CN103319991A - 一种纳米粉末涂料及其制备方法 - Google Patents

一种纳米粉末涂料及其制备方法 Download PDF

Info

Publication number
CN103319991A
CN103319991A CN2013102412552A CN201310241255A CN103319991A CN 103319991 A CN103319991 A CN 103319991A CN 2013102412552 A CN2013102412552 A CN 2013102412552A CN 201310241255 A CN201310241255 A CN 201310241255A CN 103319991 A CN103319991 A CN 103319991A
Authority
CN
China
Prior art keywords
powder coating
agent
tio
nano
nanometer powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013102412552A
Other languages
English (en)
Inventor
潘建良
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Huaguang Powder Co Ltd
Original Assignee
Jiangsu Huaguang Powder Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Huaguang Powder Co Ltd filed Critical Jiangsu Huaguang Powder Co Ltd
Priority to CN2013102412552A priority Critical patent/CN103319991A/zh
Publication of CN103319991A publication Critical patent/CN103319991A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种纳米粉末涂料及其制备方法，该粉末涂料的组分和重量百分比如下：聚酯树脂50-55%；固化剂3.7-4.2%；色料20-24%；纳米TiO2：1-3%；流平剂：6-8%；安息香：0.5-1%；沉淀硫酸钡：5-19%。本发明的配方中采用了经偶联剂处理过的纳米金红石TiO2大大改善涂料的施工性，耐候性和力学性能，适于建筑类涂料生产商规模化推广应用。

Description

一种纳米粉末涂料及其制备方法
技术领域
本发明涉及一种纳米粉末涂料及其制备方法。
背景技术
粉末涂料以其环保和经济的优越性能，广泛用于各种金属件的表面涂装。随着经济社会的发展，人们对环保的概念越来越深入，粉末涂料的应用范围也越来越大。建筑行业用的普通粉末涂料存在耐候性、施工性及力学性能的关联问题，因此，提供一种耐候性好、施工性能优良、力学性能较好的粉末涂料是当前研究的问题。
发明内容
本发明所要解决的技术问题是：提供一种耐候性好、施工性能优良、力学性能较好的纳米粉末涂料及其制备方法。
本发明解决其技术问题所采用的技术方案是：一种纳米粉末涂料，其特征是：该粉末涂料的组分和重量百分比如下：聚酯树脂50-55%；固化剂3.7-4.2%；色料20-24%；纳米TiO2：1-3%；流平剂：6-8%；安息香：0.5-1%；沉淀硫酸钡：5-19%；
所述聚酯树脂为饱和聚酯树脂；固化剂为异氰尿酸三缩水甘油脂（TGIC）；流平剂为丙烯酸流平剂；安息香为苯偶姻或二苯乙醇酮，可消除粉末涂料制备过程中和喷涂过程中产生的针孔和气泡，纳米TiO2是由铝酸酯偶联剂F-1对金红石型纳米TiO2进行干法改性而得。
纳米级TiO2具有无毒、光学性质稳定、分散性好、比表面积大、表面结合能高等特点；这些性能使得用纳米TiO2制得的涂料性质稳定、抗老化能力强、力学性能好。
进一步，该粉末涂料各组分的优选含量百分比如下：聚酯树脂50%；固化剂3.7%；色料20%；纳米TiO2：1%；流平剂：6%；安息香：0.5%；沉淀硫酸钡：18.8%。
一种纳米粉末涂料的制备方法，其特征是：该制备方法包括如下步骤：
a.按照重量百分比将聚酯树脂50-55%；固化剂3.7-4.2%；色料20-24%；纳米TiO2：1-3%；流平剂：6-8%；安息香：0.5-1%；沉淀硫酸钡：5-19%，按比例配制好放入高速混合搅拌器中充分均匀混合10-12min；
b.取步骤a中混合均匀的物料加入螺杆挤出机中充分熔融并混炼，然后挤出、压片、粉碎得成品。
本发明的配方中采用了经偶联剂处理过的纳米金红石TiO2大大改善涂料的施工性，耐候性和力学性能，适于建筑类涂料生产商规模化推广应用。
具体实施方式
实施例一
一种纳米粉末涂料，其特征是：该粉末涂料各组分的优选含量百分比如下：聚酯树脂50%；固化剂3.7%；色料20%；纳米TiO2：1%；流平剂：6%；安息香：0.5%；沉淀硫酸钡：18.8%；该纳米粉末涂料的制备方法包括如下步骤：
a.按照重量百分比将聚酯树脂；固化剂%；色料；纳米TiO2；流平剂；安息香；沉淀硫酸钡，按比例配制好放入高速混合搅拌器中充分均匀混合10-12min；
b.取步骤a中混合均匀的物料加入螺杆挤出机中充分熔融并混炼，然后挤出、压片、粉碎得成品。
实施例二
一种纳米粉末涂料，其特征是：该粉末涂料各组分的优选含量百分比如下：聚酯树脂52%；固化剂3.9%；色料20%；纳米TiO2：2%；流平剂：6%；安息香：0.5%；沉淀硫酸钡：15.6%；该纳米粉末涂料的制备方法同实施例一。
实施例三
一种纳米粉末涂料，其特征是：该粉末涂料各组分的优选含量百分比如下：聚酯树脂55%；固化剂4.2%；色料22%；纳米TiO2：3%；流平剂：8%；安息香：1%；沉淀硫酸钡：6.8%；该纳米粉末涂料的制备方法同实施例一。
将以上各实施例所得环氧粉末产品喷于金属工件上，固化条件为200℃/10min，测试结果如下：该粉末涂料D50粒径为38-42μm；固化后涂膜的抗冲击性（GB/T1732-1993）：50cm正反冲通过；耐热性：150℃，35h烘烤无失光无色变；盐雾试验500h（GB/T1771-1991）：无起泡、无开裂且无剥离现象；附着力（1mm划格法，GB/T9286-1998）：0级；铅笔硬度（GB/T6739-1996）：3H。

Claims (3)

1.一种纳米粉末涂料，其特征是：该粉末涂料的组分和重量百分比如下：聚酯树脂50-55%；固化剂3.7-4.2%；色料20-24%；纳米TiO2：1-3%；流平剂：6-8%；安息香：0.5-1%；沉淀硫酸钡：5-19%；
所述聚酯树脂为饱和聚酯树脂；固化剂为异氰尿酸三缩水甘油脂（TGIC）；流平剂为丙烯酸流平剂；安息香为苯偶姻或二苯乙醇酮，可消除粉末涂料制备过程中和喷涂过程中产生的针孔和气泡，纳米TiO2是由铝酸酯偶联剂F-1对金红石型纳米TiO2进行干法改性而得。
2.根据权利要求1所述的一种纳米粉末涂料，其特征是：该粉末涂料各组分的优选含量百分比如下：聚酯树脂50%；固化剂3.7%；色料20%；纳米TiO2：1%；流平剂：6%；安息香：0.5%；沉淀硫酸钡：18.8%。
3.一种纳米粉末涂料的制备方法，其特征是：该制备方法包括如下步骤：
a.按照重量百分比将聚酯树脂50-55%；固化剂3.7-4.2%；色料20-24%；纳米TiO2：1-3%；流平剂：6-8%；安息香：0.5-1%；沉淀硫酸钡：5-19%，按比例配制好放入高速混合搅拌器中充分均匀混合10-12min；
b.取步骤a中混合均匀的物料加入螺杆挤出机中充分熔融并混炼，然后挤出、压片、粉碎得成品。
CN2013102412552A 2013-06-18 2013-06-18 一种纳米粉末涂料及其制备方法 Pending CN103319991A (zh)