CN109913067A - One kind batch colorful water-water coating of scratch-type and preparation method thereof - Google Patents
One kind batch colorful water-water coating of scratch-type and preparation method thereof Download PDFInfo
- Publication number
- CN109913067A CN109913067A CN201910223141.2A CN201910223141A CN109913067A CN 109913067 A CN109913067 A CN 109913067A CN 201910223141 A CN201910223141 A CN 201910223141A CN 109913067 A CN109913067 A CN 109913067A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- base paint
- preparation
- scratch
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of batch of colorful water-water coating of scratch-type and preparation method thereof, belongs to technical field of coatings.It includes base paint, continuous phase, protecting colloid, and base paint mixes batch colorful water-water coating of scratch-type after toning and after protecting colloid granulation, then with continuous phase.Preparation method includes: step (1): base paint preparation, continuous phase preparation, step (2): protecting colloid preparation mixes colours to base paint semi-finished product；Step (3): granulation is carried out after the base paint semi-finished product after toning are mixed with protecting colloid and forms color grain；Step (4): the colorful water-water coating of scratch-type in batch is prepared by continuous phase and after being granulated the color grain mixing formed.The present invention, which passes through, uses the substances such as two different the third modified copolymer emulsions of silicon, GTS solution, using special preparation method, improves and sprays the imitative big-pattern marble fidelity of colorful water-water, accomplish bulky grain effect.
Description
Technical field
The present invention relates to technical field of coatings, in particular to a kind of batch of colorful water-water coating of scratch-type and preparation method thereof.
Background technique
Marble slabs are colorful, and tone multiplicity, none is identical for decorative pattern, this is exactly the rare glamour institute of marble slabs
?.Coating is the continuous film for being coated in the body surface protected or decorated, and capable of forming firm attachment with coated article, is led to
It is often to add or do not add pigment, filler based on resin or oil or lotion, corresponding additive is added, with organic solvent or water
The thick liquid being formulated.Wherein multicolor finish is to imitate marmorean ideal coating, on the pattern of multicolor finish surface, color
Polyisocyanate, aesthetic feeling is full, and simulation quality is strong, and the surface constructed has three-dimensional sense and multi-color decorative aesthetic feeling.Water-in-water multicolor coating is
In recent years new product type very popular in building coating industry, product is with physicochemical colloid technology and process for treating surface
For theoretical basis；Liquid aqueous resin is refined and is rolled into a variety of gluey hydrate colour particles that are of different sizes, varying in color,
And even stable suspension dispersion is in special continuous phase aqueous emulsion paint, by a construction molding, and finished product
The effect of decorative patterns of artificial granite stone material can achieve the degree mixed the spurious with the genuine；Product is and big in recent years to spray as form of construction work
Amount be applied to decoration of exterior wall substitute stone material, but have the characteristics that environmental protection and energy saving, it is easy for construction, durable, reprocess it is convenient, develop
Prospect is very wide.Multicolor finish can imitate out marmorean visual effect, cannot but imitate out all types of marbles.At present
It is not high enough that market mainstream water-in-water multicolor coating imitates bulky grain marble fidelity.
Summary of the invention
The object of the present invention is to provide one kind batch colorful water-water coating of scratch-type and preparation method thereof, by with two kinds not
The substances such as the third modified copolymer emulsion of silicon together, GTS solution, using special preparation method, so that coating has big-pattern Dali
The high emulation of stone multicolor finish improves and sprays the imitative big-pattern marble fidelity of colorful water-water, accomplishes bulky grain effect.
