CN104078102A - 一种改性纳米碳导电银浆及其制作方法 - Google Patents

一种改性纳米碳导电银浆及其制作方法 Download PDF

Info

Publication number
CN104078102A
CN104078102A CN201410303653.7A CN201410303653A CN104078102A CN 104078102 A CN104078102 A CN 104078102A CN 201410303653 A CN201410303653 A CN 201410303653A CN 104078102 A CN104078102 A CN 104078102A
Authority
CN
China
Prior art keywords
parts
hour
conductive silver
slurry
nanometer carbon
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410303653.7A
Other languages
English (en)
Inventor
郭万东
孟祥法
董培才
陈伏洲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chinaland Solar Energy Co Ltd
Original Assignee
Chinaland Solar Energy Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chinaland Solar Energy Co Ltd filed Critical Chinaland Solar Energy Co Ltd
Priority to CN201410303653.7A priority Critical patent/CN104078102A/zh
Publication of CN104078102A publication Critical patent/CN104078102A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种改性纳米碳导电银浆，其特征在于，由下列重量份的原料制成：导电银粉50-55、液体石蜡3-5、硫酸铜0.2-0.4、葡萄糖2-4、月桂醇硫酸钠0.2-0.4、丙烯酸1-3、蓖麻油酸聚酯1.2-2.4、环氧树脂E-060.4-1.6、纳米碳2.3-3.6、助剂25-35；本发明制备方法简单，操作方便，配方合理，在配方中添加了改性纳米碳，增加了本发明浆料的导电性能，制得的导电浆料具有附着力佳、不易脱落等优点，利用本发明制得的导电银浆可广泛应用于薄膜开关、电路及电路板等生产中。

Description

一种改性纳米碳导电银浆及其制作方法
技术领域
本发明涉及导电银浆领域，具体涉及一种改性纳米碳导电银浆及其制作方法。
背景技术
导电银浆是指印刷于导电承印物上，使之具有传导电流和排除积累静电荷能力的银浆，一般是印在塑料、玻璃、陶瓷或纸板等非导电承印物上，它是由导电性填料、黏合剂、溶剂及添加剂组成。导电银浆时需要具备的特性有：导电性（抗静电性）佳、附着力强、印刷适应性好和耐溶剂性优等特性，而目前市场上现有的导电银浆有很多缺点，不仅含有铅、镉等且有毒，污染环境，而且使用在导电承印物上时附着力低、耐焊接性不佳，烧结性能差。
发明内容
本发明的目的就是提供一种改性纳米碳导电银浆及其制作方法，以克服现有技术的不足。
本发明的目的是这样实现的：
一种改性纳米碳导电银浆，其特征在于，由下列重量份的原料制成：导电银粉50-55、液体石蜡3-5、硫酸铜0.2-0.4、葡萄糖2-4、月桂醇硫酸钠0.2-0.4、丙烯酸1-3、蓖麻油酸聚酯1.2-2.4、环氧树脂E-06 0.4-1.6、纳米碳2.3-3.6、助剂25-35。
所述的助剂由下列重量份原料制成：氧化铋2-3、氧化硼3-4、乙基纤维素0.8-1.4、十二烷基硫酸钠0.3-0.4、邻苯二甲酸二甲酯0.2-0.4、卵磷脂0.3-0.5、聚硅氧烷0.2-0.3、松油醇20-25，其制备方法是将氧化铋和氧化硼放入煅烧炉中于520-610℃下煅烧1-2小时，取出冷却至室温，加入乙基纤维素研磨20-40分钟；将邻苯二甲酸二甲酯、松油醇搅拌混匀，在140-190℃下反应2-3小时，冷却至80-100℃，加入卵磷脂、聚硅氧烷、十二烷基硫酸钠，保持温度搅拌3-4小时；将以上各反应产物混合，研磨2-4小时制得300-400目浆料即得。
所述的一种改性纳米碳导电银浆的制备方法，其特征在于包括以下步骤：
（1）取液体石蜡、纳米碳混合研磨2-3小时制得200-300目浆料，加入硫酸铜、月桂醇硫酸钠继续研磨3-4小时，喷雾干燥，烘干，送入煅烧炉中在430-500℃下烧结1-2小时，制得改性纳米碳；
（2）取丙烯酸、蓖麻油酸聚酯放入反应釜中加热到55-75℃搅拌混匀，加入环氧树脂E-06，保持温度搅拌2-3小时，至环氧树脂E-06完全溶解，再加入葡萄糖，保温30-50分钟，研磨成浆；
（3）将步骤（1）、（2）反应物料及其他剩余物料混合，升温至100-120℃，搅拌反应1-2小时，冷却，研磨成粒径为10-20μm浆粒，即得。
本发明有以下有益效果：本发明制备方法简单，操作方便，配方合理，在配方中添加了改性纳米碳，增加了本发明浆料的导电性能，制得的导电浆料具有附着力佳、不易脱落等优点，利用本发明制得的导电银浆可广泛应用于薄膜开关、电路及电路板等生产中，而且导电浆料无有害物质，符合国家标准。
具体实施方式
所述的一种改性纳米碳导电银浆，其特征在于，由下列重量份的原料制成：导电银粉52、液体石蜡5、硫酸铜0.4、葡萄糖4、月桂醇硫酸钠0.4、丙烯酸2、蓖麻油酸聚酯2.4、环氧树脂E-061.6、纳米碳2.3、助剂35。
所述的助剂由下列重量份原料制成：氧化铋2、氧化硼3、乙基纤维素0.9、十二烷基硫酸钠0.3、邻苯二甲酸二甲酯0.4、卵磷脂0.3、聚硅氧烷0.3、松油醇24，其制备方法是将氧化铋和氧化硼放入煅烧炉中于520-610℃下煅烧1-2小时，取出冷却至室温，加入乙基纤维素研磨20-40分钟；将邻苯二甲酸二甲酯、松油醇搅拌混匀，在140-190℃下反应2-3小时，冷却至80-100℃，加入卵磷脂、聚硅氧烷、十二烷基硫酸钠，保持温度搅拌3-4小时；将以上各反应产物混合，研磨2-4小时制得300-400目浆料即得。
制作方法包括以下步骤：
（1）取液体石蜡、纳米碳混合研磨2-3小时制得200-300目浆料，加入硫酸铜、月桂醇硫酸钠继续研磨3-4小时，喷雾干燥，烘干，送入煅烧炉中在430-500℃下烧结1-2小时，制得改性纳米碳；
（2）取丙烯酸、蓖麻油酸聚酯放入反应釜中加热到55-75℃搅拌混匀，加入环氧树脂E-06，保持温度搅拌2-3小时，至环氧树脂E-06完全溶解，再加入葡萄糖，保温30-50分钟，研磨成浆；
（3）将步骤（1）、（2）反应物料及其他剩余物料混合，升温至100-120℃，搅拌反应1-2小时，冷却，研磨成粒径为10-20μm浆粒，即得。
通过上述实施例加工得到的导电银浆的技术指标如下：
（1）黏度：50-100PaS（Brookfield，10RPM）；
（2）附着力：＞10N/mm2；
（3）方阻：＜5mΩ/c ；
（4）可焊性优、堆烧易分离、印刷适应性好和耐溶剂性优。

