CN103333588B - 一种低温固化型粉末涂料及其制备方法 - Google Patents
一种低温固化型粉末涂料及其制备方法 Download PDFInfo
- Publication number
- CN103333588B CN103333588B CN201310242466.8A CN201310242466A CN103333588B CN 103333588 B CN103333588 B CN 103333588B CN 201310242466 A CN201310242466 A CN 201310242466A CN 103333588 B CN103333588 B CN 103333588B
- Authority
- CN
- China
- Prior art keywords
- temperature curing
- powder coating
- low temperature
- low
- polyester resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种低温固化型粉末涂料及其制备方法,该粉末涂料的组分和含量的重量百分比如下:环氧树脂:28-30%;低温固化聚酯树脂:28-30%;低温固化促进剂:0.1-1%;安息香:0.1-0.4%;进口流平剂:0.7-1.4%;氢化蓖麻油:0.4-1%;色料:5-10%;沉淀硫酸钡:25-40%。本发明的配方中采用了低温固化聚酯树脂和低温固化促进剂,所得粉末涂料产品的涂膜在较低的固化温度下固化的同时,可保证涂膜各项机械性能较为优良,适于规模化推广应用。
Description
技术领域
本发明涉及粉末涂料制备技术领域,特别是一种低温固化型粉末涂料及其制备方法。
背景技术
粉末涂料以其环保经济的优越性能,广泛用于各种金属件的表面涂装。随着经济社会的发展,人们对环保的概念越来越深入,粉末涂料的应用范围也越来越大,人们对粉末涂料的固化条件的要求也越来越高。普通的粉末涂料的固化条件大都是烘烤温度较高,烘烤时间较长,这类方法容易造成能源的浪费。因此,从节省能源,降低成本的角度考虑,低温固化型粉末涂料有着广阔的市场前景。
发明内容
本发明所要解决的技术问题是:提供一种低温固化型粉末涂料及其制备方法。
本发明解决其技术问题所采用的技术方案是:一种低温固化型粉末涂料,其特征是:该粉末涂料的组分和含量的重量百分比如下:环氧树脂:28-30%;低温固化聚酯树脂:28-30%;高活性低温固化促进剂:0.1-1%;安息香:0.1-0.4%;进口流平剂:0.7-1.4%;氢化蓖麻油:0.4-1%;色料:5-10%;沉淀硫酸钡:25-40%;
所述环氧树脂为环氧酚醛型树脂;低温固化聚酯树脂为端羧基聚酯树脂;安息香为苯偶姻或二苯乙醇酮,可消除粉末涂料制备过程中和喷涂过程中产生的针孔和气泡。
进一步,所述粉末涂料组分和含量的优选重量百分比如下:环氧树脂:30%;低温固化聚酯树脂:30%;高活性低温固化促进剂:0.4%;安息香:0.4%;进口流平剂:1%;氢化蓖麻油:0.5%;色料:5%;沉淀硫酸钡:32.7%。
一种低温固化型粉末涂料的制备方法,该方法包括如下步骤:
a.按照重量百分比将环氧树脂:28-30%;低温固化聚酯树脂:28-30%;高活性低温固化促进剂:0.1-1%;安息香:0.1-0.4%;进口流平剂:0.7-1.4%;氢化蓖麻油:0.4-1%;色料:5-10%;沉淀硫酸钡:25-40%按比例配制好放入高速混合搅拌器中充分均匀混合10-12min;
b.取步骤a中混合均匀的物料加入螺杆挤出机中充分熔融并混炼,然后挤出、压片、粉碎得成品。
本发明的配方中采用了低温固化聚酯树脂和高活性低温固化促进剂,所得粉末涂料产品的涂膜在较低的固化温度下固化的同时,可保证涂膜各项机械性能较为优良,适于规模化推广应用。
具体实施方式
实施例一
一种低温固化型粉末涂料,其特征是:该粉末涂料的组分和含量的重量百分比如下:环氧树脂:30%;低温固化聚酯树脂:30%;高活性低温固化促进剂:0.4%;安息香:0.4%;进口流平剂:1%;氢化蓖麻油:0.5%;色料:5%;沉淀硫酸钡:32.7%。
所述低温固化型粉末涂料的制备方法,该方法包括如下步骤:
a.按照重量百分比将环氧树脂;低温固化聚酯树脂;高活性低温固化促进剂;安息香;进口流平剂;氢化蓖麻油;色料;沉淀硫酸钡;按比例配制好放入高速混合搅拌器中充分均匀混合10-12min;
b.取步骤a中混合均匀的物料加入螺杆挤出机中充分熔融并混炼,然后挤出、压片、粉碎得成品。
实施例二
一种低温固化型粉末涂料,其特征是:该粉末涂料的组分和含量的重量百分比如下:环氧树脂:29%;低温固化聚酯树脂:28.5%;高活性低温固化促进剂:0.6%;安息香:0.4%;进口流平剂:1%;氢化蓖麻油:0.5%;色料:5%;沉淀硫酸钡:35%,所述制备方法同实施例一。
实施例三
一种低温固化型粉末涂料,其特征是:该粉末涂料的组分和含量的重量百分比如下:环氧树脂:30%;低温固化聚酯树脂:30%;高活性低温固化促进剂:1%;安息香:0.4%;进口流平剂:1%;氢化蓖麻油:0.5%;色料:5%;沉淀硫酸钡:32.1%,所述制备方法同实施例一。
各实施例所得环氧粉末产品喷于金属工件上,固化条件为130℃/20min,测试结果如下:
经检测:该粉末涂料D50粒径为38-42μm;固化后涂膜的抗冲击性(GB/T1732-1993):50cm正反冲通过;耐热性:150℃,35h烘烤无失光无色变;盐雾试验500h(GB/T1771-1991):无起泡、无开裂且无剥离现象;附着力(1mm划格法,GB/T9286-1998):0级;铅笔硬度(GB/T6739-1996):3H。
Claims (1)
1.一种低温固化型粉末涂料,其特征是:该粉末涂料组分和含量的重量百分比如下:环氧树脂:30%;低温固化聚酯树脂:30%;高活性低温固化促进剂:0.4%;安息香:0.4%;进口流平剂:1%;氢化蓖麻油:0.5%;色料:5%;沉淀硫酸钡:32.7%;所述环氧树脂为环氧酚醛型树脂;低温固化聚酯树脂为端羧基聚酯树脂。