The technical solution adopted by the present invention to solve the technical problems is:
One kind batch colorful water-water coating of scratch-type, it includes base paint, continuous phase, protecting colloid, and the base paint is by toning
After being granulated afterwards with protecting colloid, then is mixed with continuous phase and criticizes the colorful water-water coating of scratch-type,
The base paint is grouped as by the group of following parts by weight:
86-92 parts of water
481 8-10 parts of celluloses
1124 5-7 parts of dispersing agents
2599 5-7 parts of wetting agents
399 3-5 parts of auxiliary agents
803 2.5-3.5 parts of defoaming agents
0.8-1.2 parts of AMP95 auxiliary agent
75-85 parts of calcined kaolin
9502 4-6 parts of titanium dioxides
4-5 parts of propylene glycol
7-9 parts of coalescing agent
1.2-1.6 parts of A20 fungicide
120-140 parts of DP20 lotion
48-52 parts of GTS protective glue
2-4 parts of S60 thickener；
The continuous phase is grouped as by the group of following parts by weight:
78-82 parts of water
90-105 parts of DP20 lotion
90-105 parts of DP80 lotion
1.2-1.7 parts of A20 fungicide
0.8-1.2 parts of AMP95 auxiliary agent
5-6 parts of propylene glycol
9-12 parts of coalescing agent
700 1.5-2.3 parts of thickeners；
The protecting colloid is grouped as by the group of following parts by weight:
120-135 parts of water
160-180 parts of GTS protective glue.
Further, the coalescing agent is alcohol ester 12.
A kind of preparation method of the colorful water-water coating of batch of scratch-type, comprising the following steps:
Step (1): base paint preparation, continuous phase preparation, protecting colloid preparation,
By the component of following parts by weight:
86-92 parts of water
481 8-10 parts of celluloses
1124 5-7 parts of dispersing agents
2599 5-7 parts of wetting agents
399 3-5 parts of auxiliary agents
803 2.5-3.5 parts of defoaming agents
0.8-1.2 parts of AMP95 auxiliary agent
75-85 parts of calcined kaolin
9502 4-6 parts of titanium dioxides
4-5 parts of propylene glycol
7-9 parts of coalescing agent
1.2-1.6 parts of A20 fungicide
120-140 parts of DP20 lotion
48-52 parts of GTS protective glue
2-4 parts of S60 thickener
It is prepared into base paint semi-finished product；
By the component of following parts by weight:
78-82 parts of water
90-105 parts of DP20 lotion
90-105 parts of DP80 lotion
1.2-1.7 parts of A20 fungicide
0.8-1.2 parts of AMP95 auxiliary agent
5-6 parts of propylene glycol
9-12 parts of coalescing agent
700 1.5-2.3 parts of thickeners
It is prepared into continuous phase semi-finished product；
By the component of following parts by weight:
120-135 parts of water
160-180 parts of GTS protective glue
It is prepared into protecting colloid semi-finished product；
Step (2): it mixes colours base paint semi-finished product；
Step (3): granulation is carried out after the base paint semi-finished product after toning are mixed with protecting colloid and forms color grain；
Step (4): the colorful water-water coating of scratch-type in batch is prepared by continuous phase and after being granulated the color grain mixing formed.
Further, in the step (1), base paint preparation the following steps are included:
Step 1: 8-10 parts of 481 cellulose dissolutions dispersion is added in 86-92 parts of water；
Step 2: 5-7 parts of 1124 dispersing agents, 5-7 parts of 2599 wetting agents, 2.5-3.5 parts of 803 defoaming agents, 0.8- is added
1.2 parts of AMP95 auxiliary agent stirs evenly；
Step 3: 75-85 parts of calcined kaolin, 9502 titanium dioxide high speed dispersion 30 minutes of 4-6 parts is added；
Step 4: 1.2-1.6 parts of A20 fungicide, 4-5 parts of propylene glycol, the dispersion of 7-9 parts of coalescing agent low speed is added；
Step 5: 120-140 parts of DP20 lotion, 3-5 parts of 399 auxiliary agents, 2-4 parts of S60 thickener, 48-52 parts is added
GTS protective glue stirs at low speed, basis of formation paint semi-finished product.
