CN104112488B - 一种草木灰/银粉复合的导电银浆及其制作方法 - Google Patents

一种草木灰/银粉复合的导电银浆及其制作方法 Download PDF

Info

Publication number
CN104112488B
CN104112488B CN201410303711.6A CN201410303711A CN104112488B CN 104112488 B CN104112488 B CN 104112488B CN 201410303711 A CN201410303711 A CN 201410303711A CN 104112488 B CN104112488 B CN 104112488B
Authority
CN
China
Prior art keywords
hour
plant ash
silver paste
conductive silver
argentum powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410303711.6A
Other languages
English (en)
Other versions
CN104112488A (zh
Inventor
郭万东
孟祥法
董培才
陈伏洲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chinaland Solar Energy Co Ltd
Original Assignee
Chinaland Solar Energy Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chinaland Solar Energy Co Ltd filed Critical Chinaland Solar Energy Co Ltd
Priority to CN201410303711.6A priority Critical patent/CN104112488B/zh
Publication of CN104112488A publication Critical patent/CN104112488A/zh
Application granted granted Critical
Publication of CN104112488B publication Critical patent/CN104112488B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种草木灰/银粉复合的导电银浆,其特征在于,由下列重量份的原料制成:银粉45‑50、氧化硅0.5‑1.1、硫酸锌0.3‑0.5、硅酸钠0.4‑0.7、甲基丙烯磺酸钠1.1‑2.3、二甘醇月桂酸酯2‑4、椰子油酰二乙醇胺1‑3、草木灰2.1‑3.4、松焦油4‑6、助剂30‑40、适量水;本发明通过对草木灰进行改性,添加到原料中,提高了导电银浆的抗压性以及基板的附着力。

Description

一种草木灰 / 银粉复合的导电银浆及其 制作方法
技术领域
本发明涉及导电银浆领域,具体涉及一种草木灰/银粉复合的导电银浆及其制作方法。
背景技术
导电银浆是指印刷于导电承印物上,使之具有传导电流和排除积累静电荷能力的银浆,一般是印在塑料、玻璃、陶瓷或纸板等非导电承印物上,它是由导电性填料、黏合剂、溶剂及添加剂组成。导电银浆时需要具备的特性有:导电性(抗静电性)佳、附着力强、印刷适应性好和耐溶剂性优等特性,而目前市场上现有的导电银浆有很多缺点,不仅含有铅、镉等且有毒,污染环境,而且使用在导电承印物上时附着力低、耐焊接性不佳,烧结性能差。
发明内容
本发明的目的就是提供一种草木灰/银粉复合的导电银浆及其制作方法,以克服现有技术的不足。
本发明的目的是这样实现的:
一种草木灰/银粉复合的导电银浆,其特征在于,由下列重量份的原料制成:银粉45-50、氧化硅0.5-1.1、硫酸锌0.3-0.5、硅酸钠0.4-0.7、甲基丙烯磺酸钠1.1-2.3、二甘醇月桂酸酯2-4、椰子油酰二乙醇胺1-3、草木灰2.1-3.4、松焦油4-6、助剂30-40、适量水。
所述的助剂由下列重量份原料制成:氧化铋2-3、氧化硼3-4、乙基纤维素0.8-1.4、十二烷基硫酸钠0.3-0.4、邻苯二甲酸二甲酯0.2-0.4、卵磷脂0.3-0.5、聚硅氧烷0.2-0.3、松油醇20-25,其制备方法是将氧化铋和氧化硼放入煅烧炉中于520-610℃下煅烧1-2小时,取出冷却至室温,加入乙基纤维素研磨20-40分钟;将邻苯二甲酸二甲酯、松油醇搅拌混匀,在140-190℃下反应2-3小时,冷却至80-100℃,加入卵磷脂、聚硅氧烷、十二烷基硫酸钠,保持温度搅拌3-4小时;将以上各反应产物混合,研磨2-4小时制得300-400目浆料即得。
所述的一种草木灰/银粉复合的导电银浆的制备方法,其特征在于包括以下步骤:
(1)取草木灰送入煅烧炉中在540-630℃下烧结1-2小时,取出冷却至室温,放入3-5%的盐酸溶液中浸泡3-6小时,取出,用清水反复洗涤烘干,加适量水研磨2-3小时制得200-300目浆料,加入硫酸锌继续研磨3-4小时;
(2)取二甘醇月桂酸酯、椰子油酰二乙醇胺放入反应釜中加热到55-75℃搅拌混匀,加入松焦油,保持温度搅拌2-3小时,至完全溶解,再加入甲基丙烯磺酸钠,保温搅拌30-50分钟,研磨成浆;
(3)将步骤(1)、(2)反应物料及其他剩余物料混合,升温至100-120℃,搅拌反应1-2小时,冷却,研磨成粒径为10-20μm浆粒,即得。
本发明有以下有益效果:本发明通过对草木灰进行改性,添加到原料中,提高了导电银浆的抗压性以及基板的附着力;本发明制得的银浆具有触变性良好、接触电阻低、无铅等优点,符合环保理念,可大批量持续生产。
具体实施方式
所述的一种草木灰/银粉复合的导电银浆,其特征在于,由下列重量份的原料制成:银粉46、氧化硅0.5、硫酸锌0.4、硅酸钠0.5、甲基丙烯磺酸钠1.1、二甘醇月桂酸酯2、椰子油酰二乙醇胺3、草木灰2.1、松焦油6、助剂40、适量水。
所述的助剂由下列重量份原料制成:氧化铋2、氧化硼3、乙基纤维素0.9、十二烷基硫酸钠0.3、邻苯二甲酸二甲酯0.4、卵磷脂0.3、聚硅氧烷0.3、松油醇24,其制备方法是将氧化铋和氧化硼放入煅烧炉中于520-610℃下煅烧1-2小时,取出冷却至室温,加入乙基纤维素研磨20-40分钟;将邻苯二甲酸二甲酯、松油醇搅拌混匀,在140-190℃下反应2-3小时,冷却至80-100℃,加入卵磷脂、聚硅氧烷、十二烷基硫酸钠,保持温度搅拌3-4小时;将以上各反应产物混合,研磨2-4小时制得300-400目浆料即得。
制作方法包括以下步骤:
(1)取草木灰送入煅烧炉中在540-630℃下烧结1-2小时,取出冷却至室温,放入3-5%的盐酸溶液中浸泡3-6小时,取出,用清水反复洗涤烘干,加适量水研磨2-3小时制得200-300目浆料,加入硫酸锌继续研磨3-4小时;
(2)取二甘醇月桂酸酯、椰子油酰二乙醇胺放入反应釜中加热到55-75℃搅拌混匀,加入松焦油,保持温度搅拌2-3小时,至完全溶解,再加入甲基丙烯磺酸钠,保温搅拌30-50分钟,研磨成浆;
(3)将步骤(1)、(2)反应物料及其他剩余物料混合,升温至100-120℃,搅拌反应1-2小时,冷却,研磨成粒径为10-20μm浆粒,即得。
通过上述实施例加工得到的导电银浆的技术指标如下:
(1)黏度:50-100PaS(Brookfield,10RPM);
(2)附着力:>10N/mm2
(3)方阻:<5mΩ/c ;
(4)可焊性优、堆烧易分离、印刷适应性好和耐溶剂性优。

