CN102417787A - 一种覆盖电容器铝壳涂料及其制备方法 - Google Patents
一种覆盖电容器铝壳涂料及其制备方法 Download PDFInfo
- Publication number
- CN102417787A CN102417787A CN2011103297092A CN201110329709A CN102417787A CN 102417787 A CN102417787 A CN 102417787A CN 2011103297092 A CN2011103297092 A CN 2011103297092A CN 201110329709 A CN201110329709 A CN 201110329709A CN 102417787 A CN102417787 A CN 102417787A
- Authority
- CN
- China
- Prior art keywords
- compsn
- paint
- capacitor
- stirrer
- silane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种覆盖电容器铝壳涂料及其制备方法,其主要是将组成原料中组合物A和组合物B按一定重量份混合搅拌得到,组合物A由聚氨酯多元醇、甲酮、异丙醇、聚甲基苯烯酸甲酯、乙酸乙酯和凹凸棒土构成;组合物B由聚氯乙烯树脂、聚二甲基硅氧烷、丙烯酸酯类共聚物改性剂、钛白粉、二氧化钛、秸秆灰烬、硅烷偶联剂、云母和硅烷构成。本发明配方合理,制备方法简单,在电容器铝壳上固化效果好,有效的进行保护电容器,制得的覆膜涂料具有耐热耐磨性能、增加了电容器的使用寿命。
Description
技术领域
本发明涉及电容器外壳及化学组合物,具体涉及一种覆盖电容器铝壳涂料及其制备方法。
背景技术
随着电子行业技术的进步,电子线路板的制造技术也有很大的进步,为了缩小电子产品的体积和降低消耗,电解电容器作为电子线路板上的通用元件之一,不仅对它的耐温、耐击穿要求是越来越高,而且要求其占位面积也是越小越好。电解电容器占位面积要小,首先是电容器铝壳要有高的长径比,电容器直径小占位面积就小;其次是电容器外壳要有高的空气耐温性能,否则在紧凑的空问中容易损坏而缩短使用寿命,传统的电容器铝壳是先冲制成形,后热缩封上一层绝缘材料,使绝缘材料经加热后紧紧裹在电容器外壳上。这种热缩性塑膜电容器其缺点是热封的绝缘材料耐空气温度不够高,在热封处理的过程中也会产生很多塑膜废料。也有中国台湾雅铂兴业股份有限公司公开的一种电解电容器铝壳体绝缘膜的涂覆方法,中国发明专利申请公开号CNl944704,该方法主要是采取1000~20000伏特的高电位差,使气体离子撞击特氟隆聚四氟乙烯(polytetrafluoroethylene),撞击出氟原子,同时氧化生成氧化氟,氧化氟在高温作用下即会产生强力粘着性,并沉积于铝壳体表面上黏覆而形成氧化氟的绝缘皮膜层。这个方法实际上仅是减少了的含氯覆料的二次污染,但还是存在着耐温性差、生产成本较高的问题。
发明内容
为了缓解现有技术的不足和缺陷,本发明的目的在于提供一种覆盖电容器铝壳涂料及其制备方法,本发明配方合理,制备方法简单,在电容器铝壳上固化效果好,有效的进行保护电容器,制得的覆膜涂料具有耐热耐磨性能、增加了电容器的使用寿命。
为了实现上述目的本发明采用如下技术方案:
覆盖电容器铝壳涂料,其特征在于其组成原料的重量份为:包括组合物A和组合物B,所述的组合物A:聚氨酯多元醇60-70份、甲酮20-30份、异丙醇15-25份、聚甲基苯烯酸甲酯15-25份、乙酸乙酯15-25份和凹凸棒土10-15份;所述的组合物B:聚氯乙烯树脂20-30份、聚二甲基硅氧烷5-10份、丙烯酸酯类共聚物改性剂5-10份、钛白粉5-10份、二氧化钛5-10份、秸秆灰烬5-10份、硅烷偶联剂5-10份、云母5-10份和硅烷5-10份。
所述的覆盖电容器铝壳涂料的制备方法,其特征在于包括以下步骤:
(1)按组成原料的重量份称取各原料,将聚氨酯多元醇、甲酮、异丙醇、聚甲基苯烯酸甲酯、乙酸乙酯和凹凸棒土加入搅拌机中,常温下搅拌30-45分钟,混合均匀得到组合物A,再将聚氯乙烯树脂、聚二甲基硅氧烷、丙烯酸酯类共聚物改性剂、钛白粉、二氧化钛、秸秆灰烬、硅烷偶联剂、云母和硅烷加入搅拌机中,常温下搅拌30-45分钟,混合均匀得到组合物B;
