CN103965747B - 一种含有纳米凹凸棒土散热涂料 - Google Patents

一种含有纳米凹凸棒土散热涂料 Download PDF

Info

Publication number
CN103965747B
CN103965747B CN201410195189.4A CN201410195189A CN103965747B CN 103965747 B CN103965747 B CN 103965747B CN 201410195189 A CN201410195189 A CN 201410195189A CN 103965747 B CN103965747 B CN 103965747B
Authority
CN
China
Prior art keywords
raw material
attapulgite
heat radiation
prepared
nano
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410195189.4A
Other languages
English (en)
Other versions
CN103965747A (zh
Inventor
李峰
郑志龙
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Fuhe Packaging Technology Co.,Ltd.
Original Assignee
ANHUI MENGNIU COLOR PRINTING PACKAGING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI MENGNIU COLOR PRINTING PACKAGING Co Ltd filed Critical ANHUI MENGNIU COLOR PRINTING PACKAGING Co Ltd
Priority to CN201410195189.4A priority Critical patent/CN103965747B/zh
Publication of CN103965747A publication Critical patent/CN103965747A/zh
Application granted granted Critical
Publication of CN103965747B publication Critical patent/CN103965747B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种附着性能佳的含有纳米凹凸棒土散热涂料，其是由下述重量份的原料制得：A料40-50、B料30-40；所述的A料由下述重量份的原料制得：乙酸乙酯30-40、酮醛树脂1-2、二苯胺2-3、戊二酸二甲酯1-2、石油磺酸钙1-2、NP-10 0.1-0.2、玻璃纤维1-2、癸二酸二辛酯1-2、纳米凹凸棒土2-4；本发明原料含有纳米凹凸棒土，颗粒粒径小，同时经过研磨，使得本发明的涂膜附着性能佳，快干，不易脱落。

Description

一种含有纳米凹凸棒土散热涂料
技术领域
本发明涉及散热涂料领域，确切地说是一种含有纳米凹凸棒土散热涂料。
背景技术
散热涂料是一种提高物体表面的散热效率，降低体系温度的特种涂料现有散热涂料功能单一，无法满足人们的多种需求。
发明内容
本发明的目的在于提供一种含有纳米凹凸棒土散热涂料。
上述目的通过以下方案实现：
一种含有纳米凹凸棒土散热涂料，其特征在于：其是由下述重量份的原料制得：
A料40-50、B料30-40；
所述的A料由下述重量份的原料制得：
乙酸乙酯30-40、酮醛树脂1-2、二苯胺2-3、戊二酸二甲酯1-2、石油磺酸钙1-2、NP-100.1-0.2、玻璃纤维1-2、癸二酸二辛酯1-2、纳米凹凸棒土2-4；
所述的B料由下述重量份的原料制得：
丙二醇4-6、环氧丙烯酸树脂50-60、乙酸正丁酯1-2、抗氧剂6263-5、二丁基二月桂酸锡1-2、抗氧剂10761-2，氮化铝1-2、水杨酸1-2、胺类固化剂1-2、醋酸丁酯0.2-0.3、抗氧剂10101-2、硅烷偶联剂DL6021.4-2.5。
所述的一种含有纳米凹凸棒土散热涂料，其特征在于：制备方法包括以下步骤：
(1)将A料各原料混合均匀，加热至55-60℃，在400-500r/min的速度下搅拌反应1-2小时，研磨1-2小时后得A料备用；
(2)将B料各原料混合均匀，加热至50-70℃，在700-800r/min的速度下搅拌反应1-2小时，得B料备用；
(3)将A料、B料按重量份混合搅拌均匀，加热至40-50℃，在600-700r/min的速度下搅拌20-30分钟后，即得。
施工时，散热涂料喷涂施工，在60℃下烘干1小时，即可成膜，制成80-100μm散热涂层。
本发明的有益效果为：本发明原料含有纳米凹凸棒土，颗粒粒径小，同时经过研磨，使得本发明的涂膜附着性能佳，快干，不易脱落。
具体实施方式
一种含有纳米凹凸棒土散热涂料，其是由下述重量kg的原料制得：
A料50、B料30；
所述的A料由下述重量kg的原料制得：
乙酸乙酯40、酮醛树脂1、二苯胺3、戊二酸二甲酯2、石油磺酸钙2、NP-100.2、玻璃纤维2、癸二酸二辛酯2、纳米凹凸棒土4；
所述的B料由下述重量kg的原料制得：
丙二醇6、环氧丙烯酸树脂60、乙酸正丁酯2、抗氧剂6265、二丁基二月桂酸锡2、抗氧剂10762，氮化铝2、水杨酸2、胺类固化剂2、醋酸丁酯0.3、抗氧剂10101、硅烷偶联剂DL6021.5。
所述的一种含有纳米凹凸棒土散热涂料，制备方法包括以下步骤：
(1)将A料各原料混合均匀，加热至60℃，在500r/min的速度下搅拌反应2小时，研磨2小时后得A料备用；
(2)将B料各原料混合均匀，加热至70℃，在800r/min的速度下搅拌反应2小时，得B料备用；
(3)将A料、B料按重量份混合搅拌均匀，加热至50℃，在600r/min的速度下搅拌30分钟后，即得。
施工时，散热涂料喷涂施工，在60℃下烘干1小时，即可成膜，制成80-100μm散热涂层。
将实施例制得的散热涂料直接喷涂于经过清洗干净的玻璃灯具上，得到下述实验数据：
耐温测试：烘箱烘烤210℃/3h后，烘箱烘烤145℃/15天后玻璃灯具上涂料色泽无明显变化；
抗紫外线测试：紫外线照射4.5h，涂料不脱粉不发黄，在135℃和270W紫外光辐照条件下人工加速老化试验，耐老化时间5350小时；
耐温高温270℃，粘结剪切力21.2MPa，导热系数341W/(m·K)。

Claims (2)

1.一种含有纳米凹凸棒土散热涂料，其特征在于：其是由下述重量份的原料制得：
A料40-50、B料30-40；
所述的A料由下述重量份的原料制得：
乙酸乙酯30-40、酮醛树脂1-2、二苯胺2-3、戊二酸二甲酯1-2、石油磺酸钙1-2、NP-100.1-0.2、玻璃纤维1-2、癸二酸二辛酯1-2、纳米凹凸棒土2-4；
所述的B料由下述重量份的原料制得：
丙二醇4-6、环氧丙烯酸树脂50-60、乙酸正丁酯1-2、抗氧剂6263-5、二丁基二月桂酸锡1-2、抗氧剂10761-2，氮化铝1-2、水杨酸1-2、胺类固化剂1-2、醋酸丁酯0.2-0.3、抗氧剂10101-2、硅烷偶联剂DL6021.4-2.5。
2.根据权利要求1所述的含有纳米凹凸棒土散热涂料，其特征在于：制备方法包括以下步骤：
（1）将A料各原料混合均匀，加热至55-60℃，在400-500r/min的速度下搅拌反应1-2小时，研磨1-2小时后得A料备用；
（2）将B料各原料混合均匀，加热至50-70℃，在700-800r/min的速度下搅拌反应1-2小时，得B料备用；
(3)将A料、B料按重量份混合搅拌均匀，加热至40-50℃，在600-700r/min的速度下搅拌20-30分钟后，即得。
CN201410195189.4A 2014-05-09 2014-05-09 一种含有纳米凹凸棒土散热涂料 Active CN103965747B (zh)