CN104493073A - 一种耐高温紫木节型砂及其制备方法 - Google Patents

一种耐高温紫木节型砂及其制备方法 Download PDF

Info

Publication number
CN104493073A
CN104493073A CN201410689046.9A CN201410689046A CN104493073A CN 104493073 A CN104493073 A CN 104493073A CN 201410689046 A CN201410689046 A CN 201410689046A CN 104493073 A CN104493073 A CN 104493073A
Authority
CN
China
Prior art keywords
parts
sand
molding sand
obsidian
particle
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410689046.9A
Other languages
English (en)
Inventor
张在武
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
MAANSHAN HENGDA WEAR-RESISTANT MATERIALS Co Ltd
Original Assignee
MAANSHAN HENGDA WEAR-RESISTANT MATERIALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by MAANSHAN HENGDA WEAR-RESISTANT MATERIALS Co Ltd filed Critical MAANSHAN HENGDA WEAR-RESISTANT MATERIALS Co Ltd
Priority to CN201410689046.9A priority Critical patent/CN104493073A/zh
Publication of CN104493073A publication Critical patent/CN104493073A/zh
Pending legal-status Critical Current

Abstract

一种耐高温紫木节型砂，由下列重量份的原料制成：饱和脂肪酸2-3、高炉瓦斯泥70-80、紫木节160-180、黑曜岩30-40、脱硫灰30-40、重烧氧化镁28-33、马铃薯渣粉2-3、膨润土11-13、水适量、助剂20-30；本发明型砂通过使用高炉瓦斯泥、紫木节等原料造粒烧结，耐热性好，透气性好、分散性好，铸件气孔现象少；通过使用铃薯渣粉，不仅湿拉强度高，而且溃散性好，不粘铸件；通过使用黑曜岩，润滑性好，易造型。

Description

一种耐高温紫木节型砂及其制备方法
技术领域
本发明涉及铸造领域，尤其涉及一种耐高温紫木节型砂及其制备方法。
背景技术
目前型砂存在粒径大小难控制的问题，影响铸件的成品率和造型精度。还有，对于不同种类的铸件缺少专门的型砂，使得铸造精度不高，成品率低。
传统粘土型砂有很多优点，但是存在不易回收利用，透气性差、流动性不好、分散性不好、溃散性差、散热不好、环境污染严重的缺点。紫木节粘土较普通粘土具有优良的特性，烧结后能耐较高的温度，可以作为型砂的原料。
以上缺点需要改进。
发明内容
本发明的目的在于提供一种耐高温紫木节型砂及其制备方法，该型砂耐热性好，透气性好、分散性好，铸件气孔现象少，润滑性好，易造型。
本发明的技术方案如下：
一种耐高温紫木节型砂，其特征在于由下列重量份的原料制成：饱和脂肪酸2-3、高炉瓦斯泥70-80、紫木节160-180、黑曜岩30-40、脱硫灰30-40、重烧氧化镁28-33、马铃薯渣粉2-3、膨润土11-13、水适量、助剂20-30；
    所述助剂由下列重量份的原料制成：铬铁矿砂6-8、陶瓷砂4-5、核桃砂2-3、氧化铝3-4、二氧化硅4-5、宝珠砂5-7、粘土2-3、硅烷偶联剂kh-550 0.5-1、氧化镁0.4-0.7；制备方法为：将氧化铝、氧化镁、二氧化硅混合后进行球磨，过200目筛，在1400-1500℃下煅烧2-2.5小时，加入冷水中激冷，再粉碎成粒径小于2mm的颗粒，加入铬铁矿砂、核桃砂，研磨30-40分钟，加入其他剩余成分，研磨20-30分钟，即得。
所述耐高温紫木节型砂的制备方法，其特征在于包括以下步骤：
（1）将高炉瓦斯泥、紫木节、脱硫灰、重烧氧化镁混合，粉碎，过50目筛，加入7-9%重量份的水搅拌均匀，造粒，粒径在0.05-2.5mm，送入煅烧炉中，在300-400℃下预烧20-25分钟，然后在1300-1340℃下烧结，取出，打磨至表面粗糙度≤0.1mm，得到粘土颗粒；
（2）将黑曜岩加热至融化，加入冷水中激冷，粉碎成0.05-1.5mm的黑曜岩颗粒；
（3）将所述粘土颗粒、黑曜岩颗粒与其他剩余成分混合，再加入3.2-3.5%重量份的水混合8-13分钟，即得。
本发明的有益效果
本发明型砂通过使用高炉瓦斯泥、紫木节等原料造粒烧结，耐热性好，透气性好、分散性好，铸件气孔现象少；通过使用铃薯渣粉，不仅湿拉强度高，而且溃散性好，不粘铸件；通过使用黑曜岩，润滑性好，易造型。本发明助剂耐高温，分散性好，润滑性好，与粘土颗粒的亲合力好，能增加型砂的可塑性、透气性、流动性、耐热性，防止粘土颗粒粘结，提高铸件的成品率。
具体实施方式
一种耐高温紫木节型砂，由下列重量份（公斤）的原料制成：饱和脂肪酸2.5、高炉瓦斯泥75、紫木节170、黑曜岩35、脱硫灰35、重烧氧化镁30、马铃薯渣粉2.5、膨润土12、水适量、助剂25；
    所述助剂由下列重量份（公斤）的原料制成：铬铁矿砂7、陶瓷砂4.5、核桃砂2.5、氧化铝3.5、二氧化硅4.5、宝珠砂6、粘土2.5、硅烷偶联剂kh-550 0.7、氧化镁0.6；制备方法为：将氧化铝、氧化镁、二氧化硅混合后进行球磨，过200目筛，在1450℃下煅烧2.3小时，加入冷水中激冷，再粉碎成粒径小于2mm的颗粒，加入铬铁矿砂、核桃砂，研磨35分钟，加入其他剩余成分，研磨25分钟，即得。
所述耐高温紫木节型砂的制备方法，包括以下步骤：
（1）将高炉瓦斯泥、紫木节、脱硫灰、重烧氧化镁混合，粉碎，过50目筛，加入8%重量份的水搅拌均匀，造粒，粒径在0.05-2.5mm，送入煅烧炉中，在350℃下预烧23分钟，然后在1330℃下烧结，取出，打磨至表面粗糙度≤0.1mm，得到粘土颗粒；
（2）将黑曜岩加热至融化，加入冷水中激冷，粉碎成0.05-1.5mm的黑曜岩颗粒；
（3）将所述粘土颗粒、黑曜岩颗粒与其他剩余成分混合，再加入3.3%重量份的水混合11分钟，即得。
本实施例得到的型砂试验数据如下：湿压强度为80KPa，透气性110，湿拉强度为2.7KPa。