Compared to the prior art the present invention, has the following advantages that and effect: two different silicon third are used in formula composition
Modified copolymer emulsion: DP20, DP80 and GTS solution.The single use lotion of existing multicolor finish is DP50 or DP66,
DP20 is a kind of pure silicon the third polymer emulsion product with unique true emulsion system, cannot be only used for modulated color and texture
Plentiful stable base paint " color dot " is also used as firm packet of the continuous phase emulsion completion to color dot of water-in-water multicolor coating
It covers and the defencive function that forms a film, the pure acrylate for having used hardness reasonably combined and high-quality organic silicon monomer combined polymerization, DP20
Lotion has excellent film forming and mechanical strength.DP20, which is added, in coating not only has weatherability outstanding, scrub resistance, anti-is stained with
Dirt and splendid color developing need to add the organic coalescing agent of a small amount of volatility in coating substantially without addition or only
Form high-quality coating.DP80 is modified by the Functional silicones third of organosilicon functional group formation high balance self-crosslinking structure
Copolymer emulsion.Lotion has ultra-fine grain diameter, forms the water-white paint film of high resistance with a variety of protective glues, DP80 has easily toning, stream
Whole features needed for the multicolor finishes such as denaturation can be controllable, the white dirt-resistant of water resistant, and long term storage is stablized, the coating after DP80 is added
Has the advantages that the controllable fidelity for being more conducive to improving big-pattern marble multicolor finish of rheological property, this is all addition
Not available for the coating of DP50 and DP66 lotion.Both lotions are added very few opposite performance and can be reduced, product it is resistance to
Hou Xing, adhesive force and unfading etc. all have a certain impact.GTS, which is that a kind of warp is special, is selected grade, and activated modified production
Product, it is not dissolved in water but can expand to form colourless transparent liquid in water, can be at 12 months when dosage is 20% in water
Interior holding flowing.Very strong thixotropy and thickening power can be quickly formed under conditions of having a small amount of electrolyte.GTS is water packet
Water multicolor finish system and develop, excellent water resistance, splendid storage stability, it is splendid to common water quality stability.It is added
The stability of multicolor finish is improved afterwards.Lacquer spray gun spraying, rather than multicolor finish Spray painting tool are used in process aspect.
When multicolor finish Spray painting tool sprays multicolor finish, the large-minded colorful structure that can destroy coating is not easy to spray dotted face larger
Facing；Narrow-minded it will cause spraying is that atomization is uneven, wastes coating.Because of the formula of batch colorful water-water coating of scratch-type
The unique design of progress, which makes it be different from other multicolor finishes, can be used lacquer spray gun and is sprayed, and directly criticize after spraying
It smears, such operation can make batch colorful water-water coating of scratch-type is simpler more efficient to produce high emulation marble
Effect.The present invention, which passes through, uses the substances such as two different the third modified copolymer emulsions of silicon, GTS solution, using special preparation
Method improves so that coating has the high emulation of big-pattern marble multicolor finish and sprays the imitative big-pattern Dali of colorful water-water
Stone fidelity accomplishes bulky grain effect.
Specific embodiment
Below by embodiment, the present invention is described in further detail, following embodiment be explanation of the invention and
The invention is not limited to following embodiments.
Embodiment one
One kind batch colorful water-water coating of scratch-type, it includes base paint, continuous phase, protecting colloid, and the base paint is by toning
After being granulated afterwards with protecting colloid, then is mixed with continuous phase and criticize the colorful water-water coating of scratch-type.
The base paint is grouped as by the group of following parts by weight:
86 parts of water
481 8 parts of celluloses
1124 5.2 parts of dispersing agents
2599 5 parts of wetting agents
399 3 parts of auxiliary agents
803 2.5 parts of defoaming agents
0.8 part of AMP95 auxiliary agent
75 parts of calcined kaolin
9502 4 parts of titanium dioxides
4.2 parts of propylene glycol
12 parts of alcohol ester
1.2 parts of A20 fungicide
120 parts of DP20 lotion
48 parts of GTS protective glue
2 parts of S60 thickener；
The continuous phase is grouped as by the group of following parts by weight:
78 parts of water
90 parts of DP20 lotion
90 parts of DP80 lotion
1.3 parts of A20 fungicide
0.8 part of AMP95 auxiliary agent
5.2 parts of propylene glycol
12 parts of alcohol ester
700 1.5 parts of thickeners；
The protecting colloid is grouped as by the group of following parts by weight:
120 parts of water
160 parts of GTS protective glue.
