CN104157325B - 一种铜粉/珍珠粉复合的导电银浆及其制作方法 - Google Patents

一种铜粉/珍珠粉复合的导电银浆及其制作方法 Download PDF

Info

Publication number
CN104157325B
CN104157325B CN201410368833.3A CN201410368833A CN104157325B CN 104157325 B CN104157325 B CN 104157325B CN 201410368833 A CN201410368833 A CN 201410368833A CN 104157325 B CN104157325 B CN 104157325B
Authority
CN
China
Prior art keywords
powder
hour
copper powder
silicone polymer
dimethyl silicone
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410368833.3A
Other languages
English (en)
Other versions
CN104157325A (zh
Inventor
蒋智谋
周施峰
周梅永
胡加峰
谢水兵
张超
崔海威
吴华
董子侠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANGHAI KUANGYU TECHNOLOGY CO.,LTD.
Original Assignee
Anhui Zhuangyuanlang Electronic Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Zhuangyuanlang Electronic Technology Co Ltd filed Critical Anhui Zhuangyuanlang Electronic Technology Co Ltd
Priority to CN201410368833.3A priority Critical patent/CN104157325B/zh
Publication of CN104157325A publication Critical patent/CN104157325A/zh
Application granted granted Critical
Publication of CN104157325B publication Critical patent/CN104157325B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种铜粉/珍珠粉复合的导电银浆，其特征在于，由下列重量份的原料制成：银粉35‑45、铜粉4‑6、珍珠粉2‑4、耐磨炭黑1‑3、沸石粉2‑5、环氧化甘油三酸酯4‑7、碳酸氢铵0.4‑0.8、尿素0.5‑1.2、肉豆蔻酸异丙酯3‑6、聚二甲基硅氧烷1.2‑2.4、助剂30‑40、适量水；本发明添加铜粉、珍珠粉、耐磨炭黑，减少了银粉的使用量降低了生产成本，提高了银浆的导电性能，进而提高了生产效率。

Description

一种铜粉/珍珠粉复合的导电银浆及其制作方法
技术领域
本发明涉及导电银浆领域，具体涉及一种铜粉/珍珠粉复合的导电银浆及其制作方法。
背景技术
导电银浆是指印刷于导电承印物上，使之具有传导电流和排除积累静电荷能力的银浆，一般是印在塑料、玻璃、陶瓷或纸板等非导电承印物上，它是由导电性填料、黏合剂、溶剂及添加剂组成。导电银浆需要具备的特性有：导电性（抗静电性）佳、附着力强、印刷适应性好和耐溶剂性优等特性，而目前市场上现有的导电银浆有很多缺点，不仅含有铅、镉等且有毒，污染环境，而且使用在导电承印物上时附着力低、耐焊接性不佳，烧结性能差。
发明内容
本发明的目的就是提供一种铜粉/珍珠粉复合的导电银浆及其制作方法，以克服现有技术的不足。
本发明的目的是这样实现的：
一种铜粉/珍珠粉复合的导电银浆，其特征在于，由下列重量份的原料制成：银粉35-45、铜粉4-6、珍珠粉2-4、耐磨炭黑1-3、沸石粉2-5、环氧化甘油三酸酯4-7、碳酸氢铵0.4-0.8、尿素0.5-1.2、肉豆蔻酸异丙酯3-6、聚二甲基硅氧烷1.2-2.4、助剂30-40、适量水。
所述的助剂由下列重量份原料制成：三氧化二铝2-3、氧化硼3-5、聚乙烯醇7-9、松香14-18、3-氨丙基三甲氧基硅烷1.2-2.4、聚二甲基硅氧烷0.3-0.4、丙酮9-14、环己酮7-10，其制备方法是将三氧化二铝、氧化硼放入煅烧炉中于520-610℃下煅烧1-2小时，取出冷却至室温，加入聚乙烯醇研磨20-40分钟；将环己酮、松香混合，在100-120℃下反应2-3小时，冷却至40-50℃，加入丙酮、3-氨丙基三甲氧基硅烷、聚二甲基硅氧烷，保持温度搅拌3-4小时；将以上各反应产物混合，研磨2-4小时制得300-400目浆料即得。
所述的一种铜粉/珍珠粉复合的导电银浆的制备方法，其特征在于包括以下步骤：
（1）取铜粉、珍珠粉加适量水研磨1-2小时，加入尿素继续研磨30-40分钟，喷雾干燥，放入煅烧炉中在450-510℃下烧结1-2小时；
（2）取环氧化甘油三酸酯、肉豆蔻酸异丙酯加热到45-65℃，加入聚二甲基硅氧烷、碳酸氢铵搅拌30-40分钟至混匀，放入耐磨炭黑、沸石粉研磨2-3小时成浆；
（3）将步骤（1）、（2）反应物料及其他剩余物料混合，升温至100-120℃，搅拌反应1-2小时，冷却，研磨成粒径为10-20μm浆粒，即得。
本发明有以下有益效果：本发明添加铜粉、珍珠粉、耐磨炭黑，减少了银粉的使用量降低了生产成本，提高了银浆的导电性能，进而提高了生产效率。
具体实施方式
所述的一种铜粉/珍珠粉复合的导电银浆，其特征在于，由下列重量份的原料制成：银粉42、铜粉5、珍珠粉3、耐磨炭黑3、沸石粉5、环氧化甘油三酸酯4、碳酸氢铵0.4、尿素1.2、肉豆蔻酸异丙酯4、聚二甲基硅氧烷1.8、助剂40、适量水。
所述的助剂由下列重量份原料制成：三氧化二铝2、氧化硼4、聚乙烯醇7、松香15、3-氨丙基三甲氧基硅烷1.5、聚二甲基硅氧烷0.3、丙酮12、环己酮8，其制备方法是将三氧化二铝、氧化硼放入煅烧炉中于520-610℃下煅烧1-2小时，取出冷却至室温，加入聚乙烯醇研磨20-40分钟；将环己酮、松香混合，在100-120℃下反应2-3小时，冷却至40-50℃，加入丙酮、3-氨丙基三甲氧基硅烷、聚二甲基硅氧烷，保持温度搅拌3-4小时；将以上各反应产物混合，研磨2-4小时制得300-400目浆料即得。
制作方法包括以下步骤：
（1）取铜粉、珍珠粉加适量水研磨1-2小时，加入尿素继续研磨30-40分钟，喷雾干燥，放入煅烧炉中在450-510℃下烧结1-2小时；
（2）取环氧化甘油三酸酯、肉豆蔻酸异丙酯加热到45-65℃，加入聚二甲基硅氧烷、碳酸氢铵搅拌30-40分钟至混匀，放入耐磨炭黑、沸石粉研磨2-3小时成浆；
（3）将步骤（1）、（2）反应物料及其他剩余物料混合，升温至100-120℃，搅拌反应1-2小时，冷却，研磨成粒径为10-20μm浆粒，即得。
通过上述实施例加工得到的导电银浆的技术指标如下：
（1）黏度：50-100Pa·s（Brookfield，10RPM）；
（2）附着力：＞10N/mm2；
（3）方阻：＜5mΩ/c ；
（4）铅镉含量：＜100ppm ；
（5）可焊性优、堆烧易分离、印刷适应性好和耐溶剂性优。

