CN104151978B - Aqueousance artificial granite coating - Google Patents
Aqueousance artificial granite coating Download PDFInfo
- Publication number
- CN104151978B CN104151978B CN201410423575.4A CN201410423575A CN104151978B CN 104151978 B CN104151978 B CN 104151978B CN 201410423575 A CN201410423575 A CN 201410423575A CN 104151978 B CN104151978 B CN 104151978B
- Authority
- CN
- China
- Prior art keywords
- water
- particle
- particles
- percentage
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses aqueousance artificial granite coating, comprise the colorful particles such as Silicone acrylic emulsion, deionized water, water-based wetting and dispersing auxiliary agent, water-based defoamer, water-based leveling auxiliary agent, anticorrisive agent, water-based PH conditioning agent, waterborne film-forming auxiliary agent, homemade red particles, yellow particles, black particles, brown particles, grey colored particle, orange particle, blue particles, make obtain according to the mass percent of technological requirement; The present invention utilizes functional form Silicone acrylic emulsion, adopts in special nucleocapsid gold technology self-control soft outer tough, the colorful particle that cohesive force is strong, guarantees that form trait performance and the fingerprinting stress performance of finished product paint colorful particle in storage, transportation is good; Easy construction, can directly spray, tiltedly spray, even brushes, roller coat, all there will not be particle fragmentation, fuzzy phenomenon.
Description
Technical field
The present invention relates to the technical field of paint preparation of building coating, be specifically related to a kind of superior performance, aqueousance artificial granite coating that natural-like stone is true to nature and preparation method thereof.
Background technology
Building coating industry belongs to fine chemistry industry. Press GB/T2705-2003 " coating products taxonomy and nomenclature ", building coating is divided into wall covering, water-repellent paint, floor coatings and Functional Architectural Coatings in China. Architectural Paint in China demand is in the first in the world for a long time, and often has growth in various degree every year. International top-brand is being captured domestic middle and high-end market for a long time. But it is lower that domestic construction coating industry enters gate threshold, and manufacturing enterprise is various, and the technological element of a product is low, low quality, and added value is little, production capacity surplus.
Aqueousance artificial granite coating belongs to functional form art coatings in building coating field. In prior art, the aqueousance artificial granite coating that sell in market has following deficiency:
1. all adopt benzene emulsion to produce, its water proofing property, uvioresistant, pliability difference, 2-3 just there will be the quality problems such as xanthochromia, cracking, coating blackout.
2. the shelf-life is short, film forming is difficult, washmarking, even coating cracking, come off.
3. poor storage stability, along with the phenomenon that particle dissolves appears in the prolongation of time.
4. execution conditions are relatively harsh, can only spray and spray gun, air pressure, spray distance need to be fixed, and even need to accomplish without any letup, otherwise flower pattern can be caused abnormal, and flower grain size is fuzzy, cause losing granite effect in a jumble.
Summary of the invention
The present invention is intended to solve the typical problem of above four aspects in aqueousance artificial granite coating prior art, and a kind of superior performance, aqueousance artificial granite coating that natural-like stone fidelity is very high are provided.
