CN106497281A - A kind of preparation method of aqueous colorful granite coating - Google Patents
A kind of preparation method of aqueous colorful granite coating Download PDFInfo
- Publication number
- CN106497281A CN106497281A CN201610927830.8A CN201610927830A CN106497281A CN 106497281 A CN106497281 A CN 106497281A CN 201610927830 A CN201610927830 A CN 201610927830A CN 106497281 A CN106497281 A CN 106497281A
- Authority
- CN
- China
- Prior art keywords
- granite coating
- aqueous colorful
- parts
- deionized water
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation method of aqueous colorful granite coating, comprises the following steps：(1) preparation of artificial color tablets：By montmorillonite, Kaolin, pigment and water mix after at 1000～1200 DEG C 3～5min of calcination；(2) artificial color tablets, sodium alginate, Part I deionized water are stirred 10～20min in the case of 30～40 DEG C；(3) silicone acrylic emulsion, dispersant, xanthan gum, remaining deionized water, mix homogeneously is added to obtain the aqueous colorful granite coating in the mixture obtained to step (2).The painting color prepared by the present invention is bright-coloured, is evenly distributed, and decorative effect is true to nature, and property is homogeneous, stable, while each raw material is biological good, health environment-friendly can be preserved steadily in the long term.
Description
Technical field
The present invention relates to the technical field of the technical field of building coating, more particularly to artificial granite paint.
Background technology
Artificial granite paint refer to a kind of spray rear material appearance and have exactly like the decorative effect of natural granite stone material
Stone-like coating, can be applicable to the interior wall of building, exterior wall, cylinder, lines etc., give elegance, harmony, serious U.S.
Sense, reaches vivid, effect of back to nature.In prior art, artificial granite paint is mainly with synthetic resin emulsion as base
Material, then add the solids such as the natural smalt of different-grain diameter, compound sliver, mica sheet, last adding assistant and water are formulated, wherein
The decorative effect of artificial granite is mainly produced by natural smalt, compound sliver, mica sheet etc., but in order to improve the safety collar of coating
Guarantor property, current coating system mostly are aqueous systems, and natural smalt, compound sliver etc. are difficult to stable dispersion wherein, cause
Coating effect is had a greatly reduced quality.
Content of the invention
It is an object of the invention to propose a kind of use can produce that multicolour, decorative effect be good and health environment-friendly imitative
The preparation method of granite water paint.
Technical scheme is as follows：
A kind of preparation method of aqueous colorful granite coating, comprises the following steps：(1) preparation of artificial color tablets：To cover
De- soil, Kaolin, pigment and water mix after at 1000～1200 DEG C 3～5min of calcination；
(2) artificial color tablets, sodium alginate, Part I deionized water are stirred 10～20min under heating state；
(3) silicone acrylic emulsion, dispersant, xanthan gum, remaining deionized water are added in the mixture obtained to step (2),
Mix homogeneously, that is, obtain the aqueous colorful granite coating；
Wherein artificial color tablets are 1 with the mass ratio of Part I deionized water:0.3～1.
Preferably：In parts by mass, the raw material of the aqueous colorful granite coating includes：Silicone acrylic emulsion 30～60
Part, 10～50 parts of deionized water, 3～5 parts of dispersant, 0.5～1.5 part of xanthan gum, 0.1～0.3 part of sodium alginate, artificial color tablets
20～30 parts.
It is also preferred that：The dispersant is polyvinyl alcohol.
It is also preferred that：The raw material of the aqueousance artificial granite coating also includes levelling agent and/or defoamer.
It is also preferred that：In the artificial color tablets, montmorillonite is 3.1～1 with the mass ratio of Kaolin and water：1～2：
1.5～0.5.
The painting color prepared by the present invention is bright-coloured, is evenly distributed, and decorative effect is true to nature, and property is homogeneous, stable, with
When each raw material biological good, health environment-friendly can be preserved steadily in the long term.
Specific embodiment
Embodiment 1
Aqueous colorful granite coating is prepared by following steps
(1) preparation of artificial color tablets：By 3.1 parts of montmorillonite, 1 part of Kaolin is the pigment of different colours, such as phthalocyanine blue, big
After 0.1 part of Hydrargyri Oxydum Rubrum etc., and 0.5 part of mix homogeneously of water at 1000 DEG C calcination 5min；
(2) 30 parts of artificial color tablets, 0.3 part of sodium alginate, 30 parts of deionized water are stirred 20min in the case of 30 DEG C；
(3) in the mixture obtained to step (2) add silicone content be 10%, glass transition temperature be 30～40 DEG C
60 parts of silicone acrylic emulsion, 5 parts of polyethylene of dispersing agent alcohol, 1.5 parts of xanthan gum, 20 parts of deionized water, mix homogeneously obtain the water
The colorful granite coating of property.
Wherein artificial color tablets are 1 with the mass ratio of Part I deionized water:1～2.
Embodiment 2
Aqueous colorful granite coating is prepared by following steps
(1) preparation of artificial color tablets：By 1 part of montmorillonite, 2 parts of Kaolin is the pigment of different colours, such as phthalocyanine blue, bright red
After 0.3 part of powder etc., and 1.5 parts of mix homogeneously of water at 1200 DEG C calcination 3min；
(2) 20 parts of artificial color tablets, 0.1 part of sodium alginate, 6 parts of deionized water are stirred 30min in the case of 40 DEG C；
(3) in the mixture obtained to step (2) add silicone content be 15%, glass transition temperature be 30～40 DEG C
30 parts of silicone acrylic emulsion, 3 parts of polyethylene of dispersing agent alcohol, 0.5 part of xanthan gum, 4 parts of deionized water, mix homogeneously obtain the water
The colorful granite coating of property.
Claims (5)
1. a kind of preparation method of aqueous colorful granite coating, it is characterised in that：Comprise the following steps：
(1) preparation of artificial color tablets：After montmorillonite, Kaolin, pigment and water are mixed at 1000～1200 DEG C calcination 3～
5min；
(2) artificial color tablets, sodium alginate, Part I deionized water are stirred 10～20min in the case of 30～40 DEG C；
(3) silicone acrylic emulsion, dispersant, xanthan gum, remaining deionized water, mixing are added in the mixture obtained to step (2)
Uniformly, that is, the aqueous colorful granite coating is obtained；
Wherein artificial color tablets are 1 with the mass ratio of Part I deionized water:0.3～1.
2. aqueous colorful granite coating according to claim 1, it is characterised in that：In parts by mass, the aqueouss are more
The raw material of color granite coating includes：30～60 parts of silicone acrylic emulsion, 10～50 parts of deionized water, 3～5 parts of dispersant, xanthan gum
0.5～1.5 part, 0.1～0.3 part of sodium alginate, 20～30 parts of artificial color tablets.
3. aqueous colorful granite coating according to claim 1, it is characterised in that：The dispersant is polyvinyl alcohol.
4. aqueous colorful granite coating according to claim 1, it is characterised in that：The aqueous colorful granite coating
Raw material also include levelling agent and/or defoamer.
5. aqueous colorful granite coating according to claim 1, it is characterised in that：In the artificial color tablets montmorillonite with
The mass ratio of Kaolin and water is 3.1～1：1～2：1.5～0.5.