CN1040828A - 热浸镀铝的铬合金钢 - Google Patents

热浸镀铝的铬合金钢 Download PDF

Info

Publication number
CN1040828A
CN1040828A CN89106964A CN89106964A CN1040828A CN 1040828 A CN1040828 A CN 1040828A CN 89106964 A CN89106964 A CN 89106964A CN 89106964 A CN89106964 A CN 89106964A CN 1040828 A CN1040828 A CN 1040828A
Authority
CN
China
Prior art keywords
steel band
described steel
atmosphere
plating
temperature
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN89106964A
Other languages
English (en)
Other versions
CN1020928C (zh
Inventor
史蒂文·L·博斯顿
理查德·A·科利曼
法雷尔·M·基尔班
丹尼·E·李
威廉·R·西伊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Armco Inc
Original Assignee
Armco Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=22895771&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=CN1040828(A) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by Armco Inc filed Critical Armco Inc
Publication of CN1040828A publication Critical patent/CN1040828A/zh
Application granted granted Critical
Publication of CN1020928C publication Critical patent/CN1020928C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明涉及连续热浸镀铝的铁素体铬合金钢带。在直接燃烧炉中加热至温度不大于650℃左右使钢带净化。净化的钢带在至少含有95％(按体积)氢的保护性气氛中进一步加热。在保护性氢气氛中冷却至接近或稍高于铝镀敷金属的熔点，然后送入铝镀敷金属熔池。低的直接燃烧炉净化温度和氢保护气氛提供了良好的铬合金钢表面润湿性以致防止在铝镀层中出现未镀敷区或针孔。

Description

本发明涉及连续热浸镀金属的碳素体铬合金铁基带材以及增强带材表面被熔融铝润湿的方法。
热浸镀铝钢具有很高的耐盐腐蚀性并发现在自动排气系统和燃烧装置中有许多应用。近年来，对排气系统在耐用性和美观方面的要求已有增加。因此，要求用镀铝的铬合金钢代替镀铝的低碳或低合金钢以增加耐高温氧化性能和耐盐腐蚀性能。至于高温氧化性，是在使用期间由于加热使至少部分的铝镀层可以扩散到铁基以致形成Fe-Al合金层。如果镀铝层中存在未镀敷区，倘若不是连续在基体金属上形成Fe-Al合金就可能产生因加速氧化而导致的基体金属穿孔。低温时，铝镀层充当一个对大气条件的保护屏和高盐份环境中的阴极镀层。而且，如果存在未镀敷区，会发生加速腐蚀以致破环镀敷结构。
