CN103740900A - 无缝钢管的热处理工艺 - Google Patents

无缝钢管的热处理工艺 Download PDF

Info

Publication number
CN103740900A
CN103740900A CN201310621648.6A CN201310621648A CN103740900A CN 103740900 A CN103740900 A CN 103740900A CN 201310621648 A CN201310621648 A CN 201310621648A CN 103740900 A CN103740900 A CN 103740900A
Authority
CN
China
Prior art keywords
temperature
heating
heat treatment
cooling
speed
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310621648.6A
Other languages
English (en)
Inventor
须晓东
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGSHU DONGXIN STEEL PIPE Co Ltd
Original Assignee
CHANGSHU DONGXIN STEEL PIPE Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHU DONGXIN STEEL PIPE Co Ltd filed Critical CHANGSHU DONGXIN STEEL PIPE Co Ltd
Priority to CN201310621648.6A priority Critical patent/CN103740900A/zh
Publication of CN103740900A publication Critical patent/CN103740900A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种无缝钢管的热处理工艺,包括如下步骤:1)分级加热淬火热处理:先以40-50℃/s的加热速度升温至600-610℃,保温1-2小时,再以45-55℃/s的加热速度升温至950-960℃,保温2-3小时,再以250-260℃/s的冷却速度急速冷却至400℃,再自然冷却;2)回火热处理:先以30-35℃/s的加热速度升温至500-510℃,保温3-4小时,再以45-50℃/s的加热速度升温至800-810℃,保温2-3小时,再以100-150℃/s的冷却速度冷却至250℃,再自然冷却。本发明处理的无缝钢管硬度高、热膨胀系数低、抗拉强度和屈服强度强、耐蚀抗氧化性和焊接性好。

Description

无缝钢管的热处理工艺技术领域
[0001 ] 本发明涉及无缝钢管的热处理工艺。
背景技术
[0002] 无缝钢管的热处理过程中,通常采用了正火热处理工艺,该工艺能使证材料具有一定的抗拉强度、屈服强度,但材料的韧性不足、抗弯曲和扭曲性能力低下。
发明内容
[0003] 本发明的目的在于提供一种无缝钢管的热处理工艺,其处理的无缝钢管硬度高、热膨胀系数低、抗拉强度和屈服强度强、耐蚀抗氧化性和焊接性好。
[0004] 为实现上述目的,本发明的技术方案是设计一种无缝钢管的热处理工艺,包括如下步骤:
1)分级加热淬火热处理:
先以40-50°C /s的加热速度升温至600-610°C,保温1_2小时,
再以45-55°C /s的加热速度升温至950-960°C,保温2_3小时,
再以250-260°C /s的冷却速度急速冷却至400°C,
再自然冷却;
2)回火热处理:
先以30-35°C /s的加热速度升温至500-510°C,保温3_4小时,
再以45-50°C /s的加热速度升温至800-810°C,保温2_3小时,
再以100-150°C /s的冷却速度冷却至250°C,
再自然冷却。
[0005] 本发明的优点和有益效果在于:提供一种无缝钢管的热处理工艺,其处理的无缝钢管硬度高、热膨胀系数低、抗拉强度和屈服强度强、耐蚀抗氧化性和焊接性好。
具体实施方式
[0006] 下面结合实施例,对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案,而不能以此来限制本发明的保护范围。
[0007] 本发明具体实施的技术方案是:
实施例1
一种无缝钢管的热处理工艺,包括如下步骤:
O分级加热淬火热处理:
先以40°C /s的加热速度升温至600°C,保温I小时,
再以45°C /s的加热速度升温至950°C,保温2小时,
再以250°C /s的冷却速度急速冷却至400°C,
再自然冷却;2)回火热处理:
先以35°C /s的加热速度升温至510°C,保温4小时,
再以50°C /s的加热速度升温至810°C,保温3小时,
再以150°C /s的冷却速度冷却至250°C,
再自然冷却。
[0008] 实施例2
一种无缝钢管的热处理工艺,包括如下步骤:
O分级加热淬火热处理:
先以45°C /s的加热速度升温至607°C,保温1.5小时,
再以50°C /s的加热速度升温至955°C,保温2.5小时, 再以254°C /s的冷却速度急速冷却至400°C,
再自然冷却;
2)回火热处理:
先以32°C /s的加热速度升温至504°C,保温3.5小时,
再以47°C /s的加热速度升温至806°C,保温2.5小时,
再以120°C /s的冷却速度冷却至250°C,
再自然冷却。
[0009] 实施例3
一种无缝钢管的热处理工艺,包括如下步骤:
O分级加热淬火热处理:
先以50°C /s的加热速度升温至610°C,保温2小时,
再以55°C /s的加热速度升温至960°C,保温3小时,
再以260°C /s的冷却速度急速冷却至400°C,
再自然冷却;
2)回火热处理:
先以35°C /s的加热速度升温至510°C,保温4小时,
再以50°C /s的加热速度升温至810°C,保温3小时,
再以150°C /s的冷却速度冷却至250°C,
再自然冷却。
[0010] 以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明技术原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。

Claims (1)

1.无缝钢管的热处理工艺,其特征在于,包括如下步骤:O分级加热淬火热处理:先以40-50°C /s的加热速度升温至600-610°C,保温1_2小时,再以45-55°C /s的加热速度升温至950-960°C,保温2_3小时,再以250-260°C /s的冷却速度急速冷却至400°C,再自然冷却;2)回火热处理: 先以30-35°C /s的加热速度升温至500-510°C,保温3_4小时,再以45-50°C /s的加热速度升温至800-810°C,保温2_3小时,再以100-150°C /s的冷却速度冷却至250°C,再自然冷却。
CN201310621648.6A 2013-11-30 2013-11-30 无缝钢管的热处理工艺 Pending CN103740900A (zh)