CN103484612B - 钢的淬火方法 - Google Patents

钢的淬火方法 Download PDF

Info

Publication number
CN103484612B
CN103484612B CN201310434567.5A CN201310434567A CN103484612B CN 103484612 B CN103484612 B CN 103484612B CN 201310434567 A CN201310434567 A CN 201310434567A CN 103484612 B CN103484612 B CN 103484612B
Authority
CN
China
Prior art keywords
steel
cooled
quenching method
heated
quenching
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201310434567.5A
Other languages
English (en)
Other versions
CN103484612A (zh
Inventor
杨龙兴
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Fawkes Machinery Group Co ltd
Original Assignee
Wuxi Yanggong Machinery Manufacturing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuxi Yanggong Machinery Manufacturing Co Ltd filed Critical Wuxi Yanggong Machinery Manufacturing Co Ltd
Priority to CN201310434567.5A priority Critical patent/CN103484612B/zh
Publication of CN103484612A publication Critical patent/CN103484612A/zh
Application granted granted Critical
Publication of CN103484612B publication Critical patent/CN103484612B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供了一种能很好的对H13类钢进行淬火冷却的钢的淬火冷却方法。包括以下步骤：将待处理的H13类钢进行加热，加热到奥氏体化温度区间，保温1-2小时；在冷却时先用风冷将工件冷却至760-780℃；再采用大水量的连续水流使工件急速冷却至200-220℃，最后空冷。应用本发明的淬火方法制备的H13类钢具备良好的马氏体组织，工件不开裂。

Description

钢的淬火方法
技术领域
本发明属于热处理技术领域，具体涉及一种钢的淬火方法。
背景技术
压铸模普遍使用淬透性较好的H13 类钢。较为常用的淬火方式有水淬和油淬，但是对于淬透性较好的H13 类钢来说不宜全程采取水淬，因为水有较强烈的冷却能力，直接淬火，在马氏体转变温度区的冷速太大，在组织应力和热应力的双重作用，内应力急剧增大，使零件发生严重变形甚至开裂；也不宜采用油淬，因为油淬冷却速度小，淬透直径小，大型工件不易淬透。
目前，尚未有一种简单方便的淬火冷却工艺能使H13 类钢获得良好的马氏体组织。
发明内容
本发明提供了一种能很好的对H13类钢进行淬火冷却的钢的淬火冷却方法。
    本发明提供一种钢的淬火方法，所述钢为H13类钢，包括以下步骤：将待处理的H13类钢进行加热，加热到奥氏体化温度区间，保温1-2小时；在冷却时先用风冷将工件冷却至760-780℃；再采用大水量的连续水流使工件急速冷却至200-220℃，最后空冷。
作为优选，在冷却时先用风冷将工件在100min-120min内冷却至760-780℃。
作为优选，根据权利要求1所述的钢的淬火方法，其特征在于：所述大水量的连续水流的流速为30-40L/min。
作为优选，所述大水量的连续水流的流速为40L/min。
本发明的第二个目的是提供应用上述的淬火方法得到的钢。
应用本发明的淬火方法制备的H13类钢具备良好的马氏体组织，工件不开裂。
具体实施方式
实施例1
本发明提供的钢的淬火方法包括以下步骤：     将待处理的H13类钢进行加热，加热到奥氏体化温度区间，保温1小时；在冷却时先用风冷将工件在100分钟冷却至760℃；再采用流速为40L/min的大水量的连续水流使工件急速冷却至200℃，最后空冷，得到淬火后的H13类钢。
实施例2
本发明提供的钢的淬火方法包括以下步骤：     将待处理的H13类钢进行加热，加热到奥氏体化温度区间，保温2小时；在冷却时先用风冷将工件在110分钟冷却至780℃；再采用流速为30L/min的大水量的连续水流使工件急速冷却至220℃，最后空冷，得到淬火后的H13类钢。
实施例3
本发明提供的钢的淬火方法包括以下步骤：     将待处理的H13类钢进行加热，加热到奥氏体化温度区间，保温1.5小时；在冷却时先用风冷将工件在120分钟冷却至770℃；再采用流速为35L/min的大水量的连续水流使工件急速冷却至210℃，最后空冷，得到淬火后的H13类钢。
实施例4
本发明提供的钢的淬火方法包括以下步骤：     将待处理的H13类钢进行加热，加热到奥氏体化温度区间，保温1小时；在冷却时先用风冷将工件在115分钟冷却至760℃；再采用流速为40L/min的大水量的连续水流使工件急速冷却至220℃，最后空冷，得到淬火后的H13类钢。
应用本发明的钢的淬火方法能很好的对H13 类钢进行淬火冷却。
最后应说明的是：以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (4)

1.一种钢的淬火方法，所述钢为H13类钢，其特征在于：包括以下步骤：将待处理的H13类钢进行加热，加热到奥氏体化温度区间，保温1-2小时；在冷却时先用风冷将工件在100min-120min内冷却至760-780℃；再采用大水量的连续水流使工件急速冷却至200-220℃，最后空冷。
2.根据权利要求1所述的钢的淬火方法，其特征在于：所述大水量的连续水流的流速为30-40L/min。
3.根据权利要求1所述的钢的淬火方法，其特征在于：所述大水量的连续水流的流速为40L/min。
4.应用权利要求1-3任一所述的钢的淬火方法得到的钢。
CN201310434567.5A 2013-09-23 2013-09-23 钢的淬火方法 Expired - Fee Related CN103484612B (zh)