众所周知，在无熔剂的情况下热浸镀低碳钢带材是将带材经过清除油、污物和氧化铁等表面清洁的预处理使之容易被镀敷金属润湿。颁发给C、A、Turner的美国专利3，320，085描述了用于低碳钢的预先在线退火处理的一种类型。Turner流程，也是大家所知的Selas流程，用于制备热浸镀金属的低碳钢带材，它包括将钢带通过一个具有温度至少加热到2400°F（1316℃）气氛的直接燃烧炉。由燃料和空气（但没有游离氧）燃烧的气体产物形成这种气氛。控制燃料-空气的比率以便提供能有效净化钢带所必需的还原特性。调节燃料-空气比率使得燃料稍微过剩以致没有游离氧但有过剩的一氧化碳和氢形式的可燃物。至少具有3%过剩可燃物的至少维持在1316℃的炉气氛被降低到使钢温达1700°F（927℃）。Turner指出，在净化过的带材进入浸镀槽之前要通过一具有中性或保护性气氛的密封输送通道。关于用熔融锌镀覆，Turner指出将钢带加热至最高为1000°F（（538℃）。至于用熔融铝镀敷，Turner指出，在直接燃烧炉中温度为1250-1300°F（677-704℃）范围内加热钢带，因为在这种温度条件下炉内气氛对钢一直是还原性气氛。
现代直接燃烧炉包括一般用辐射管加热的附加炉段。这个炉段含有与上述输送通道相同的中性或还厚性保护气氛，即75%氮，25%氢。
颁发给Flinchum等人的美国专利No，3，925，579，描述了一个用于热浸镀铝的低合金钢带的在线预处理，它用来增强被镀敷金属润湿的性能。这种钢（按重量）含有高达5%铬，高达3%铝，高达2%硅和高达1%钛中的一种或几种。钢带在使铁氧化形成表面氧化物层的氧化气氛中被加热至温度高于1100°F（593℃），在使氧化铁还原的状态下进一步处理从而使表面层还原成含有合金元素氧化物均匀弥散的纯净铁基质。
铁素体铬合金钢上铝镀层不润湿的问题是众所周知的。热浸铝镀层对铁素体合金钢基体金属的润湿性很弱，因而一般在铝镀层中都有未镀敷或裸露点。粘附力弱这意味着在弯折钢带时镀层会起鳞或产生裂纹。为了解决粘附力的问题，有人建议热处理镀过铝的钢使得镀层固定在基体金属上。另外再稍加轧制镀敷过的铬合金钢以致铝镀层粘牢。最终，涉及未镀敷点的这些问题一般由连续热浸镀而得以避免。更确切地说，熔池型热浸镀或喷镀方法业已被使用。例如，在制成铬合金钢制品之后，在镀铝池中浸渍一段时间以形成一很薄的镀层。
颁发给F、M、Kilbane等人的美国专利NO        4，675，214，其中讲到，建议增强用热浸铝镀层连续镀敷铁素体铬合金钢带的润湿性的解决办法。Kibane流程包括清洁处理铁素体铬合金钢、并在进入镀铝池之前将净化过的钢通过基本上无氮的保护性氢气氛。只要钢不是通过在直接燃烧炉中加热至一高温的方法来净化，该流程就能提高铁素体铬合金的润湿性。按照Turner流程，具有至少3%加热至2400°F（1316℃）可燃物气氛的直接燃烧炉温度降低使钢温升至1700°F（927℃）。尽管如此，在无游离氧的直接燃烧炉气氛中在约1250°F（677℃）或高于此温度下加热铁素体铬合金钢，继而使钢材通过基本上为纯氢的保护性气氛，然后立即热浸镀铝的方法仍然有许多未镀敷区。没有理论根据，但认为无游离氧的直接燃烧炉气氛由于有水存在而具有明显的氧化潜力而且显然是氧化铬合金钢带中所含的铬。钢带表面上形成的氧化铬在进入浸镀池之前显然不能充分地被保护性氢气氛去除，因而妨碍钢带表面完全润湿。
本发明涉及连续用铝浸镀在直接燃烧炉中通过燃料和空气的燃烧加热的铁素体铬合金钢，炉中燃烧的气体产物没有游离氧。钢带表面加热到其温度足以去除油、污物、氧化铁及其它，但低于引起带钢基体金属中铬过于氧化的温度。钢带在另一炉段进一步加热并冷却（如果需要）使之接近或稍高于铝镀敷金属的熔点。然后将钢带通过至少有95%（按体积）氢的保护性气氛，随后进入铝镀敷金属熔池使钢带上镀一层镀敷金属。
本发明的主要目的是形成一种镀敷金属润湿性能很强的热浸镀铝的铁素体铬合金钢。
本发明的另一目的是在直接燃烧炉中净化的铬合金钢带上形成一热浸铝镀层。
本发明还有一目的是在深冲铬合金钢带上形成一热浸铝镀层，该钢带是在镀敷流线上进行在线退火。
本发明的一个特征是对铝镀层润湿性很强的铁素体铬合金钢带是通过在镀铝流线上的直接燃烧炉中低于使钢带中所含铬发生过氧化的温度下加热钢带的方法进行清洁处理。