A kind of preparation method of the colorful water-water coating of batch of scratch-type, comprising the following steps:
Step (1): base paint preparation, continuous phase preparation, protecting colloid preparation,
By the component of following parts by weight:
86 parts of water
481 8 parts of celluloses
1124 5.2 parts of dispersing agents
2599 5 parts of wetting agents
399 3 parts of auxiliary agents
803 2.5 parts of defoaming agents
0.8 part of AMP95 auxiliary agent
75 parts of calcined kaolin
9502 4 parts of titanium dioxides
4.2 parts of propylene glycol
12 parts of alcohol ester
1.2 parts of A20 fungicide
120 parts of DP20 lotion
48 parts of GTS protective glue
2 parts of S60 thickener
It is prepared into base paint semi-finished product；
By the component of following parts by weight:
78 parts of water
90 parts of DP20 lotion
90 parts of DP80 lotion
1.3 parts of A20 fungicide
0.8 part of AMP95 auxiliary agent
5.2 parts of propylene glycol
12 parts of alcohol ester
700 1.5 parts of thickeners
It is prepared into continuous phase semi-finished product；
By the component of following parts by weight:
120 parts of water
160 parts of GTS protective glue
It is prepared into protecting colloid semi-finished product；
Step (2): it mixes colours base paint semi-finished product；
Step (3): granulation is carried out after the base paint semi-finished product after toning are mixed with protecting colloid and forms color grain；
Step (4): the colorful water-water coating of scratch-type in batch is prepared by continuous phase and after being granulated the color grain mixing formed.
In the step (1), base paint preparation the following steps are included:
Step 1: 8 parts of 481 cellulose dissolutions dispersion is added in 86 parts of water；
Step 2: 5.2 parts of 1124 dispersing agents are added, and 5 parts of 2599 wetting agents, 2.5 parts of 803 defoaming agents, 0.8 part
AMP95 auxiliary agent stirs evenly；
Step 3: 75 parts of calcined kaolin, 9502 titanium dioxide high speed dispersion 30 minutes of 4 parts is added；
Step 4: 1.2 parts of A20 fungicide, 4.2 parts of propylene glycol, the dispersion of 7-9 parts of 12 low speed of alcohol ester is added；
Step 5: it is low that 120 parts of DP20 lotion, 3 parts of 399 auxiliary agents, 2 parts of S60 thickener, 48 parts of GTS protective glue is added
Speed stirs evenly, basis of formation paint semi-finished product.
Batch colorful water-water coating of scratch-type being prepared after testing, obtains following technical indicator, see Table 1 for details.
The technical indicator of the colorful water-water coating of 1 batch of scratch-type of table
Embodiment two
One kind batch colorful water-water coating of scratch-type, it includes base paint, continuous phase, protecting colloid, and the base paint is by toning
After being granulated afterwards with protecting colloid, then is mixed with continuous phase and criticize the colorful water-water coating of scratch-type.
The base paint is grouped as by the group of following parts by weight:
90 parts of water
481 9 parts of celluloses
1124 6 parts of dispersing agents
2599 5 parts of wetting agents
399 4 parts of auxiliary agents
803 3 parts of defoaming agents
1 part of AMP95 auxiliary agent
80 parts of calcined kaolin
9502 5 parts of titanium dioxides
4.5 parts of propylene glycol
12 parts of alcohol ester
1.5 parts of A20 fungicide
130 parts of DP20 lotion
50 parts of GTS protective glue
3 parts of S60 thickener；
The continuous phase is grouped as by the group of following parts by weight:
80 parts of water
100 parts of DP20 lotion
100 parts of DP80 lotion
1.5 parts of A20 fungicide
1 part of AMP95 auxiliary agent
5.5 parts of propylene glycol
12 parts of alcohol ester
700 2 parts of thickeners；
The protecting colloid is grouped as by the group of following parts by weight:
130 parts of water
170 parts of GTS protective glue.