The object of the present invention is achieved like this: aqueousance artificial granite coating, is characterized in that: comprise following component and proportioning:
| Composition | Percentage by weight (%) |
| Silicone acrylic emulsion | 25～45 |
| Deionized water | 15～35 |
| Waterborne film-forming auxiliary agent | 2.0～5.0 |
| Water-based PH conditioning agent | 0.2～0.3 |
| Water-based defoamer | 0.3～0.6 |
| Water-based leveling auxiliary agent | 0.1～0.5 |
| Waterborne preservative | 0.1～0.3 |
| Water-based wetting dispersing agent | 2.0～5.0 |
| Make colorful particle by oneself | 15～30 |
Wherein Silicone acrylic emulsion is: adopt the product that German BASF, U.S. DOW, Guangdong Ahmedabad richness or Jiangsu sunrise are produced, wherein any or wherein two or three mix with arbitrary proportion;
Wherein water-based wetting and dispersing auxiliary agent is: a kind of in polycarboxylic acids ammonium salt dispersant, non-ionic surface active dispersant or anion surface active dispersant or any two kinds mix with arbitrary proportion;
Wherein water-based defoamer is: in the mixture defoamer of mineral oil antifoam agent, aliphatic hydrocarbon and emulsifying agent any or wherein two kinds mix with arbitrary proportion;
Wherein water-based leveling auxiliary agent is: in organically-modified silica alkane levelling agent, fluorine-carbon modified ammonium polyacrylate salt levelling agent, association type alkali swollen thickener, association type PU levelling agent any or wherein two kinds mix with arbitrary proportion;
Wherein anticorrisive agent is: isothiazolinone, l, 2-benzisothiazole-3-ketone (or this ketone), 2, In 2-dibromo one cyanoacetamide (or this amine), di-2-ethylhexylphosphine oxide thiocyanates (or this ester class) any or wherein two kinds mix with arbitrary proportion;
Wherein water-based PH conditioning agent is: the one in ammoniacal liquor, triethanolamine, dimethylethanolamine, or wherein two or three mixes with arbitrary proportion;
Wherein waterborne film-forming auxiliary agent is: the one in lauric acid ester, propane diols, ethylene glycol, butyl glycol ether, propylene glycol monomethyl ether, 1-Methoxy-2-propyl acetate, or wherein two or three mixes with arbitrary proportion;
Wherein making colorful particle by oneself is: red particles, yellow particles, black particles, brown particles, grey colored particle, orange particle, blue particles, wherein any, two kinds or three kinds or four kinds or five kinds or six kinds or whole seven kinds of ratio mixing that are greater than zero with mass percent separately;
The percentage by weight of the each component of red particles is: protection rubber powder 1-3%, deionized water 62-82%, aqueous dispersion 0.1-0.3%, water-based defoamer 0.01-0.2%, iron oxide red 15-35%;
Yellow particles percentage by weight is: protection rubber powder 1-3%, deionized water 62-82%, aqueous dispersion 0.1-0.3%, water-based defoamer 0.01-0.2%, iron oxide yellow 15-35%'s;
Orange particle weight percentage is: protection rubber powder 1-3%, deionized water 62-82%, aqueous dispersion 0.1-0.3%, water-based defoamer 0.01-0.2%, iron oxide red 8-18%, iron oxide yellow 8-20%;
Blue particles percentage by weight is: protection rubber powder 1.5-10%, deionized water 75-90%, aqueous dispersion 0.1-0.8%, water-based defoamer 0.01-0.5%, phthalocyanine blue 4-15%;
Grey particle weight percentage is: protection rubber powder 1-5%, deionized water 62-82%, aqueous dispersion 0.1-0.3%, water-based defoamer 0.01-0.2%, titanium dioxide 5-20%, hard black 0.3-13%;
Black particles percentage by weight is: protection rubber powder 1.5-10%, deionized water 75-90%, aqueous dispersion 0.1-0.8%, water-based defoamer 0.01-0.5%, hard black 4-15%;
Brown particles percentage by weight is: protection rubber powder 1-5%, deionized water 62-82%, aqueous dispersion 0.1-0.3%, water-based defoamer 0.01-0.2%, iron oxide red 5-20%, hard black 0.3-13%;
Protection rubber powder is wherein K201 rubber powder, belongs to modified magnesium aluminium silicate.
Further feature is: adding before colorful particle, and covered with gold leaf processing carried out to colorful particle: the percentage by weight of particle: 50-70%, Silicone acrylic emulsion percentage by weight is: 25-45%, and borax solution percentage by weight is: 4-10%; Using selected particle as particle core material, under the rotating speed that meets technological requirement stirs, in Silicone acrylic emulsion, add borax solution, plasticizing a period of time, till treating the not obvious rising of viscosity; Then, by process stipulation order number, in establish uniform rotation scraping blade granulation sieve colorful particle core material is added, core material surface superscribes layer of substance, obtains core material colorful particle covered with gold leaf.
With respect to prior art, the present invention has following features:
1, utilize functional form Silicone acrylic emulsion, adopt in special nucleocapsid gold technology self-control soft outer tough, the colorful particle that cohesive force is strong, guarantee that form trait performance and the fingerprinting stress performance of finished product paint colorful particle in storage, transportation is good. Functional form Silicone acrylic emulsion, not being only finished product paint provides weatherability, the resistance to water of excellence. The more important thing is and contribute to keep the stability of colorful particle under storage, transport and Construction State.
