CN104091627A - 一种晶体硅太阳能电池用无铅导电银浆及其制作方法 - Google Patents

一种晶体硅太阳能电池用无铅导电银浆及其制作方法 Download PDF

Info

Publication number
CN104091627A
CN104091627A CN201410303650.3A CN201410303650A CN104091627A CN 104091627 A CN104091627 A CN 104091627A CN 201410303650 A CN201410303650 A CN 201410303650A CN 104091627 A CN104091627 A CN 104091627A
Authority
CN
China
Prior art keywords
hour
silver paste
conductive silver
parts
lead
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410303650.3A
Other languages
English (en)
Inventor
郭万东
孟祥法
董培才
陈伏洲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chinaland Solar Energy Co Ltd
Original Assignee
Chinaland Solar Energy Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chinaland Solar Energy Co Ltd filed Critical Chinaland Solar Energy Co Ltd
Priority to CN201410303650.3A priority Critical patent/CN104091627A/zh
Publication of CN104091627A publication Critical patent/CN104091627A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种晶体硅太阳能电池用无铅导电银浆，其特征在于，由下列重量份的原料制成：银粉40-50、甲酸甲酯2-3、乙二胺四乙酸二钠1-2、酒石酸钾钠0.4-0.9、硬脂酸1.4-2.6、可再分散乳胶粉2.3-3.6、二壬基萘磺酸钡0.3-0.7、十二烯基丁二酸1.2-2.8、助剂30-40、适量水；本发明通过优化生产工艺和配方，能够有效减少银颗粒的氧化，提高电池的开路电压和电池的电性能，使太阳能电池具有高的转换效率。

Description

一种晶体硅太阳能电池用无铅导电银浆及其制作方法
技术领域
本发明涉及导电银浆领域，具体涉及一种晶体硅太阳能电池用无铅导电银浆及其制作方法。
背景技术
导电银浆是指印刷于导电承印物上，使之具有传导电流和排除积累静电荷能力的银浆，一般是印在塑料、玻璃、陶瓷或纸板等非导电承印物上，它是由导电性填料、黏合剂、溶剂及添加剂组成。导电银浆时需要具备的特性有：导电性（抗静电性）佳、附着力强、印刷适应性好和耐溶剂性优等特性，而目前市场上现有的导电银浆有很多缺点，不仅含有铅、镉等且有毒，污染环境，而且使用在导电承印物上时附着力低、耐焊接性不佳，烧结性能差。
发明内容
本发明的目的就是提供一种晶体硅太阳能电池用无铅导电银浆及其制作方法，以克服现有技术的不足。
本发明的目的是这样实现的：
一种晶体硅太阳能电池用无铅导电银浆，其特征在于，由下列重量份的原料制成：银粉40-50、甲酸甲酯2-3、乙二胺四乙酸二钠1-2、酒石酸钾钠0.4-0.9、硬脂酸1.4-2.6、可再分散乳胶粉2.3-3.6、二壬基萘磺酸钡0.3-0.7、十二烯基丁二酸1.2-2.8、助剂30-40、适量水。
所述的助剂由下列重量份原料制成：氧化铋2-3、氧化硼3-4、乙基纤维素0.8-1.4、十二烷基硫酸钠0.3-0.4、邻苯二甲酸二甲酯0.2-0.4、卵磷脂0.3-0.5、聚硅氧烷0.2-0.3、松油醇20-25，其制备方法是将氧化铋和氧化硼放入煅烧炉中于520-610℃下煅烧1-2小时，取出冷却至室温，加入乙基纤维素研磨20-40分钟；将邻苯二甲酸二甲酯、松油醇搅拌混匀，在140-190℃下反应2-3小时，冷却至80-100℃，加入卵磷脂、聚硅氧烷、十二烷基硫酸钠，保持温度搅拌3-4小时；将以上各反应产物混合，研磨2-4小时制得300-400目浆料即得。
所述的一种晶体硅太阳能电池用无铅导电银浆的制备方法，其特征在于包括以下步骤：
（1）取乙二胺四乙酸二钠加适量水研磨2-3小时制得200-300目浆料，加入可再分散乳胶粉继续研磨3-4小时，喷雾干燥，烘干；
（2）取硬脂酸、十二烯基丁二酸放入反应釜中加热到55-75℃搅拌混匀，加入甲酸甲酯，保温搅拌30-50分钟，冷却加入酒石酸钾钠研磨成浆；
（3）将步骤（1）、（2）反应物料及其他剩余物料混合，升温至100-120℃，搅拌反应1-2小时，冷却，研磨成粒径为10-20μm浆粒，即得。
本发明有以下有益效果：本发明通过优化生产工艺和配方，能够有效减少银颗粒的氧化，提高电池的开路电压和电池的电性能，使太阳能电池具有高的转换效率。
具体实施方式
所述的一种晶体硅太阳能电池用无铅导电银浆，其特征在于，由下列重量份的原料制成：银粉42、甲酸甲酯3、乙二胺四乙酸二钠1、酒石酸钾钠0.4、硬脂酸1.4、可再分散乳胶粉2.3、二壬基萘磺酸钡0.3、十二烯基丁二酸1.2、助剂34、适量水。
所述的助剂由下列重量份原料制成：氧化铋2、氧化硼3、乙基纤维素0.9、十二烷基硫酸钠0.3、邻苯二甲酸二甲酯0.4、卵磷脂0.3、聚硅氧烷0.3、松油醇24，其制备方法是将氧化铋和氧化硼放入煅烧炉中于520-610℃下煅烧1-2小时，取出冷却至室温，加入乙基纤维素研磨20-40分钟；将邻苯二甲酸二甲酯、松油醇搅拌混匀，在140-190℃下反应2-3小时，冷却至80-100℃，加入卵磷脂、聚硅氧烷、十二烷基硫酸钠，保持温度搅拌3-4小时；将以上各反应产物混合，研磨2-4小时制得300-400目浆料即得。
制作方法包括以下步骤：
（1）取乙二胺四乙酸二钠加适量水研磨2-3小时制得200-300目浆料，加入可再分散乳胶粉继续研磨3-4小时，喷雾干燥，烘干；
（2）取硬脂酸、十二烯基丁二酸放入反应釜中加热到55-75℃搅拌混匀，加入甲酸甲酯，保温搅拌30-50分钟，冷却加入酒石酸钾钠研磨成浆；
（3）将步骤（1）、（2）反应物料及其他剩余物料混合，升温至100-120℃，搅拌反应1-2小时，冷却，研磨成粒径为10-20μm浆粒，即得。
通过上述实施例加工得到的导电银浆的技术指标如下：
（1）黏度：50-100PaS（Brookfield，10RPM）；
（2）附着力：＞10N/mm2；
（3）铅镉含量：＜100ppm ；
（4）可焊性优、堆烧易分离、印刷适应性好和耐溶剂性优。

