CN104844154A - 一种釉里红陶瓷 - Google Patents
一种釉里红陶瓷 Download PDFInfo
- Publication number
- CN104844154A CN104844154A CN201510284219.3A CN201510284219A CN104844154A CN 104844154 A CN104844154 A CN 104844154A CN 201510284219 A CN201510284219 A CN 201510284219A CN 104844154 A CN104844154 A CN 104844154A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- ceramic
- silicon nitride
- under
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种釉里红陶瓷，该陶瓷坯体组成为：废瓷，天然粘土，烧滑石，长石，氧化铝微粉，氮化硅，乌土，硅灰石；该釉里红陶瓷组成为：氧化亚铜，石英，石灰石，锂长石，钠硼解石，碳化硅，氮化硅，三氧化二铁，二氧化锡，硅酸锆，硼酸锌，蒙脱石，羟甲基纤维素钠，腐植酸钠，通过优化陶瓷坯体和釉料的组成，来提高陶瓷的呈色效果、硬度和稳定性等物化性能，产品档次完全符合工业和生活需求，起到废物利用的效果。
Description
技术领域
本发明属于陶瓷领域，特别涉及一种废瓷回收利用的釉里红陶瓷。
背景技术
陶瓷是我国一个古老而又传统行业。随着科技的发展，在日常生活中，釉里红陶瓷也随处可见。陶瓷是以粘土为主要原料以及各种天然矿物经过粉碎混炼、成型和煅烧制得的材料以及各种制品。人们把一种陶土制作成的在专门的窑炉中高温烧制的物品叫陶瓷，陶瓷是陶器和瓷器的总称。陶瓷的传统概念是指所有以粘土等无机非金属矿物为原料的人工工业产品。它包括由粘土或含有粘土的混合物经混炼，成形，煅烧而制成的各种制品。
不过随着人类对于釉里红陶瓷的色彩、环保以及健康性能的要求越来越高，传统的釉里红陶瓷已经不能满足人类的需求，同时，废瓷日益增多，利用率低，污染环境等一系列的负面影响日益突出，废瓷的回收利用对陶瓷工业的可持续发展具有重要意义。
发明内容
本发明的目的是针对上述问题，研制出一种综合考利废瓷制备釉里红陶瓷，通过优化陶瓷坯体和釉料的组成，来提高陶瓷的呈色效果、硬度和稳定性等物化性能，产品档次完全符合工业和生活需求，起到废物利用的效果。
一种釉里红陶瓷，该陶瓷坯体重量组成如下：
废瓷70-90份，天然粘土30-40份，烧滑石10-20份，钠长石10-20份，氧化铝微粉10-15份，氮化硅2-5份，乌土1-2份，硅灰石1-2份；
该釉里红陶瓷重量份数如下，
氧化亚铜30-50份，石英8-10份，石灰石6-10份，锂长石5-8份，钠硼解石3-5份，碳化硅1-3份，氮化硅1-3份，三氧化二铁1-2份，二氧化锡1-2份，硼酸锌1-2份，蒙脱石1-2份，硅酸锆1-2份，羟甲基纤维素钠1-2份，腐植酸钠1-2份。
作为优选，陶瓷坯体重量组成如下：废瓷80份，天然粘土40份，烧滑石15份，钠长石20份，氧化铝微粉15份，氮化硅3份，乌土1份，硅灰石1份。
