CN103031025B - 触摸屏临时保护用热固化非溶剂型可剥蓝胶及制备方法 - Google Patents

触摸屏临时保护用热固化非溶剂型可剥蓝胶及制备方法 Download PDF

Info

Publication number
CN103031025B
CN103031025B CN201310003438.0A CN201310003438A CN103031025B CN 103031025 B CN103031025 B CN 103031025B CN 201310003438 A CN201310003438 A CN 201310003438A CN 103031025 B CN103031025 B CN 103031025B
Authority
CN
China
Prior art keywords
resin
parts
epoxy
touch
blue gel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201310003438.0A
Other languages
English (en)
Other versions
CN103031025A (zh
Inventor
王晓颖
陈三多
史伟同
李守平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BEIJING TIANSHAN NEW MATERIAL TECHNOLOGY CO., LTD.
Original Assignee
Beijing Hystic New Materials Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Beijing Hystic New Materials Co Ltd filed Critical Beijing Hystic New Materials Co Ltd
Priority to CN201310003438.0A priority Critical patent/CN103031025B/zh
Publication of CN103031025A publication Critical patent/CN103031025A/zh
Application granted granted Critical
Publication of CN103031025B publication Critical patent/CN103031025B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明是一种触摸屏临时保护用热固化非溶剂型可剥蓝胶及制备方法，该可剥蓝胶配方组成为：氯醋树脂30~50份，丙烯酸酯树脂10~30份，环氧树脂10~20份，增塑剂20-30份，触变剂？？0.1-1.0份，颜料0.1-1.0份。其制备方法为：按配方比例准确称取各种原料，先将氯醋树脂、丙烯酸酯树脂、环氧树脂、增塑剂、颜料依次加入反应釜中搅拌，待搅拌均匀后，加入触变剂，分散均匀后出料。本发明为非溶剂体系，更加安全环保具有更长的适用期，较少由于溶剂挥发造成的施胶困难和施胶工艺性不稳定的问题；在保证可剥蓝胶可剥离性的同时提高了其在触摸屏生产工艺过程中的耐介质侵蚀性能，大大降低了触摸屏生产的不良率。

Description

触摸屏临时保护用热固化非溶剂型可剥蓝胶及制备方法
技术领域
本发明涉及一种热固化、非溶剂型可剥蓝胶及其制备方法，该可剥蓝胶主要应用于触摸屏制造工艺中的临时保护。
背景技术
随着信息技术和平面显示技术的迅速发展，触摸屏的应用越来越普遍。大到公共场所的信息查询系统，小到个人电脑、平板电脑、手机，触摸屏和我们的生活息息相关。在触摸屏的生产工艺过程中，需要通过使用可剥蓝胶对触摸屏玻璃进行多次的临时保护。目前市面上的可剥蓝胶多为溶剂型体系，施胶过程中污染严重，对产线工人的健康造成较大的影响。由于溶剂的挥发，溶剂型可剥蓝胶开盖后适用期仅为2小时，放置后粘度升高，施胶困难。此外，可剥蓝胶的可剥离性和耐介质侵蚀性的矛盾问题没有很好的解决，触摸屏生产过程中不良率较高。
理想的可剥蓝胶不仅要安全环保、较长的适用期、稳定的施胶工艺性能，还要在保证可剥离性的同时提高耐介质侵蚀性能，从而降低触摸屏生产过程的不良率。
发明内容
本发明的目的在于提供一种热固化，非溶剂型，施胶工艺性好，具有优异的耐介质侵蚀性的可剥蓝胶及其制备方法。
为了实现本发明的目的，提出一种触摸屏临时保护用热固化非溶剂型可剥蓝胶，所述可剥蓝胶配方组成如下：
氯醋树脂30~50份
丙烯酸酯树脂10~30份
环氧树脂10~20份
增塑剂20-30份
触变剂0.1-1.0份
颜料0.1-1.0份
其中，所述氯醋树脂为分子量为20000-50000，醋酸乙烯含量为5%-40%的二元氯醋树脂中的一种或几种；
所述的丙烯酸酯树脂为甲基丙烯酸甲酯树脂、甲基丙烯酸丁酯树脂、甲基丙烯酸月桂酯树脂、甲基丙烯酸环己酯树脂、环氧丙烯酸树脂和聚氨酯丙烯酸树脂中的一种或几种；
所述的环氧树脂为双酚A环氧树脂，环氧树脂E-51、环氧树脂128、环氧树脂E-44、环氧树脂E-54和环氧树脂E-56中的一种或几种；
所述的的增塑剂为邻苯二甲酸二辛脂、对苯二甲酸二辛酯、二乙二醇二苯甲酸酯、乙酰柠檬酸三丁酯、己二酸二辛脂、癸二酸二丁酯、癸二酸二辛酯、环氧大豆油、环氧亚麻子油、环氧油酸丁酯、环氧硬脂酸辛酯、环氧化甘油三酸酯和环氧四氢邻苯二甲酸二辛酯中的一种或几种；
所述的触变剂为气相法二氧化硅、沉淀二氧化硅、有机膨润土、石棉、高岭土和凹凸棒土中的一种或几种；
所述的颜料为铁蓝、群青蓝、钴蓝或酞菁蓝。
所述氯醋树脂还可以为羟基改性三元氯醋树脂、羧基改性三元氯醋树脂和环氧基改性三元氯醋树脂中的一种或几种。
本发明还提出两种可剥蓝胶具体配方，组成分别为：
配方1
氯醋树脂LC-4040份
甲基丙烯酸甲酯树脂15份
环氧树脂12810份
己二酸二辛酯23份
环氧大豆油10份
有机膨润土1.0份
酞菁蓝1.0份。
配方2
氯醋树脂VMC35份
甲基丙烯酸甲酯树脂10份
环氧树脂1288份
环氧树脂E-445份
邻苯二甲酸二辛脂30份
环氧亚麻子油10份
沉淀二氧化硅1.0份
酞菁蓝1.0份。
本发明还提出一种触摸屏临时保护用热固化非溶剂型可剥蓝胶的制备方法，所述方法为：
按配方比例准确称取各种原料，先将氯醋树脂、丙烯酸酯树脂、环氧树脂、增塑剂、颜料依次加入反应釜中搅拌，待搅拌均匀后，加入触变剂，分散均匀后出料。

