CN104445937A - 一种琉璃配方 - Google Patents

一种琉璃配方 Download PDF

Info

Publication number
CN104445937A
CN104445937A CN201410599787.8A CN201410599787A CN104445937A CN 104445937 A CN104445937 A CN 104445937A CN 201410599787 A CN201410599787 A CN 201410599787A CN 104445937 A CN104445937 A CN 104445937A
Authority
CN
China
Prior art keywords
consumption
oxygenant
quartz sand
finings
coloured glaze
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410599787.8A
Other languages
English (en)
Inventor
孙武
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Taicang Scientific Educational New Town Glass Art Planning Central
Original Assignee
Taicang Scientific Educational New Town Glass Art Planning Central
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Taicang Scientific Educational New Town Glass Art Planning Central filed Critical Taicang Scientific Educational New Town Glass Art Planning Central
Priority to CN201410599787.8A priority Critical patent/CN104445937A/zh
Publication of CN104445937A publication Critical patent/CN104445937A/zh
Pending legal-status Critical Current

Abstract

一种琉璃配方，包括石英砂、氧化剂、澄清剂与着色剂，其特征在于：所述澄清剂的用量为氧化剂用量的10-20%，所述着色剂的用量为氧化剂用量的40-60%，所述氧化剂用量为石英砂用量的5-10%；所述石英砂的粒度范围是1—0.5mm。实际使用中，通过使用本发明的琉璃配方能够制得品质优良的琉璃。

