KR900003397A - 용융 알루미늄 코팅된 크롬 합금강 - Google Patents
용융 알루미늄 코팅된 크롬 합금강 Download PDFInfo
- Publication number
- KR900003397A KR900003397A KR1019890012310A KR890012310A KR900003397A KR 900003397 A KR900003397 A KR 900003397A KR 1019890012310 A KR1019890012310 A KR 1019890012310A KR 890012310 A KR890012310 A KR 890012310A KR 900003397 A KR900003397 A KR 900003397A
- Authority
- KR
- South Korea
- Prior art keywords
- strip
- temperature
- coating
- heating
- atmosphere
- Prior art date
Abstract
내용 없음
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 철 모재 스트립을 가공하고 있는 본 발명을 구체화한 용융 알루미늄 코팅 라인의 개략도이고,
제2도는 유입 선단 및 코팅 포트를 나타낸 제1도의 코팅 라인의 부분 개략도이다.
Claims (21)
- (a) 철(III) 크롬 합금강 스트립을 연료와 공기의 가스상 연소 생성물로 형성된 유리 산소를 함유하지 않는 분위기에서 스트립의 온도가 스트립중의 크롬을 과도하게 산화시키기에는 불충분한 온도로 가열하는공정, (b) 상기 스트립을 적어도 95용적%의 수소를 함유하는 보호 분위기를 통과시키는 공정,(c) 상기 스트립을 알루미늄 코팅 금속의 용융조에 침지시켜 스트립상에 코팅층을 침착시키는 공정으로 구성되고, 상기 코팅층이 실질적으로 미코팅된 부분을 갖지 않고, 상기 세척된 스트립에 단단히 부착되는 것을 특징으로하는, 강 스트립을 알루미늄으로 연속 용융 코팅시키는 방법.
- (a) 철(III) 크롬 합금강 스트립을 연료와 공기의 가스상 연소 생성물로 형성된 유리 산소를 함유하지 않는 분위기에서 스트립의 온도가 스트립중의 크롬을 과도하게 산하시키기에는 불충분한 온도로 가열하는 공정, (b) 상기 스트립을 알루미늄 코팅 금속의 융점 이상의 온도로 추가 가열하는 공정, (c) 상기 스트립을 필요에 따라서 상기 융점 근처 또는 그보다 약간 더 높은 온도로 냉각시키는 공정, (d) 상기 스트립을 적어도 95용적%의 수소를 함유하는 보호 분위기를 통과시키는 공정, (e) 상기 스트립을 상기 코팅 금속의 용융조에 침지시켜 스트립상에 코팅층을 침착시키는 공정으로 구성되고, 상기 코팅층이 실질적으로 미코팅된 부분을 갖지 않고, 상기 세척된 스트립에 단단히 부착되는 것을 특징으로하는, 강 스트립을 알루미늄으로 연속 용융 코팅시키는 방법.
- (a) 철(III) 크롬 합금강 스트립을 연료와 공기의 직접 연소에 의한 유리 산소를 함유하지 않는 가스상 연소 생성물에 의해 약 650℃이하의 온도로 가열하는 공정, (b) 상기 스트립을 적어도 약 830℃의 온도로 추가가열하고,이 스트립을 알루미늄 코팅 금속의 융점 근처 또는 그보다 약간 더 높은 온도로 냉각시키는 공정, (c) 상기 스트립을 적어도 95용적%의 수소를 함유하는 보호 분위기를 통과시키는 공정, (d) 상기 스트립을 상기 코팅 금속의 용융조에 침지시켜 스트립상에 코팅층을 침착시키는 공정으로 구성되고, 상기 코팅층이 실질적으로 미코팅된 부분을 갖지 않고, 상기 세척된 스트립에 단단히 부착되는 것을 특징으로하는, 강 스트립을 알루미늄으로 연속 용융 코팅시키는 방법.
- 제3항에 있어서, 상기 스트립을 연료와 공기의 직접 연소에 의해 약 621℃이하의 온도로 가열하는 것을 특징으로 하는 방법.
- 제3항에 있어서, 상기 스트립을 상기 분위기하에서 845℃ 내지 955℃의 온도로 추가 가열하는 것을 특징으로 하는 방법.
- 제3항에 있어서, 상기 스트립을 상기 분위기하에서 냉각시키는 것을 특징으로 하는 방법.
- 제3항에 있어서, 상기 분위기가 약 200ppm미만의 산소를 함유하고, 약 +4℃미만의 노점을 갖는 것을 특징으로 하는 방법.
- 제3항에 있어서, 상기 코팅 금속이 실질적으로 순수한 알루미늄인 것을 특징으로 하는 방법.
- 제3항에 있어서, 상기 스트립이 적어도 10중량%의 크롬을 함유하는 것을 특징으로 하는 방법.
