CN103131304B - 一种含有改性电石渣的粉末涂料 - Google Patents

一种含有改性电石渣的粉末涂料 Download PDF

Info

Publication number
CN103131304B
CN103131304B CN201310040650.4A CN201310040650A CN103131304B CN 103131304 B CN103131304 B CN 103131304B CN 201310040650 A CN201310040650 A CN 201310040650A CN 103131304 B CN103131304 B CN 103131304B
Authority
CN
China
Prior art keywords
carbide slag
powder coating
raw
modified carbide
modified
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310040650.4A
Other languages
English (en)
Other versions
CN103131304A (zh
Inventor
倪进培
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhongshan Hong Li new Mstar Technology Ltd
Original Assignee
倪进培
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 倪进培 filed Critical 倪进培
Priority to CN201310040650.4A priority Critical patent/CN103131304B/zh
Publication of CN103131304A publication Critical patent/CN103131304A/zh
Application granted granted Critical
Publication of CN103131304B publication Critical patent/CN103131304B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种含有改性电石渣的粉末涂料,是由下述重量份的原料制得:双酚A型环氧树脂100-105,聚乙烯醇35-38,萜稀树脂T120??10-15,甲基纤维素5-7,抗氧剂264?0.8-1.5,抗氧剂168?0.8-1.5,无机填料100-110,丙烯酸酯流平剂3-5,钛白粉30-40,安息香0.7-1.5,氢氧化镁1-2,乙撑双硬脂酰胺3.7-4.8,己二酸二辛酯1.5-2,环氧硬脂酸辛酯0.4-0.6,四甲氧基甲基甘脲5-7,鳞片状锌粉4-6,微粉蜡4-6,硅烷偶联剂KH560?2.1-3.2,松香1-2。本发明绿色环保,机械强度高;既使用方便,又无毒无害阻燃,耐候性强。

Description

一种含有改性电石渣的粉末涂料
技术领域
[0001] 本发明涉及涂料领域,确切地说是一种含有改性电石渣的粉末涂料。
背景技术
[0002] 粉末涂料是一种新型的不含溶剂100%固体粉末状涂料。具有无溶剂、无污染、可回收、环保、节省能源和资源、减轻劳动强度和涂膜机械强度高等特点。粉末涂料是与一般涂料完全不同的形态,它是以微细粉末的状态存在的。由于不使用溶剂,所以称为粉末涂料。粉末涂料的主要特点有:具有无公害、高效率、节省资源的特点。
发明内容
[0003] 本发明的目的在于提供一种阻燃,耐候性强的含有改性电石渣的粉末涂料。
[0004] 上述目的通过以下方案实现:
[0005] 一种含有改性电石渣的粉末涂料,其特征在于,是由下述重量份的原料制得:双酚A型环氧树脂100-105,聚乙烯醇35-38,萜稀树脂T120 10-15,甲基纤维素5_7,抗氧剂264 0.8-1.5,抗氧剂168 0.8-1.5,无机填料100-110,丙烯酸酯流平剂3_5,钛白粉30-40,安息香0.7-1.5,氢氧化镁1-2,乙撑双硬脂酰胺3.7-4.8,己二酸二辛酯1.5-2,环氧硬脂酸辛酯0.4-0.6,四甲氧基甲基甘脲5-7,鳞片状锌粉4-6,微粉蜡4_6,硅烷偶联剂 KH560 2.1-3.2,松香 1-2。
[0006] 所述的一种含有改性电石渣的粉末涂料,其特征在于:所述的无机填料由下述重量份的原料组成:纳米二氧化钛10-20、纳米氧化锌18-25、改性电石渣10-15、秸杆灰15-20、纳米三氧化二铝13-15。
[0007] 所述的改性电石渣的制备方法为:将电石渣于700-800 °C下煅烧4-6小时,冷却后,破碎,过100-200目筛,然后于8-10%的乙酸溶液中浸泡5-7小时后,取出,去离子水洗涤至中性,加入相当于电石渣重量2-3%的硬脂酸钠,1-2%的马来酸二辛酯,混匀后,烘干,研磨成纳米粉末,即得。
[0008] 所述的一种含有改性电石渣的粉末涂料,其特征在于:
[0009] 制备方法包括以下步骤:
[0010] (I )、按所述重量份精确称量各原料,先于500-600转/分下搅拌混合3-4分钟,于2800-3000转/分下搅拌混合8-10分钟,后于400-500转/分下搅拌混合1_2分钟,停止搅拌,得混合物料;
[0011] (2)、将混合物料用挤出机在100-115°c的温度下挤出,得挤出料;
[0012] (3)、挤出料粉碎后过100-200目筛,即得。
[0013] 本发明的有益效果为:本发明绿色环保,机械强度高;既使用方便,又无毒无害阻燃,耐候性强。
具体实施方式
[0014] 一种含有改性电石渣的粉末涂料,是由下述重量份(kg)的原料制得:双酚A型环氧树脂105,聚乙烯醇38,萜稀树脂T120 15,甲基纤维素7,抗氧剂264 1.2,抗氧剂168 1.1,无机填料103,丙烯酸酯流平剂5,钛白粉40,安息香1.5,氢氧化镁2,乙撑双硬脂酰胺4.2,己二酸二辛酯1.7,环氧硬脂酸辛酯0.6,四甲氧基甲基甘脲7,鳞片状锌粉6,微粉蜡4.6,硅烷偶联剂KH560 2.5,松香2。
[0015] 所述的无机填料由下述重量份的原料组成:纳米二氧化钛20、纳米氧化锌21、改性电石渣15、秸杆灰20、纳米三氧化二铝15。
[0016] 所述的改性电石渣的制备方法为:将电石渣于800°C下煅烧6小时,冷却后,破碎,过180目筛,然后于8%的乙酸溶液中浸泡7小时后,取出,去离子水洗涤至中性,加入相当于电石渣重量3%的硬脂酸钠,1%的马来酸二辛酯,混匀后,烘干,研磨成纳米粉末,即得。
[0017] 所述的一种含有改性电石渣的粉末涂料,
[0018] 制备方法包括以下步骤:
[0019] (I )、按所述重量份精确称量各原料,先于600转/分下搅拌混合3分钟,于3000转/分下搅拌混合10分钟,后于500转/分下搅拌混合2分钟,停止搅拌,得混合物料;
[0020] (2)、将混合物料用挤出机在115°C的温度下挤出,得挤出料;
[0021] (3)、挤出料粉碎后过200目筛,即得。
[0022] 将本实施例所得涂料采用高压静电喷涂于铸件上,电压为60KV,平均膜厚为70-100微米,固化条件为180°C烘烤20分钟;
[0023] 性能指标如下:
[0024] 按照GB/T1732测试,抗冲击性彡50kg.cm ;
[0025] 按照GB/T6739测试,铅笔硬度彡H级;
[0026] 480h QUV-B加速光老化试验测试得,保光率达89%。
[0027] 所得涂层表面平整,无气泡,颗粒、缩孔、针孔。