本发明的另一特征是进一步加热净化过的铬合金钢使之在至少含有约95%（按体积）氢的保护性气氛的另一炉段中是完全退火状态。
本发明的第三个特征是，提供的热能小于镀铝流线上的直接燃烧炉中使深冲铁素体铬合金钢完全退火所需总热能的80%。
本发明的第四个特征是，在至少含有约95%（按体积）氢、小于200ppm氧且露点低于+40°F（+4℃）的保护性气氛中保存净化过的铬合金钢带，直到净化过的钢带通过并进入铝镀敷金属中。
本发明的第五个特征是，在至少含有95%（按体积）氢且露点不高于0°F（-18℃）的保护性气氛中完全退火和冷却加热过的铬合金钢带，将钢带通过具有至少含97%（按体积）氢且露点不大于-20°F（-29℃）的保护性气氛的炉口，然后将带材浸入铝镀敷金属中。
本发明的优点是消除未镀敷区并提高直接燃烧炉中净化的铁素体铬合金钢带的粘附力以及连续用铝热浸镀。
图1是铁基钢带通过包括本发明之热浸镀铝流线进行加工的工艺流程图。
图2是图1所示镀敷流线的部分流程图，它示出炉口和镀槽。
以下就附图详细说明本发明。
现在参看图1，参考序号10表示卷有钢带11的钢带盘，由此通过并绕过轧辊12、13和14，然后进入第一炉段15的顶部。第一炉段是由燃料和空气燃烧加热的直接燃烧型。燃料和空气之比是成比例的以致燃烧的气体产物中没有游离氧，而且最好有至少3%（按体积）的过剩可燃物。炉子15的气氛最好是加热至高于2400°F（1316℃）并且钢带11保持在足够的速度以致当除去轧机油膜、污物、氧化铁皮及其它诸如此类的表面沾污时钢带表面温度不会使铬过份氧化。除了以后详细解释的一个短暂时间外，钢带在炉段15中时应加热到温度不高于1200°F（649℃）左右，最好是不高于1150°F（621℃）。
序号16所表示的炉子的第二段，可以是一个辐射管型的。钢带11进一步加热至温度至少为铝镀敷金属的熔点即1200°F（649℃）左右，并在18位置达到最高温度，即达1750°F（955℃）左右。在炉段16中以及以下将要描述的后续炉段中最好保持至少含有95%（按体积）氢的保护性气氛。
炉段20和22是冷却区。钢带11由炉段22越过翻折辊24，通过炉口26然后进入装有熔融铝的镀槽28。钢带在镀槽中逗留一很短时间即2-5秒钟。两侧带有镀敷金属层的钢带11从镀槽28垂直拉出。镀层固化，而镀过的钢带绕过旋转轧辊32被卷成带钢卷34以备贮存或进一步加工。如上面所指示的那样，炉段20、22和26含有保护性氢气氛。
参看图2，炉口26由于具有浸没在铝镀敷金属42的表面44以下的下口或进口端26a使之与大气隔离。适合于翻转的安装是镀槽辊36和38以及稳定辊40。它从镀槽28拉出时留在带钢11上的镀敷金属的重量通过喷射刮刀（jet        knives）30之类的精整装置来控制。带钢11在炉段20、22和26中冷却到温度接近或稍高于铝镀敷金属的熔点，然后进入镀槽28。这个温度对铝合金镀敷金属来说可低到1150°F（620℃），对工业纯铝镀敷金属（如工类）可高到1350°F（732℃）左右。
图2所示装置是用空气精整的两侧镀层。如熟悉颈领域的技术人员所了解的那样，也可采用含有非氧化气氛的密封套的精整。
工业纯的氢气可通过炉口26中的进口27送入炉区以致最好能获得含有低于200ppm氧且露点不大于+40°F（+4℃）的氢保护性气氛。根据氢流量和炉容积这类的因素还可要求在炉段16、20和22中添加氢气进口。
本文所定义的铁素体铬合金钢包括铁基磁性材料，其特征在于它为体心立方结构并约有0.5%（重量）或更多的铬。例如，本发明特别适用于含铬量高达35%（按重量）左右热浸镀铝的铁素体不锈钢，并用于包括厚度等于或大于1.2mm大型发动机排气管的自动排气系统，用作催化转换器催化剂载体的由镀铝钢带冷轧而成的厚度小于0.25mm的板片，以及深冲成要求两侧镀铝总面积不大于185gm/m2的轻量铝镀层部件（例如管道、马弗炉部件，催化转化器、共振器及其它）的完全退火钢带。完全退火是指在炉子16中加热到至少830℃左右并在拉伸试验中测得的伸长率至少25%左右。409型铁素体不锈钢特别适合于用作本发明的起始材料。这种钢具有标准组成，即按重量，约11%铬，约0.5硅，余量主要为铁。更概括地说，按重量含量约10.0%～14.5%铬，约0.1%～1.0%硅，和余量主要是铁的铁素体钢是最佳的。以下是说明本发明的非限制性实施例。