Claims (2)

1.一种晶体硅太阳能电池用无铅导电银浆，其特征在于，由下列重量份的原料制成：银粉40-50、甲酸甲酯2-3、乙二胺四乙酸二钠1-2、酒石酸钾钠0.4-0.9、硬脂酸1.4-2.6、可再分散乳胶粉2.3-3.6、二壬基萘磺酸钡0.3-0.7、十二烯基丁二酸1.2-2.8、助剂30-40、适量水；所述的助剂由下列重量份原料制成：氧化铋2-3、氧化硼3-4、乙基纤维素0.8-1.4、十二烷基硫酸钠0.3-0.4、邻苯二甲酸二甲酯0.2-0.4、卵磷脂0.3-0.5、聚硅氧烷0.2-0.3、松油醇20-25，其制备方法是将氧化铋和氧化硼放入煅烧炉中于520-610℃下煅烧1-2小时，取出冷却至室温，加入乙基纤维素研磨20-40分钟；将邻苯二甲酸二甲酯、松油醇搅拌混匀，在140-190℃下反应2-3小时，冷却至80-100℃，加入卵磷脂、聚硅氧烷、十二烷基硫酸钠，保持温度搅拌3-4小时；将以上各反应产物混合，研磨2-4小时制得300-400目浆料即得。
2.根据权利要求1所述的一种晶体硅太阳能电池用无铅导电银浆的制作方法，其特征在于包括以下步骤：
（1）取乙二胺四乙酸二钠加适量水研磨2-3小时制得200-300目浆料，加入可再分散乳胶粉继续研磨3-4小时，喷雾干燥，烘干；
（2）取硬脂酸、十二烯基丁二酸放入反应釜中加热到55-75℃搅拌混匀，加入甲酸甲酯，保温搅拌30-50分钟，冷却加入酒石酸钾钠研磨成浆；
（3）将步骤（1）、（2）反应物料及其他剩余物料混合，升温至100-120℃，搅拌反应1-2小时，冷却，研磨成粒径为10-20μm浆粒，即得。
CN201410303650.3A 2014-06-30 2014-06-30 一种晶体硅太阳能电池用无铅导电银浆及其制作方法 Pending CN104091627A (zh)