CN106543833A - A kind of preparation method of environmentally friendly artificial granite paint - Google Patents
A kind of preparation method of environmentally friendly artificial granite paint Download PDFInfo
- Publication number
- CN106543833A CN106543833A CN201610927828.0A CN201610927828A CN106543833A CN 106543833 A CN106543833 A CN 106543833A CN 201610927828 A CN201610927828 A CN 201610927828A CN 106543833 A CN106543833 A CN 106543833A
- Authority
- CN
- China
- Prior art keywords
- environmentally friendly
- preparation
- artificial
- granite paint
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation method of environmentally friendly artificial granite paint, comprises the following steps：(1) preparation of artificial color tablets；(2) artificial color tablets are heated into 30～60min at 50～70 DEG C with covering and water, the solid particle for obtaining is leached；(3) solid particle that will be obtained by step (2) is mixed homogeneously with silicone acrylic emulsion, coalescents, dispersant and deionized water, that is, obtain the environmentally friendly artificial granite paint；Ratio of the present invention by the artificial color tablets of allotment different colours, different decorative effects can be obtained, granite natural particle, effect artificial granite paint true to nature can be presented, simultaneously by the effect of covering, can effectively prevent the volatile ingredient in coating from overflowing and environment is worked the mischief.
Description
Technical field
The present invention relates to the technical field of building coating, the technical field of more particularly to environmentally friendly artificial granite paint.
Background technology
Artificial granite paint refer to it is a kind of spray rear material appearance and have exactly like the decorative effect of natural granite stone material
Stone-like coating, can be applicable to the interior wall of building, exterior wall, cylinder, lines etc., give elegance, harmony, serious U.S.
Sense, reaches vivid, effect of back to nature.In prior art, environmentally friendly artificial granite paint with synthetic resin emulsion is mainly
Base material, then add the solids such as the natural smalt of different-grain diameter, compound sliver, mica sheet, last adding assistant and water are formulated, its
The decorative effect of middle artificial granite is mainly produced by natural smalt, compound sliver, mica sheet etc., but these natural minerals generally with
Resin emulsion bonding is difficult, and dispersion effect is not good, and after causing molding, appreciation effect is poor.
The content of the invention
It is an object of the invention to propose a kind of preparation method of the environmentally friendly artificial granite paint using artificial color tablets.
Technical scheme is as follows：
A kind of preparation method of environmentally friendly artificial granite paint, comprises the following steps：
(1) preparation of artificial color tablets：The calcination 3 at 800～1000 DEG C after montmorillonite, Kaolin, pigment and water are mixed
～5min；
(2) artificial color tablets are heated into 30～60min at 50～70 DEG C with covering and water, the solid particle for obtaining is filtered
Go out；
(3) by the solid particle obtained by step (2) and artificial color tablets, silicone acrylic emulsion, coalescents dispersant and go from
Sub- water mix homogeneously, that is, obtain the environmentally friendly artificial granite paint；The covering is tetraethyl orthosilicate.
Preferably：The quality of the covering is 1～3 times of the artificial color tablets quality.
Preferably：In the artificial color tablets, montmorillonite and the mass ratio of Kaolin and water are 3.1～1：1～2：1.5～
0.5。
It is also preferred that：The sintering temperature of the artificial color tablets is 800～1000 DEG C.
It is also preferred that：The dispersant is polyvinyl alcohol.
It is also preferred that：The raw material of the environmentally friendly artificial granite paint also includes levelling agent and/or defoamer.
It is also preferred that：The raw material of the environmentally friendly artificial granite paint includes：30～60 parts of silicone acrylic emulsion, deionized water
10～15 parts, 1.0～6.0 parts of coalescents, 5～10 parts of dispersant, 10～30 parts of artificial color tablets.
The invention has the advantages that：
(1) present invention is simple to operate, and controlling is good；
(2) only once can be sprayed using coating obtained in the present invention, easy construction, high working efficiency；Gained is applied
Material can pass through the ratio of the artificial color tablets for allocating different colours, can obtain different decorative effects, and granite can be presented certainly
Right granule, effect are true to nature；Coating homogeneity is good simultaneously, occurs without the phenomenons such as discoloration, colour fading, stress cracking；
(3) nuisanceless generation during present invention construction, environment protection health.