A kind of preparation method of the colorful water-water coating of batch of scratch-type, comprising the following steps:
Step (1): base paint preparation, continuous phase preparation, protecting colloid preparation,
By the component of following parts by weight:
90 parts of water
481 9 parts of celluloses
1124 6 parts of dispersing agents
2599 5 parts of wetting agents
399 4 parts of auxiliary agents
803 3 parts of defoaming agents
1 part of AMP95 auxiliary agent
80 parts of calcined kaolin
9502 5 parts of titanium dioxides
4.5 parts of propylene glycol
12 parts of alcohol ester
1.5 parts of A20 fungicide
130 parts of DP20 lotion
50 parts of GTS protective glue
3 parts of S60 thickener
It is prepared into base paint semi-finished product；
By the component of following parts by weight:
80 parts of water
100 parts of DP20 lotion
100 parts of DP80 lotion
1.5 parts of A20 fungicide
1 part of AMP95 auxiliary agent
5.5 parts of propylene glycol
12 parts of alcohol ester
700 2 parts of thickeners
It is prepared into continuous phase semi-finished product；
By the component of following parts by weight:
130 parts of water
170 parts of GTS protective glue
It is prepared into protecting colloid semi-finished product；
Step (2): it mixes colours base paint semi-finished product；
Step (3): granulation is carried out after the base paint semi-finished product after toning are mixed with protecting colloid and forms color grain；
Step (4): the colorful water-water coating of scratch-type in batch is prepared by continuous phase and after being granulated the color grain mixing formed.
Further, in the step (1), base paint preparation the following steps are included:
Step 1: 9 parts of 481 cellulose dissolutions dispersion is added in 90 parts of water；
Step 2: 6 parts of 1124 dispersing agents, 5 parts of 2599 wetting agents, 3 parts of 803 defoaming agents, 1 part of AMP95 auxiliary agent is added
It stirs evenly；
Step 3: 80 parts of calcined kaolin, 9502 titanium dioxide high speed dispersion 30 minutes of 5 parts is added；
Step 4: 1.5 parts of A20 fungicide, 4.5 parts of propylene glycol, the dispersion of 8 parts of coalescing agent low speed is added；
Step 5: it is low that 130 parts of DP20 lotion, 4 parts of 399 auxiliary agents, 3 parts of S60 thickener, 50 parts of GTS protective glue is added
Speed stirs evenly, basis of formation paint semi-finished product.
Batch colorful water-water coating of scratch-type being prepared after testing, obtains following technical indicator, see Table 2 for details.
The technical indicator of the colorful water-water coating of 2 batches of scratch-type of table
Embodiment three
One kind batch colorful water-water coating of scratch-type, it includes base paint, continuous phase, protecting colloid, and the base paint is by toning
After being granulated afterwards with protecting colloid, then is mixed with continuous phase and criticizes the colorful water-water coating of scratch-type,
The base paint is grouped as by the group of following parts by weight:
91.3 parts of water
481 9.2 parts of celluloses
1124 6.5 parts of dispersing agents
2599 6.5 parts of wetting agents
399 4.5 parts of auxiliary agents
803 3.2 parts of defoaming agents
1.0 parts of AMP95 auxiliary agent
80 parts of calcined kaolin
9502 4.3 parts of titanium dioxides
4.8 parts of propylene glycol
12 parts of alcohol ester
1.5 parts of A20 fungicide
135 parts of DP20 lotion
50.9 parts of GTS protective glue
3.2 parts of S60 thickener；
The continuous phase is grouped as by the group of following parts by weight:
80.5 parts of water
103 parts of DP20 lotion
103 parts of DP80 lotion
1.6 parts of A20 fungicide
1.1 parts of AMP95 auxiliary agent
5.7 parts of propylene glycol
12 parts of alcohol ester
700 2.1 parts of thickeners；
The protecting colloid is grouped as by the group of following parts by weight:
130 parts of water
175 parts of GTS protective glue.
