CN105176225A - 一种易剥离型可剥蓝胶及其制备方法 - Google Patents
一种易剥离型可剥蓝胶及其制备方法 Download PDFInfo
- Publication number
- CN105176225A CN105176225A CN201510439591.7A CN201510439591A CN105176225A CN 105176225 A CN105176225 A CN 105176225A CN 201510439591 A CN201510439591 A CN 201510439591A CN 105176225 A CN105176225 A CN 105176225A
- Authority
- CN
- China
- Prior art keywords
- parts
- easy
- peelable blue
- stripping type
- blue gel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种易剥离型可剥蓝胶及其制备方法,按重量份数计包括下列组分:聚氯乙烯树脂25~35份、氨基树脂20~30份、触变剂5~14份、低粘度增塑剂2~12份、剥离力改性剂5~14份、颜料3~9份、消泡剂1~6份、纳米填料8~15份。本发明制备的易剥离型可剥蓝胶,加入剥离力改性剂,改善了可剥蓝胶粘结强度,临时保护完以后,轻轻用力就可以将可剥蓝胶与盖板玻璃分离,且无任何残胶。其膜层的拉伸强度高,膜层不会被撕裂。
Description
技术领域
本发明涉及可剥胶技术领域,尤其涉及一种易剥离型可剥蓝胶及其制备方法。
背景技术
随着信息技术和平面显示技术的迅速发展,触摸屏的应用越来越普遍。大到公共场所的信息查询系统,小到个人电脑、平板电脑、手机,触摸屏和我们的生活息息相关。
在触摸屏的生产工艺过程中,需要对触摸屏玻璃进行多次的临时保护。可剥蓝胶为一种特殊的胶粘剂,它可以对触摸屏产品表面在生产过程进行临时性保护,以防止机械划伤、磨损、污染、腐蚀等。完成保护任务后,再剥离下来,不影响材料本身。
然而,目前市场上的可剥蓝胶存在与盖板玻璃的粘结度较大,不易剥离,有残胶。且膜层的拉伸强度低,剥离过程中膜层会被撕裂。
发明内容
本发明的目的在于克服上述现有技术存在的不足,提供一种粘结强度适中、易剥离、拉伸强度高的可剥蓝胶。
同时,本发明还提供了一种易剥离型可剥蓝胶的制备方法。
为达到上述目的,本发明是通过以下技术方案实现的:
一种易剥离型可剥蓝胶,按重量份数计包括下列组分:聚氯乙烯树脂25~35份、氨基树脂20~30份、触变剂5~14份、低粘度增塑剂2~12份、剥离力改性剂5~14份、颜料3~9份、消泡剂1~6份、纳米填料8~15份。
优选的,所述触变剂为气相二氧化硅、有机膨润土、氢化蓖麻油、聚酰胺蜡中的任意一种。
优选的,所述低粘度增塑剂为环氧类增塑剂、柠檬酸酯类增塑剂、聚酯类增塑剂中的任意一种。
优选的,所述剥离力改性剂为聚乙烯蜡、四氟乙烯蜡浆、聚二甲基硅氧烷中的任意一种。
优选的,所述颜料为群青蓝、钴蓝、酞菁蓝中的任意一种。
优选的,所述纳米填料为纳米碳酸钙、纳米滑石粉、纳米硫酸钡中的任意一种。
上述的易剥离型可剥蓝胶,其制备工艺步骤如下:
(1)按重量分数称取原料配方中的材料;
(2)将聚氯乙烯树脂、氨基树脂、触变剂加入反应釜中,在40~60℃下搅拌1~3小时,搅拌速度200~400转/分钟,冷却至常温,得基胶;
(3)取剥离力改性剂加入基胶中,在70~80℃下搅拌混合2~4小时,搅拌速度300~600转/分钟;将其余原料加入基胶中,在75~85℃下保温搅拌30~60分钟,搅拌速度400~600转/分钟,搅拌均匀,即得易剥离型可剥蓝胶。
本发明的有益效果:
本发明制备的易剥离型可剥蓝胶,加入剥离力改性剂,改善了可剥蓝胶粘结强度,临时保护完以后,轻轻用力就可以将可剥蓝胶与盖板玻璃分离,且无任何残胶。其膜层的拉伸强度高,膜层不会被撕裂。
具体实施方式
下面结合具体实施例对本发明进行详细说明。以下实施例将有助于本领域的技术人员进一步理解本发明,但不以任何形式限制本发明。应当指出的是,对本领域的普通技术人员来说,在不脱离本发明构思的前提下,还可以做出若干变形和改进。这些都属于本发明的保护范围。
一种易剥离型可剥蓝胶,按重量份数计包括下列组分:聚氯乙烯树脂25~35份、氨基树脂20~30份、触变剂5~14份、低粘度增塑剂2~12份、剥离力改性剂5~14份、颜料3~9份、消泡剂1~6份、纳米填料8~15份。
其制备工艺步骤如下:
(1)按重量分数称取原料配方中的材料;
(2)将聚氯乙烯树脂、氨基树脂、触变剂加入反应釜中,在40~60℃下搅拌1~3小时,搅拌速度200~400转/分钟,冷却至常温,得基胶;
