CN103676440A - 一种单丝压纹投影布及其生产工艺 - Google Patents
一种单丝压纹投影布及其生产工艺 Download PDFInfo
- Publication number
- CN103676440A CN103676440A CN201310414820.0A CN201310414820A CN103676440A CN 103676440 A CN103676440 A CN 103676440A CN 201310414820 A CN201310414820 A CN 201310414820A CN 103676440 A CN103676440 A CN 103676440A
- Authority
- CN
- China
- Prior art keywords
- monofilament
- cloth
- pvc film
- projection cloth
- embossing projection
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种单丝压纹投影布,包括基布,所述基布上下表面均热贴合有PVC膜,基布为单丝网布。本发明选用2000D单丝做在保持其良好的遮光效果的同时又美观、耐用。选用超宽幅热贴贴合机生产,使产品的剥离强度大大增加,运用了压花辊进行压纹,使得产品具有更好的光学性能。选用2000D单丝网布做基材,当门幅达到5米时也不会出现卷边现象。在PVC膜的加工中,为了提高PVC膜的平整度,调整优化压延技术,采用了超宽幅4辊压延机生产PVC膜,使得产品的平整度有了更好的保障。
Description
技术领域
本发明涉及一种投影仪专用投影幕布及其生产工艺,特别涉及一种门幅为5米超宽投影布的生产工艺。
背景技术
网络信息时代使人们对于共享信息和集合信息的需要日益突出,这也导致了对超大屏幕显示的极大要求,多媒体教学、商务演示、现代化会议室建设、自动化监控、家庭娱乐等,使大屏幕投影显示系统成为信息传播的重要手段之一,据不完全统计,2013我国的投影设备市场容量将超过550万台,我国已成为仅次于美国的全球第二大投影消费市场。放眼世界,投影技术及设备的发展前景更是不可估量,这给投影布产业带来了前所未有的机遇和挑战。
随着大屏幕投影仪的快速升级,要求需要门幅超宽的投影幕布。传统的投影布通常采用200D*200D经编布作为基材的,当门幅达到3米以上时就会出现卷边等现象,严重影响了使用效果。另外传统的投影布通常冷贴技术进行贴合,生产出来的产品表面平整度和剥离强度都比较差。
发明内容
本发明所要解决的技术问题是:提供一种单丝压纹投影布及其生产工艺,本发明的投影布门幅宽、光学性能好、不卷边且平整度好。
为了解决上述技术问题,本发明采用以下技术方案:
一种单丝压纹投影布,包括基布,其特征在于:所述基布上下表面均热贴合有PVC膜,基布为单丝网布。
所述基布选用2000D涤纶单丝网布
所述PVC膜表面具有压花辊压出的花纹。
所述PVC膜为超宽幅4辊压延机生产。
所述投影布的门幅为5米。
一种单丝压纹投影布生产工艺,其特征在于包括以下步骤:
1)PVC膜压延工艺:采用超宽幅4辊压延机生产门幅为5000±20mm 的PVC膜,其中PVC树脂按以下重量份配制: PVC树脂粉90-100kg,增塑剂DOP 45-50kg,钡铬锌稳定剂4-5kg,环氧大豆油4-5kg,重质碳酸钙30-40kg,防寒剂DOA4-5kg, 钛白粉8-10kg,色料0.4-0.6kg;
2)PVC膜与基布贴合工艺:采用热贴机将PVC膜面膜、单丝网布、PVC膜底膜贴合,制成投影布;
3)表面压纹工艺:运用压花辊与橡胶辊对投影布表面进行压纹处理。
进一步包括以下步骤:将面膜、底膜充分加热或预热后,在贴合压花装置把面膜、网布、底膜三层同时贴合在一起,正面是一支压花钢辊,底面是橡胶,压花辊与橡胶辊内通入冷水,贴合时两支辊之间加压,把PVC膜和网布结合在一起;贴合压力为3-5Mpa,贴合温度160-180℃,贴合辊速度8-15m/min.
优选地,所述PVC树脂按以下重量份配制: PVC树脂粉100kg,增塑剂DOP50kg,钡铬锌稳定剂5kg,环氧大豆油 5kg,重质碳酸钙40kg,防寒剂DOA5kg,钛白粉10kg,色料0.5kg。
本发明与现有技术相比具有以下有益效果:本发明选用2000D单丝做在保持其良好的遮光效果的同时又美观、耐用。选用超宽幅热贴贴合机生产,使产品的剥离强度大大增加,运用了压花辊进行压纹,使得产品具有更好的光学性能。传统的投影布通常采用200D*200D经编布作为基材的,当门幅达到3米以上时就会出现卷边等现象,严重影响了使用效果,本发明选用2000D单丝网布做基材,当门幅达到5米时也不会出现卷边现象。5米单丝压纹投影布采用PVC树脂粉为主要原料,辅以增塑剂、稳定剂、大豆油、钛白粉、钙粉、防寒剂等添加剂制得PVC膜,将PVC膜与基布经加热贴合最终生产出产品。在PVC膜的加工中,为了提高PVC膜的平整度,调整优化压延技术,采用了超宽幅4辊压延机生产PVC膜,使的产品的平整度有了更好的保障。
附图说明
图1为本发明的剖面图。
具体实施方式
实施例一
参见图1,本投影布的门幅为5米,投影布包括基布1及PVC膜2,基布1上下表面选用了超宽幅热贴合机均热贴合有PVC膜2,即投影布由第一层PVC膜、第二层单丝网、第三层PVC膜,一共三层贴合而成,PVC膜2采用超宽幅4辊压延机生产,使的产品的平整度有了更好的保障。基布1选用2000D单丝网布,相对于普通网布,单丝网布有以下好处:1.网布不会移位。2.产品的平整度更好。3.产品的剥离强度更强4、当门幅达到5米时也不会出现卷边现象。
PVC膜2表面具有压花辊压出的花纹。使用压花辊生产出来的投影布光学性能更佳,投影时的成像画面更好。
本投影布的生产工艺如下:
PVC树脂配方:PVC树脂粉100kg,增塑剂DOP50kg,钡铬锌稳定剂5kg,环氧大豆油 5kg,重质碳酸钙40kg,防寒剂DOA5kg,钛白粉10kg,色料0.5kg,色料选用黑色料。
1)PVC膜压延工艺(采用超宽幅4辊压延机生产门幅为5000±20mm 的PVC膜):筛料→配料(按上述PVC树脂配方)→高速搅拌→行星挤出→精炼塑化→过滤→压延→冷却→裁边→卷取;
2)PVC膜与基布贴合工艺:采用热贴机将PVC膜(面膜)、单丝网布、PVC膜(底膜)贴合,制成投影布。具体包括:基布放卷→加热→压合→冷却→卷取;
3)、表面压纹工艺:运用压花辊与橡胶辊对投影布表面进行压纹处理。
将面膜、底膜充分加热或预热后,在贴合压花装置把面膜、网布、底膜三层同时贴合在一起,正面是一支压花钢辊,底面是橡胶,压花辊与橡胶辊内通入冷水,贴合时两支辊之间加压,把PVC膜和网布结合在一起;贴合压力为3-5Mpa,贴合温度160-180℃,贴合辊速度8-15m/min.
