CN103771826B - 一种含有纳米凹凸棒土的日用陶瓷制品 - Google Patents

一种含有纳米凹凸棒土的日用陶瓷制品 Download PDF

Info

Publication number
CN103771826B
CN103771826B CN201410002620.9A CN201410002620A CN103771826B CN 103771826 B CN103771826 B CN 103771826B CN 201410002620 A CN201410002620 A CN 201410002620A CN 103771826 B CN103771826 B CN 103771826B
Authority
CN
China
Prior art keywords
parts
attapulgite
daily use
nano
auxiliary agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201410002620.9A
Other languages
English (en)
Other versions
CN103771826A (zh
Inventor
舒小山
章建武
宫平
汤兴友
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI HANSHAN PORCELAIN Co Ltd
Original Assignee
ANHUI HANSHAN PORCELAIN Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI HANSHAN PORCELAIN Co Ltd filed Critical ANHUI HANSHAN PORCELAIN Co Ltd
Priority to CN201410002620.9A priority Critical patent/CN103771826B/zh
Publication of CN103771826A publication Critical patent/CN103771826A/zh
Application granted granted Critical
Publication of CN103771826B publication Critical patent/CN103771826B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及日用陶瓷制品，具体涉及一种含有纳米凹凸棒土的日用陶瓷制品及其制作工艺，该陶瓷制品由以下重量份的原料制成：天然粘土50-55、高岭土熟料20-23、钾长石12-14、白云石5-6、铵明矾2-3、陶土40-45、二氧化锆1-2、纳米凹凸棒土10-15、纳米二氧化钛3-5、二硼化钽1-2、硼化钒1-2、助剂5-6；本发明利用纳米凹凸棒土、纳米二氧化钛等纳米原料的独特性能，降低了烧结温度，减少了生产能耗，再结合其它原料，最终制得的成品具有良好的白度和光泽度，釉面附着紧密，色泽均匀，无毒无害，抗冲击性能得到提高，美观耐用，应用范围广。

