CN103396517A - 一种耐高温型乙烯基酯树脂 - Google Patents
一种耐高温型乙烯基酯树脂 Download PDFInfo
- Publication number
- CN103396517A CN103396517A CN2013103082329A CN201310308232A CN103396517A CN 103396517 A CN103396517 A CN 103396517A CN 2013103082329 A CN2013103082329 A CN 2013103082329A CN 201310308232 A CN201310308232 A CN 201310308232A CN 103396517 A CN103396517 A CN 103396517A
- Authority
- CN
- China
- Prior art keywords
- vinyl ester
- ester resin
- high temperature
- minutes
- temperature resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种耐高温型乙烯基酯树脂，首先按所述投料比例，将邻甲酚型酚醛型环氧树脂投入四口烧瓶中，搅拌升温至100℃，加入三分之一的一元酸，搅拌均匀后，再将混有三苯基膦和对苯二酚的剩余一元酸慢慢滴入反应瓶中。90分钟滴完，升温至115℃，反应45分钟后，每隔10分钟测一次酸值，待酸值达到10±2时，反应结束，降温至60℃，加苯乙烯，搅拌60分钟，即得产品。该乙烯基酯树脂有更耐高温，较之于现有产品有极大的优势。
Description
技术领域
本发明属于乙烯基酯树脂技术领域，具体涉及到一种耐高温型乙烯基酯树脂。
背景摘要
酚醛型环氧乙烯基酯树脂是一种酚醛型环氧树脂和一种含烯键的不饱和算的加成反应产物。所用的酚醛型环氧树脂有多种，包括普通的酚醛型环氧树脂，邻甲酚型酚醛型环氧树脂等，最常用的酸是丙烯酸和甲基丙烯酸。
普通双酚A型环氧树脂乙烯基酯树脂要比普通的不饱和树脂具有更高的机械性能与耐温性，更具有耐腐蚀性，通常耐温性在120--135℃，而酚醛型环氧乙烯基酯树脂比双酚A型环氧乙烯基酯树脂具有更高的强度，耐温性，以及耐腐蚀性能，其制成的鳞片胶泥更适合用于发电厂的烟囱等一些高温腐蚀场所，尽管如此，其耐高温性仍有局限性，不能满处更高层次的用户需求。
发明内容
针对普通双酚A型环氧乙烯基酯树脂耐温的局限性，本发明提供一种可耐更高温度的乙烯基酯树脂。
一种耐高温型乙烯基酯树脂，其特征在于原料的重量份数为：酚醛型环氧树脂30-35份，丙烯酸25-30份，苯乙烯30-40份。
一种耐高温型乙烯基酯树脂，其特征在于原料的重量份数为：酚醛型环氧树脂30-35份，甲基丙烯酸25-30份，苯乙烯30-40份。
一种耐高温型乙烯基酯树脂，其特征在于原料的重量份数为：邻甲酚型酚醛型环氧树脂30-35份，丙烯酸25-30份，苯乙烯30-40份。
一种耐高温型乙烯基酯树脂，其特征在于原料的重量份数为：邻甲酚型酚醛型环氧树脂30-35份，甲基丙烯酸25-30份，苯乙烯30-40份。
所述的一种耐高温型乙烯基酯树脂，其特征在于还含有0.03-0.05份的阻聚剂和0.3-0.5份的催化剂，所述阻聚剂包括0.01-0.02的苯三酚和0.03-0.04的对苯二酚，所述催化剂为0.2-0.3份的三苯基膦和0.2-0.3份的N，N-二甲基苯胺。
