CN106519856A - Granite-imitating coating - Google Patents
Granite-imitating coating Download PDFInfo
- Publication number
- CN106519856A CN106519856A CN201610928017.2A CN201610928017A CN106519856A CN 106519856 A CN106519856 A CN 106519856A CN 201610928017 A CN201610928017 A CN 201610928017A CN 106519856 A CN106519856 A CN 106519856A
- Authority
- CN
- China
- Prior art keywords
- artificial
- parts
- granite paint
- granite
- artificial granite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a granite-imitating coating. The granite-imitating coating comprises the following raw materials: a silicone-acrylate emulsion, deionized water, a coalescing agent, a dispersant and artificial masterbatch, wherein the artificial masterbatch is obtained by mixing and sintering montmorillonite, kaolin, pigments and water. By adjusting the proportions of artificial masterbatch in different colors, different decorative effects can be obtained, and the coating can show natural granite particles, so that the effect is vivid.
Description
Technical field
The present invention relates to the technical field of the technical field of building coating, more particularly to artificial granite paint.
Background technology
Artificial granite paint refer to it is a kind of spray rear material appearance and have exactly like the decorative effect of natural granite stone material
Stone-like coating, can be applicable to the interior wall of building, exterior wall, cylinder, lines etc., give elegance, harmony, serious U.S.
Sense, reaches vivid, effect of back to nature.In prior art, artificial granite paint is mainly with synthetic resin emulsion as base
Material, then add the solids such as the natural smalt of different-grain diameter, compound sliver, mica sheet, last adding assistant and water are formulated, wherein
The decorative effect of artificial granite is mainly produced by natural smalt, compound sliver, mica sheet etc., but these natural minerals generally with tree
Fat liquor bonding is difficult, and dispersion effect is not good, and after causing shaping, appreciation effect is poor.
The content of the invention
It is an object of the invention to propose a kind of artificial granite paint using artificial color tablets.
Technical scheme is as follows：
A kind of artificial granite paint, its raw material include：Silicone acrylic emulsion, deionized water, coalescents, dispersant, artificial color
Grain, wherein artificial color tablets are sintered after being mixed by montmorillonite, kaolin, pigment, water forming.
Preferably：In the artificial color tablets, montmorillonite and the mass ratio of kaolin and water are 3.1～1：1～2：1.5～
0.5。
It is also preferred that：The sintering temperature of the artificial color tablets is 800～1000 DEG C.
It is also preferred that：The dispersant is polyvinyl alcohol.
It is also preferred that：The raw material of the artificial granite paint also includes levelling agent and/or defoamer.
It is also preferred that：The raw material of the artificial granite paint includes：30～60 parts of silicone acrylic emulsion, deionized water 10～
15 parts, 1.0～6.0 parts of coalescents, 5～10 parts of dispersant, 10～30 parts of artificial color tablets.
The invention has the advantages that：
(1) only once can be sprayed using the coating of the present invention, easy construction, high working efficiency；
(2) present invention can obtain different decorative effects by the ratio of the artificial color tablets of allotment different colours,
Granite natural particle is presented, effect is true to nature；
(3) homogeneity of the present invention is good, occurs without the phenomenons such as discoloration, colour fading, stress cracking；
(4) nuisanceless generation during present invention construction, environment protection health.
Specific embodiment
Embodiment 1
A kind of artificial granite paint, in parts by mass, including silicone content be 10%, glass transition temperature be 30～40 DEG C
60 parts of silicone acrylic emulsion, 15 parts of deionized water, 6.0 parts of coalescents propandiol butyl ether, 10 parts of polyethylene of dispersing agent alcohol, artificial color
30 parts of grain, wherein artificial color tablets are by 3.1 parts of montmorillonite, 1 part of kaolin, the pigment of different colours, such as phthalocyanine blue, red etc.
0.1 part, and at 800 DEG C, calcination 5min is obtained after 0.5 part of water is well mixed.
Embodiment 2
A kind of artificial granite paint, in parts by mass, including silicone content be 15%, glass transition temperature be 30～40 DEG C
30 parts of silicone acrylic emulsion, 10 parts of deionized water, 1.0 parts of coalescents propandiol butyl ether, 5 parts of polyethylene of dispersing agent alcohol, artificial color
10 parts of grain, wherein artificial color tablets are by 1 part of montmorillonite, 2 parts of kaolin, the pigment of different colours, such as phthalocyanine blue, red etc. 0.3
Part, and at 1000 DEG C, calcination 3min is obtained after 1.5 parts of water is well mixed.
Claims (6)
1. a kind of artificial granite paint, it is characterised in that：The raw material of the artificial granite paint includes：Silicone acrylic emulsion, deionization
Water, coalescents, dispersant, artificial color tablets, wherein artificial color tablets are by sintering after montmorillonite, kaolin, pigment, water mixing
Into.
2. artificial granite paint according to claim 1, it is characterised in that：Montmorillonite and kaolin in the artificial color tablets
And the mass ratio of water is 3.1～1：1～2：1.5～0.5.
3. artificial granite paint according to claim 1, it is characterised in that：The sintering temperature of the artificial color tablets is 800
～1000 DEG C.
4. artificial granite paint according to claim 1, it is characterised in that：The dispersant is polyvinyl alcohol.
5. artificial granite paint according to claim 1, it is characterised in that：The raw material of the artificial granite paint also includes
Levelling agent and/or defoamer.
6. artificial granite paint according to claim 1, it is characterised in that：In parts by mass, the artificial granite paint
Raw material include：30～60 parts of silicone acrylic emulsion, 10～15 parts of deionized water, 1.0～6.0 parts of coalescents, dispersant 5～10
Part, 10～30 parts of artificial color tablets.