CN103666015A - Light-curable printing ink taking LED as light source and preparation method of light-curable printing ink - Google Patents
Light-curable printing ink taking LED as light source and preparation method of light-curable printing ink Download PDFInfo
- Publication number
- CN103666015A CN103666015A CN201310601903.0A CN201310601903A CN103666015A CN 103666015 A CN103666015 A CN 103666015A CN 201310601903 A CN201310601903 A CN 201310601903A CN 103666015 A CN103666015 A CN 103666015A
- Authority
- CN
- China
- Prior art keywords
- parts
- printing ink
- light
- hydroxyl
- light source
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a light-curable printing ink taking LED as a light source. The light-curable printing ink is characterized by be prepared from the following raw materials in parts by weight: 1-2 parts of a pigment, 20-24 parts of UV ultraviolet-curing acrylic resin, 1-2 parts of egg shell powder, 1-2 parts of sodium silicate, 3-4 parts of HAPK, 1-2 parts of carboxymethyl cellulose, 5-8 parts of methyl methacrylate, 2-6 parts of hexabromocyclododecane, 3-4 parts of diethylene glycol monobutyl ether, 6-9 parts of ethyl acrylate, 8-10 parts of propenoic acid-4-hydroxybutyl ester, 6-9 parts of 1-hydroxy-benzoylcyclohexane, 3-4 parts of methyl triethoxysilane, 1-2 parts of nano silicon carbide, 2-3 parts of anti-oxidant DLTP, and 4-5 parts of an additive. The additive improves the tenacity of the printing ink, enables the printing ink to disperse uniformly and maintains the stability of the printing ink. Moreover, during use, the printing ink generates less pollution, is high in curing rate, generates less heat, and has low probability of causing deformation or damage to processed materials. Therefore, the printing ink has a wide application prospect.
Description
Technical field
The present invention relates to a kind of ink and preparation method thereof, particularly a kind ofly take light-curable ink that LED is light source and preparation method thereof.
Background technology
Ultraviolet light polymerization (UV) ink refers under uviolizing, utilizes the UV-light of different wave length and energy to make ink film forming and dry ink.Utilize different UV spectrum, can produce different-energy, the monomer polymerization in different ink vehicles is become to polymkeric substance, so the look film of UV ink has good machinery and chemical property.The major advantage of UV ink has: (1) is without solvent; (2) rate of drying is fast, and power consumption is few; (3) good luster, bright in luster; (4) water-fast, resistance to solvent, wear resisting property is good.In UV ink, light trigger is a kind of light activated compound that is subject to, and after absorb light is shone, is excited into free radical, and energy is transferred to photosensitivity molecule or photocrosslinking agent, makes UV China ink that photocuring reaction occur.UV China ink has become a kind of more ripe ink technology at present, and its pollutant emission is almost nil.Except not containing solvent, UV China ink is also just like being difficult for scumming, and site is clear, the bright-coloured light of mass colour, the advantage such as chemical resistance is excellent, low-consuming.But, also there is apparent shortcoming in UV photocuring technology, as, UV luminous energy is high, and in use heat release seriously, easily causes the distortion of handled material, even damage etc.In addition, UV trimmed book body is also a kind of environomental pollution source.
Summary of the invention
Light-curable ink that to the object of this invention is to provide a kind of LED of take be light source and preparation method thereof.
In order to realize object of the present invention, the present invention passes through following scheme implementation:
The light-curable ink that the LED of take is light source, is made by the raw material of following weight part: pigment 1-2, UV ultraviolet curing acrylic resin 20-24, egg-shell meal 1-2, water glass 1-2, alpha-hydroxyalkyl benzophenone 3-4, carboxymethyl cellulose 1-2, methyl methacrylate 5-8, hexabromocyclododecane 2-6, Diethylene Glycol butyl ether 3-4, ethyl propenoate 6-9, vinylformic acid-4-hydroxyl butyl ester 8-10,1-hydroxyl-ring base in the sixth of the twelve Earthly Branches phenyl ketone 6-9, Union carbide A-162 3-4, nanometer silicon carbide 1-2, anti-oxidant DLTP 2-3, auxiliary agent 4-5;
Described auxiliary agent is prepared from by the raw material of following weight part: nano diatomite powder 0.2-0.3, nano mica powder 0.2-0.3, silane resin acceptor kh-550 2-3, methacrylic acid-2-hydroxy methacrylate 2-3, neopentyl glycol 5-8, vinyl acetate 12-15, linking agent TAC2-3, oxidation inhibitor 1035 2-3, N hydroxymethyl acrylamide 1-2, Tenox PG 2-3, coix seed oil 1-2; Its preparation method is by each mixing of materials, is heated to 60-70 ℃, and stirring reaction 30-40 minute, obtains.
Of the present inventionly take the light-curable ink that LED is light source, by following concrete steps, made: first add pigment, UV ultraviolet curing acrylic resin, egg-shell meal, water glass, alpha-hydroxyalkyl benzophenone, carboxymethyl cellulose, methyl methacrylate, hexabromocyclododecane, Diethylene Glycol butyl ether stirring and evenly mixing, be heated to 80-90 ℃, stir 25-35 minute; Then add all the other remaining components except 1-hydroxyl-ring base in the sixth of the twelve Earthly Branches phenyl ketone, stirring reaction 3-5 hour; Finally be cooled to 60-70 ℃, add 1-hydroxyl-ring base in the sixth of the twelve Earthly Branches phenyl ketone, stirring reaction 40-50 minute, cooling after, grind and to obtain 20-40 μ m slurry, obtain.