该釉里红陶瓷重量份数如下，氧化亚铜40份，石英9份，石灰石6份，锂长石5份，钠硼解石5份，碳化硅3份，氮化硅3份，三氧化二铁2份，二氧化锡2份，硼酸锌1份，蒙脱石1份，硅酸锆1份，羟甲基纤维素钠1份，腐植酸钠1份。
该釉里红陶瓷由如下工艺流程制得：
配料-细磨-过筛-陈腐-练泥-成型-修坯-干燥-素烧-半成品打磨-装饰-施釉-烧成-打磨-釉烧-成品。
本发明的有益效果：
(1)整体而言，通过优化陶瓷坯体和釉料的组成，来提高陶瓷的呈色效果、硬度和稳定性等物化性能，产品档次完全符合工业和生活需求，起到废物利用的效果；按本发明所提供的配方材料制成的陶瓷，具有低摩擦、高耐磨的特性，断裂次品率大大降低，降低了生产成本。
(2)在坯体配料中，硅灰石与烧滑石在烧结过程中也会形成透辉石，有利于提高坯体的机械性能和强度，同时，由于坯体原料中含有硅灰石，会使得原料中含有一定量的氧化钙，有利于提高产品的抗龟裂性。而氧化铝微粉、氮化硅的加入，也将有利于调节坯体的烧成温度、缩短烧成周期，提高坯体的强度和硬度；具体针对于废瓷，由于天然粘土、乌土具有颗粒细、可塑性好、保水性好等特点，因此，可以减少废瓷给坯体带来的不利影响。
(4)在釉料配料中，虽然采用的原料为很普通的原料，但是通过合理的原料组成以及份量的调整，各原料之间也具有协同作用，如加入氧化铁和氧化锡，能够提高氧化亚铜的稳定性；而选择加入合适量的羟甲基纤维素钠和腐植酸钠，也能提高色料的着色力和颜色的均匀度，本申请所制备出来的陶瓷色调鲜艳、颜色饱满，富有光彩，且具有较好的稳定性。
同时，添加了硅酸锆的釉料，具有很强的遮盖能力，因此可以减弱废瓷所带来的瓷坯色度不佳的效果，继而提高外观性能，提高产品档次。
具体实施方式
下面结合具体的实施例，并参照数据进一步详细描述本发明。应理解，这些实施例只是为了举例说明本发明，而非以任何方式限制本发明的范围。
实施例1：
一种釉里红陶瓷，该陶瓷坯体重量组成如下：废瓷80份，天然粘土40份，烧滑石15份，钠长石20份，氧化铝微粉15份，氮化硅3份，乌土1份，硅灰石1份；该釉里红陶瓷重量份数如下，氧化亚铜40份，石英9份，石灰石6份，锂长石5份，钠硼解石5份，碳化硅3份，氮化硅3份，三氧化二铁2份，二氧化锡2份，硼酸锌1份，蒙脱石1份，硅酸锆1份，羟甲基纤维素钠1份，腐植酸钠1份。该釉里红陶瓷由如下工艺流程制得：配料-细磨-过筛-陈腐-练泥-成型-修坯-干燥-素烧-半成品打磨-装饰-施釉-烧成-打磨-釉烧-成品。
实施例2：
一种釉里红陶瓷，该陶瓷坯体重量组成如下：废瓷70份，天然粘土30份，烧滑石15份，钠长石20份，氧化铝微粉15份，氮化硅3份，乌土1份，硅灰石1份；该釉里红陶瓷重量份数如下，氧化亚铜40份，石英9份，石灰石6份，锂长石5份，钠硼解石5份，碳化硅3份，氮化硅3份，三氧化二铁2份，二氧化锡2份，硼酸锌1份，蒙脱石1份，硅酸锆1份，羟甲基纤维素钠1份，腐植酸钠1份。该釉里红陶瓷由如下工艺流程制得：配料-细磨-过筛-陈腐-练泥-成型-修坯-干燥-素烧-半成品打磨-装饰-施釉-烧成-打磨-釉烧-成品。
实施例3：