Claims (2)

1.一种含有改性电石渣的粉末涂料,其特征在于,是由下述重量份的原料制得••双酚A型环氧树脂100-105,聚乙烯醇35-38,萜烯树脂T120 10-15,甲基纤维素5_7,抗氧剂264 0.8-1.5,抗氧剂168 0.8-1.5,无机填料100-110,丙烯酸酯流平剂3_5,钛白粉30-40,安息香0.7-1.5,氢氧化镁1-2,乙撑双硬脂酰胺3.7-4.8,己二酸二辛酯1.5-2,环氧硬脂酸辛酯0.4-0.6,四甲氧基甲基甘脲5-7,鳞片状锌粉4-6,微粉蜡4_6,硅烷偶联剂 KH560 2.1-3.2,松香 1-2 ; 所述的无机填料由下述重量份的原料组成:纳米二氧化钛10-20、纳米氧化锌18-25、改性电石渣10-15、秸杆灰15-20、纳米三氧化二铝13-15 ; 所述的改性电石渣的制备方法为:将电石渣于700-800°C下煅烧4-6小时,冷却后,破碎,过100-200目筛,然后于8-10%的乙酸溶液中浸泡5-7小时后,取出,去离子水洗涤至中性,加入相当于电石渣重量2-3%的硬脂酸钠,1-2%的马来酸二辛酯,混匀后,烘干,研磨成纳米粉末,即得。
2.根据权利要求1所述的一种含有改性电石渣的粉末涂料,其特征在于:制备方法包括以下步骤: (1)、按所述重量份精确称量各原料,先于500-600转/分下搅拌混合3-4分钟,于2800-3000转/分下搅拌混合8-10分钟,后于400-500转/分下搅拌混合1_2分钟,停止搅拌,得混合物料; (2)、将混合物料用挤出机在100-115°C的温度下挤出,得挤出料; (3)、挤出料粉碎后过100-200目筛,即得。
CN201310040650.4A 2013-02-03 2013-02-03 一种含有改性电石渣的粉末涂料 Active CN103131304B (zh)