CN104152016A - 一种加快电路板散热的三防漆 - Google Patents
一种加快电路板散热的三防漆 Download PDFInfo
- Publication number
- CN104152016A CN104152016A CN201410310031.7A CN201410310031A CN104152016A CN 104152016 A CN104152016 A CN 104152016A CN 201410310031 A CN201410310031 A CN 201410310031A CN 104152016 A CN104152016 A CN 104152016A
- Authority
- CN
- China
- Prior art keywords
- circuit board
- polyester resin
- unsaturated polyester
- auxiliary agent
- heat radiation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及印制电路板防护技术领域,具体涉及一种加快电路板散热的三防漆,本发明三防漆以不饱和聚酯树脂作为成膜物质,先将其在溶剂中经超声处理,使其与其它原料更易反应和相容,加快固化速率,改善漆膜性能,加入的银浆具有良好的导热系数,能够加快漆膜散热,正硅酸乙酯、二乙二醇二苯甲酸酯等原料能够改善不饱和聚酯树脂的性能,减小收缩率,避免漆膜开裂;本发明制备的三防漆在常温下即可实现快速固化,且漆膜透明度高、丰满牢固,耐热氧化,易喷涂,不仅具备传统的三防性能,还具有良好的导热能力,能够加快电路板散热,避免热量堆积对电路板的损害,提高工作安全性。
Description
技术领域
本发明涉及印制电路板防护技术领域,具体涉及一种加快电路板散热的三防漆及其制备方法。
背景技术
印制电路板是指在绝缘基材上,按照预定设计形成从点到点互联线路以及印制元件,是电子元器件电气连接的提供者。电路板在日常生活中非常常见,小到手机、U盘、照相机,大到航天航空、高铁动车等高端产品。随着电子产品种类及数量的日趋增加,要提高电子产品的竞争力,严控电路板的质量是尤为重要的环节。在实际应用过程中,电路板的使用环境复杂多样,可能面临潮湿、高热、盐雾、低温、震动、高尘等环境,如果不进行相应有效的防护,电路板将会迅速出现腐蚀、变形、霉变、老化等问题,最终导致电路失效,设备出现故障。
为了减轻外界环境对电路板的破坏,保证设备正常运作,常在电路板表面喷涂防护漆,也称之为三防漆,其主要的化学成分为丙烯酸酯、硅酮、聚氨酯、环氧树脂等,工作原理是在电路板表面形成一层保护膜,以使电路板免受工作环境损害,从而增进电路板的质量可靠性,现有的三防漆主要存在防护周期短、高温易脱落、不能抵御环境污染物,尤其是化学污染物的腐蚀、不易返修、有毒有害等缺点,因此有必要改进三防漆配方,进一步加强电路板的综合性能,提升防护效果,以满足集成电路技术迅猛发展的需求。
发明内容
本发明的目的在于,提供一种加快电路板散热的三防漆,提高漆膜的导热系数,减缓设备工作产生的高温对电路板的损害,为了达到上述目的,本发明采用的技术方案如下:
一种加快电路板散热的三防漆,其特征在于,该三防漆由40-50重量份的主料和2-4重量份的助剂制成,主料包含以下重量份的原料:硬脂酸锌1-3、196不饱和聚酯树脂40-48、过氧化二异丙苯0.5-1、正硅酸乙酯6-8、环烷酸锌1-2、吡啶硫酮锌1-2、二乙二醇二苯甲酸酯6-9、促进剂D1-2、二甲苯8-10、异丙醇铝1-2、银浆0.1-0.2;助剂包含以下重量份的原料:负离子粉1-2、亚磷酸三乙酯6-8、丙二醇甲醚10-12、苯并环丁烯4-6、异丙醇胺2-4、熟桐油12-15、十二烷基葡萄糖苷2-3、香柠檬油0.1-0.2、苯甲醇4-6、聚二甲基硅氧烷1-2;
所述的一种加快电路板散热的三防漆,其制备方法如下:
(1)助剂的制备:先将负离子粉与十二烷基葡萄糖苷、亚磷酸三乙酯混合,搅拌均匀后研磨15-20min,制成负离子粉浆料备用,将苯并环丁烯、熟桐油与丙二醇甲醚、苯甲醇混合,搅拌30-40min,再加入其它剩余物料混合搅拌20-30min,最后滴加负离子粉浆料,边滴加边搅拌,滴加结束即得;
