CN104418557B - 一种轻质高强蛭石硅酸钙板及其制备方法 - Google Patents

一种轻质高强蛭石硅酸钙板及其制备方法 Download PDF

Info

Publication number
CN104418557B
CN104418557B CN201310401006.5A CN201310401006A CN104418557B CN 104418557 B CN104418557 B CN 104418557B CN 201310401006 A CN201310401006 A CN 201310401006A CN 104418557 B CN104418557 B CN 104418557B
Authority
CN
China
Prior art keywords
vermiculite
calcium silicate
silicate board
hours
strength light
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310401006.5A
Other languages
English (en)
Other versions
CN104418557A (zh
Inventor
陈克俭
上官军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Cimic Health Environment Technology Co ltd
Shanghai Yuexin Health Group Co ltd
Original Assignee
Shanghai Yuexin Health Group Co Ltd
Shanghai Cimic Health Environment Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Yuexin Health Group Co Ltd, Shanghai Cimic Health Environment Technology Co Ltd filed Critical Shanghai Yuexin Health Group Co Ltd
Priority to CN201310401006.5A priority Critical patent/CN104418557B/zh
Publication of CN104418557A publication Critical patent/CN104418557A/zh
Application granted granted Critical
Publication of CN104418557B publication Critical patent/CN104418557B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种轻质高强蛭石硅酸钙板及其制备方法，(1)取料：按重量份称取蛭石、玻化珠、纤维素、纸浆、沸石、石英砂、水泥、防水剂、分散剂为原料；(2)拌料：将上述原料通过搅拌器混合、搅拌均匀；(3)成型：将搅拌均匀的物料通过高压泵注入皮带中，采用皮带流浆输送滚筒压制成型；(4)烘干：成型后的产品先常温养护4小时，然后100℃蒸压18小时，最后以120℃烘干温度烘5小时。与现有技术相比，本发明具有装饰效果好、功能强大、实用性强等优点。