- (a) 철(III) 크롬 합금강 스트립을 직접 연소형 노의 제1부분내에서 가열하는 공정, (b) 상기 스트립을 노의 제2부분에서 추가 가열하는 공정, (c) 상기 스트립을 알루미늄 코팅 금속의융점 근처 또는 그 보다 약간 더 높은 온도로 냉각시키는 공정, (d) 상기 스트립을 적어도 95용적%의 수소를 함유하는 보호 분위기를 통과시키는 공정, (e) 상기 스트립을 알루미늄 코팅 금속의 용융조에 침지시켜 스트립상에 코팅층을 침착시키는 공정으로 구성되고, 상기 제1노 부분에서의 가열이 상기 제2노 부분에서의 추가 가열후의 상기스트립의 전체 열량의 80%미만을 제공하며, 상기 코팅층이 실질적으로 미코팅된 부분을 갖지 않고 상기 스트립에 단단히 부착되는 것을 특징으로 하는, 강 스트립을 알루미늄으로 연속 용융 코팅시키는 방법.
- (a) 철(III) 크롬 합금강 스트립을 직접 연소형 노의 제1부분에서 상기 스트립의 온도가 상기 스트립중의 크롬을 과도하게 산화시키기에는 불충분한 온도로 가열하는 공정, (b) 상기 스트립을 제2노 부분에서 약 830℃이상의 온도로 추가 가열함으로써 충분히 어닐링시키는 공정, (c) 상기 스트립을 적어도 약 95용적%이 수소를 함유하는 보호 분위기에서 알루미늄 코팅 금속의 융점 근처 또는 그보다 약간 더 높은 온도로 냉각시키는 공정, (d) 상기 스트립을 상기 코팅 금속의 용융조에 침지시켜 스트립상에 코팅층을 침착시키는 공정으로 구성되고, 상기 제1노 부분에서의 스트립온도는 스트립의 상기 충분한 어닐링에 필요한 전체 열량의80% 미만을 제공하는 온도이며, 상기 코팅층이 실질적으로 미코팅된 부분을 갖지 않고 상기세척된 스트립에 단단히 부착되는 것을 특징으로 하는, 강 스트립을 알루미늄으로 연속 용융 코팅시키는 방법.
- 제11항에 있어서, 상기 제2노 부분이 상기 분위기를 갖는 것을 특징으로 하는 방법.
- 제12항에 있어서, 상기 제1노 부분에서이 스트립 온도가 약 650℃미만인 것을 특징으로 하는 방법.
- 제13항에있어서, 상기 냉각된 스트립을 적어도 약 97용적%의 수소를 함유하는 상기 분위기에서 상기 용융조중에 침지시킬 때까지 유지시키는 것을 특징으로 하는 방법.
- 제14항에 있어서, 상기 분위기가 2000ppm 미만의 산소를 함유하고, 약 -18℃미만의 노점을 갖는 것을 특징으로 하는 방법.
- (a) 철(III) 크롬 합금강 스트립을 직접 연소형 노의 제1부분에서 스트림의 온도가 스트립 중의 크롬을 과도하게 산화시키기에는 불충분한 온도로 가열하는 공정, (b) 제2노 부분에서 스트립을 약 830℃이상의 온도로 추가 가열함으로써 스트립을 충분히 어닐링시키는 공정, (c) 스트립을 알루미늄 코팅 금속의 융점 근처 또는 그 보다 약간 더 높은 온도로 냉각시키는 공정,(d) 스트립을 적어도 95용적%의 수소를 함유하는 보호 분위기를 통과시키는 공정, (e) 스트립을 알루미늄 코팅 금속의 용융조에 침지시켜 스트립상에 코팅층을 침착시키는 공정으로 구성되며, 상기 코팅층이 실질적으로 미코팅된 부분을 갖지 않고 상기 스트립에 단단히 부착하는 것을 특징으로 하는, 강 스트립을 알루미늄으로 연속 용융 코팅시키는 방법.
- 제16항에 있어서,스트립을 상기 충분한 어닐링 및 냉각 공정 동안 상기 분위기하에 유지시키는 것을 특징으로하는 방법.
- 제17항에 있어서, 상기 분위기가 200ppm미만의 산소를 함유하고, 약 -18℃미만의 노점을 갖는 것을 특징으로 하는 방법.
- (a) 철(III) 크롬 합금강 스트립을 직접 연소형 노의 제1부분에서 약 650℃이하의온도로 가열하는 공정, (b) 상기 스트립을 적어도 약 95용적%의 수소를 함유하고, -18℃이하의 노점을 갖는 보호 분위기의 제2노 부분에서 적어도 약 830℃이상의 온도로 추가 가열하는 공정, (c) 상기 분위기 중의 스트립을 알루미늄 코팅 금속의 융점 근처 또는 그보다 약간 더 높은 온도로 냉각시키는 공정, (d) 상기 스트립을 상기 분위기를 갖는 밀폐된 선단을 거쳐 상기 코팅 금속의 용융조에 통과시킴으로써 스트립상에 코팅층을 침착시키는 공정으로 구성되고, 상기 선단중의 분위기는 적어도 약 97용적%의 수소를 함유하고, -29℃이하의 노점을 가지며,상기 코팅층이 실질적으로 미코팅된 부분을 갖지 않고 상기 스트립에 단단히 부착되는 것을 특징으로 하는, 강 스트립을 알루미늄으로 연속 용융 코팅시키는 방법.
- 제16항의 방법에 의해 제조된 디이프 드로우잉 가능한 (deep drawable) 알루미늄 코팅된 스트립.
- 제10항에 있어서, 적어도 10중량%의크롬을 함유학, 염에 대한 내식성이 크며, 내고온 산화성을 갖는 것을 특징으로 하는 스트립.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.