(2)将助剂、硬脂酸锌、吡啶硫酮锌、异丙醇铝、银浆加入二甲苯中,加热至35-50℃,缓慢搅拌40-50min,至物料完全溶解分散;
(3)将不饱和聚酯树脂加入步骤(2)所得的物料中,超声分散20-30min,加入其它剩余物料,搅拌40-50min,搅拌结束后冷却至室温即得,成品在1-2h内使用完毕即可。
与现有技术相比,本发明制备的三防漆优点在于:以不饱和聚酯树脂作为成膜物质,并将其在溶剂中先进行超声处理,改变其表面活性,使其与其它原料更易反应和相容,从而加快固化速率,提高漆膜性能,银浆具有良好的导热系数,能够加快电路板散热,正硅酸乙酯、二乙二醇二苯甲酸酯等原料能够改善不饱和聚酯树脂的性能,改善漆膜干燥时的收缩率,避免漆膜干燥后开裂;本发明制备的三防漆在常温下即可实现快速固化,且漆膜透明度高、丰满牢固,耐热氧化,易喷涂,不易老化开裂,不仅具备传统的三防性能,还具有良好的导热能力,能够加快电路板散热,避免热量堆积对电路板的损害,提高工作安全性。
具体实施方式
实施例
本实施例三防漆中的包含45份主料与4份助剂,主料中各组分及其重量份如下:硬脂酸锌2、196不饱和聚酯树脂45、过氧化二异丙苯0.8、正硅酸乙酯8、环烷酸锌1、吡啶硫酮锌2、二乙二醇二苯甲酸酯8、促进剂D2、二甲苯10、异丙醇铝1、银浆0.2;助剂中各组分及其重量份如下:负离子粉2、亚磷酸三乙酯8、丙二醇甲醚12、苯并环丁烯6、异丙醇胺2、熟桐油14、十二烷基葡萄糖苷3、香柠檬油0.1、苯甲醇6、聚二甲基硅氧烷1。
该印制电路板用三防漆的制备方法如下:
(1)助剂的制备:先将负离子粉与十二烷基葡萄糖苷、亚磷酸三乙酯混合,搅拌均匀后研磨20min,制成负离子粉浆料备用,将苯并环丁烯、熟桐油与丙二醇甲醚、苯甲醇混合,搅拌40min,再加入其它剩余物料混合搅拌30min,最后滴加负离子粉浆料,边滴加边搅拌,滴加结束即得;
(2)将助剂、硬脂酸锌、吡啶硫酮锌、异丙醇铝、银浆加入二甲苯中,加热至35-50℃,缓慢搅拌50min,至物料完全溶解分散;
(3)将不饱和聚酯树脂加入步骤(2)所得的物料中,超声分散20min,加入其它剩余物料,搅拌50min,搅拌结束后冷却至室温即得,成品在1-2h内使用完毕即可。
本发明三防漆的性能测试结果为:
测试项目 | 技术指标 |
外观 | 漆膜平整、光亮丰满 |
涂层厚度(mm) | 0.1-0.3 |
表干时间(min,25℃) | ≤10 |
实干时间(h,25℃) | ≤5 |
漆膜硬度(shore D) | 64±2 |
冲击强度kg/cm | ≥50 |
附着力等级 | ≥4B |
耐盐雾性(25℃×48h) | 不起泡、不分层、不脱落 |
耐湿热性(65℃×48h) | 不起泡、不分层、不脱落 |
耐酸、碱性(68h) | 不起泡、不分层、不脱落 |
工作温度范围(℃) | -50-150 |
上述测试均遵循相关标准进行。
Claims (1)
1.一种加快电路板散热的三防漆,其特征在于,该三防漆由以下重量份的主料和助剂制成:主料40-50,助剂2-4;
所述的主料中各组分及其重量份为:硬脂酸锌1-3、196不饱和聚酯树脂40-48、过氧化二异丙苯0.5-1、正硅酸乙酯6-8、环烷酸锌1-2、吡啶硫酮锌1-2、二乙二醇二苯甲酸酯6-9、促进剂D 1-2、二甲苯8-10、异丙醇铝1-2、银浆0.1-0.2;
所述的助剂包含的组分及其重量份为:负离子粉1-2、亚磷酸三乙酯6-8、丙二醇甲醚10-12、苯并环丁烯4-6、异丙醇胺2-4、熟桐油12-15、十二烷基葡萄糖苷2-3、香柠檬油0.1-0.2、苯甲醇4-6、聚二甲基硅氧烷1-2;
如权利要求1所述的一种加快电路板散热的三防漆,其制备方法如下:
(1)助剂的制备:先将负离子粉与十二烷基葡萄糖苷、亚磷酸三乙酯混合,搅拌均匀后研磨15-20min,制成负离子粉浆料备用,将苯并环丁烯、熟桐油与丙二醇甲醚、苯甲醇混合,搅拌30-40min,再加入其它剩余物料混合搅拌20-30min,最后滴加负离子粉浆料,边滴加边搅拌,滴加结束即得;
(2)将助剂、硬脂酸锌、吡啶硫酮锌、异丙醇铝、银浆加入二甲苯中,加热至35-50℃,缓慢搅拌40-50min,至物料完全溶解分散;
(3)将不饱和聚酯树脂加入步骤(2)所得的物料中,超声分散20-30min,加入其它剩余物料,搅拌40-50min,搅拌结束后冷却至室温即得,成品在1-2h内使用完毕即可。