A kind of preparation method of the colorful water-water coating of batch of scratch-type, comprising the following steps:
Step (1): base paint preparation, continuous phase preparation, protecting colloid preparation,
By the component of following parts by weight:
91.3 parts of water
481 9.2 parts of celluloses
1124 6.5 parts of dispersing agents
2599 6.5 parts of wetting agents
399 4.5 parts of auxiliary agents
803 3.2 parts of defoaming agents
1.0 parts of AMP95 auxiliary agent
80 parts of calcined kaolin
9502 4.3 parts of titanium dioxides
4.8 parts of propylene glycol
12 parts of alcohol ester
1.5 parts of A20 fungicide
135 parts of DP20 lotion
50.9 parts of GTS protective glue
3.2 parts of S60 thickener
It is prepared into base paint semi-finished product；
By the component of following parts by weight:
80.5 parts of water
103 parts of DP20 lotion
103 parts of DP80 lotion
1.6 parts of A20 fungicide
1.1 parts of AMP95 auxiliary agent
5.7 parts of propylene glycol
12 parts of alcohol ester
700 2.1 parts of thickeners
It is prepared into continuous phase semi-finished product；
By the component of following parts by weight:
130 parts of water
175 parts of GTS protective glue
It is prepared into protecting colloid semi-finished product；
Step (2): it mixes colours base paint semi-finished product；
Step (3): granulation is carried out after the base paint semi-finished product after toning are mixed with protecting colloid and forms color grain；
Step (4): the colorful water-water coating of scratch-type in batch is prepared by continuous phase and after being granulated the color grain mixing formed.
Further, in the step (1), base paint preparation the following steps are included:
Step 1: 9.2 parts of 481 cellulose dissolutions dispersion is added in 91.3 parts of water；
Step 2: 6.5 parts of 1124 dispersing agents are added, and 6.5 parts of 2599 wetting agents, 3.2 parts of 803 defoaming agents, 1.0 parts
AMP95 auxiliary agent stirs evenly；
Step 3: 80 parts of calcined kaolin, 9502 titanium dioxide high speed dispersion 30 minutes of 4.3 parts is added；
Step 4: 1.5 parts of A20 fungicide, 4.8 parts of propylene glycol, the dispersion of 8.2 parts of coalescing agent low speed is added；
It is protected step 5: 135 parts of DP20 lotion, 4.5 parts of 399 auxiliary agents, 3.2 parts of S60 thickener, 50.9 parts of GTS is added
Shield glue stirs at low speed, basis of formation paint semi-finished product.
Batch colorful water-water coating of scratch-type being prepared after testing, obtains following technical indicator, see Table 3 for details.
The technical indicator of the colorful water-water coating of 3 batches of scratch-type of table
Example IV
One kind batch colorful water-water coating of scratch-type, it includes base paint, continuous phase, protecting colloid, and the base paint is by toning
After being granulated afterwards with protecting colloid, then is mixed with continuous phase and criticizes the colorful water-water coating of scratch-type,
The base paint is grouped as by the group of following parts by weight:
92 parts of water
481 10 parts of celluloses
1124 7 parts of dispersing agents
2599 7 parts of wetting agents
399 5 parts of auxiliary agents
803 3.5 parts of defoaming agents
1.2 parts of AMP95 auxiliary agent
85 parts of calcined kaolin
9502 6 parts of titanium dioxides
5 parts of propylene glycol
12 parts of alcohol ester
1.6 parts of A20 fungicide
140 parts of DP20 lotion
52 parts of GTS protective glue
4 parts of S60 thickener；
The continuous phase is grouped as by the group of following parts by weight:
82 parts of water
105 parts of DP20 lotion
105 parts of DP80 lotion
1.7 parts of A20 fungicide
1.2 parts of AMP95 auxiliary agent
6 parts of propylene glycol
12 parts of alcohol ester
700 2.3 parts of thickeners；
The protecting colloid is grouped as by the group of following parts by weight:
135 parts of water
180 parts of GTS protective glue.