Claims (2)

1.一种耐高温紫木节型砂，其特征在于由下列重量份的原料制成：饱和脂肪酸2-3、高炉瓦斯泥70-80、紫木节160-180、黑曜岩30-40、脱硫灰30-40、重烧氧化镁28-33、马铃薯渣粉2-3、膨润土11-13、水适量、助剂20-30；
    所述助剂由下列重量份的原料制成：铬铁矿砂6-8、陶瓷砂4-5、核桃砂2-3、氧化铝3-4、二氧化硅4-5、宝珠砂5-7、粘土2-3、硅烷偶联剂kh-550 0.5-1、氧化镁0.4-0.7；制备方法为：将氧化铝、氧化镁、二氧化硅混合后进行球磨，过200目筛，在1400-1500℃下煅烧2-2.5小时，加入冷水中激冷，再粉碎成粒径小于2mm的颗粒，加入铬铁矿砂、核桃砂，研磨30-40分钟，加入其他剩余成分，研磨20-30分钟，即得。
2.根据权利要求1所述耐高温紫木节型砂的制备方法，其特征在于包括以下步骤：
（1）将高炉瓦斯泥、紫木节、脱硫灰、重烧氧化镁混合，粉碎，过50目筛，加入7-9%重量份的水搅拌均匀，造粒，粒径在0.05-2.5mm，送入煅烧炉中，在300-400℃下预烧20-25分钟，然后在1300-1340℃下烧结，取出，打磨至表面粗糙度≤0.1mm，得到粘土颗粒；
（2）将黑曜岩加热至融化，加入冷水中激冷，粉碎成0.05-1.5mm的黑曜岩颗粒；
（3）将所述粘土颗粒、黑曜岩颗粒与其他剩余成分混合，再加入3.2-3.5%重量份的水混合8-13分钟，即得。
CN201410689046.9A 2014-11-26 2014-11-26 一种耐高温紫木节型砂及其制备方法 Pending CN104493073A (zh)