CN104446352A - 龙泉青瓷茶具 - Google Patents

龙泉青瓷茶具 Download PDF

Info

Publication number
CN104446352A
CN104446352A CN201410731867.4A CN201410731867A CN104446352A CN 104446352 A CN104446352 A CN 104446352A CN 201410731867 A CN201410731867 A CN 201410731867A CN 104446352 A CN104446352 A CN 104446352A
Authority
CN
China
Prior art keywords
parts
tea set
glaze
longquan celadon
temperature
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410731867.4A
Other languages
English (en)
Inventor
黄文香
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410731867.4A priority Critical patent/CN104446352A/zh
Publication of CN104446352A publication Critical patent/CN104446352A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种龙泉青瓷茶具，制作方法包括以下步骤：（1）制备坯体：按重量份数取坯体原材料，混合后经碾碎、沉淀、陈腐，过100目筛成坯泥备用；（2）制备釉料：按重量份数取釉料原材料，混合均匀，湿磨5h，过250目筛筛余0.2%成釉浆备用；（3）将坯泥注浆成型为坯体，干燥后900～980℃素烧5～6h，自然冷却至室温，备用；（4）坯体上采用浸釉法施釉，釉层厚度1.5～1.8mm，干燥后入窑烧制，烧制条件为：以15℃/min的速率升温至580℃，保温3h，再以10℃/min的速率升温至900℃，保温1.5h，再以5℃/min的速率升温至1280℃，保温2h，自然冷却，得到龙泉青瓷茶具。所制得龙泉青瓷茶具釉层丰润，釉色青碧，光泽柔和，晶莹滋润，胜似翡翠，可与古代技艺相媲美。

Description

龙泉青瓷茶具
技术领域
 本发明涉及茶具领域，更具体地，涉及一种龙泉青瓷茶具。
背景技术
龙泉青瓷是汉族传统制瓷工艺的珍品，南朝时期，龙泉汉族劳动人民利用当地优越的自然条件，制造青瓷。靖舍龙泉青瓷是现阶段的杰出代表。在南宋时烧制出了晶莹如玉的粉青釉和梅子青釉，标志着龙泉青瓷达到了颠峰，青如玉、明如镜、薄如纸、声如磬，赏之让人心情畅然。但时代久远，烧制技艺已逐渐失传，现在难以再烧制出完美的龙泉青瓷。
发明内容
本发明的目的是提供一种龙泉青瓷茶具，其釉层丰润，釉色青碧，光泽柔和，晶莹滋润，胜似翡翠，可与古代技艺相媲美。
本发明目的通过以下技术方案予以实现：
提供一种龙泉青瓷茶具坯料，其重量百分比组成：生石灰12～18份，石英18～23份，砂岩8～13份，瓷土19～25份，海蓝宝石0.2～0.5份，十胜石1～3份。
提供一种龙泉青瓷茶具釉料，其重量百分比组成：釉土28～33份，硅灰石17～22份，坦桑石0.8～2份，木变石6～10份，萤石2～5份。
提供一种龙泉青瓷茶具，制作方法包括以下步骤：
（1）制备坯体：按重量份数取生石灰12～18份，石英18～23份，砂岩8～13份，瓷土19～25份，海蓝宝石0.2～0.5份，十胜石1～3份，混合后经碾碎、沉淀、陈腐，过100目筛成坯泥备用；
（2）制备釉料：按重量份数取釉土28～33份，硅灰石17～22份，坦桑石0.8～2份，木变石6～10份，萤石2～5份，混合均匀，湿磨5h，过250目筛筛余0.2%成釉浆备用；
（3）将坯泥注浆成型为坯体，干燥后900～980℃素烧5～6h，自然冷却至室温，备用；
（4）坯体上采用浸釉法施釉，釉层厚度1.5～1.8mm，干燥后入窑烧制，烧制条件为：以15℃/min的速率升温至580℃，保温3h，再以10℃/min的速率升温至900℃，保温1.5h，再以5℃/min的速率升温至1280℃，保温2h，自然冷却，得到龙泉青瓷茶具。
与现有技术相比，本发明具有以下有益效果：
本发明提供了一种龙泉青瓷茶具，其釉层丰润，釉色青碧，光泽柔和，晶莹滋润，胜似翡翠，可与古代技艺相媲美。
具体实施方式
下面结合具体实施例对本发明作进一步的说明。
实施例1
本实施例公开了一种龙泉青瓷茶具坯料，其重量百分比组成：生石灰12份，石英18份，砂岩8份，瓷土19份，海蓝宝石0.2份，十胜石1份。
实施例2
本实施例公开了一种龙泉青瓷茶具坯料，其重量百分比组成：生石灰18份，石英23份，砂岩13份，瓷土25份，海蓝宝石0.5份，十胜石3份。
实施例3
本实施例公开了一种龙泉青瓷茶具坯料，其重量百分比组成：生石灰15份，石英20份，砂岩10份，瓷土21份，海蓝宝石0.4份，十胜石2份。
实施例4
本实施例公开了一种龙泉青瓷茶具釉料，其重量百分比组成：釉土28份，硅灰石17份，坦桑石0.8份，木变石6份，萤石2份。
实施例5
本实施例公开了一种龙泉青瓷茶具釉料，其重量百分比组成：釉土33份，硅灰石22份，坦桑石2份，木变石10份，萤石5份。
实施例6
本实施例公开了一种龙泉青瓷茶具釉料，其重量百分比组成：釉土30份，硅灰石19份，坦桑石1份，木变石8份，萤石4份。
实施例7
本实施例公开了一种龙泉青瓷茶具，制作方法包括以下步骤：
（1）制备坯体：按重量份数取实施例1～3的坯料，混合后经碾碎、沉淀、陈腐，过100目筛成坯泥备用；
（2）制备釉料：按重量份数取实施例4～6的釉料，混合均匀，湿磨5h，过250目筛筛余0.2%成釉浆备用；
（3）将坯泥注浆成型为坯体，干燥后950℃素烧5h，自然冷却至室温，备用；
（4）坯体上采用浸釉法施釉，釉层厚度1.7mm，干燥后入窑烧制，烧制条件为：以15℃/min的速率升温至580℃，保温3h，再以10℃/min的速率升温至900℃，保温1.5h，再以5℃/min的速率升温至1280℃，保温2h，自然冷却，得到龙泉青瓷茶具。
所制得龙泉青瓷茶具釉层丰润，釉色青碧，光泽柔和，晶莹滋润，胜似翡翠，可与古代技艺相媲美。

