CN103352368A - 机洗蚕丝被用蚕丝的制作方法 - Google Patents
机洗蚕丝被用蚕丝的制作方法 Download PDFInfo
- Publication number
- CN103352368A CN103352368A CN2013102337373A CN201310233737A CN103352368A CN 103352368 A CN103352368 A CN 103352368A CN 2013102337373 A CN2013102337373 A CN 2013102337373A CN 201310233737 A CN201310233737 A CN 201310233737A CN 103352368 A CN103352368 A CN 103352368A
- Authority
- CN
- China
- Prior art keywords
- silk
- solution
- quilt
- silk fiber
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种机洗蚕丝被用蚕丝。它需要解决的技术问题是,对蚕丝纤维进行接枝,增加了蚕丝纤维上自由空腔,使水洗后,特别是机洗后蚕丝之间不容易板结粘连,保持蚕丝的蓬松性和保暖性。本方案按如下步骤:1)制备溶液:β-环糊精,和七元瓜环或八元瓜环,以1:1~9的重量比例混合,加水至浓度为1~30克/升,用醋酸调节pH为6~7,在25℃~30℃的温度下用超声2~3小时至溶解;2)浸渍接枝:将蚕丝纤维浸入该溶液,蚕丝纤维:溶液的重量比为2~1:1,在室温下浸渍时间为5~7天;3)将反应后的蚕丝纤维冲洗净,干燥得产品。
Description
技术领域
本发明涉及一种个人用品,具体是机洗蚕丝被用蚕丝的制作方法。
背景技术
目前,公知的蚕丝被是由拉伸后的蚕丝绵和外套组成。蚕丝被轻薄、蓬松、保暖性强。但由于蚕丝绵含有丝胶性能的所限,被子不能经常清洗,只能通过日晒和通风来处理,易生螨虫、沉积灰尘,影响床品卫生。而床上用品及衣物一般采用水洗,操作简便、清洁度好,且成本低廉。但由于蚕丝浸水后容易板结、黏连,从而失去蓬松感和保暖性,故蚕丝被不能采用水洗方式进行清洁,特别是100%桑蚕丝、柞蚕丝等长丝绵为填充物的蚕丝被。因此,开发可经常性清洗、并可以水为介质机洗的蚕丝被是被褥类产品的发展趋势。
中国专利文献CN101187160公开了“一种蚕丝功能纤维的制备方法”,它是将环糊精通过化学键接枝到蚕丝纤维上,得到具有环糊精立体手性疏水空腔的蚕丝功能纤维产品;但该方法需要对蚕丝纤维进行脱胶处理。中国专利文献CN101735326公开了“一种利用微波无极灯快速将瓜与瓜环在有机溶剂中进行混合,在微波反应器中进行光聚合反应,快速将环键合到纤维素的方法,利用微波激发无极灯光,以巯基纤维素为载体,瓜环固载到纤维素上(固载到蚕丝纤维上尚无报道)。其键合有瓜环的纤维素可以用作有机、无机污染物的吸附剂、过滤剂等;此方法需要微波无极灯装置。以上两方法均用一种物质,且比较复杂。
发明内容
本发明需要解决的技术问题是,简化反应步骤,用混合物对蚕丝纤维进行接枝,增加了蚕丝纤维上自由空腔,使蚕丝之间不容易板结粘连,保持蚕丝的蓬松性和保暖性,制成的蚕丝被具有可洗性,特别是机洗性。
本发明的机洗蚕丝被用蚕丝的制作方法,其特征在于按如下步骤:
1)制备溶液:β-环糊精,和七元瓜环或八元瓜环,以1:1~9的重量比例混合,加水至浓度为1~30克/升,用醋酸调节pH为6~7,在25℃~30℃的温度下用超声2~3小时至溶解;
2)浸渍接枝:将蚕丝纤维浸入该溶液,蚕丝纤维:溶液的重量比为2~1:1,在室温下浸渍时间为5~7天;
3)将反应后的蚕丝纤维冲洗净,干燥(一般要求至含水率≤12%)得产品。
本发明利用了环糊精和瓜环结构中含有空腔的特性,巧妙地将两种物质按比例混合起来接枝,不但简化了脱丝胶的必须步骤,无需特殊的制作装置,而且接枝后蚕丝纤维的透气空间更大,弹性提高,更耐水洗,特别是机洗性。
本发明有益的技术效果是,该蚕丝被不仅能水洗,而且能用家用洗衣机进行清洗,清洗后依然能够保持蚕丝被原有的保暖性、蓬松感等特性。
具体实施方法
下面结合实施例,对本发明做进一步详细描述。
实施例:
1)制备溶液:一氯三嗪-β-环糊精,和七元瓜环以1:5的重量比例混合,加水至浓度为15克/升,用醋酸调节pH为6.5,在25℃的温度下用超声2小时溶解;
2)浸渍接枝:将蚕丝纤维浸入该溶液,蚕丝纤维:溶液的重量比为2:1,溶液温度为23℃,浸渍时间为7天;
3)将反应后的蚕丝纤维冲洗净,晾干至含水率≤12%得产品。
实施例产品机洗试验数据对比表
从实验发现,处理后机洗20次的效果比未处理机洗一次的效果还要好。
Claims (1)
1.一种机洗蚕丝被用蚕丝的制作方法,其特征在于按如下步骤:
1)制备溶液:β-环糊精,和七元瓜环或八元瓜环,以1:1~9的重量比例混合,加水至浓度为1~30克/升,用醋酸调节pH为6~7,在25℃~30℃的温度下用超声2~3小时至溶解;
2)浸渍接枝:将蚕丝纤维浸入该溶液,蚕丝纤维:溶液的重量比为2~1:1,在室温下浸渍时间为5~7天;
3)将反应后的蚕丝纤维冲洗净,干燥得产品。