CN103013236A - 工业漆用对颜料分散性优异丙烯酸树脂及其制备方法 - Google Patents

工业漆用对颜料分散性优异丙烯酸树脂及其制备方法 Download PDF

Info

Publication number
CN103013236A
CN103013236A CN2012104686980A CN201210468698A CN103013236A CN 103013236 A CN103013236 A CN 103013236A CN 2012104686980 A CN2012104686980 A CN 2012104686980A CN 201210468698 A CN201210468698 A CN 201210468698A CN 103013236 A CN103013236 A CN 103013236A
Authority
CN
China
Prior art keywords
acrylic resin
pigment
hours
initiator
industrial paint
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012104686980A
Other languages
English (en)
Other versions
CN103013236B (zh
Inventor
薛正彪
宋坤宗
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGMEN SANMU CHEMICAL Co Ltd
Original Assignee
Jiangsu Sanmu Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Sanmu Chemical Co Ltd filed Critical Jiangsu Sanmu Chemical Co Ltd
Priority to CN201210468698.0A priority Critical patent/CN103013236B/zh
Publication of CN103013236A publication Critical patent/CN103013236A/zh
Application granted granted Critical
Publication of CN103013236B publication Critical patent/CN103013236B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供了一种工业漆用的对颜料分散性优异丙烯酸树脂，属于高分子技术领域。由按照重量百分比计的37%～40%单体、7.5%～10%丙烯酸丁酯、0.5%～2%甲基丙烯酸二甲胺乙酯、0.5%～2%引发剂、0.5%～1%丙烯酸、有机溶剂50%作为原料制成，所述的单体为苯乙烯或甲基丙烯酸甲酯。本发明提供的工业漆用的丙烯酸树脂，应用于涂料、油漆中时，其对于颜料的分散性能好，所得油漆细度小。