一种釉里红陶瓷，该陶瓷坯体重量组成如下：废瓷90份，天然粘土40份，烧滑石15份，钠长石20份，氧化铝微粉15份，氮化硅3份，乌土1份，硅灰石1份；该釉里红陶瓷重量份数如下，氧化亚铜40份，石英9份，石灰石6份，锂长石5份，钠硼解石5份，碳化硅3份，氮化硅3份，三氧化二铁2份，二氧化锡2份，硼酸锌1份，蒙脱石1份，硅酸锆1份，羟甲基纤维素钠1份，腐植酸钠1份。该釉里红陶瓷由如下工艺流程制得：配料-细磨-过筛-陈腐-练泥-成型-修坯-干燥-素烧-半成品打磨-装饰-施釉-烧成-打磨-釉烧-成品。
实施例4：
一种釉里红陶瓷，该陶瓷坯体重量组成如下：废瓷70份，天然粘土30份，烧滑石15份，钠长石20份，氧化铝微粉15份，氮化硅3份，乌土1份，硅灰石1份；该釉里红陶瓷重量份数如下，氧化亚铜30份，石英10份，石灰石6份，锂长石5份，钠硼解石5份，碳化硅3份，氮化硅3份，三氧化二铁2份，二氧化锡2份，硼酸锌1份，蒙脱石1份，硅酸锆2份，羟甲基纤维素钠1份，腐植酸钠1份。该釉里红陶瓷由如下工艺流程制得：配料-细磨-过筛-陈腐-练泥-成型-修坯-干燥-素烧-半成品打磨-装饰-施釉-烧成-打磨-釉烧-成品。
实施例5：
一种釉里红陶瓷，该陶瓷坯体重量组成如下：废瓷80份，天然粘土40份，烧滑石15份，钠长石20份，氧化铝微粉15份，氮化硅3份，乌土1份，硅灰石1份；该釉里红陶瓷重量份数如下，氧化亚铜50份，石英10份，石灰石6份，锂长石5份，钠硼解石5份，碳化硅3份，氮化硅3份，三氧化二铁2份，二氧化锡2份，硼酸锌1份，蒙脱石1份，硅酸锆2份，羟甲基纤维素钠1份，腐植酸钠1份。该釉里红陶瓷由如下工艺流程制得：配料-细磨-过筛-陈腐-练泥-成型-修坯-干燥-素烧-半成品打磨-装饰-施釉-烧成-打磨-釉烧-成品。
对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。
此外，应当理解，虽然本说明书按照实施方式加以描述，但并非每个实施方式仅包含一个独立的技术方案，说明书的这种叙述方式仅仅是为清楚起见，本领域技术人员应当将说明书作为一个整体，各实施例中的技术方案也可以经适当组合，形成本领域技术人员可以理解的其他实施方式。
Claims (3)
1.一种釉里红陶瓷，其特征在于：
该陶瓷坯体重量组成如下：
废瓷70-90份，天然粘土30-40份，烧滑石10-20份，钠长石10-20份，氧化铝微粉10-15份，氮化硅2-5份，乌土1-2份，硅灰石1-2份；
该陶瓷釉料重量份数如下，
氧化亚铜30-50份，石英8-10份，石灰石6-10份，锂长石5-8份，钠硼解石3-5份，碳化硅1-3份，氮化硅1-3份，三氧化二铁1-2份，二氧化锡1-2份，硼酸锌1-2份，蒙脱石1-2份，硅酸锆1-2份，羟甲基纤维素钠1-2份，腐植酸钠1-2份。
2.一种如权利要求1所述的釉里红陶瓷，其特征在于，该陶瓷坯体重量组成如下：废瓷80份，天然粘土40份，烧滑石15份，钠长石20份，氧化铝微粉15份，氮化硅3份，乌土1份，硅灰石1份。
3.一种如权利要求1或3所述的釉里红陶瓷，其特征在于，该陶瓷釉料重量份数如下，氧化亚铜40份，石英9份，石灰石6份，锂长石5份，钠硼解石5份，碳化硅3份，氮化硅3份，三氧化二铁2份，二氧化锡2份，硼酸锌1份，蒙脱石1份，硅酸锆1份，羟甲基纤维素钠1份，腐植酸钠1份。