Description

一种含有纳米凹凸棒土的日用陶瓷制品
技术领域
本发明涉及日用陶瓷制品，具体涉及一种含有纳米凹凸棒土的日用陶瓷制品及其制作工艺。
背景技术
陶瓷在我国具有悠久的使用历史，如今已在全世界范围内广泛使用，日用陶瓷俨然已成为人们日常生活中不可或缺的一部分，形形色色的餐具、茶具、各类洁具等随处可见，这些陶瓷不仅美观大方、造型多样，同时还具有易清洗、耐温、耐磨耐腐蚀等优点，深受消费者的喜爱，然而陶瓷产品普遍存在性脆、不耐冲击、韧性差、釉色不均易脱落、生产能耗大等缺点，导致其在生产运输及应用过程中破损较严重，从而增加生产成本，因此迫切需要对其性能进行改进，推动日用陶瓷产业向低成本、绿色环保方向发展。
发明内容
本发明的目的在于，提供一种含有纳米凹凸棒土的日用陶瓷制品，以改善传统陶瓷制品的性能，降低生产能耗，为了实现上述目的，本发明采用的技术方案如下：
一种含有纳米凹凸棒土的日用陶瓷制品，其特征在于，本发明材料由以下重量份的原料制成：天然粘土50-55、高岭土熟料20-23、钾长石12-14、白云石5-6、铵明矾2-3、陶土40-45、二氧化锆1-2、纳米凹凸棒土10-15、纳米二氧化钛3-5、二硼化钽1-2、硼化钒1-2、助剂5-6。
所述的助剂由以下重量份的原料制成：棕刚玉粉2-3、三聚磷酸钠5-6、玉石粉4-5、硅烷偶联剂KH-550 1-2、碳化硅粉4-5、氢氧化铝8-10；其制备方法是将各物料混合，研磨分散均匀，即得。
所述的一种含有纳米凹凸棒土的日用陶瓷制品，其制作工艺包含以下步骤：
（1）先将钾长石、白云石粉碎，过100-200目筛；
（2）将除助剂外的其它剩余成分与步骤（1）得到的物料混合，加入球磨机中研磨，过400-600目筛；
（3）将助剂加入步骤（2）得到的物料中，搅拌均匀后，加水制成胚料，胚料经除铁、粗练、陈腐、精练处理后塑形得胚体；
（4）胚体经干燥、清洗、上釉后，在1300-1350℃温度下烧结12-15小时，即得成品。
本发明的优点在于：利用纳米凹凸棒土、纳米二氧化钛等纳米原料的独特性能，降低了原料研磨时间和胚体烧结温度，减少生产能耗，同时还提高了陶瓷制品白度和光泽度，在配合其它原料，使得本发明陶瓷制品兼具良好的硬度和柔韧性，更耐磨损、耐酸碱腐蚀，耐高温，吸水率低，釉面结合紧密，色泽均匀，这种陶瓷制品美观与实用兼具，适用范围广。
具体实施方式
实施例
本实施例陶瓷制品由以下重量份原料制成：天然粘土55、高岭土熟料22、钾长石14、白云石6、铵明矾3、陶土45、二氧化锆1、纳米凹凸棒土15、纳米二氧化钛4、二硼化钽2、硼化钒2、助剂6。
所述的助剂由以下重量份的原料制成：棕刚玉粉3、三聚磷酸钠5、玉石粉4、硅烷偶联剂KH-550 2、碳化硅粉4、氢氧化铝8；其制备方法是将各物料混合，研磨分散均匀，即得。
所述的一种含有纳米凹凸棒土的日用陶瓷制品，其制作工艺包含以下步骤：
（1）先将钾长石、白云石粉碎，过200目筛；
（2）将除助剂外的其它剩余成分与步骤（1）得到的物料混合，加入球磨机中研磨，过600目筛；
（3）将助剂加入步骤（2）得到的物料中，搅拌均匀后，加水制成胚料，胚料经除铁、粗练、陈腐、精练处理后塑形得胚体；
（4）胚体经干燥、清洗、上釉后，在1320℃温度下烧结14小时，即得成品。
本实施例制得的日用陶瓷制品的烧结温度较同类产品烧结温度降低近180-200℃，制品釉面色泽均匀，光亮致密无针孔，性能检测结果为：吸水率≤0.4%，光泽度≥87%，铅镉溶出量≤0.1mg/L，耐热性：200℃-20℃交换三次无裂纹出现，抗折强度达到113MPa，较普通陶瓷提高15-20%。

Claims (2)

1.一种含有纳米凹凸棒土的日用陶瓷制品，其特征在于，该陶瓷由以下重量份的原料制成：天然粘土50-55、高岭土熟料20-23、钾长石12-14、白云石5-6、铵明矾2-3、陶土40-45、二氧化锆1-2、纳米凹凸棒土10-15、纳米二氧化钛3-5、二硼化钽1-2、硼化钒1-2、助剂5-6；
所述的助剂由以下重量份的原料制成：棕刚玉粉2-3、三聚磷酸钠5-6、玉石粉4-5、硅烷偶联剂KH-550 1-2、碳化硅粉4-5、氢氧化铝8-10；其制备方法是将各物料混合，研磨分散均匀，即得。
2.如权利要求1所述的一种含有纳米凹凸棒土的日用陶瓷制品，其制作工艺包含以下步骤：
（1）先将钾长石、白云石粉碎，过100-200目筛；
（2）将除助剂外的其它剩余成分与步骤（1）得到的物料混合，加入球磨机中研磨，过400-600目筛；
（3）将助剂加入步骤（2）得到的物料中，搅拌均匀后，加水制成坯料，坯料经除铁、粗练、陈腐、精练处理后塑形得坯体；
（4）坯体经干燥、清洗、上釉后，在1300-1350℃温度下烧结12-15小时，即得成品。
CN201410002620.9A 2014-01-04 2014-01-04 一种含有纳米凹凸棒土的日用陶瓷制品 Expired - Fee Related CN103771826B (zh)