2, adopt special nucleocapsid gold technology self-control interior soft outer tough, the colorful particle that cohesive force is strong, for guaranteeing that artificial grantie effect can perfectly embody under multiple form of construction work.
3, easy construction, can directly spray, tiltedly spray, even brush. All there will not be particle fragmentation, fuzzy phenomenon.
4, in actual production, controllability is strong, by the rotating speed of dispersing apparatus and jitter time, particle size effectively can be controlled completely for different color grains.
In a word: the present invention adopts import functional form Silicone acrylic emulsion, mix with adopting the colorful particle collocation that the homemade pliability of special nucleocapsid gold technology and weatherability are comparatively strong, extended storage stability is good, making aqueousance artificial granite coating, is the crucial part that this Project Product is succeeded in developing.
Detailed description of the invention
Aqueousance artificial granite paint ingredient of the present invention and percentage by weight are as follows: component of the present invention, mainly comprise Silicone acrylic emulsion, deionized water, colorful particle, waterborne film-forming auxiliary agent, water-based PH conditioning agent, water-based defoamer, waterborne preservative, water-based wetting dispersing agent etc., its percentage by weight is as follows
| Composition | Percentage by weight (%) |
| Silicone acrylic emulsion | 25～45 |
| Deionized water | 15～35 |
| Waterborne film-forming auxiliary agent | 2.0～5.0 |
| Water-based PH conditioning agent | 0.2～0.3 |
| Water-based defoamer | 0.3～0.6 |
| Water-based leveling auxiliary agent | 0.1～0.5 |
| Waterborne preservative | 0.1～0.3 |
| Water-based wetting dispersing agent | 2.0～5.0 |
| Make colorful particle by oneself | 15～30 |
Wherein Silicone acrylic emulsion is: adopt the product that German BASF, U.S. DOW, Guangdong Ahmedabad richness or Jiangsu sunrise are produced, wherein any or wherein two or three with arbitrary proportion mixing, component ratio is separately greater than zero; In emulsion, silicone content is between 8-15%, and optimum range is between 10-12%;
Wherein water-based wetting and dispersing auxiliary agent is: (polycarboxylic acids ammonium salt class has several concrete materials to polycarboxylic acids ammonium salt dispersant, structurally have tiny difference each other, but can be suitable for), in non-ionic surface active dispersant or anion surface active dispersant any or wherein two kinds mix with arbitrary proportion; Non-ionic surface active dispersant or anion surface active dispersant are existing, have a variety of, substantially can be suitable for, and it is suitable to select.
Wherein water-based defoamer is: in the mixture defoamer of mineral oil antifoam agent, aliphatic hydrocarbon and emulsifying agent any or wherein two kinds mix with arbitrary proportion. Mineral oil antifoam agent is existing, has a variety of, substantially can be suitable for; The mixture of aliphatic hydrocarbon and emulsifying agent is existing, can use as defoamer, has a variety of, substantially can be suitable for.
Wherein water-based leveling auxiliary agent is: organically-modified silica alkane levelling agent, fluorine-carbon modified ammonium polyacrylate salt levelling agent, association type alkali swollen thickener, association type PU(polyurethane) in levelling agent any or wherein two kinds mix with arbitrary proportion. Organically-modified silica alkane levelling agent, fluorine-carbon modified ammonium polyacrylate salt levelling agent, association type alkali swollen thickener, association type PU(polyurethane) levelling agent, all existing material (or component), can use as leveling auxiliary agent, have a variety of, substantially can be suitable for.
Wherein anticorrisive agent is: isothiazolinone, l, 2-benzisothiazole-3-ketone (or this ketone), 2, In 2-dibromo one cyanoacetamide (or this amine), di-2-ethylhexylphosphine oxide thiocyanates (or this ester class) any or wherein two kinds mix with arbitrary proportion. Aforesaid four kinds of materials (or component), are all existing materials, can use as anticorrisive agent, have a variety of, substantially can be suitable for.
Wherein water-based PH conditioning agent is: the one in ammoniacal liquor, triethanolamine, dimethylethanolamine, or wherein two or three mixes with arbitrary proportion. Aforesaid three kinds of materials (or component) are all existing materials, PH conditioning agent can be served as and use, have a variety of, substantially can be suitable for.