(2)将组合物A和组合物B加入搅拌机中,混合均匀,搅拌机中溶液搅拌至透明溶液。
本发明的有益效果:
本发明配方合理,制备方法简单,在电容器铝壳上固化效果好,有效的进行保护电容器,制得的覆膜涂料具有耐热耐磨性能、增加了电容器的使用寿命。
具体实施方式
实施例1:覆盖电容器铝壳涂料,其特征在于其组成原料的重量份为:包括组合物A和组合物B,所述的组合物A:聚氨酯多元醇60份、甲酮20份、异丙醇15份、聚甲基苯烯酸甲酯15份、乙酸乙酯15份和凹凸棒土10份;所述的组合物B:聚氯乙烯树脂20份、聚二甲基硅氧烷5份、丙烯酸酯类共聚物改性剂5份、钛白粉5份、二氧化钛5份、秸秆灰烬5份、硅烷偶联剂5份、云母5份和硅烷5份。
覆盖电容器铝壳涂料的制备方法,包括以下步骤:
(1)按组成原料的重量份称取各原料,将聚氨酯多元醇、甲酮、异丙醇、聚甲基苯烯酸甲酯、乙酸乙酯和凹凸棒土加入搅拌机中,常温下搅拌30-45分钟,混合均匀得到组合物A,再将聚氯乙烯树脂、聚二甲基硅氧烷、丙烯酸酯类共聚物改性剂、钛白粉、二氧化钛、秸秆灰烬、硅烷偶联剂、云母和硅烷加入搅拌机中,常温下搅拌30-45分钟,混合均匀得到组合物B;
(2)将组合物A和组合物B加入搅拌机中,混合均匀,搅拌机中溶液搅拌至透明溶液。
涂布铝壳时,铝壳需要用添加NaOH的热水清洗,NaOH浓度为4-6%,清洗后放置160-180℃干燥氧化1-2分钟,然后将上述制得的覆盖电容器铝壳涂料在室温的环境下均匀涂布到预处理的铝板表面上,然后将铝板放置210-220℃的环境下固化,固化至少1分钟。
实施例2:覆盖电容器铝壳涂料,其组成原料的重量份为:包括组合物A和组合物B,所述的组合物A:聚氨酯多元醇70份、甲酮30份、异丙醇25份、聚甲基苯烯酸甲酯25份、乙酸乙酯25份和凹凸棒土15份;所述的组合物B:聚氯乙烯树脂30份、聚二甲基硅氧烷10份、丙烯酸酯类共聚物改性剂10份、钛白粉10份、二氧化钛10份、秸秆灰烬10份、硅烷偶联剂10份、云母10份和硅烷10份。
覆盖电容器铝壳涂料的制备方法,包括以下步骤:
(1)按组成原料的重量份称取各原料,将聚氨酯多元醇、甲酮、异丙醇、聚甲基苯烯酸甲酯、乙酸乙酯和凹凸棒土加入搅拌机中,常温下搅拌30-45分钟,混合均匀得到组合物A,再将聚氯乙烯树脂、聚二甲基硅氧烷、丙烯酸酯类共聚物改性剂、钛白粉、二氧化钛、秸秆灰烬、硅烷偶联剂、云母和硅烷加入搅拌机中,常温下搅拌30-45分钟,混合均匀得到组合物B;
(2)将组合物A和组合物B加入搅拌机中,混合均匀,搅拌机中溶液搅拌至透明溶液。
涂布铝壳时,铝壳需要用添加NaOH的热水清洗,NaOH浓度为4-6%,清洗后放置160-180℃干燥氧化1-2分钟,然后将上述制得的覆盖电容器铝壳涂料在室温的环境下均匀涂布到预处理的铝板表面上,然后将铝板放置210-220℃的环境下固化,固化至少1分钟。
实施例3:涂有实施例1与实施例2的覆盖电容器铝壳涂料,其中的固化温度、时间及所得覆膜铝壳制成的电容器覆膜铝壳技术指标为:
实施例1 | 实施例2 | |
固化温度(℃) | 215 | 215 |
固化时间(s) | 60 | 60 |
要求指标 | 符合 | 符合 |
长径比 | 3.4:1 | 3.6:1 |
Claims (2)
1.一种覆盖电容器铝壳涂料,其特征在于其组成原料的重量份为:包括组合物A和组合物B,所述的组合物A:聚氨酯多元醇60-70份、甲酮20-30份、异丙醇15-25份、聚甲基苯烯酸甲酯15-25份、乙酸乙酯15-25份和凹凸棒土10-15份;所述的组合物B:聚氯乙烯树脂20-30份、聚二甲基硅氧烷5-10份、丙烯酸酯类共聚物改性剂5-10份、钛白粉5-10份、二氧化钛5-10份、秸秆灰烬5-10份、硅烷偶联剂5-10份、云母5-10份和硅烷5-10份。
2.一种如权利要求1所述的覆盖电容器铝壳涂料的制备方法,其特征在于包括以下步骤:
(1)按组成原料的重量份称取各原料,将聚氨酯多元醇、甲酮、异丙醇、聚甲基苯烯酸甲酯、乙酸乙酯和凹凸棒土加入搅拌机中,常温下搅拌30-45分钟,混合均匀得到组合物A,再将聚氯乙烯树脂、聚二甲基硅氧烷、丙烯酸酯类共聚物改性剂、钛白粉、二氧化钛、秸秆灰烬、硅烷偶联剂、云母和硅烷加入搅拌机中,常温下搅拌30-45分钟,混合均匀得到组合物B;
(2)将组合物A和组合物B加入搅拌机中,混合均匀,搅拌机中溶液搅拌至透明溶液。