CN103484610B - 一种h13类钢的淬火方法 - Google Patents

一种h13类钢的淬火方法 Download PDF

Info

Publication number
CN103484610B
CN103484610B CN201310434475.7A CN201310434475A CN103484610B CN 103484610 B CN103484610 B CN 103484610B CN 201310434475 A CN201310434475 A CN 201310434475A CN 103484610 B CN103484610 B CN 103484610B
Authority
CN
China
Prior art keywords
cooling
quenching method
workpiece
water vapour
class steel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310434475.7A
Other languages
English (en)
Other versions
CN103484610A (zh
Inventor
杨龙兴
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nantong Juxing casting and Forging Co. Ltd.
Original Assignee
Wuxi Yanggong Machinery Manufacturing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuxi Yanggong Machinery Manufacturing Co Ltd filed Critical Wuxi Yanggong Machinery Manufacturing Co Ltd
Priority to CN201310434475.7A priority Critical patent/CN103484610B/zh
Publication of CN103484610A publication Critical patent/CN103484610A/zh
Application granted granted Critical
Publication of CN103484610B publication Critical patent/CN103484610B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供一种H13类钢的淬火方法，步骤如下：（1）、将工件先加热至600-700℃，保温1-2小时；（2）、再将工件加热到奥氏体温度，保温2-3小时；（3）、在冷却时先用水蒸气冷却，冷却至500-650℃，然后空冷。应用本发明的淬火方法制备的H13类钢具备良好的马氏体组织，工件不开裂。

Description

一种H13类钢的淬火方法
技术领域
本发明属于热处理技术领域，具体涉及一种H13类钢的淬火方法。
背景技术
压铸模普遍使用淬透性较好的H13 类钢。较为常用的淬火方式有水淬和油淬，但是对于淬透性较好的H13 类钢来说不宜全程采取水淬，因为水有较强烈的冷却能力，直接淬火，在马氏体转变温度区的冷速太大，在组织应力和热应力的双重作用，内应力急剧增大，使零件发生严重变形甚至开裂；也不宜采用油淬，因为油淬冷却速度小，淬透直径小，大型工件不易淬透。
目前，尚未有一种简单方便的淬火冷却工艺能使H13 类钢获得良好的马氏体组织。
发明内容
本发明提供了一种能很好的对H13类钢进行淬火冷却的钢的淬火冷却方法。
    本发明提供了一种H13类钢的淬火方法，步骤如下：
（1）、将工件先加热至600-700℃，保温1-2小时；
（2）、再将工件加热到奥氏体温度，保温2-3小时；
（3）、在冷却时先用水蒸气冷却，冷却至500-650℃，然后空冷。
    优选地，步骤（1）中，将工件先加热至650℃，保温1.5小时。
    优选地，步骤（2）中，保温时间为2小时。
    优选地，步骤（3）中，所述水蒸气的流速为1.0-2.5m3/s。
    优选地，所述水蒸气的流速为1.8m3/s。
    优选地，在冷却时先用水蒸气冷却，冷却至570℃，然后空冷。
应用本发明的淬火方法制备的H13类钢具备良好的马氏体组织，工件不开裂。
具体实施方式
实施例1
本发明的H13类钢的淬火方法步骤如下：
（1）、将工件先加热至650℃，保温1.5小时；
（2）、再将工件加热到奥氏体温度，保温2小时；
（3）、在冷却时先用水蒸气冷却，水蒸气的流速为1.8m3/s，冷却至570℃，然后空冷。
实施例2
本发明的H13类钢的淬火方法步骤如下：
（1）、将工件先加热至680℃，保温1小时；
（2）、再将工件加热到奥氏体温度，保温2小时；
（3）、在冷却时先用水蒸气冷却，水蒸气的流速为2.0m3/s，冷却至570℃，然后空冷。
实施例3
本发明的H13类钢的淬火方法步骤如下：
（1）、将工件先加热至680℃，保温1.5小时；
（2）、再将工件加热到奥氏体温度，保温2小时；
（3）、在冷却时先用水蒸气冷却，水蒸气的流速为2.0m3/s，冷却至600℃，然后空冷。
实施例4
本发明的H13类钢的淬火方法步骤如下：
（1）、将工件先加热至700℃，保温2小时；
（2）、再将工件加热到奥氏体温度，保温3小时；
（3）、在冷却时先用水蒸气冷却，水蒸气的流速为2.5m3/s，冷却至600℃，然后空冷。
实施例5
本发明的H13类钢的淬火方法步骤如下：
（1）、将工件先加热至600℃，保温2小时；
（2）、再将工件加热到奥氏体温度，保温2小时；
（3）、在冷却时先用水蒸气冷却，水蒸气的流速为1.0m3/s，冷却至600℃，然后空冷。
实施例6
本发明的H13类钢的淬火方法步骤如下：
（1）、将工件先加热至680℃，保温2小时；
（2）、再将工件加热到奥氏体温度，保温2小时；
（3）、在冷却时先用水蒸气冷却，水蒸气的流速为1.5m3/s，冷却至500℃，然后空冷。
实施例7
本发明的H13类钢的淬火方法步骤如下：
（1）、将工件先加热至630℃，保温2小时；
（2）、再将工件加热到奥氏体温度，保温2.5小时；
（3）、在冷却时先用水蒸气冷却，水蒸气的流速为1.9m3/s，冷却至620℃，然后空冷。
最后应说明的是：以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (6)

1.一种H13类钢的淬火方法，步骤如下：
（1）、将工件先加热至600-700℃，保温1-2小时；
（2）、再将工件加热到奥氏体温度，保温2-3小时；
（3）、在冷却时先用水蒸气冷却，冷却至500-650℃，然后空冷。
2.根据权利要求1所述的淬火方法，其特征在于：步骤（1）中，将工件先加热至650℃，保温1.5小时。
3.根据权利要求1所述的淬火方法，其特征在于：步骤（2）中，保温时间为2小时。
4.根据权利要求1所述的淬火方法，其特征在于：步骤（3）中，所述水蒸气的流速为1.0-2.5m3/s。
5.根据权利要求4所述的淬火方法，其特征在于：所述水蒸气的流速为1.8m3/s。
6.根据权利要求4或5所述的淬火方法，其特征在于：在冷却时先用水蒸气冷却，冷却至570℃，然后空冷。
CN201310434475.7A 2013-09-23 2013-09-23 一种h13类钢的淬火方法 Active CN103484610B (zh)