CN104475644A - 一种铸造造型面砂及其制备方法 - Google Patents

一种铸造造型面砂及其制备方法 Download PDF

Info

Publication number
CN104475644A
CN104475644A CN201410607474.2A CN201410607474A CN104475644A CN 104475644 A CN104475644 A CN 104475644A CN 201410607474 A CN201410607474 A CN 201410607474A CN 104475644 A CN104475644 A CN 104475644A
Authority
CN
China
Prior art keywords
parts
weight
water
good
clay
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410607474.2A
Other languages
English (en)
Inventor
孙修财
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
FANCHANG QIXIANG CASTING FACTORY
Original Assignee
FANCHANG QIXIANG CASTING FACTORY
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by FANCHANG QIXIANG CASTING FACTORY filed Critical FANCHANG QIXIANG CASTING FACTORY
Priority to CN201410607474.2A priority Critical patent/CN104475644A/zh
Publication of CN104475644A publication Critical patent/CN104475644A/zh
Pending legal-status Critical Current

Abstract

一种铸造造型面砂,由下列重量份的原料制成:氟硅酸钠3-4、金属硅粉18-22、蓝晶石10-15、黑云母6-8、疏水炭黑3-5、椰子油酸1-2、磷酸钙1-2、甲醇3-4、蓖麻油硼酸酯2-3、硬酯酸钠1-2、氧化铁红4-5、有机膨润土3-4、粘土220-240、水适量、助剂20-30;本发明型砂使用了金属硅粉,增加了型砂的耐高温性能,型砂溃散性好;通过使用氟硅酸钠、硬酯酸钠、氧化铁红、有机膨润土,粘结性好,而且脱模性好,防止落砂;通过使用粘土,粒径大小合适,不仅透气性好、流动性好、分散性好,而且铸件表面光滑,还可以回收再利用;该型砂适用于面砂,铸件表面光洁,不易落砂。

Description

一种铸造造型面砂及其制备方法
技术领域
[0001] 本发明涉及铸造领域,尤其涉及一种铸造造型面砂及其制备方法。
背景技术
[0002] 目前型砂存在的主要问题有:1、粒径大小难控制,如果型砂粒径太大,虽然透气性较好,但是铸件表面比较粗糙,光洁度不好;如果型砂料径太小,导致砂型透气性不好,铸件有气孔产生。2、散热不良,激冷效果差,复杂铸件内部易出现缩松、缩孔现象。3、分散性、流动性不好,易结块、起砂豆。4、落砂严重,报废率高。5、对于不同种类的铸件缺少专门的型砂。
[0003] 传统粘土型砂有很多优点,但是存在不易回收利用,透气性差、流动性不好、分散性不好、溃散性差、散热不好、环境污染严重的缺点。
[0004] 因此,型砂存在的以上缺点需要克服。
发明内容
[0005] 本发明的目的在于提供一种铸造造型面砂及其制备方法,该型砂溃散性好,粘结性好,而且脱模性好,防止落砂,粒径大小合适,不仅透气性好、流动性好、分散性好,而且铸件表面光滑,还可以回收再利用,适用于面砂,铸件表面光洁,不易落砂。
[0006] 本发明的技术方案如下:
一种铸造造型面砂,其特征在于由下列重量份的原料制成:氟硅酸钠3-4、金属硅粉18-22、蓝晶石10-15、黑云母6-8、疏水炭黑3-5、椰子油酸1_2、磷酸钙1_2、甲醇3_4、蓖麻油硼酸酯2-3、硬酯酸钠1-2、氧化铁红4-5、有机膨润土 3-4、粘土 220-240、水适量、助剂20-30 ;
所述助剂由下列重量份的原料制成:钾长石2-3、光伏硅切割固体废料20-23、炭黑1-2、渣油液0.5-1、酚醛树脂1-1.4、碳酸钠0.8-1.2、膨润土 2-2.5、阳离子淀粉1-1.4、水适量;制备方法为:将钾长石、光伏硅切割固体废料、炭黑混合,进行球磨,过150目筛,力口入7-9重量份的水,搅拌均匀,再加入酚醛树脂,搅拌均匀,造粒,粒径在0.5-2mm,然后在1400-1600°C下煅烧20-30分钟,得到颗粒;将碳酸钠、膨润土、阳离子淀粉混合,加入5-7重量份的水,加热至70-80°C,搅拌3-4分钟,加入所述颗粒,搅拌均匀,烘干,粉碎,粒径在
0.5-2.5mm,再与其他剩余成分混合,搅拌均匀,即得。
[0007] 所述铸造造型面砂的制备方法,其特征在于包括以下步骤:
(1)将粘土、金属硅粉、蓝晶石、黑云母混合,粉碎,过50目筛,加入7-9%重量份的水搅拌均匀,造粒,粒径在0.05-2.5mm,送入煅烧炉中,在300-400°C下预烧20-25分钟,然后在1230-1270°C下烧结,取出,打磨至表面粗糙度彡0.1mm,得到粘土颗粒;
(2)将氟硅酸钠、疏水炭黑、椰子油酸、磷酸钙、甲醇、蓖麻油硼酸酯、硬酯酸钠混合,研磨10-15分钟,得到混合物料;
(3)将所述粘土颗粒、第(2)步得到的物料与其他剩余成分混合,再加入2-3%重量份的水混合均匀,即得。
[0008] 本发明的有益效果
本发明型砂使用了金属硅粉,增加了型砂的耐高温性能,型砂溃散性好;通过使用氟硅酸钠、硬酯酸钠、氧化铁红、有机膨润土,粘结性好,而且脱模性好,防止落砂;通过使用粘土,粒径大小合适,不仅透气性好、流动性好、分散性好,而且铸件表面光滑,还可以回收再利用;该型砂适用于面砂,铸件表面光洁,不易落砂。本发明助剂利用了光伏硅切割固体废料,含有碳化硅等耐高温材料,增加了型砂的耐热性,防止粘土颗粒粘结,减少了环境污染,有利于型砂回收利用,表面有膨润土,粘结性好,可塑性好。
具体实施方式
[0009] 一种铸造造型面砂,由下列重量份(公斤)的原料制成:氟硅酸钠3.5、金属硅粉20、蓝晶石13、黑云母7、疏水炭黑4、椰子油酸1.5、磷酸钙1.5、甲醇3.5、蓖麻油硼酸酯
2.5、硬酯酸钠1.5、氧化铁红4.5、有机膨润土 3.5、粘土 230、水适量、助剂25 ;
所述助剂由下列重量份(公斤)的原料制成:钾长石2.5、光伏硅切割固体废料21、炭黑
1.5、渣油液0.7、酚醛树脂1.2、碳酸钠1、膨润土 2.3、阳离子淀粉1.2、水适量;制备方法为:将钾长石、光伏硅切割固体废料、炭黑混合,进行球磨,过150目筛,加入8重量份的水,搅拌均匀,再加入酚醛树脂,搅拌均匀,造粒,粒径在0.5-2mm,然后在1500°C下煅烧25分钟,得到颗粒;将碳酸钠、膨润土、阳离子淀粉混合,加入6重量份的水,加热至76°C,搅拌3分钟,加入所述颗粒,搅拌均匀,烘干,粉碎,粒径在0.5-2.5mm,再与其他剩余成分混合,搅拌均匀,即得。
[0010] 所述铸造造型面砂的制备方法,包括以下步骤:
(1)将粘土、金属硅粉、蓝晶石、黑云母混合,粉碎,过50目筛,加入8%重量份的水搅拌均匀,造粒,粒径在0.05-2.5mm,送入煅烧炉中,在350°C下预烧23分钟,然后在1250°C下烧结,取出,打磨至表面粗糙度< 0.1mm,得到粘土颗粒;
(2)将氟硅酸钠、疏水炭黑、椰子油酸、磷酸钙、甲醇、蓖麻油硼酸酯、硬酯酸钠混合,研磨13分钟,得到混合物料;
(3)将所述粘土颗粒、第(2)步得到的物料与其他剩余成分混合,再加入2.5%重量份的水混合均匀,即得。
[0011] 本实施例得到的型砂试验数据如下:湿压强度为112KPa,透气性45,热湿拉强度为2.2KPa,常温湿拉强度为24KPa。