所述的一种耐高温型乙烯基酯树脂的制备方法，其特征在于该制备方法包括下述步骤：按所述投料比例，将酚醛型环氧树脂投入四口烧瓶中，搅拌升温至100℃，加入三分之一的一元酸，搅拌均匀后，再将混有三苯基膦和对苯二酚的剩余一元酸慢慢滴入反应瓶中。90分钟滴完，升温至115℃，反应45分钟后，每隔10分钟测一次酸值，待酸值达到10±2时，反应结束，降温至60℃，加苯乙烯，搅拌60分钟，即得产品。
所述的一种耐高温型乙烯基酯树脂的制备方法，其特征在于该制备方法包括下述步骤：按所述投料比例，将邻甲酚型酚醛型环氧树脂投入四口烧瓶中，搅拌升温至100℃，加入三分之一的一元酸，搅拌均匀后，再将混有三苯基膦和对苯二酚的剩余一元酸慢慢滴入反应瓶中。90分钟滴完，升温至115℃，反应45分钟后，每隔10分钟测一次酸值，待酸值达到10±2时，反应结束，降温至60℃，加苯乙烯，搅拌60分钟，即得产品。
具体实施方式
按照原料的反应组合可以得出四种产品，分别是TH-230-1(丙烯酸型酚醛型环氧乙烯基酯树脂)，TH-230-2(甲基丙烯酸型酚醛型环氧乙烯基酯树脂)，TH-250-1(丙烯酸型邻甲酚型酚醛型环氧乙烯基酯树脂)，TH-250-2(甲丙烯酸型酚醛型邻甲酚型环氧乙烯基酯树脂)。
性能测试
将上诉四种树脂和双酚A型环氧树脂乙烯基树脂TH-110按照GB/T2567-2008及GB/T1643.2制成测试样条进行测试。
将上诉五组样条进行测试后，得出如下表所述数据：
由上表不难看出：
1)采用酚醛型环氧树脂为原料合成出的乙烯基酯树脂，机械性能及耐温性都要高于双酚A型环氧乙烯基酯树脂，
2)同种酚醛型环氧树脂为原材料合成出的乙烯基酯树脂，一元酸为甲基丙烯酸的合成物，其机械性能和耐热性都要高出丙烯酸型的乙烯基酯树脂。
3)采用邻甲酚型酚醛型环氧树脂合成出的乙烯基酯树脂机械性能与耐温性要高于普通的酚醛型环氧乙烯基树脂。
Claims (8)
1.一种耐高温型乙烯基酯树脂，其特征在于原料的重量份数为：酚醛型环氧树脂30-35份，一元不饱和酸25-30份，稀释剂30-40份。
2.根据权利要求1所述的一种耐高温型乙烯基酯树脂，其特征在于原料的重量份数：邻甲酚型酚醛型环氧树脂30-35份，一元不饱和酸25-30份，稀释剂30-40份。
3.根据权利要求1所述的一种耐高温型乙烯基酯树脂，其特征在于所述一元酸由下述重量份数组成：丙烯酸25-30份。
4.根据权利要求1所述的一种耐高温型乙烯基酯树脂，其特征在于所述一元酸由下述重量份数组成：甲基丙烯酸25-30份。
5.根据权利要求1所述的一种耐高温型乙烯基酯树脂，其特征在于所述稀释剂由下述重量份数组成：苯乙烯30-40份。
6.根据权利要求1所述的一种耐高温型乙烯基酯树脂，其特征在于还含有0.03-0.05份的阻聚剂和0.3-0.5份的催化剂，所述阻聚剂包括0.01-0.02的苯三酚和0.03-0.04的对苯二酚，所述催化剂为0.2-0.3份的三苯基膦和0.2-0.3份的N，N-二甲基苯胺。
7.根据权利要求1所述的一种耐高温型乙烯基酯树脂的制备方法，其特征在于该制备方法包括下述步骤：按所述投料比例，将酚醛型环氧树脂投入四口烧瓶中，搅拌升温至100℃，加入三分之一的一元酸，搅拌均匀后，再将混有三苯基膦和对苯二酚的剩余一元酸慢慢滴入反应瓶中，90分钟滴完，升温至115℃，反应45分钟后，每隔10分钟测一次酸值，待酸值达到10±2时，反应结束，降温至60℃，加苯乙烯，搅拌60分钟，即得产品。
8.根据权利要求1所述的一种耐高温型乙烯基酯树脂的制备方法，其特征在于该制备方法包括下述步骤：按所述投料比例，将邻甲酚型酚醛型环氧树脂投入四口烧瓶中，搅拌升温至100℃，加入三分之一的一元酸，搅拌均匀后，再将混有三苯基膦和对苯二酚的剩余一元酸慢慢滴入反应瓶中，90分钟滴完，升温至115℃，反应45分钟后，每隔10分钟测一次酸值，待酸值达到10±2时，反应结束，降温至60℃，加苯乙烯，搅拌60分钟，即得产品。