Claims (2)

1.一种草木灰/银粉复合的导电银浆,其特征在于,由下列重量份的原料制成:银粉45-50、氧化硅0.5-1.1、硫酸锌0.3-0.5、硅酸钠0.4-0.7、甲基丙烯磺酸钠1.1-2.3、二甘醇月桂酸酯2-4、椰子油酰二乙醇胺1-3、草木灰2.1-3.4、松焦油4-6、助剂30-40、适量水;所述的助剂由下列重量份原料制成:氧化铋2-3、氧化硼3-4、乙基纤维素0.8-1.4、十二烷基硫酸钠0.3-0.4、邻苯二甲酸二甲酯0.2-0.4、卵磷脂0.3-0.5、聚硅氧烷0.2-0.3、松油醇20-25,所述助剂的制备方法是将氧化铋和氧化硼放入煅烧炉中于520-610℃下煅烧1-2小时,取出冷却至室温,加入乙基纤维素研磨20-40分钟;将邻苯二甲酸二甲酯、松油醇搅拌混匀,在140-190℃下反应2-3小时,冷却至80-100℃,加入卵磷脂、聚硅氧烷、十二烷基硫酸钠,保持温度搅拌3-4小时;将以上各反应产物混合,研磨2-4小时制得300-400目浆料即得。
2.根据权利要求1所述的一种草木灰/银粉复合的导电银浆的制作方法,其特征在于包括以下步骤:
(1)取草木灰送入煅烧炉中在540-630℃下烧结1-2小时,取出冷却至室温,放入3-5%的盐酸溶液中浸泡3-6小时,取出,用清水反复洗涤烘干,加适量水研磨2-3小时制得200-300目浆料,加入硫酸锌继续研磨3-4小时;
(2)取二甘醇月桂酸酯、椰子油酰二乙醇胺放入反应釜中加热到55-75℃搅拌混匀,加入松焦油,保持温度搅拌2-3小时,至完全溶解,再加入甲基丙烯磺酸钠,保温搅拌30-50分钟,研磨成浆;
(3)将步骤(1)、(2)反应产物及其他剩余物料混合,升温至100-120℃,搅拌反应1-2小时,冷却,研磨成粒径为10-20μm浆粒,即得。
CN201410303711.6A 2014-06-30 2014-06-30 一种草木灰/银粉复合的导电银浆及其制作方法 Active CN104112488B (zh)