Claims (4)

1.一种触摸屏临时保护用热固化非溶剂型可剥蓝胶，其特征在于，所述可剥蓝胶配方组成如下：
氯醋树脂30~50份
丙烯酸酯树脂10~30份
环氧树脂10~20份
增塑剂20-30份
触变剂0.1-1.0份
颜料0.1-1.0份
所述氯醋树脂选自羟基改性三元氯醋树脂、羧基改性三元氯醋树脂、环氧基改性三元氯醋树脂中的一种或者几种；或者分子量为20000-50000，醋酸乙烯含量为5%-40%的二元氯腊树脂中的一种或者几种；
所述的丙烯酸酯树脂为甲基丙烯酸甲酯树脂、甲基丙烯酸丁酯树脂、甲基丙烯酸月桂酯树脂、甲基丙烯酸环己酯树脂、环氧丙烯酸树脂和聚氨酯丙烯酸树脂中的一种或几种；
所述的环氧树脂为双酚A环氧树脂，环氧树脂E-51、环氧树脂128、环氧树脂E-44、环氧树脂E-54和环氧树脂E-56中的一种或几种；
所述的的增塑剂为邻苯二甲酸二辛脂、对苯二甲酸二辛酯、二乙二醇二苯甲酸酯、乙酰柠檬酸三丁酯、己二酸二辛脂、癸二酸二丁酯、癸二酸二辛酯、环氧大豆油、环氧亚麻子油、环氧油酸丁酯、环氧硬脂酸辛酯、环氧化甘油三酸酯和环氧四氢邻苯二甲酸二辛酯中的一种或几种；
所述的触变剂为气相法二氧化硅、沉淀二氧化硅、有机膨润土、石棉、高岭土和凹凸棒土中的一种或几种；
所述的颜料为铁蓝、群青蓝、钴蓝或酞菁蓝。
2.根据权利要求 1所述的触摸屏临时保护用热固化非溶剂型可剥蓝胶，其特征在于，所述可剥蓝胶配方组成如下：
氯醋树脂LC-4040份
甲基丙烯酸甲酯树脂15份
环氧树脂12810份
己二酸二辛酯23份
环氧大豆油10份
有机膨润土1.0份
酞菁蓝1.0份。
3.根据权利要求2所述的触摸屏临时保护用热固化非溶剂型可剥蓝胶，其特征在于，所述可剥蓝胶配方组成如下：
氯醋树脂VMC35份
甲基丙烯酸甲酯树脂10份
环氧树脂1288份
环氧树脂E-445份
邻苯二甲酸二辛脂30份
环氧亚麻子油10份
沉淀二氧化硅1.0份
酞菁蓝1.0份。
4.制备如权利要求1-3中之一所述的触摸屏临时保护用热固化非溶剂型可剥蓝胶的制备方法，其特征在于，按配方比例准确称取各种原料，先将氯醋树脂、丙烯酸酯树脂、环氧树脂、增塑剂、颜料依次加入反应釜中搅拌，待搅拌均匀后，加入触变剂，分散均匀后出料。
CN201310003438.0A 2013-01-06 2013-01-06 触摸屏临时保护用热固化非溶剂型可剥蓝胶及制备方法 Expired - Fee Related CN103031025B (zh)