The invention has the beneficial effects as follows: auxiliary agent of the present invention has improved the toughness of ink, make distributes ink even, and maintained the stability of ink; That the prepared LED light-curable ink of the inventive method in use pollutes is little, quick solidifying, heat release are few, be difficult for causing handled material distortion or damage, has broad application prospects.
Specific embodiments
Below by specific examples, the present invention is described in detail.
The light-curable ink that the LED of take is light source, by following weight part (kilogram) raw material make: pigment 1, UV ultraviolet curing acrylic resin 20, egg-shell meal 1, water glass 1, alpha-hydroxyalkyl benzophenone 3, carboxymethyl cellulose 1, methyl methacrylate 5, hexabromocyclododecane 2, Diethylene Glycol butyl ether 3, ethyl propenoate 6, vinylformic acid-4-hydroxyl butyl ester 8,1-hydroxyl-ring base in the sixth of the twelve Earthly Branches phenyl ketone 6, Union carbide A-162 3, nanometer silicon carbide 1, anti-oxidant DLTP 2, auxiliary agent 4;
Described auxiliary agent by following weight part (kilogram) raw material be prepared from: nano diatomite powder 0.2, nano mica powder 0.2, silane resin acceptor kh-550 2, methacrylic acid-2-hydroxy methacrylate 2, neopentyl glycol 5, vinyl acetate 12, linking agent TAC2, oxidation inhibitor 1,035 2, N hydroxymethyl acrylamide 1, Tenox PG 2, coix seed oil 1; Its preparation method is by each mixing of materials, is heated to 60-70 ℃, and stirring reaction 30-40 minute, obtains.
Of the present inventionly take the light-curable ink that LED is light source, by following concrete steps, made: first add pigment, UV ultraviolet curing acrylic resin, egg-shell meal, water glass, alpha-hydroxyalkyl benzophenone, carboxymethyl cellulose, methyl methacrylate, hexabromocyclododecane, Diethylene Glycol butyl ether stirring and evenly mixing, be heated to 80-90 ℃, stir 25-35 minute; Then add all the other remaining components except 1-hydroxyl-ring base in the sixth of the twelve Earthly Branches phenyl ketone, stirring reaction 3-5 hour; Finally be cooled to 60-70 ℃, add 1-hydroxyl-ring base in the sixth of the twelve Earthly Branches phenyl ketone, stirring reaction 40-50 minute, cooling after, grind and to obtain 20-40 μ m slurry, obtain.
The ink of gained, is used cross-hatching ox-hide tape stripping, draws compartment apart from 1mm, and 100% adheres to; Spirituous cotton balls is soaked in use, and 300 grams of pressure wipings 50 times, are as good as shape; Be soaked in salad oil (normal temperature) 8 hours, be as good as shape; Use is soaked with the cotton balls of salt solution, and 300 grams of pressure wipings 50 times, are as good as shape.
Claims (2)
1. take the light-curable ink that LED is light source for one kind, it is characterized in that, by the raw material of following weight part, made: pigment 1-2, UV ultraviolet curing acrylic resin 20-24, egg-shell meal 1-2, water glass 1-2, alpha-hydroxyalkyl benzophenone 3-4, carboxymethyl cellulose 1-2, methyl methacrylate 5-8, hexabromocyclododecane 2-6, Diethylene Glycol butyl ether 3-4, ethyl propenoate 6-9, vinylformic acid-4-hydroxyl butyl ester 8-10,1-hydroxyl-ring base in the sixth of the twelve Earthly Branches phenyl ketone 6-9, Union carbide A-162 3-4, nanometer silicon carbide 1-2, anti-oxidant DLTP 2-3, auxiliary agent 4-5;
Described auxiliary agent is prepared from by the raw material of following weight part: nano diatomite powder 0.2-0.3, nano mica powder 0.2-0.3, silane resin acceptor kh-550 2-3, methacrylic acid-2-hydroxy methacrylate 2-3, neopentyl glycol 5-8, vinyl acetate 12-15, linking agent TAC2-3, oxidation inhibitor 1035 2-3, N hydroxymethyl acrylamide 1-2, Tenox PG 2-3, coix seed oil 1-2; Its preparation method is by each mixing of materials, is heated to 60-70 ℃, and stirring reaction 30-40 minute, obtains.
2. the light-curable ink that the LED of take is according to claim 1 light source, it is characterized in that, by following concrete steps, made: first add pigment, UV ultraviolet curing acrylic resin, egg-shell meal, water glass, alpha-hydroxyalkyl benzophenone, carboxymethyl cellulose, methyl methacrylate, hexabromocyclododecane, Diethylene Glycol butyl ether stirring and evenly mixing, be heated to 80-90 ℃, stir 25-35 minute; Then add all the other remaining components except 1-hydroxyl-ring base in the sixth of the twelve Earthly Branches phenyl ketone, stirring reaction 3-5 hour; Finally be cooled to 60-70 ℃, add 1-hydroxyl-ring base in the sixth of the twelve Earthly Branches phenyl ketone, stirring reaction 40-50 minute, cooling after, grind and to obtain 20-40 μ m slurry, obtain.