A kind of preparation method of the colorful water-water coating of batch of scratch-type, comprising the following steps:
Step (1): base paint preparation, continuous phase preparation, protecting colloid preparation,
By the component of following parts by weight:
92 parts of water
481 10 parts of celluloses
1124 7 parts of dispersing agents
2599 7 parts of wetting agents
399 5 parts of auxiliary agents
803 3.5 parts of defoaming agents
1.2 parts of AMP95 auxiliary agent
85 parts of calcined kaolin
9502 6 parts of titanium dioxides
5 parts of propylene glycol
12 parts of alcohol ester
1.6 parts of A20 fungicide
140 parts of DP20 lotion
52 parts of GTS protective glue
4 parts of S60 thickener
It is prepared into base paint semi-finished product；
By the component of following parts by weight:
82 parts of water
105 parts of DP20 lotion
105 parts of DP80 lotion
1.7 parts of A20 fungicide
1.2 parts of AMP95 auxiliary agent
6 parts of propylene glycol
12 parts of alcohol ester
700 2.3 parts of thickeners
It is prepared into continuous phase semi-finished product；
By the component of following parts by weight:
135 parts of water
180 parts of GTS protective glue
It is prepared into protecting colloid semi-finished product；
Step (2): it mixes colours base paint semi-finished product；
Step (3): granulation is carried out after the base paint semi-finished product after toning are mixed with protecting colloid and forms color grain；
Step (4): the colorful water-water coating of scratch-type in batch is prepared by continuous phase and after being granulated the color grain mixing formed.
Further, in the step (1), base paint preparation the following steps are included:
Step 1: 10 parts of 481 cellulose dissolutions dispersion is added in 92 parts of water；
Step 2: 7 parts of 1124 dispersing agents, 7 parts of 2599 wetting agents, 3.5 parts of 803 defoaming agents, 1.2 parts of AMP95 is added
Auxiliary agent stirs evenly；
Step 3: 85 parts of calcined kaolin, 9502 titanium dioxide high speed dispersion 30 minutes of 6 parts is added；
Step 4: 1.6 parts of A20 fungicide, 5 parts of propylene glycol, the dispersion of 9 parts of coalescing agent low speed is added；
Step 5: it is low that 140 parts of DP20 lotion, 5 parts of 399 auxiliary agents, 9 parts of S60 thickener, 52 parts of GTS protective glue is added
Speed stirs evenly, basis of formation paint semi-finished product.
Batch colorful water-water coating of scratch-type being prepared after testing, obtains following technical indicator, see Table 4 for details.
The technical indicator of the colorful water-water coating of 4 batches of scratch-type of table
Above content is only illustrations made for the present invention described in this specification.The technical field of the invention
Technical staff can make various modifications or additions to the described embodiments or be substituted in a similar manner,
Content without departing from description of the invention or beyond the scope defined by this claim, should belong to of the invention
Protection scope.