用图1和图2所示之镀敷流线在699～704℃温度下用纯的熔融铝镀料（2类）镀敷厚度为1.02mm宽度为122cm的409型不锈钢带材。将工业纯氢以约380m3/小时的速率送入炉口26，并在炉段16保持氮为75%（体积）和氢为25%（体积）气氛。炉口26中纯的保护性氢气氛的露点开始是+48°F（+9℃）。直接燃烧炉段15中的燃料/空气比被控制成约有5%（体积）的过剩可燃烧物。对各种带速和温度，做如下目侧。
带速 DFF（℃）＊
试样 （m/分钟） T(℃)＊＊ ＊＊＊氧化物 镀敷状况
ABCD 37465537 760704649649 917917871871 深蓝色浅蓝色金色金色 无规则未镀敷区″仅钢带边缘未镀敷镀敷良好
＊炉段15处的带钢温度
＊＊炉段16处的带钢温度
＊＊＊从炉段15通过的带钢11的表面外观
如上所示，在燃烧产物不含游离氧的气氛中加热到温度至少为649℃时，铁素体铬合金钢被氧化。由于至少有一些铁和/或铬氧化物被氢气氛还原成金属和水，炉口26中氢气氛的露点增加到最大，为+58°F（+14℃）左右。在直接燃料炉中加热到至少704℃的试样A和B被过份氧化并且不能很好地被铝镀敷金属润湿。在直接燃烧炉中加热到至少649℃时，钢带的氧化量或多或少是过量的，显示出沿试样C的一个边缘镀敷润湿性很差。使用一种极干燥的保护性氢气氛例如露点不大于0℃（-19°F）的气氛，在炉段16、20、22和炉口26这一区间很可能足以除去试样C上的氧化物，结果是有较好的铝镀敷金属润湿性。与低碳钢的普通常识相反，铁素体铬钢当加热到至少649℃时，很容易在不含游离氧但含过剩可燃物的气氛中氧化。
实施例2
除了在炉段16和冷却区20、22中也保持保护性纯氢气氛外，其它条件与实施例1相类似，用2类铝以183gm/m（两侧总面积）镀敷厚度为1.64mm宽为94cm的一卷409型不锈钢带。在该钢带通过镀敷流线之前，炉口26中氢气氛的露点为-9°F（（-23℃）。对各种带钢温度下的镀层做出如下观测：
试样        DFF（℃）        RT（℃）        镀层外观
A        817        908        不好，常见未镀敷点
B        620        841        好，不常见未镀敷点
实施例3
除了炉口26中氢气氛的露点为-50°F（-46℃）和辐射管炉段16中的露点为-4°F（-20℃）外，其它条件与实施例2相类似，处理并用2类铝以737gm/m（两侧总面积）镀敷三卷409型不锈钢。对各种钢带温度下的镀层做出如下观测。
厚度        宽度        DFF        RT        镀层外观
试样        （mm）        （cm）        （℃）        （℃）
A        1.4        117        676        892        有若干未镀敷点
B        1.3        91        677        902        特别是离一边缘的10cm处
有分散的未镀敷点
C        1.4        76        604        871        没有未镀敷点
实施例1-3清楚地表明，在直接燃烧炉中将带钢加热到至少676℃导致了带钢过氧化。使用极干燥保护性氢气氛的整个炉段16、20、22和炉口26这一区域不足以去除氧化物以获得良好的镀敷金属润湿性。另一方面，在直接燃烧炉中将带钢加热至不高于650℃，并在辐射管炉中将带钢进一步加热至温度高于830℃以致在可以深冲的完全退火带钢上粘附未镀敷区为最少的铝镀层，并且不起鳞或产生裂纹
实施例4
