CN104927719A - 一种新型的耐高温可剥胶及其制备方法 - Google Patents

一种新型的耐高温可剥胶及其制备方法 Download PDF

Info

Publication number
CN104927719A
CN104927719A CN201410096000.6A CN201410096000A CN104927719A CN 104927719 A CN104927719 A CN 104927719A CN 201410096000 A CN201410096000 A CN 201410096000A CN 104927719 A CN104927719 A CN 104927719A
Authority
CN
China
Prior art keywords
peelable glue
preparation
high temperature
temperature resistant
resistant peelable
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410096000.6A
Other languages
English (en)
Inventor
邢槐泽
邢孔球
邢孔繁
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ge Laite Printing Material Co Ltd Of Shenzhen
Original Assignee
Ge Laite Printing Material Co Ltd Of Shenzhen
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ge Laite Printing Material Co Ltd Of Shenzhen filed Critical Ge Laite Printing Material Co Ltd Of Shenzhen
Priority to CN201410096000.6A priority Critical patent/CN104927719A/zh
Publication of CN104927719A publication Critical patent/CN104927719A/zh
Pending legal-status Critical Current

Abstract

一种新型的耐高温可剥胶及其制备方法，它涉及OGS工艺中各个制程加工保护的可剥胶制备工艺技术领域。耐高温可剥胶按质量比的原料组成为：氯醋树脂60％-65％、环氧树脂10％-12％、甲阶酚醛树脂8％-10％、邻苯二甲酸酯7％-9％、硬脂酸钡1％-2％、磷酸三苯酯1％-3％、碳酸钙1％-2％、二氧化硅1％-2％、酞菁蓝0.5％-1％、消泡剂0.13％-0.21％、流平剂0.1％-0.3％。它具有成膜强度好，耐高温，断裂伸长小等特点，适用范围比较广泛，特别是OGS工艺中切割、精雕、印刷、镀膜等工序的保护，满足了一些高技术领域耐高温性及强度、韧性等综合性能的高要求。