Claims (2)

1.一种铸造造型面砂,其特征在于由下列重量份的原料制成:氟硅酸钠3-4、金属硅粉18-22、蓝晶石10-15、黑云母6-8、疏水炭黑3-5、椰子油酸1_2、磷酸钙1_2、甲醇3_4、蓖麻油硼酸酯2-3、硬酯酸钠1-2、氧化铁红4-5、有机膨润土 3-4、粘土 220-240、水适量、助剂20-30 ; 所述助剂由下列重量份的原料制成:钾长石2-3、光伏硅切割固体废料20-23、炭黑1-2、渣油液0.5-1、酚醛树脂1-1.4、碳酸钠0.8-1.2、膨润土 2-2.5、阳离子淀粉1-1.4、水适量;制备方法为:将钾长石、光伏硅切割固体废料、炭黑混合,进行球磨,过150目筛,力口入7-9重量份的水,搅拌均匀,再加入酚醛树脂,搅拌均匀,造粒,粒径在0.5-2mm,然后在1400-1600°C下煅烧20-30分钟,得到颗粒;将碳酸钠、膨润土、阳离子淀粉混合,加入5-7重量份的水,加热至70-80°C,搅拌3-4分钟,加入所述颗粒,搅拌均匀,烘干,粉碎,粒径在0.5-2.5mm,再与其他剩余成分混合,搅拌均匀,即得。
2.根据权利要求1所述铸造造型面砂的制备方法,其特征在于包括以下步骤: (1)将粘土、金属硅粉、蓝晶石、黑云母混合,粉碎,过50目筛,加入7-9%重量份的水搅拌均匀,造粒,粒径在0.05-2.5mm,送入煅烧炉中,在300-400°C下预烧20-25分钟,然后在1230-1270°C下烧结,取出,打磨至表面粗糙度彡0.1mm,得到粘土颗粒; (2)将氟硅酸钠、疏水炭黑、椰子油酸、磷酸钙、甲醇、蓖麻油硼酸酯、硬酯酸钠混合,研磨10-15分钟,得到混合物料; (3)将所述粘土颗粒、第(2)步得到的物料与其他剩余成分混合,再加入2-3%重量份的水混合均匀,即得。
CN201410607474.2A 2014-11-03 2014-11-03 一种铸造造型面砂及其制备方法 Pending CN104475644A (zh)