将厚度1.08mm宽度76cm的409型不锈钢带成功地用含9%硅（重量）的铝合金（1类）以119gm/m2（两侧总面积）连续热浸镀。操作条件与实施例2相同。带钢在炉段15加热至627℃左右，并在炉段16加热至829℃。观察到极少的未镀敷区。
实施例5-10
实施例5-10是含铬（按重量）2.01，4，22和5，99%的铁素体、低碳、钛稳定钢带，厚为0.38mm，宽为12.7cm。这些试样在类似于图1和图2的实验室镀敷流线上以类似于实施例2的条件连续热镀铝。不测量镀层的重量。
速度 DFF＊ %H2＊＊
试样号        %Cr        m/分钟        状况
5        2.01        7.6        1204        25        镀层不好
6        4.22        12.2        1093        25        镀层不好
7        5.99        12.2        1193        25        镀层不好
8        2.01        9.1        1227        100        镀层极好
9        4.22        9.1        1238        100        镀层好
10        5.99        9.1        -        100        镀层好
＊.炉区温度
＊＊.保护性气氛中的氢含量
尽管不测量从直接燃烧炉中出来的带钢温度，但数据显然支持除直接燃烧部分外炉子的全部区城都使用100%（按体积）氢气氛。由于实施例5-10中的铬含量低于前几个实施例（11（重量）%），有理由预期直接燃烧炉钢带的出口温度与较低铬合金（2，4，6（重量）%）的关系较少。换句话说，铬含量较少则氧化的可能性就较少。
如上所述，燃料和不含游离氧的空气燃烧所产生的气体产物构成的直接燃烧气氛在1200°F（649℃）左右使铁素体铬合金钢氧化。因此，直接燃烧炉段15中的钢带温度不应超过此温度，特别是铬含量等于或大于10%（重量）的铁素体不锈钢尤其如此。这种钢带的净化温度最好不超过1150℃（621℃）左右。尽管如此，由于带钢宽度和/或尺寸变化，钢带温度有时要超过649℃。可以通过精心控制整个炉段16、冷却区20、22和炉口26这一区域的保护性气氛条件来暂时排除，即低于10分钟的约等于或稍高649℃的温度是允许的。由于在炉段16，冷却区20、22和炉口26保持至少含有约95%（体积）氢的保护性气氛，则可以消除炉段15中带钢11产生的氧化作用至最少。在这方面，我们已特别有利地规定在保护性氢气氛中保持极低的露点以平衡铁和铬的氧化物被保护性气氛中的氢还原时所生成的水。炉口26中的保护性气氛最好是至少含有97%（体积）氢，且露点不超过-20°F（-29℃）。在炉段16和冷却区20、22中最好保持0°F（-18℃）的露点。
如美国专利4，675，214所公开的那样，铝镀敷金属的反应性在高温下增加。因此，将铝镀层保持在1280～1320°F（693-716℃）也有助于除去没有被保护性气氛除去的残余表面氧化物。然而，当浸没在铝镀敷金属熔池中时不希望从带钢表面上除去氧化物，因为被还原的氧化物在镀池表面上形成氧化铝（渣）。氧化铝在钢带出镀槽时作为碎片粘附在钢带上防碍铝镀敷金属与钢带之间的金属结合以致形成未镀敷区。
当带钢温度高时即高于830℃时，本发明的指教尤为重要，要求完全退火以便生产用于高成型产品的深冲带钢。关于低碳钢带材的高温退火，高达90%的总热量进入带钢是在炉子的直接燃烧部分中完成的。下表示出低碳钢（先有技术）和铁素体铬合金钢（本发明）在直接燃烧区所达到的总热含量的百分数。
先有技术
                                                                                                                                                MW/Hr,MW/Hr
