉璃生产过程中放出分解气体,或自身气化,产生大量的气泡,吸纳周边的小气泡,伴随灰泡上升而促进琉璃澄清。
目前常用的澄清剂有二氧化铈、白砒等,但是白砒为剧毒物质,威胁操作人员健康并严重污染环境;二氧化铈的澄清效果尚可,但澄清时间较长,而且铈为稀土元素,成本较昂贵。因此亟需一种软化点低、料性长、澄清效果好、澄清时间短、制品品质优良的琉璃配方。
发明内容
本发明所要解决的技术问题是提供一种高品质琉璃,通过相应的配方使生产的品质更佳。
为了解决上述技术问题,本发明所采用的技术方案是:
一种高品质琉璃,其组成成分及其重量份比例为:
粒径范围是0.2mm-0.5mm的石英砂40%-50%;
助熔剂:氧化钙10%-15%和氧化镁2%-5%;
澄清剂:硝酸铵6%-12%和、氯化钠5%-10%和氯化铵2%-5%;
氧化剂:过氧化氢2%-5%;
着色剂:氧化铜3%-5%,氧化镉3%-8%,三氧化二钴2%-6%和三氧化二镍3%-8%;
其他助剂:脂肪醇苯磺酸钠2%-5%,双氧水1%-4%和过硫酸盐1%-3%。
前述的一种高品质琉璃,其特征在于:所述石英砂的粒径为0.3mm。
前述的一种高品质琉璃,其特征在于:所述石英砂42%,氧化钙10%,氧化镁2%,硝酸铵6%,氯化钠5%,氯化铵2%,过氧化氢2%,氧化铜3%,氧化镉3%,三氧化二钴2%,三氧化二镍3%。
前述的一种高品质琉璃,其特征在于:所述石英砂45%,氧化钙12%,氧化镁3%,硝酸铵7%,氯化钠5%,氯化铵2%,过氧化氢2%,氧化铜3%,氧化镉3%,三氧化二钴2%,三氧化二镍6%。
前述的一种高品质琉璃,其特征在于:所述石英砂48%,氧化钙10%,氧化镁2%,硝酸铵8%,氯化钠5%,氯化铵4%,过氧化氢2%,氧化铜3%,氧化镉5%,三氧化二钴4%,三氧化二镍5%。
前述的一种高品质琉璃,其特征在于:所述石英砂50%,氧化钙15%,氧化镁4%,硝酸铵6%,氯化钠5%,氯化铵2%,过氧化氢2%,氧化铜3%,氧化镉3%,三氧化二钴4%,三氧化二镍3%。
本发明的有益效果是:通过选择较合适的原料种类,同时各类原料选择了较佳的用量,这样各类原料通过彼此的共同作用,能够使制得的琉璃工艺品具有较佳的品质。
具体实施方式
下面将结合具体实施例,对本发明作进一步的说明。
本发明提供了一种高品质琉璃,其组成成分及其重量份比例为:
粒径范围是0.2mm-0.5mm的石英砂40%-50%;
助熔剂:氧化钙10%-15%和氧化镁2%-5%;
澄清剂:硝酸铵6%-12%和、氯化钠5%-10%和氯化铵2%-5%;
氧化剂:过氧化氢2%-5%;
着色剂:氧化铜3%-5%,氧化镉3%-8%,三氧化二钴2%-6%和三氧化二镍3%-8%;
其他助剂:脂肪醇苯磺酸钠2%-5%,双氧水1%-4%和过硫酸盐1%-3%。
其中,所述石英砂的粒径为0.3mm。
实施例1
石英砂42%,氧化钙10%,氧化镁2%,硝酸铵6%,氯化钠5%,氯化铵2%,过氧化氢2%,氧化铜3%,氧化镉3%,三氧化二钴2%,三氧化二镍3%。
实施例2
石英砂45%,氧化钙12%,氧化镁3%,硝酸铵7%,氯化钠5%,氯化铵2%,过氧化氢2%,氧化铜3%,氧化镉3%,三氧化二钴2%,三氧化二镍6%。
实施例3
石英砂48%,氧化钙10%,氧化镁2%,硝酸铵8%,氯化钠5%,氯化铵4%,过氧化氢2%,氧化铜3%,氧化镉5%,三氧化二钴4%,三氧化二镍5%。
实施例4
石英砂50%,氧化钙15%,氧化镁4%,硝酸铵6%,氯化钠5%,氯化铵2%,过氧化氢2%,氧化铜3%,氧化镉3%,三氧化二钴4%,三氧化二镍3%。
以上显示和描述了本发明的基本原理、主要特征及优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界。
Claims (6)
1.一种高品质琉璃,其特征在于:其组成成分及其重量份比例为:
粒径范围是0.2mm-0.5mm的石英砂40%-50%;
助熔剂:氧化钙10%-15%和氧化镁2%-5%;
澄清剂:硝酸铵6%-12%和、氯化钠5%-10%和氯化铵2%-5%;
氧化剂:过氧化氢2%-5%;
着色剂:氧化铜3%-5%,氧化镉3%-8%,三氧化二钴2%-6%和三氧化二镍3%-8%;
其他助剂:脂肪醇苯磺酸钠2%-5%,双氧水1%-4%和过硫酸盐1%-3%。
2.根据权利要求1所述的一种高品质琉璃,其特征在于:所述石英砂的粒径为0.3mm。
3.根据权利要求1所述的一种高品质琉璃,其特征在于:所述石英砂42%,氧化钙10%,氧化镁2%,硝酸铵6%,氯化钠5%,氯化铵2%,过氧化氢2%,氧化铜3%,氧化镉3%,三氧化二钴2%,三氧化二镍3%。
4.根据权利要求2所述的一种高品质琉璃,其特征在于:所述石英砂45%,氧化钙12%,氧化镁3%,硝酸铵7%,氯化钠5%,氯化铵2%,过氧化氢2%,氧化铜3%,氧化镉3%,三氧化二钴2%,三氧化二镍6%。
5.根据权利要求2所述的一种高品质琉璃,其特征在于:所述石英砂48%,氧化钙10%,氧化镁2%,硝酸铵8%,氯化钠5%,氯化铵4%,过氧化氢2%,氧化铜3%,氧化镉5%,三氧化二钴4%,三氧化二镍5%。
6.根据权利要求1所述的一种高品质琉璃,其特征在于:所述石英砂50%,氧化钙15%,氧化镁4%,硝酸铵6%,氯化钠5%,氯化铵2%,过氧化氢2%,氧化铜3%,氧化镉3%,三氧化二钴4%,三氧化二镍3%。