Claims (2)

1.一种铜粉/珍珠粉复合的导电银浆，其特征在于，由下列重量份的原料制成：银粉35-45、铜粉4-6、珍珠粉2-4、耐磨炭黑1-3、沸石粉2-5、环氧化甘油三酸酯4-7、碳酸氢铵0.4-0.8、尿素0.5-1.2、肉豆蔻酸异丙酯3-6、聚二甲基硅氧烷1.2-2.4、助剂30-40、适量水；所述的助剂由下列重量份原料制成：三氧化二铝2-3、氧化硼3-5、聚乙烯醇7-9、松香14-18、3-氨丙基三甲氧基硅烷1.2-2.4、聚二甲基硅氧烷0.3-0.4、丙酮9-14、环己酮7-10，其制备方法是将三氧化二铝、氧化硼放入煅烧炉中于520-610℃下煅烧1-2小时，取出冷却至室温，加入聚乙烯醇研磨20-40分钟；将环己酮、松香混合，在100-120℃下反应2-3小时，冷却至40-50℃，加入丙酮、3-氨丙基三甲氧基硅烷、聚二甲基硅氧烷，保持温度搅拌3-4小时；将以上各反应产物混合，研磨2-4小时制得300-400目浆料即得。
2.根据权利要求1所述的一种铜粉/珍珠粉复合的导电银浆的制作方法，其特征在于包括以下步骤：
（1）取铜粉、珍珠粉加适量水研磨1-2小时，加入尿素继续研磨30-40分钟，喷雾干燥，放入煅烧炉中在450-510℃下烧结1-2小时；
（2）取环氧化甘油三酸酯、肉豆蔻酸异丙酯加热到45-65℃，加入聚二甲基硅氧烷、碳酸氢铵搅拌30-40分钟至混匀，放入耐磨炭黑、沸石粉研磨2-3小时成浆；
（3）将步骤（1）、（2）反应物料及其他剩余物料混合，升温至100-120℃，搅拌反应1-2小时，冷却，研磨成粒径为10-20μm浆粒，即得。
CN201410368833.3A 2014-07-30 2014-07-30 一种铜粉/珍珠粉复合的导电银浆及其制作方法 Active CN104157325B (zh)