Description

工业漆用对颜料分散性优异丙烯酸树脂及其制备方法
技术领域
本发明提供了一种异丙烯酸树脂，特别涉及一种工业漆用的对颜料分散性优异丙烯酸树脂，属于高分子技术领域。
背景技术
常用丙烯酸树脂对炭黑、酞青兰等颜料分散性比较差，在涂料制造过程中主要使用迪高、埃夫科纳等涂料助剂公司生产的颜料润湿分散剂达来增加颜料的分散性，增加了成本和操作步骤。
发明内容
本发明需要解决的技术问题是：提供一种具有良好的对颜料分散性能的丙烯酸树脂。采用的技术方案是：
一种工业漆用对颜料分散性优异丙烯酸树脂，由按照重量百分比计的37%～40%单体、7.5%～10%丙烯酸丁酯、0.5%～2%甲基丙烯酸二甲胺乙酯、0.5%～2%引发剂、0.5%～1%丙烯酸、有机溶剂50%组成，所述的单体为苯乙烯或甲基丙烯酸甲酯。
上述的有机溶剂可以采用甲苯或醋酸丁酯中至少一种。
上述的引发剂可以采用过氧化二苯甲酰或偶氮二异丁氰。
制备方法是：
S1：将单体、丙烯酸、丙烯酸丁酯、甲基丙烯酸二甲氨基乙酯、85～95%总量的引发剂混合均匀；
S2：把有机溶剂投入反应釜，升温回流并保持10～20分钟
S3：滴加步骤S1所得混合物，在2.5～3小时内滴加完毕，并在回流状态下保持1.5～2.5小时
S4：在反应釜中加入剩余引发剂，并在回流状态下保持1.5～2.5小时，放冷，即可。
本发明提供的工业漆用的丙烯酸树脂，应用于涂料、油漆中时，其对于颜料的分散性能好，所得油漆细度小。
具体实施方式
实施例1
表1原料组成
组分 重量（g）
甲苯 30
醋酸丁酯 20
苯乙烯 37
丙烯酸 1
丙烯酸丁酯 8
过氧化二苯甲酰 2
甲基丙烯酸二甲胺乙酯 2
制备方法:把20克醋酸丁酯和30克甲苯投入反应器，把苯乙烯37克、丙烯酸1克、丙烯酸丁酯8克、甲级丙烯酸二甲氨基乙酯2克、引发剂1.8克（总量的90%）混合均匀放入滴加漏斗。溶剂回流15分钟后开始滴加混合单体，在2.5到3小时以内均匀滴加完毕。滴完后保持回流状态2小时。补加引发剂0.2克（总量的10%），再保持回流2小时后出料。
实施例2
表2原料组成
组分 重量（g）
甲苯 50
甲基丙烯酸甲酯 40
丙烯酸 0.5
丙烯酸丁酯 7.5
过氧化二苯甲酰 1.5
甲基丙烯酸二甲胺乙酯 0.5
制备方法:把50克甲苯投入反应器，把甲基丙烯酸甲酯40克、丙烯酸0.5克、过氧化二苯甲酰1.35克、丙烯酸丁酯7.5克、甲级丙烯酸二甲氨基乙酯0.5克、混合均匀放入滴加漏斗。溶剂回流15分钟后开始滴加混合单体，在2.5到3小时以内均匀滴加完毕。滴完后保持回流状态2小时。补加过氧化二苯甲酰0.15克，再保持回流2小时后出料。
实施例3
表3原料组成
组分 重量（g）
醋酸丁酯 50
甲基丙烯酸甲酯 38.5
丙烯酸 0.5
丙烯酸丁酯 10
过氧化二苯甲酰 0.5
甲基丙烯酸二甲胺乙酯 0.5
制备方法:把50克醋酸丁酯投入反应器，把甲基丙烯酸甲酯38.5克、丙烯酸0.5克、过氧化二苯甲酰0.45克、丙烯酸丁酯10克、甲级丙烯酸二甲氨基乙酯0.5克、混合均匀放入滴加漏斗。溶剂回流15分钟后开始滴加混合单体，在2.5小时到3小时以内均匀滴加完毕。滴完后保持回流状态1.5小时。补加过氧化二苯甲酰0.05克，再保持回流1.5小时后出料。实施例4
表4原料组成
组分 重量（g）
甲苯 50
甲基丙烯酸甲酯 37
丙烯酸 1
丙烯酸丁酯 9
偶氮二异丁氰 2
甲基丙烯酸二甲胺乙酯 1
制备方法:把50克甲苯投入反应器，把甲基丙烯酸甲酯40克、丙烯酸1克、偶氮二异丁氰1.8克、丙烯酸丁酯9克、甲级丙烯酸二甲氨基乙酯1克、混合均匀放入滴加漏斗。溶剂回流15分钟后开始滴加混合单体，在2.5到3小时以内均匀滴加完毕。滴完后保持回流状态2.5小时。补加偶氮二异丁氰0.2克，再保持回流2.5小时后出料。
实施例5
表5原料组成
组分 重量（g）
甲苯 50
甲基丙烯酸甲酯 37
丙烯酸 0.9
丙烯酸丁酯 8.9
偶氮二异丁氰 2
甲基丙烯酸二甲胺乙酯 1.1
制备方法:把50克甲苯投入反应器，把甲基丙烯酸甲酯37克、丙烯酸0.9克、偶氮二异丁氰1.8克、丙烯酸丁酯8.9克、甲级丙烯酸二甲氨基乙酯1.1克、混合均匀放入滴加漏斗。溶剂回流15分钟后开始滴加混合单体，在2.5到3小时以内均匀滴加完毕。滴完后保持回流状态2小时。补加偶氮二异丁氰0.2克，再保持回流2小时后出料。
实施例6对照例
表6原料组成
组分 重量（g）
甲苯 50
甲基丙烯酸甲酯 40
丙烯酸 0.5
丙烯酸丁酯 8
过氧化二苯甲酰 1.5
制备方法：把50克甲苯投入反应器，把甲基丙烯酸甲酯40克、丙烯酸0.5克、过氧化二苯甲酰1.35克、丙烯酸丁酯8克、混合均匀放入滴加漏斗。溶剂回流15分钟后开始滴加混合单体，在2.5到3小时以内均匀滴加完毕。滴完后保持回流状态2小时。补加过氧化二苯甲酰0.15克，再保持回流2小时后出料。
实施例7丙烯酸树脂在油漆中的应用
表7油漆原料组成
组分 重量（g）
丙烯酸树脂 65
AX3301消泡剂 0.2
炭黑 3
二甲苯 5.2
醋酸丁酯 5
乙二醇乙醚醋酸酯 3
对颜料分散性比较方法：中华人民共和国国家标准涂料细度测定法GB 1724-79
表8油漆性能检测表
检测指标 实施例1 实施例2 实施例3 实施例4 实施例5 实施例6 比较例
细度 小于10μm 小于10μm 小于10μm 小于10μm 小于10μm 小于10μm 大于25μm

Claims (4)

1.一种工业漆用对颜料分散性优异丙烯酸树脂，由按照重量百分比计的37%～40%单体、7.5%～10%丙烯酸丁酯、0.5%～2%甲基丙烯酸二甲胺乙酯、0.5%～2%引发剂、0.5%～1%丙烯酸、有机溶剂50%作为原料制成，所述的单体为苯乙烯或甲基丙烯酸甲酯。
2.根据权利要求1所述的工业漆用对颜料分散性优异丙烯酸树脂，其特征在于：所述的有机溶剂是甲苯或醋酸丁酯中至少一种。
3.根据权利要求1所述的工业漆用对颜料分散性优异丙烯酸树脂，其特征在于：所述的引发剂是过氧化二苯甲酰或偶氮二异丁氰。
4.一种权利要求1～3任一项所述的工业漆用对颜料分散性优异丙烯酸树脂的制备方法：包括下述步骤：
S1：将单体、丙烯酸、丙烯酸丁酯、甲基丙烯酸二甲氨基乙酯、85～95%总量的引发剂混合均匀；
S2：把有机溶剂投入反应釜，升温回流并保持10～20分钟
S3：滴加步骤S1所得混合物，在2.5～3小时内滴加完毕，并在回流状态下保持1.5～2.5小时
S4：在反应釜中加入剩余引发剂，并在回流状态下保持1.5～2.5小时，放冷，即可。
CN201210468698.0A 2012-11-19 2012-11-19 工业漆用对颜料分散性优异丙烯酸树脂及其制备方法 Expired - Fee Related CN103013236B (zh)