(3)取剥离力改性剂加入基胶中,在70~80℃下搅拌混合2~4小时,搅拌速度300~600转/分钟;将其余原料加入基胶中,在75~85℃下保温搅拌30~60分钟,搅拌速度400~600转/分钟,搅拌均匀,即得易剥离型可剥蓝胶。
本发明制备的易剥离型可剥蓝胶,具有粘结强度适中、易剥离、拉伸强度高的优点。
实施例1
本发明的易剥离型可剥蓝胶,按重量份数计包括下列组分:聚氯乙烯树脂25份、氨基树脂30份、气相二氧化硅5份、环氧类增塑剂12份、聚乙烯蜡5份、群青蓝3份、消泡剂1份、纳米碳酸钙15份。
其制备工艺步骤如下:
(1)按重量分数称取原料配方中的材料;
(2)将聚氯乙烯树脂、氨基树脂、气相二氧化硅加入反应釜中,在40℃下搅拌1小时,搅拌速度200转/分钟,冷却至常温,得基胶;
(3)取聚乙烯蜡加入基胶中,在70℃下搅拌混合2小时,搅拌速度300转/分钟;将其余原料加入基胶中,在75℃下保温搅拌30分钟,搅拌速度400转/分钟,搅拌均匀,即得易剥离型可剥蓝胶。
实施例2
本发明的易剥离型可剥蓝胶,按重量份数计包括下列组分:聚氯乙烯树脂35份、氨基树脂20份、有机膨润土14份、柠檬酸酯类增塑剂2份、四氟乙烯蜡浆14份、钴蓝9份、消泡剂6份、纳米滑石粉8份。
其制备工艺步骤如下:
(1)按重量分数称取原料配方中的材料;
(2)将聚氯乙烯树脂、氨基树脂、有机膨润土加入反应釜中,在60℃下搅拌3小时,搅拌速度400转/分钟,冷却至常温,得基胶;
(3)取四氟乙烯蜡浆加入基胶中,在80℃下搅拌混合4小时,搅拌速度600转/分钟;将其余原料加入基胶中,在85℃下保温搅拌60分钟,搅拌速度600转/分钟,搅拌均匀,即得易剥离型可剥蓝胶。
实施例3
本发明的易剥离型可剥蓝胶,按重量份数计包括下列组分:聚氯乙烯树脂29份、氨基树脂25份、氢化蓖麻油9份、聚酯类增塑剂7份、聚二甲基硅氧烷10份、酞菁蓝6份、消泡剂3份、纳米硫酸钡12份。
其制备工艺步骤如下:
(1)按重量分数称取原料配方中的材料;
(2)将聚氯乙烯树脂、氨基树脂、触变剂加入反应釜中,在50℃下搅拌1~3小时,搅拌速度300转/分钟,冷却至常温,得基胶;
(3)取剥离力改性剂加入基胶中,在75℃下搅拌混合3小时,搅拌速度450转/分钟;将其余原料加入基胶中,在80℃下保温搅拌40分钟,搅拌速度500转/分钟,搅拌均匀,即得易剥离型可剥蓝胶。
实施例4
本发明的易剥离型可剥蓝胶,按重量份数计包括下列组分:聚氯乙烯树脂25份、氨基树脂27份、聚酰胺蜡11份、柠檬酸酯类增塑剂5份、聚乙烯蜡14份、酞菁蓝3份、消泡剂3份、纳米硫酸钡11份。
其制备工艺步骤如下:
(1)按重量分数称取原料配方中的材料;
(2)将聚氯乙烯树脂、氨基树脂、触变剂加入反应釜中,在40℃下搅拌3小时,搅拌速度400转/分钟,冷却至常温,得基胶;
(3)取剥离力改性剂加入基胶中,在80℃下搅拌混合3小时,搅拌速度400转/分钟;将其余原料加入基胶中,在75℃下保温搅拌40分钟,搅拌速度500转/分钟,搅拌均匀,即得易剥离型可剥蓝胶。
性能测试
本发明的主要技术性能如表1所示:
表1
从表1可见,本发明制备的易剥离型可剥蓝胶,具有粘结强度适中、易剥离、拉伸强度高的优点。
以上对本发明的具体实施例进行了描述。需要理解的是,本发明并不局限于上述特定实施方式,本领域技术人员可以在权利要求的范围内做出各种变形或修改,这并不影响本发明的实质内容。
Claims (7)
1.一种易剥离型可剥蓝胶,其特征在于,按重量份数计包括下列组分:聚氯乙烯树脂25~35份、氨基树脂20~30份、触变剂5~14份、低粘度增塑剂2~12份、剥离力改性剂5~14份、颜料3~9份、消泡剂1~6份、纳米填料8~15份。
2.根据权利要求1所述的易剥离型可剥蓝胶,其特征在于:所述触变剂为气相二氧化硅、有机膨润土、氢化蓖麻油、聚酰胺蜡中的任意一种。
3.根据权利要求1所述的易剥离型可剥蓝胶,其特征在于:所述低粘度增塑剂为环氧类增塑剂、柠檬酸酯类增塑剂、聚酯类增塑剂中的任意一种。
4.根据权利要求1所述的易剥离型可剥蓝胶,其特征在于:所述剥离力改性剂为聚乙烯蜡、四氟乙烯蜡浆、聚二甲基硅氧烷中的任意一种。
5.根据权利要求1所述的易剥离型可剥蓝胶,其特征在于:所述颜料为群青蓝、钴蓝、酞菁蓝中的任意一种。
6.根据权利要求1所述的易剥离型可剥蓝胶,其特征在于:所述纳米填料为纳米碳酸钙、纳米滑石粉、纳米硫酸钡中的任意一种。
7.一种如权利要求1所述的易剥离型可剥蓝胶的制备方法,其特征在于,包括以下步骤:
(1)按重量分数称取原料配方中的材料;
(2)将聚氯乙烯树脂、氨基树脂、触变剂加入反应釜中,在40~60℃下搅拌1~3小时,搅拌速度200~400转/分钟,冷却至常温,得基胶;
(3)取剥离力改性剂加入基胶中,在70~80℃下搅拌混合2~4小时,搅拌速度300~600转/分钟;将其余原料加入基胶中,在75~85℃下保温搅拌30~60分钟,搅拌速度400~600转/分钟,搅拌均匀,即得易剥离型可剥蓝胶。