t(mm) W(cm) tXw S(mpm) T1(℃) T2(℃) 至T1至T2％T＊2
0.81        76                62            95                760                857                3.9        4.4        88.4
1.40        76                106        64                749                857                4.4        5.0        87.0
1.75        86                151        43                760                857                4.3        4.9        88.4
                                                                                本发明
0.81        76        62        64        624        831        2.1        2.9        74.5
1.40        76        106        40        628        832        2.3        3.1        74.8
1.75        86        151        33        631        849        2.8        3.8        73.6
t＝带钢厚度
W＝带钢宽度
S＝通过直接燃烧炉的带钢速度
T1＝直接燃烧炉中的带钢温度
T2＝辐射管加热炉中的带钢温度
＊＝%总热含量
如上所述，完全退火低碳钢的近90%的总热含量在炉子的直接燃烧段获得，而另一方面，如果避免过氧化作用，则低于80%的完全退火热浸镀铝的铬合金钢的总热含量可以在炉子的直接燃烧段获得。换句话说，对于本发明之完全退火钢带，允许的最高直接燃烧炉带钢温度必须低于提供至少80%总热量输入所需要的温度。
不违反本发明的精神和范围的情况下，即只要是铬合金钢带在直接燃烧炉中不被加热至使钢带发生过氧化的温度并且在进入镀敷金属熔池之前通过一至少含有大约95%（按体积）氢的保护性气氛，可对本发明做各种变更。例如，在直接燃烧和镀槽输送通道之间整个镀敷流线的任何加热和冷却段都可以使用氢气氛。镀敷金属可以包括纯铝和铝基合金。镀敷金属量可由空气中的精整或密封套来控制。为此，本发明的限制由附上的权利要求来确定。

Claims (21)

1、连续用铝热浸镀钢带的方法，该方法包括以下步骤：
由燃料和空气燃烧的气体产物所形成的气氛中加热铁素体铬合金钢带，其中所述气氛没有游离氧而且所述钢带的温度不足以过氧化所述带钢中的铬；
将所述钢带通过至少约有95%(按体积)氢的保护性气氛；
将所述钢带浸入铝镀敷金属的熔池中以致在所述钢带上镀敷一层镀层；
所述镀层基本上无未镀敷区并且牢固地粘附在所述净化过的钢带上。
2、连续用铝热浸镀钢带的方法，该方法包括以下步骤：
由燃料和空气燃烧的气体产物所形成的气氛中加热铁素体铬合金钢带，其中所述气氛没有游离氧而且所述钢带的温度不足以过氧化所述带钢中的铬;
进一步加热所述钢带使温度不低于铝镀敷金属的熔点;
如果需要，将所述钢带冷却至接近或稍高于上述熔点;
将所述钢带通过至少约有95%（按体积）氢的保护性气氛;
将所述钢带浸入铝镀敷金属的熔池中以致在所述钢带上镀敷一层镀层;
所述镀层基本上无未镀敷区并且牢固地粘附在所述钢带上。
3、连续用铝热浸镀钢带的方法，该方法包括以下步骤：
由燃料和空气燃烧的气体产物所形成的气氛中加热铁素体铬合金钢带，其中所述燃烧的气体产物没有游离氧;
进一步加热所述钢带使温度至少约为830℃;