Description

一种琉璃配方
技术领域
 本发明涉及无机非晶态材料制备技术领域，尤其涉及一种琉璃配方。
背景技术
琉璃是一种硅酸盐制品，具有悠久的历史，其品质晶莹剔透，光彩夺目，变幻瑰丽，充分体现出东方人的精致、细腻和含蓄，是一种重要的装饰构件，琉璃的主要成分为SiO2。(即二氧化硅)、氧化铝、助熔剂氧化铅和颜料等。
琉璃成分以软化点低、料性长为有优良特性，如此便于工艺制造，适合琉璃成形，琉璃制品的品质体现在光泽好，气泡、条纹、结石少。琉璃的软化点、料性主要取决于琉璃配方中成分的种类及其比例，而在琉璃基础成分中加入澄清剂可以使琉璃熔化温度降低、熔化质量得到提高，避免产生气泡、条纹、结石等缺陷。澄清剂能够在琉璃生产过程中放出分解气体，或自身气化，产生大量的气泡，吸纳周边的小气泡，伴随灰泡上升而促进琉璃澄清。目前常用的澄清剂有二氧化铈、白砒等，但是白砒为剧毒物质，威胁操作人员健康并严重污染环境；二氧化铈的澄清效果尚可，但澄清时间较长，而且铈为稀土元素，成本较昂贵。因此亟需一种软化点低、料性长、澄清效果好、澄清时间短、制品品质优良的琉璃配方。
专利文献CN201210526726.X，公开日2013.03.06，公开了一种建筑用轻质彩色琉璃瓦，所述建筑用轻质彩色琉璃瓦是在每千克氯化镁溶液中加入0.4-0.6kg氧化镁，搅拌6-8分钟，然后依次加入0.05-0.1kg硅酸镁、0.02-0.03kg脲醛树脂、0.06-0.1g碳酸铵、2-3g磷酸三钠和2-3g色料，搅拌20-30分钟，接着将搅拌好的料倒在玻璃纤维布上，刮平压实，自然固化干燥后制得，通过上述方式，、建筑用轻质彩色琉璃瓦表面光滑整洁、色泽鲜艳亮丽，永不褪色，具有优良的抗折抗压、耐急冷急热、耐酸碱性能和耐冻性能，质量轻，吸水率低，且保温和隔音效果好，成本低。但是目前关于适用于制备琉璃工艺品、品质优良的琉璃配方报道较少。
发明内容
本发明所要解决的技术问题是提供一种品质优良的琉璃配方。
为解决上述技术问题，本发明提供一种琉璃配方，包括石英砂、氧化剂、澄清剂与着色剂，所述澄清剂的用量为氧化剂用量的10-20%，所述着色剂的用量为氧化剂用量的40-60%，所述氧化剂用量为石英砂用量的5-10%；所述石英砂的粒度范围是1—0.5mm。
所述澄清剂的用量为氧化剂用量的15%，所述着色剂的用量为氧化剂用量的50%，所述氧化剂用量为石英砂用量的8%；所述石英砂的粒度范围是0.7mm。
所述澄清剂的用量为氧化剂用量的18%，所述着色剂的用量为氧化剂用量的55%，所述氧化剂用量为石英砂用量的7%；所述石英砂的粒度范围是0.8mm。
所述氧化剂为硝酸钾
所述澄清剂为氧化锑。
所述着色剂的组成成分及其重量比例为氧化铁10-20份、氧化铜30-50份、氧化钴5-10份。
与现有技术相比，本发明的有益效果为：由于本发明的琉璃配方中包括石英砂、氧化剂、澄清剂与着色剂，所述澄清剂的用量为氧化剂用量的10-20%，所述着色剂的用量为氧化剂用量的40-60%，所述氧化剂用量为石英砂用量的5-10%；所述石英砂的粒度范围是1—0.5mm，该设计中氧化剂、澄清剂与着色剂在较佳的用量下通过彼此的共同作用，能够使琉璃具有较佳的品质。
具体实施方式
    为使本发明的目的、技术方案和优点更加清楚明白，下面结合实施方式和附图，对本发明做进一步详细说明。在此，本发明的示意性实施方式及说明用于解释本发明，但并不作为对本发明的限定。
本发明的一种琉璃配方，包括石英砂、氧化剂、澄清剂与着色剂，所述澄清剂的用量为氧化剂用量的10-20%，所述着色剂的用量为氧化剂用量的40-60%，所述氧化剂用量为石英砂用量的5-10%；所述石英砂的粒度范围是1—0.5mm。
优选澄清剂的用量为氧化剂用量的15%，所述着色剂的用量为氧化剂用量的50%，所述氧化剂用量为石英砂用量的8%；所述石英砂的粒度范围是0.7mm。
优选澄清剂的用量为氧化剂用量的18%，所述着色剂的用量为氧化剂用量的55%，所述氧化剂用量为石英砂用量的7%；所述石英砂的粒度范围是0.8mm。
优选氧化剂为硝酸钾
优选澄清剂为氧化锑。
优选着色剂的组成成分及其重量比例为氧化铁10-20份、氧化铜30-50份、氧化钴5-10份。
实施例1：
一琉璃配方，包括石英砂、氧化剂、澄清剂与着色剂，澄清剂的用量为氧化剂用量的15%，所述着色剂的用量为氧化剂用量的50%，所述氧化剂用量为石英砂用量的8%；所述石英砂的粒度范围是0.7mm。且在此实施例中，氧化剂为硝酸钾；澄清剂为氧化锑；着色剂的组成成分及其重量比例为氧化铁15份、氧化铜40份、氧化钴8份。
实施例2
一琉璃配方，包括石英砂、氧化剂、澄清剂与着色剂，澄清剂的用量为氧化剂用量的18%，所述着色剂的用量为氧化剂用量的55%，所述氧化剂用量为石英砂用量的7%；所述石英砂的粒度范围是0.8mm。且在此实施例中，氧化剂为硝酸钾；澄清剂为氧化锑；着色剂的组成成分及其重量比例为氧化铁18份、氧化铜48份、氧化钴6份。
本发明的配方即与组分有关又与组分的含量有关，具体的氧化剂、澄清剂与着色剂在较佳的用量下通过彼此的共同作用，能够使琉璃具有优良的品质。

Claims (6)

1.一种琉璃配方，包括石英砂、氧化剂、澄清剂与着色剂，其特征在于：所述澄清剂的用量为氧化剂用量的10-20%，所述着色剂的用量为氧化剂用量的40-60%，所述氧化剂用量为石英砂用量的5-10%；所述石英砂的粒度范围是1—0.5mm。
2.根据权利要求1所述的琉璃配方，其特征在于：所述澄清剂的用量为氧化剂用量的15%，所述着色剂的用量为氧化剂用量的50%，所述氧化剂用量为石英砂用量的8%；所述石英砂的粒度范围是0.7mm。
3.根据权利要求1所述的琉璃配方，其特征在于：所述澄清剂的用量为氧化剂用量的18%，所述着色剂的用量为氧化剂用量的55%，所述氧化剂用量为石英砂用量的7%；所述石英砂的粒度范围是0.8mm。
4.根据权利要求1所述的琉璃配方，其特征在于：所述氧化剂为硝酸钾。
5.根据权利要求1所述的琉璃配方，其特征在于：所述澄清剂为氧化锑。
6.根据权利要求1所述的琉璃配方，其特征在于：所述着色剂的组成成分及其重量比例为氧化铁10-20份、氧化铜30-50份、氧化钴5-10份。
CN201410599787.8A 2014-10-31 2014-10-31 一种琉璃配方 Pending CN104445937A (zh)