Description

一种新型的耐高温可剥胶及其制备方法
技术领域：
本发明涉及OGS工艺中各个制程加工保护的可剥胶制备工艺技术领域，尤其涉及一种新型的耐高温可剥胶及其制备方法。
背景技术：
耐高温可剥胶应用非常普遍，在航天、航空、机械、电子、医疗等领域得到了广泛的应用，但在运用中存在着韧性较差、固化物脆性大、耐冲击性和振动性差，容易开裂等缺陷，作为结构粘接剂，必须进行必要的改性增韧，才能满足其特殊的技术工艺要求，目前的耐高温可剥胶技术有很多种，虽然强度和韧性得到了较大的提高，但是其耐热性能的改善仍然不够，难以同时满足一些高技术领域耐高温性及强度、韧性等综合性能的高要求。
发明内容：
本发明的目的是提供一种新型的耐高温可剥胶及其制备方法，它具有成膜强度好，耐高温，断裂伸长小等特点，适用范围比较广泛，特别是OGS工艺中切割、精雕、印刷、镀膜等工序的保护，满足了一些高技术领域耐高温性及强度、韧性等综合性能的高要求。
为了解决背景技术所存在的问题，本发明是采用以下技术方案：耐高温可剥胶按质量比的原料组成为：氯醋树脂60％-65％、环氧树脂10％-12％、甲阶酚醛树脂8％-10％、邻苯二甲酸酯7％-9％、硬脂酸钡1％-2％、磷酸三苯酯1％-3％、碳酸钙1％-2％、二氧化硅1％-2％、酞菁蓝0.5％-1％、消泡剂0.13％-0.21％、流平剂0.1％-0.3％。
所述的消泡剂采用聚醚类消泡剂。
所述的流平剂采用聚丙烯酸类流平剂。
本发明耐高温可剥胶的制备方法：将氯醋树脂加热至110-130℃回流脱水0.5-1.5h，降温至50-55℃，加入环氧树脂、甲阶酚醛树脂和邻苯二甲酸酯，缓慢升温至65-75℃，保温并匀速搅拌反应1.5-2.5小时，然后加入碳酸钙、二氧化硅和酞菁蓝，搅拌均匀后用三辊研磨机研磨四次，在研磨后的物料中加入硬脂酸钡和甲阶酚醛树脂，用行星搅拌机在90-110℃条件下搅拌并保温0.5-2小时，搅拌均匀后加入消泡剂进行消泡处理，最后加入流平剂在干燥成膜过程中形成一个平整、光滑、均匀的涂膜。
本发明具有成膜强度好，耐高温，断裂伸长小等特点，适用范围比较广泛，特别是OGS工艺中切割、精雕、印刷、镀膜等工序的保护，满足了一些高技术领域耐高温性及强度、韧性等综合性能的高要求。具体实施方式：
本具体实施方式采用以下技术方案：耐高温可剥胶按质量比的原料组成为：氯醋树脂60％-65％、环氧树脂10％-12％、甲阶酚醛树脂8％-10％、邻苯二甲酸酯7％-9％、硬脂酸钡1％-2％、磷酸三苯酯1％-3％、碳酸钙1％-2％、二氧化硅1％-2％、酞菁蓝0.5％-1％、消泡剂0.13％-0.21％、流平剂0.1％-0.3％。
所述的消泡剂采用聚醚类消泡剂。
所述的流平剂采用聚丙烯酸类流平剂。
本具体实施方式耐高温可剥胶的制备方法：将氯醋树脂加热至110-130℃回流脱水0.5-1.5h，降温至50-55℃，加入环氧树脂、甲阶酚醛树脂和邻苯二甲酸酯，缓慢升温至65-75℃，保温并匀速搅拌反应1.5-2.5小时，然后加入碳酸钙、二氧化硅和酞菁蓝，搅拌均匀后用三辊研磨机研磨四次，在研磨后的物料中加入硬脂酸钡和甲阶酚醛树脂，用行星搅拌机在90-110℃条件下搅拌并保温0.5-2小时，搅拌均匀后加入消泡剂进行消泡处理，最后加入流平剂在干燥成膜过程中形成一个平整、光滑、均匀的涂膜。
本具体实施方式具有成膜强度好，耐高温，断裂伸长小等特点，适用范围比较广泛，特别是OGS工艺中切割、精雕、印刷、镀膜等工序的保护，满足了一些高技术领域耐高温性及强度、韧性等综合性能的高要求。

Claims (4)

1.一种新型的耐高温可剥胶及其制备方法，其特征在于耐高温可剥胶按质量比的原料组成为：氯醋树脂60％-65％、环氧树脂10％-12％、甲阶酚醛树脂8％-10％、邻苯二甲酸酯7％-9％、硬脂酸钡1％-2％、磷酸三苯酯1％-3％、碳酸钙1％-2％、二氧化硅1％-2％、酞菁蓝0.5％-1％、消泡剂0.13％-0.21％、流平剂0.1％-0.3％。
2.根据权利要求1所述的一种新型的耐高温可剥胶及其制备方法，其特征在于所述的消泡剂采用聚醚类消泡剂。
3.根据权利要求1所述的一种新型的耐高温可剥胶及其制备方法，其特征在于所述的流平剂采用聚丙烯酸类流平剂。
4.根据权利要求1所述的一种新型的耐高温可剥胶及其制备方法，其特征在于耐高温可剥胶的制备方法：将氯醋树脂加热至110-130℃回流脱水0.5-1.5h，降温至50-55℃，加入环氧树脂、甲阶酚醛树脂和邻苯二甲酸酯，缓慢升温至65-75℃，保温并匀速搅拌反应1.5-2.5小时，然后加入碳酸钙、二氧化硅和酞菁蓝，搅拌均匀后用三辊研磨机研磨四次，在研磨后的物料中加入硬脂酸钡和甲阶酚醛树脂，用行星搅拌机在90-110℃条件下搅拌并保温0.5-2小时，搅拌均匀后加入消泡剂进行消泡处理，最后加入流平剂在干燥成膜过程中形成一个平整、光滑、均匀的涂膜。
CN201410096000.6A 2014-03-17 2014-03-17 一种新型的耐高温可剥胶及其制备方法 Pending CN104927719A (zh)