Claims (3)

1.一种龙泉青瓷茶具坯料，其特征在于，其重量百分比组成：生石灰12～18份，石英18～23份，砂岩8～13份，瓷土19～25份，海蓝宝石0.2～0.5份，十胜石1～3份。
2.一种龙泉青瓷茶具釉料，其特征在于，其重量百分比组成：釉土28～33份，硅灰石17～22份，坦桑石0.8～2份，木变石6～10份，萤石2～5份。
3.一种龙泉青瓷茶具，其特征在于，所述龙泉青瓷茶具的制作方法包括以下步骤：
（1）制备坯体：按重量份数取生石灰12～18份，石英18～23份，砂岩8～13份，瓷土19～25份，海蓝宝石0.2～0.5份，十胜石1～3份，混合后经碾碎、沉淀、陈腐，过100目筛成坯泥备用；
（2）制备釉料：按重量份数取釉土28～33份，硅灰石17～22份，坦桑石0.8～2份，木变石6～10份，萤石2～5份，混合均匀，湿磨5h，过250目筛筛余0.2%成釉浆备用；
（3）将坯泥注浆成型为坯体，干燥后900～980℃素烧5～6h，自然冷却至室温，备用；
（4）坯体上采用浸釉法施釉，釉层厚度1.5～1.8mm，干燥后入窑烧制，烧制条件为：以15℃/min的速率升温至580℃，保温3h，再以10℃/min的速率升温至900℃，保温1.5h，再以5℃/min的速率升温至1280℃，保温2h，自然冷却，得到龙泉青瓷茶具。
CN201410731867.4A 2014-12-06 2014-12-06 龙泉青瓷茶具 Pending CN104446352A (zh)