Wherein waterborne film-forming auxiliary agent is: the one in lauric acid ester, propane diols, ethylene glycol, butyl glycol ether, propylene glycol monomethyl ether, 1-Methoxy-2-propyl acetate, or wherein two or three mixes with arbitrary proportion. Aforesaid six kinds of materials (or component), are all existing materials, waterborne film-forming substance migration can be served as, have a variety of, substantially can be suitable for.
Wherein homemade colorful particle is: red particles, yellow particles, black particles, brown particles, grey colored particle, orange particle, blue particles, wherein any, two kinds or three kinds or four kinds or five kinds or six kinds or whole seven kinds with arbitrary proportion mixing, the ratio mixing that is greater than zero with mass percent separately.
Being prepared as follows of the colorful particle of the present invention:
(1) each colored particle representative formula is as following table:
In upper table, protection rubber powder is K201 rubber powder, belongs to modified magnesium aluminium silicate, is easy to dispersion, has good storage stability. Iron oxide red, iron oxide yellow, phthalocyanine blue, titanium dioxide, hard black etc., and aqueous dispersion, water-based defoamer are all existing materials, or choose dispersant suitable in prior art as water-based, choose defoamer suitable in prior art as water-based defoamer, then this is not described further.
Red particles, yellow particles, black particles, brown particles, grey colored particle, orange particle, blue particles, all comprise the components such as protection rubber powder, deionized water, aqueous dispersion, water-based defoamer,
Weight (quality) percentage of the each component of red particles is: protection rubber powder 1-3%, deionized water 62-82%, aqueous dispersion 0.1-0.3%, water-based defoamer 0.01-0.2%, iron oxide red 15-35%;
Yellow particles percentage by weight is: protection rubber powder 1-3%, deionized water 62-82%, aqueous dispersion 0.1-0.3%, water-based defoamer 0.01-0.2%, iron oxide yellow 15-35%;
Orange particle weight percentage is: protection rubber powder 1-3%, deionized water 62-82%, aqueous dispersion 0.1-0.3%, water-based defoamer 0.01-0.2%, iron oxide red 8-18%, iron oxide yellow 8-20%;
Blue particles percentage by weight is: protection rubber powder 1.5-10%, deionized water 75-90%, aqueous dispersion 0.1-0.8%, water-based defoamer 0.01-0.5%, phthalocyanine blue 4-15%;
Grey particle weight percentage is: protection rubber powder 1-5%, deionized water 62-82%, aqueous dispersion 0.1-0.3%, water-based defoamer 0.01-0.2%, titanium dioxide 5-20%, hard black 0.3-13%;
Black particles percentage by weight is: protection rubber powder 1.5-10%, deionized water 75-90%, aqueous dispersion 0.1-0.8%, water-based defoamer 0.01-0.5%, hard black 4-15%;
Brown particles percentage by weight is: protection rubber powder 1-5%, deionized water 62-82%, aqueous dispersion 0.1-0.3%, water-based defoamer 0.01-0.2%, iron oxide red 5-20%, hard black 0.3-13%;
According to the preparation technology of aqueous color paste, aforementioned particle slurry of all kinds is dispersed to less than 50 microns of fineness, for subsequent use as colorful particle core material.
(2) colorful particle core is covered with gold leaf processes (typical proportion):
| Raw material title | Consumption (g) |
| Particle core material of all kinds | 65 |
| Silicone acrylic emulsion | 40 |
| Borax solution (0.5%) | 5 |
| Add up to | 110 |
Select red particles, yellow particles, black particles, brown particles, grey colored particle, orange particle, blue particles, one or two kinds or three kinds or four kinds or five kinds or six kinds or whole seven kinds wherein mix with arbitrary proportion, obtain particle core material of all kinds, its weight (quality) percentage is: 50-70%, Silicone acrylic emulsion weight (quality) percentage is: 25-45%, borax solution weight (quality) percentage is: 4-10%, the mass percent concentration of borax solution, can select conventional 0.5%.
Under the rotating speed that meets technological requirement stirs (under stirring at low speed), to the borax solution (0.5% concentration) that adds 0.5% concentration in Silicone acrylic emulsion, plasticizing a period of time, as 20-60 minute, till treating the not obvious rising of viscosity, by specifying that order number is (as 50-300 order, or other suitable order numbers), core material adds by the granulation sieve of inside establishing uniform rotation scraping blade, uniformly size spherical drop is disperseed wherein, be prepared into mill base particle core and superscribe the material of one deck just as plastic sheeting sample, namely material (plastic sheeting sample shape) around various particles, is superscribed, obtain core material colorful particle covered with gold leaf, this core material (nucleocapsid) colorful particle covered with gold leaf, both soft as water, freely deformable again, and do not dissolve easily and can be very easy to be scattered in continuous phase.