(4) the product VOC free that the present invention is obtained is produced.
Specific embodiment
Embodiment 1
A kind of environmentally friendly artificial granite paint, is prepared by following steps：
(1) preparation of artificial color tablets：By 3.1 parts of montmorillonite, 1 part of Kaolin is the pigment of different colours, such as phthalocyanine blue, big
After 0.1 part of Hydrargyri Oxydum Rubrum etc., and 0.5 part of mix homogeneously of water at 800 DEG C calcination 5min；
(2) by artificial color tablets 30 parts be heated to reflux at 70 DEG C with 100 parts of 30 parts of covering tetraethyl orthosilicate and water
The solid particle for obtaining is leached thereafter by 30min；
(3) by the solid particle obtained by step (2) and silicone content be 10%, glass transition temperature be 30～40 DEG C
60 parts of silicone acrylic emulsion, 15 parts of mix homogeneously of 6.0 parts of coalescents dispersant propandiol butyl ether and deionized water, that is, obtain the ring
Protect artificial granite paint.
Embodiment 2
A kind of environmentally friendly artificial granite paint, is prepared by following steps：
(1) preparation of artificial color tablets：By 1 part of montmorillonite, 2 parts of Kaolin is the pigment of different colours, such as phthalocyanine blue, bright red
After 0.3 part of powder etc., and 1.5 parts of mix homogeneously of water at 1000 DEG C calcination 3min；
(2) 80 parts of 30 parts of 10 parts of artificial color tablets and covering tetraethyl orthosilicate and water are heated to reflux into 60min at 50 DEG C,
Thereafter the solid particle for obtaining is leached；
(3) by the solid particle obtained by step (2) and silicone content be 15%, glass transition temperature be 30～40 DEG C
30 parts of silicone acrylic emulsion, 10 parts of mix homogeneously of 1.0 parts of coalescents dispersant propandiol butyl ether and deionized water, that is, obtain the ring
Protect artificial granite paint.
Claims (7)
1. a kind of preparation method of environmentally friendly artificial granite paint, it is characterised in that：Comprise the following steps：
(1) preparation of artificial color tablets：After montmorillonite, Kaolin, pigment and water are mixed at 800～1000 DEG C calcination 3～
5min；
(2) artificial color tablets are heated into 30～60min at 50～70 DEG C with covering and water, the solid particle for obtaining is leached；
(3) solid particle that will be obtained by step (2) is mixed homogeneously with silicone acrylic emulsion, coalescents, dispersant and deionized water,
The environmentally friendly artificial granite paint is obtained；The covering is tetraethyl orthosilicate.
2. the preparation method of environmentally friendly artificial granite paint according to claim 1, it is characterised in that：The matter of the covering
Measure 1～3 times for the artificial color tablets quality.
3. the preparation method of environmentally friendly artificial granite paint according to claim 1, it is characterised in that：In the artificial color tablets
Montmorillonite is 3.1～1 with the mass ratio of Kaolin and water：1～2：1.5～0.5.
4. the preparation method of environmentally friendly artificial granite paint according to claim 1, it is characterised in that：The artificial color tablets
Sintering temperature is 800～1000 DEG C.
5. the preparation method of environmentally friendly artificial granite paint according to claim 1, it is characterised in that：The dispersant is poly-
Vinyl alcohol.
6. the preparation method of environmentally friendly artificial granite paint according to claim 1, it is characterised in that：The environmentally friendly Fang Hua hilllocks
The raw material of rock coating also includes levelling agent and/or defoamer.
7. the preparation method of environmentally friendly artificial granite paint according to claim 1, it is characterised in that：In parts by mass, institute
The raw material for stating environmentally friendly artificial granite paint includes：30～60 parts of silicone acrylic emulsion, 10～15 parts of deionized water, coalescents 1.0～
6.0 parts, 5～10 parts of dispersant, 10～30 parts of artificial color tablets.