实施例二
生产主要原料:2000D涤纶单丝网布为基布。
PVC树脂配方:PVC树脂粉90kg,增塑剂DOP50kg,钡铬锌稳定剂4kg,环氧大豆油 5kg,重质碳酸钙40kg,防寒剂DOA4kg,钛白粉8kg,色料0.6kg。色料选用白色料。
其余工艺与实施例一相同。
实施例三
生产主要原料:2000D涤纶单丝网布为基布。
PVC树脂配方:PVC树脂粉100kg,增塑剂DOP45kg,钡铬锌稳定剂5kg,环氧大豆油 4kg,重质碳酸钙30kg,防寒剂DOA5kg,钛白粉10kg,色料0.4kg。色料选用白色料。
其余工艺与实施例一相同。
在热贴加工过程中,选择2000D单丝网布作为投影布的基材,相对于普通网布有以下好处:1.网布不会移位。2.产品的平整度更好。3.产品的剥离强度更强。
经以上工艺所生产的5米单丝压纹投影布,无论是产品的平整度,还是其单位面积质量、厚度、拉伸负荷、撕裂负荷、剥离负荷、光学性能等都达到了预期的效果。产品性能优越、质量可靠,深受客户好评。
各项技术指标均符合企业产品标准,具体参数如下所示:
项目 | 要求 |
门幅(mm) | 5000±20 |
单位面积质量(g/m2) | 840±25 |
亮度系数 | β≥0.8 |
幕面解像力(线/对) | ≥80 |
表面光泽度(60°角) | ≤6 |
有效散射角 | 2α>150° |
阻燃性能 | ≥B2 |
Claims (9)
1.一种单丝压纹投影布,包括基布(1),其特征在于:所述基布(1)上下表面均热贴合有PVC膜(2),基布为单丝网布。
2.如权利要求1所述的一种单丝压纹投影布,其特征在于:所述基布选用2000D涤纶单丝网布。
3.如权利要求1所述的一种单丝压纹投影布,其特征在于:所述PVC膜表面具有压花辊压出的花纹。
4.如权利要求1所述的一种单丝压纹投影布,其特征在于:所述PVC膜为超宽幅4辊压延机生产。
5.如权利要求1所述的一种单丝压纹投影布,其特征在于:所述投影布的门幅为5米。
6.一种单丝压纹投影布生产工艺,其特征在于包括以下步骤:
1)PVC膜压延工艺:采用超宽幅4辊压延机生产门幅为5000±20mm 的PVC膜,其中PVC树脂按以下重量份配制: PVC树脂粉90-100kg,增塑剂DOP 45-50kg,钡铬锌稳定剂4-5kg,环氧大豆油4-5kg,重质碳酸钙30-40kg,防寒剂DOA4-5kg, 钛白粉8-10kg,色料0.4-0.6kg;
2)PVC膜与基布贴合工艺:采用热贴机将PVC膜面膜、单丝网布、PVC膜底膜贴合,制成投影布;
3)表面压纹工艺:运用压花辊与橡胶辊对投影布表面进行压纹处理。
7.如权利要求6所述的一种单丝压纹投影布生产工艺,其特征在于:进一步包括以下步骤:将面膜、底膜充分加热或预热后,在贴合压花装置把面膜、网布、底膜三层同时贴合在一起,正面是一支压花钢辊,底面是橡胶,压花辊与橡胶辊内通入冷水,贴合时两支辊之间加压,把PVC膜和网布结合在一起;贴合压力为3-5Mpa,贴合温度160-180℃,贴合辊速度8-15m/min。
8.如权利要求6所述的一种单丝压纹投影布生产工艺,其特征在于所述PVC树脂按以下重量份配制: PVC树脂粉100kg,增塑剂DOP50kg,钡铬锌稳定剂5kg,环氧大豆油 5kg,重质碳酸钙40kg,防寒剂DOA5kg,钛白粉10kg,色料0.5kg。
9. 如权利要求6所述的一种单丝压纹投影布生产工艺,其特征在于:所述基布选用2000D涤纶单丝网布。