Embodiment 1:
1, Silicone acrylic emulsion 350kg is taken, deionized water 200kg, as X-405 1kg and the APC 3kg of water-based wetting and dispersing auxiliary agent, as the defoamer NXZ 2kg of froth breaking effect, as the each 3kg of Canfair 6S89 and Canfair 6K9N of anticorrisive agent, as ammoniacal liquor (28%) 10kg of water-based PH conditioning agent, as the TEXNOAL 15kg of waterborne film-forming material, mix and stir, under rotating speed is 20 meter per second left and right, slowly add the colorful grain of self-control 300 kg, add as water-based leveling auxiliary agent DR-160D 3kg. Stir, pack on request after the assay was approved.
2, aqueousance artificial granite coating application technique:
1) construction tool: A, air compressor: more than 5 of power, tolerance abundance, is at least with three tracheaes, and more than three people simultaneously construction can be met. B, lower kettle spray gun: capacity 500ml, bore more than 1.3mm, capacity can not be too large, otherwise too heavy, operation inconvenience, and the little then speed of application of bore is slow, and duration may be delayed, unsuitable large-area construction. C, spray gun: point single rifle, rush-harvesting and rush-planting, three rifles etc., select monochromatic single rifle of use according to different patterns, and double-colored, polychrome rush-harvesting and rush-planting, three rifles, so that adaptation different construction, spray more preferably effect. D, various bore nozzle: 4mm, 5mm, 6mm, 8mm etc., select different nozzles according to the requirement of model, more even uniform of the less then spraying effect of bore, and greatly then flower point is larger for bore, and convex-concave sense is stronger.
2) construction process: metope base treatment → brushing seal coat → spray twice of real color bottom paint → spraying artificial granite paint → twice of spray plane oil.
3) constructing skill index: A, spraying end oil: select lower kettle spray gun, pressure 4-7Kg/ square centimeter, during construction, temperature can not lower than 10 degrees Celsius, spraying twice, 2 hours, interval, about 30 microns of thickness, air drying 12 hours. B, spraying artificial granite paint: select true mineral varnish spray gun, air-pressure controlling is thousand grams/cm of 4-7, and more than 10 degrees Celsius of construction temperatures, thickness is about 2-3mm, and as need are smeared twice, three roads, then 2 hours, interval, is dried and can polishes after 24 hours. C, polishing: adopt 400--600 order sand paper, gently polishing. Noting firmly can not be too violent, otherwise paint film can be destroyed, and causes that bottom is loosening, adhesive force can be caused bad, Paint Falling when serious. D, spray-coating surface oil: select lower kettle spray gun, thousand grams/cm of pressure 4-7, construction is not less than 10 degrees Celsius, spraying twice, 2 hours, interval, about 30 microns of thickness, and bone dry needs 7 days.
Aqueousance artificial granite coating of the present invention, by HG/T 4343-2012 " aqueous colorful building coating " standard, paint vehicle is detected, condition in container is normal, low-temperature stability never degenerates, thermal storage stability passes through, drying time (surface drying)≤4h, (48h) is without exception for composite coating resistance to water, (24h) is without exception for composite coating alkali resistance, composite coating abrasion resistance >=2000 time, composite coating covers crackle ability (standard state) >=0.5mm, (48h) is without exception for composite coating acid rain resistance, composite coating moisture-proof cold cycling (5 times) is without exception, composite coating stain resistance≤2 grade, composite coating artificial ageing resistance 1000 is non-foaming, do not peel off, flawless, without efflorescence, without obvious variable color, without obvious loss of gloss, meet HG/T 4343-2012 " aqueous colorful building coating " standard-required completely.
What finally illustrate is, above embodiment is only unrestricted in order to technical scheme of the present invention to be described, although with reference to preferred embodiment to invention has been detailed description, those of ordinary skill in the art is to be understood that, can modify to technical scheme of the present invention or be equal to replacement, and do not depart from aim and the scope of technical solution of the present invention, it all should be encompassed in the middle of right of the present invention.