冷却所述钢带至温度接近或稍高于铝镀敷金属的熔点;
将所述钢带通过至少约有95%（按体积）氢的保护性气氛;
将所述钢带浸入铝镀敷金属的熔池中以致在所述钢带上镀敷一层镀层;
所述镀层基本上无未镀敷区并且牢固地粘附在所述钢带上。
4、按照权利要求3的方法，其中，所述钢带用燃料与空气的直燃烧加热至不高于621℃左右。
5、按照权利要求3的方法，其中，所述钢带进一步在所述气氛中加热至温度为845℃～955℃。
6、按照权利要求3的方法，在所述气氛中冷却所述钢带。
7、按照权利要求3方法，其中，所述气氛含有的氧低于200ppm左右露点低于+4℃左右。
8、按照权利要求3的方法，其中，所述镀敷金属基本上是纯铝。
9、按照权利要求3的方法，其中，所述钢带至少含有10%铬（按重要）。
10、连续用铝热浸镀钢带的方法，该方法包括以下步骤：
在直接燃烧型的第一炉段加热铁素体铬合金钢带;
在第二炉段进一步加热所述钢带;
在所述第一炉段的所述加热，提供少于在所述第二炉段的所述进一步加热之后的所述钢带总热含量的80%;
冷却所述钢带使温度接近或稍高于铝镀敷金属的熔点;
将所述钢带通过至少约含95%（体积）氢的保护性气氛;
将所述钢带浸入所述镀敷金属的熔池中以致在所述钢带上镀敷一层镀层;
所述镀层基本上无未镀敷区并且牢固地粘附在所述钢带上。
11、连续用铝热镀钢带的方法，该方法包括以下步骤：
在直接燃烧型的第一炉段中加热铁素体铬合金钢带;
所述钢带的温度不足以使所述钢带中的铬过氧化;
通过在第二炉段进一步加热至温度不低于830℃左右使所述钢带完全退火;
第二炉段中的所述钢带温度，提供少于所述钢带完全退火所要求的总热含量的80%，
在至少含有95%（按体积）左右氢的保护气氛中冷却所述钢带至温度接近或稍高于铝镀敷金属的熔点;
将所述钢带浸入所述镀敷金属熔池中以致在所述钢带上镀敷一镀层;
所述镀层基本上无未镀敷区并且牢固地粘附在所述钢带上。
12、按照权利要求11的方法，其中，在所述第一炉段的所述钢带温度低于650℃左右。
13、按照权利要求12的方法，其中，所述第二炉段含有所述气氛。
14、按照权利要求13的方法，其中，所述被冷却的钢带保持在至少含有约97%（按重量）氢的所述气氛中，直到浸入所述熔池。
15、按照权利要求14的方法，其中，所述气氛含有的氧少于200ppm，且露点小于-18℃左右。
16、连续用铝热浸镀钢带的方法，该方法包括以下步骤：
在直接燃烧型的第一炉段加热铁素体铬合金钢带;
所述钢带的温度不足以使所述钢带中的铬过氧化;
在第二炉段通过加热钢带至温度不低于830℃;
冷却所述钢带使之接近或稍高于铝镀敷金属的熔点;
将所述钢带通过至少含有大约95%（体积）氢的保护性气氛;
将所述钢带浸入所述镀敷金属的熔池中以致在所述钢带上镀敷一镀层;
所述镀层基本上无未镀敷区并且牢固地粘附在所述钢带上。
17、按照权利要求15的方法，其中，所述钢带在所述完全退火和所述冷却期间被保持在所述气氛中。
18、按照权利要求17的方法，其中，所述气氛中含有的氧少于200ppm，并且露点小于-18℃左右。
19、连续用铝热浸镀钢带的方法，该方法包括以下步骤：
在直接燃烧型的第一炉段中加热铁素体铬合金钢使温度不大于650℃左右;
在第二炉段进一步加热所述钢带使温度至少约为830℃，该炉段含有露点不高于-18℃且至少有95%（按体积）左右氢的保护性气氛;
在所述气氛中冷却所述钢带至接近或稍高于铝镀敷金属的熔点;
将所述钢带通过含有所述气氛的封闭式炉口进入所述镀敷金属熔池以致在所述钢带上镀敷一镀层;
所述炉口中的所述气氛至少有大约97%（按体积）氢且露点不大于-29℃;
所述镀层基本上无未镀敷区并且牢固地粘附在所述钢带上。
20、由权利要求16之方法制得的可深冲压镀铝钢带。
21、权利要求20的钢带，它至少含有10%（按重量）的铬并具有很高的耐盐腐蚀性和耐高温氧化性。
CN89106964A 1988-08-29 1989-08-25 一种铁素体铬合金带钢连续热浸镀铝的方法 Expired - Fee Related CN1020928C (zh)