Description

一种轻质高强蛭石硅酸钙板及其制备方法
技术领域
本发明涉及一种建筑用复合板，尤其是涉及一种轻质高强蛭石硅酸钙板。
背景技术
硅酸钙板以优质高标号水泥为基体材料，并配以天然纤维增强，经先进生产工艺成型、加压、高温蒸养等特殊技术处理而制成，是一种具有优良性能的新型建筑和工业用板材其产品防火，防潮，隔音，防虫蛀，耐久性强。是吊顶，隔断的理想装饰板材。
蛭石板俗称保温板或耐火板是新型的保温隔热材料，蛭石板是用膨胀蛭石和一定剂量的黏合剂，经过热压或是冷压而制成的板材。该板材具有保温、隔热、防火等特点。此产品可以用在防火门芯，壁炉内衬，墙体材料。
目前国内外生产的蛭石板生产工艺是以人工辅料，输送通过热压成型，其缺点是；人工费用过高，产量低，生产成本高，每天生产平均每小时生产15块。
发明内容
本发明的目的就是为了克服上述现有技术存在的缺陷而提供一种人工费低，生产成本低，产量高的轻质高强蛭石硅酸钙板。
本发明的目的可以通过以下技术方案来实现：一种轻质高强蛭石硅酸钙板，其特征在于，包括以下体积百分含量组分的原料：
所述的原料包括以下体积百分含量的组分：
所述的蛭石为经过膨化处理的蛭石；所述的膨化处理是将蛭石原料置于膨化炉中于600-900℃，经过10s膨化而成。
一种轻质高强蛭石硅酸钙板的制备方法，其特征在于，包括以下步骤：
(1)取料：按体积百分含量称取蛭石、纤维素、纸浆、沸石、石英砂、水泥、电气石为原料；
(2)拌料：将上述原料通过搅拌器混合、搅拌均匀；
(3)成型：将搅拌均匀的物料通过高压泵注入皮带中，采用皮带流浆输送滚筒压制成型；
(4)烘干：成型后的产品先常温养护4小时，然后100℃蒸压18小时，最后以120℃烘干温度烘5小时。
步骤(2)所述的搅拌为高速搅拌5-10min。
步骤(3)所述的皮带流浆输送滚筒的输送速度为50m/min。
本发明轻质高强蛭石硅酸钙板生产工艺流程是以全自动流浆法生产通过冷压成型，高温养护，烘干，包装。其优点；人工费低，生产成本低，产量高，每天平均每小时生产产量200张。
与现有技术相比，本发明具有以下优点：
1.0该产品既具有蛭石的独特优势外还具有硅酸钙板的特点
1.1防火性能好，耐火级别可达A级；
1.2防腐蚀、防霉变
1.3保温隔热，导热系数低
1.4降噪、隔音
1.5强度高、抗冲击性能好
1.6耐水性能好，吸湿率高
2.0是极佳的绿色环保产品
能随着温度的变化自然呼吸，自动调节室内空气的干湿度，同时可释放负氧离子，改善室内的居住环境。
3.0产品厚度范围大，使用面广
产品既可制作成5-10MM的薄板，也可制作成20-30MM的厚板，可灵活应用。
4.0产品产量高、成本低
5.0产品轻质，施工安装方便
5.1该产品内加入了膨胀蛭石，具有轻质的优点
5.2产品的背面可旋入锚栓或螺钉，实现了机械挂贴的方式，施工安装、拆卸极其方便。
6.0应用广泛
可用于建筑的内墙板、外墙板、吊顶板、幕墙衬板、复合墙体面板等部位。
附图说明
图1为本发明复合式一体板的结构示意图。
具体实施方式
下面结合附图和具体实施例对本发明进行详细说明。
实施例1
(1)取料：按体积百分比称取原料：蛭石50％；纤维素6％；纸浆4％；沸石4％；石英砂25％；水泥10％；电气石1％；所述的蛭石为经过膨化处理的蛭石；所述的膨化处理是将蛭石原料(产地：新疆)置于膨化炉中于600-900℃，经过10s膨化而成。
(2)拌料：将上述原料通过搅拌器高速搅拌5-10min混合、搅拌均匀；
(3)成型：将搅拌均匀的物料通过高压泵注入皮带中，采用皮带流浆输送滚筒压制成型；皮带流浆输送滚筒的输送速度为50m/min；
(4)烘干：成型后的产品先常温养护4小时，然后100℃蒸压18小时，最后以120℃烘干温度烘5小时。
一种轻质高强蛭石硅酸钙板的制备方法，包括以下步骤：
实施例2
一种轻质高强蛭石硅酸钙板的制备方法，包括以下步骤：
(1)取料：按体积百分比称取原料：蛭石55.12％；纤维素4.97％；纸浆2.24％；沸石2.67％；石英砂21.59％；水泥12.98％；电气石0.43％；所述的蛭石为经过膨化处理的蛭石；所述的膨化处理是将蛭石原料(产地：新疆)置于膨化炉中于600-900℃，经过10s膨化而成。
(2)拌料：将上述原料通过搅拌器高速搅拌5-10min混合、搅拌均匀；
(3)成型：将搅拌均匀的物料通过高压泵注入皮带中，采用皮带流浆输送滚筒压制成型；皮带流浆输送滚筒的输送速度为50m/min；
(4)烘干：成型后的产品先常温养护4小时，然后100℃蒸压18小时，最后以120℃烘干温度烘5小时。
所得蛭石硅酸钙板结构如图1所示：蛭石1均匀分散在其他材料2之间。
实施例3
一种轻质高强蛭石硅酸钙板的制备方法，包括以下步骤：
(1)取料：按体积百分比称取原料：蛭石60％；纤维素3％；纸浆1％；沸石1％；石英砂20％；水泥15％；电气石0％；所述的蛭石为经过膨化处理的蛭石；所述的膨化处理是将蛭石原料(产地：新疆)置于膨化炉中于600-900℃，经过10s膨化而成。
(2)拌料：将上述原料通过搅拌器高速搅拌5-10min混合、搅拌均匀；
(3)成型：将搅拌均匀的物料通过高压泵注入皮带中，采用皮带流浆输送滚筒压制成型；皮带流浆输送滚筒的输送速度为50m/min；
(4)烘干：成型后的产品先常温养护4小时，然后100℃蒸压18小时，最后以120℃烘干温度烘5小时。
上述实施例所得蛭石硅酸钙板的性能如下：
实施例1 实施例2 实施例3
密度(g/cm3) 1.2 1.13 1.05
抗折强度MPA 11.6 10.8 10.3
空气中吸湿率(％) 15.2 20.4 24.8
湿胀率(％) 0.075 0.082 0.095
变形(浸水后烘干) 0.086 0.092 0.098
防火性能 A A A
导热系数 0.13 0.124 0.11

Claims (5)

1.一种轻质高强蛭石硅酸钙板，其特征在于，包括以下体积百分含量组分的原料：
所述的蛭石为经过膨化处理的蛭石。
2.根据权利要求1所述的轻质高强蛭石硅酸钙板，其特征在于，所述的原料包括以下体积百分含量的组分：
3.根据权利要求1或2所述的轻质高强蛭石硅酸钙板，其特征在于，所述的膨化处理是将蛭石原料置于膨化炉中于600-900℃，经过10s膨化而成。
4.一种根据权利要求1-3中任一所述的轻质高强蛭石硅酸钙板的制备方法，其特征在于，包括以下步骤：
(1)取料：按体积百分含量称取蛭石、纤维素、纸浆、沸石、石英砂、水泥、电气石为原料；
(2)拌料：将上述原料通过搅拌器混合、搅拌均匀；
(3)成型：将搅拌均匀的物料通过高压泵注入皮带中，采用皮带流浆输送滚筒压制成型；
(4)烘干：成型后的产品先常温养护4小时，然后100℃蒸压18小时，最后以120℃烘干温度烘5小时。
5.根据权利要求4所述的一种轻质高强蛭石硅酸钙板的制备方法，其特征在于，步骤(3)所述的皮带流浆输送滚筒的输送速度为50m/min。
CN201310401006.5A 2013-09-05 2013-09-05 一种轻质高强蛭石硅酸钙板及其制备方法 Active CN104418557B (zh)