Claims (1)
1. aqueousance artificial granite coating, is characterized in that: comprise following component and proportioning:
Wherein Silicone acrylic emulsion is: adopt the product that German BASF, U.S. DOW, Guangdong Ahmedabad richness or Jiangsu sunrise are produced, wherein any or wherein two or three mix with arbitrary proportion;
Wherein water-based wetting and dispersing auxiliary agent is: a kind of in polycarboxylic acids ammonium salt dispersant, non-ionic surface active dispersant or anion surface active dispersant or any two kinds mix with arbitrary proportion;
Wherein water-based defoamer is: in the mixture defoamer of mineral oil antifoam agent, aliphatic hydrocarbon and emulsifying agent any or wherein two kinds mix with arbitrary proportion;
Wherein water-based leveling auxiliary agent is: in organically-modified silica alkane levelling agent, fluorine-carbon modified ammonium polyacrylate salt levelling agent, association type alkali swollen thickener, association type PU levelling agent any or wherein two kinds mix with arbitrary proportion;
Wherein anticorrisive agent is: isothiazolinone, l, 2-benzisothiazole-3-ketone, 2, in 2-dibromo one cyanoacetamide, di-2-ethylhexylphosphine oxide thiocyanates any or wherein two kinds mix with arbitrary proportion;
Wherein water-based PH conditioning agent is: the one in ammoniacal liquor, triethanolamine, dimethylethanolamine, or wherein two or three mixes with arbitrary proportion;
Wherein waterborne film-forming material is: the one in lauric acid ester, propane diols, ethylene glycol, butyl glycol ether, propylene glycol monomethyl ether, 1-Methoxy-2-propyl acetate, or wherein two or three mixes with arbitrary proportion;
Wherein making colorful particle by oneself is: red particles, yellow particles, black particles, brown particles, grey colored particle, orange particle, blue particles, wherein any, two kinds or three kinds or four kinds or five kinds or six kinds or whole seven kinds of ratio mixing that are greater than zero with mass percent separately;
The percentage by weight of the each component of red particles is: protection rubber powder 1-3%, deionized water 62-82%, aqueous dispersion 0.1-0.3%, water-based defoamer 0.01-0.2%, iron oxide red 15-35%;
Yellow particles percentage by weight is: protection rubber powder 1-3%, deionized water 62-82%, aqueous dispersion 0.1-0.3%, water-based defoamer 0.01-0.2%, iron oxide yellow 15-35%'s;
Orange particle weight percentage is: protection rubber powder 1-3%, deionized water 62-82%, aqueous dispersion 0.1-0.3%, water-based defoamer 0.01-0.2%, iron oxide red 8-18%, iron oxide yellow 8-20%;
Blue particles percentage by weight is: protection rubber powder 1.5-10%, deionized water 75-90%, aqueous dispersion 0.1-0.8%, water-based defoamer 0.01-0.5%, phthalocyanine blue 4-15%;
Grey particle weight percentage is: protection rubber powder 1-5%, deionized water 62-82%, aqueous dispersion 0.1-0.3%, water-based defoamer 0.01-0.2%, titanium dioxide 5-20%, hard black 0.3-13%;
Black particles percentage by weight is: protection rubber powder 1.5-10%, deionized water 75-90%, aqueous dispersion 0.1-0.8%, water-based defoamer 0.01-0.5%, hard black 4-15%;
Brown particles percentage by weight is: protection rubber powder 1-5%, deionized water 62-82%, aqueous dispersion 0.1-0.3%, water-based defoamer 0.01-0.2%, iron oxide red 5-20%, hard black 0.3-13%;
Protection rubber powder is wherein K201 rubber powder, belongs to modified magnesium aluminium silicate;
Adding before colorful particle, covered with gold leaf processing carried out to colorful particle: the percentage by weight of particle: 50-70%, Silicone acrylic emulsion percentage by weight is: 25-45%, and borax solution percentage by weight is: 4-10%; Using selected particle as particle core material, under the rotating speed that meets technological requirement stirs, in Silicone acrylic emulsion, add borax solution, plasticizing a period of time, till treating the not obvious rising of viscosity; Then, by process stipulation order number, in establish uniform rotation scraping blade granulation sieve colorful particle core material is added, core material surface superscribes layer of substance, obtains core material colorful particle covered with gold leaf.