Claims (4)
1. one kind batch colorful water-water coating of scratch-type, it is characterised in that:
It includes base paint, continuous phase, protecting colloid, and the base paint is after toning and after protecting colloid is granulated, then with even
Continuous mix and the colorful water-water coating of scratch-type in batch,
The base paint is grouped as by the group of following parts by weight:
86-92 parts of water
481 8-10 parts of celluloses
1124 5-7 parts of dispersing agents
2599 5-7 parts of wetting agents
399 3-5 parts of auxiliary agents
803 2.5-3.5 parts of defoaming agents
0.8-1.2 parts of AMP95 auxiliary agent
75-85 parts of calcined kaolin
9502 4-6 parts of titanium dioxides
4-5 parts of propylene glycol
7-9 parts of coalescing agent
1.2-1.6 parts of A20 fungicide
120-140 parts of DP20 lotion
48-52 parts of GTS protective glue
2-4 parts of S60 thickener；
The continuous phase is grouped as by the group of following parts by weight:
78-82 parts of water
90-105 parts of DP20 lotion
90-105 parts of DP80 lotion
1.2-1.7 parts of A20 fungicide
0.8-1.2 parts of AMP95 auxiliary agent
5-6 parts of propylene glycol
9-12 parts of coalescing agent
700 1.5-2.3 parts of thickeners；
The protecting colloid is grouped as by the group of following parts by weight:
120-135 parts of water
160-180 parts of GTS protective glue.
2. a kind of batch of colorful water-water coating of scratch-type according to claim 1, it is characterised in that: the coalescing agent is alcohol
Ester 12.
3. the preparation method of the colorful water-water coating of a kind of batch of scratch-type according to claim 1, it is characterised in that: including with
Lower step:
Step (1): base paint preparation, continuous phase preparation, protecting colloid preparation,
By the component of following parts by weight:
86-92 parts of water
481 8-10 parts of celluloses
1124 5-7 parts of dispersing agents
2599 5-7 parts of wetting agents
399 3-5 parts of auxiliary agents
803 2.5-3.5 parts of defoaming agents
0.8-1.2 parts of AMP95 auxiliary agent
75-85 parts of calcined kaolin
9502 4-6 parts of titanium dioxides
4-5 parts of propylene glycol
7-9 parts of coalescing agent
1.2-1.6 parts of A20 fungicide
120-140 parts of DP20 lotion
48-52 parts of GTS protective glue
2-4 parts of S60 thickener
It is prepared into base paint semi-finished product；
By the component of following parts by weight:
78-82 parts of water
90-105 parts of DP20 lotion
90-105 parts of DP80 lotion
1.2-1.7 parts of A20 fungicide
0.8-1.2 parts of AMP95 auxiliary agent
5-6 parts of propylene glycol
9-12 parts of coalescing agent
700 1.5-2.3 parts of thickeners
It is prepared into continuous phase semi-finished product；
By the component of following parts by weight:
120-135 parts of water
160-180 parts of GTS protective glue
It is prepared into protecting colloid semi-finished product；
Step (2): it mixes colours base paint semi-finished product；
Step (3): granulation is carried out after the base paint semi-finished product after toning are mixed with protecting colloid and forms color grain；
Step (4): the colorful water-water coating of scratch-type in batch is prepared by continuous phase and after being granulated the color grain mixing formed.
4. the preparation method of the colorful water-water coating of a kind of batch of scratch-type according to claim 3, it is characterised in that: the step
Suddenly in (1), base paint preparation the following steps are included:
Step 1: 8-10 parts of 481 cellulose dissolutions dispersion is added in 86-92 parts of water；
Step 2: 5-7 parts of 1124 dispersing agents, 5-7 parts of 2599 wetting agents, 2.5-3.5 parts of 803 defoaming agents, 0.8- is added
1.2 parts of AMP95 auxiliary agent stirs evenly；
Step 3: 75-85 parts of calcined kaolin, 9502 titanium dioxide high speed dispersion 30 minutes of 4-6 parts is added；
Step 4: 1.2-1.6 parts of A20 fungicide, 4-5 parts of propylene glycol, the dispersion of 7-9 parts of coalescing agent low speed is added；
Step 5: 120-140 parts of DP20 lotion, 3-5 parts of 399 auxiliary agents, 2-4 parts of S60 thickener, 48-52 parts is added
GTS protective glue stirs at low speed, basis of formation paint semi-finished product.