Claims (2)

1.一种改性纳米碳导电银浆，其特征在于，由下列重量份的原料制成：导电银粉50-55、液体石蜡3-5、硫酸铜0.2-0.4、葡萄糖2-4、月桂醇硫酸钠0.2-0.4、丙烯酸1-3、蓖麻油酸聚酯1.2-2.4、环氧树脂E-06 0.4-1.6、纳米碳2.3-3.6、助剂25-35；所述的助剂由下列重量份原料制成：氧化铋2-3、氧化硼3-4、乙基纤维素0.8-1.4、十二烷基硫酸钠0.3-0.4、邻苯二甲酸二甲酯0.2-0.4、卵磷脂0.3-0.5、聚硅氧烷0.2-0.3、松油醇20-25，其制备方法是将氧化铋和氧化硼放入煅烧炉中于520-610℃下煅烧1-2小时，取出冷却至室温，加入乙基纤维素研磨20-40分钟；将邻苯二甲酸二甲酯、松油醇搅拌混匀，在140-190℃下反应2-3小时，冷却至80-100℃，加入卵磷脂、聚硅氧烷、十二烷基硫酸钠，保持温度搅拌3-4小时；将以上各反应产物混合，研磨2-4小时制得300-400目浆料即得。
2.根据权利要求1所述的一种改性纳米碳导电银浆的制作方法，其特征在于包括以下步骤：
（1）取液体石蜡、纳米碳混合研磨2-3小时制得200-300目浆料，加入硫酸铜、月桂醇硫酸钠继续研磨3-4小时，喷雾干燥，烘干，送入煅烧炉中在430-500℃下烧结1-2小时，制得改性纳米碳；
（2）取丙烯酸、蓖麻油酸聚酯放入反应釜中加热到55-75℃搅拌混匀，加入环氧树脂E-06，保持温度搅拌2-3小时，至环氧树脂E-06完全溶解，再加入葡萄糖，保温30-50分钟，研磨成浆；
（3）将步骤（1）、（2）反应物料及其他剩余物料混合，升温至100-120℃，搅拌反应1-2小时，冷却，研磨成粒径为10-20μm浆粒，即得。
CN201410303653.7A 2014-06-30 2014-06-30 一种改性纳米碳导电银浆及其制作方法 Pending CN104078102A (zh)