CN102898815A - 一种汽车发动机隔音垫专用软轻质pu泡沫板 - Google Patents
一种汽车发动机隔音垫专用软轻质pu泡沫板 Download PDFInfo
- Publication number
- CN102898815A CN102898815A CN201210379134XA CN201210379134A CN102898815A CN 102898815 A CN102898815 A CN 102898815A CN 201210379134X A CN201210379134X A CN 201210379134XA CN 201210379134 A CN201210379134 A CN 201210379134A CN 102898815 A CN102898815 A CN 102898815A
- Authority
- CN
- China
- Prior art keywords
- sound insulating
- insulating pad
- cystose
- engine sound
- motor car
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种汽车发动机隔音垫专用软轻质PU泡沫板，其特点是它由下述重量配比的原料制成，高分子量聚醚多元醇80-90份，多官能度聚醚10-20份，硅油1-2份、胺类催化剂0.4-1.2份、发泡剂10-20份、开孔剂1-2份、阻燃剂3-8份、石墨10-20份混合均匀制成A料，A料与粗MDI（异氰酸酯）100-120份进行反应发成大泡块，切片后制成软轻质PU泡沫板，其具有弹性密度在16~20Kg/m3,用于制作汽车发动机隔音垫，其密度低质轻，手感柔软，有弹性，热塑性宜成型，无气味，具有隔音、隔热、阻燃的作用。
Description
技术领域：
本发明涉及汽车发动机用聚氨酯发泡生产技术领域，具体地讲是一种汽车发动机隔音垫专用软轻质PU泡沫板。
背景技术：
传统的汽车内发动机隔音垫大都用废纺毡等制作而成，即废纺毡+黑色无纺布等经过模压、冲切制成为汽车发动机隔音垫，一般具有气味大、重量大、污染大等问题；国内也有用软质PU泡沫板+带胶膜的黑色无纺布制作汽车发动机隔音垫，这种软质PU泡沫板的密度一般大于35 Kg/m3并且容易变形。
随着生产技术的提高、汽车环保要求的提高及降低成本等的需求，新的材料越来越多的应用于汽车发动机隔音垫，其中低密度的软轻质PU泡沫板具有手感柔软有弹性、质轻吸音效果好、容易成型、低气味等优点，越来越受到重视，而目前国内制作密度小于35 Kg/m3的软轻质PU泡沫板的组合料为进口，生产成本较高。
发明内容：
本发明的目的是克服上述已有技术的不足，而提供一种汽车发动机隔音垫专用软轻质PU泡沫板，主要解决传统材料的密度高质量重、气味大、污染重、密度小于35 Kg/m3的软轻质PU泡沫板组合料需要进口等问题。
为了达到上述目的，本发明是这样实现的：一种汽车发动机隔音垫专用软轻质PU泡沫板，其特殊之处在于它由下述重量配比的原料制成，高分子量聚醚多元醇80-90份、多官能度聚醚10-20份，硅油1-2份、胺类催化剂0.4-1.2份、发泡剂 10-20份、开孔剂1-2份、阻燃剂TCPP 3-8份、石墨10-20份，粗MDI 100-120份，所述的软轻质PU泡沫板具有弹性密度在：16~20kg/m3。
本发明的一种汽车发动机隔音垫专用软轻质PU泡沫板，它由下述最佳重量配比的原料制成：高分子量聚醚多元醇80份、多官能度聚醚多元醇20份、硅油1.5份、胺类催化剂0.8份、发泡剂16份、开孔剂2份、阻燃剂TCPP 5份、石墨15份，粗MDI 105份。
其中，所述的高分子量聚醚多元醇的分子量为4500以上，高分子量聚醚多元醇为聚醚ZS-1618A、聚醚TEP-330N、聚醚TEP-3600、聚醚ZS-1406中的一种或两种以上混合。
其中，所述的硅油为：AK7731、B8110 、Y-10366中的一种或两种混合。
其中，所述的胺类催化剂为A-33、HP1056、HP115中的一种或两种的混合。
其中，所述的发泡剂为水、HCFC-141b、HFC-245fa中的一种或两种混合。
其中，所述的粗MDI为PM-200、M20S 、MR-100、M-200中的一种。
其中，所述的开孔剂为AK9955表面活性剂。
其中，所述的多官能度聚醚多元醇为聚醚G350，其官能度为5-7。
其中，所述的石墨为80目的膨胀石墨。
本发明的一种汽车发动机隔音垫专用软轻质PU泡沫板是在现有的软质聚氨酯泡沫材料的基础上，在其原料配比中加入最佳比例的硅油使泡沫孔径均匀有序利于吸音，加入开孔剂使软轻质PU泡沫板具备开孔性提高尺寸稳定性，具备热塑性利于成型，加入多官能度聚醚多元醇，使得断裂伸长率及压缩强度提高且泡沫不收缩，加入阻燃剂使软轻质PU泡沫板具有阻燃性，加入石墨使软轻质PU泡沫板具有离火自熄性。
本发明的一种汽车发动机隔音垫专用软轻质PU泡沫，其制备方法是由高分子量聚醚多元醇、多官能度聚醚多元醇、硅油、胺类催化剂、发泡剂、开孔剂、阻燃剂、石墨混合均匀制成A料，A料与粗MDI（异氰酸酯）进行反应，发泡成为聚氨酯大泡块，塑化好的聚氨酯泡块进行切边、切片，制得汽车发动机隔音垫专用的软轻质PU泡沫板，其具有弹性密度在16～20Kg/m3。
本发明的一种汽车发动机隔音垫专用软轻质PU泡沫板与已有技术相比具有突出的实质性特点和显著进步，体现在软轻质PU泡沫板具备热塑性宜成型，尺寸稳定性好，产品不变形使用寿命长，手感柔软有弹性，具有质轻、隔音、隔热、阻燃、无气味、污染小、成本低等优点。
具体实施方式：
为了更好地理解与实施，下面结合实施例详细说明本发明。
实施例1，准确地称取高分子量聚醚TEP-330N和聚醚TEP-3600 85Kg，多官能度聚醚G350 15 Kg，硅油AK7731 1.8Kg，胺类催化剂HP115和HP1056 0.7Kg，发泡剂水 、HFC-245fa 13Kg，开孔剂AK9955 1.5Kg，阻燃剂TCPP 5.0Kg,，石墨16Kg，将其混合均匀制成A料，A料与PM-200 115 Kg混合高速搅拌30秒，发泡成为聚氨酯大泡块，塑化好的聚氨酯泡块进行切边、切片，制得汽车发动机隔音垫专用的软轻质PU泡沫板。
实施例2，准确地称取高分子量聚醚TEP-330N 90 Kg，多官能度聚醚G350 10Kg，混合硅油AK-7731、Y-10366 1.2Kg，胺类催化剂A-33 1.2Kg，发泡剂水 10Kg，开孔剂AK9955 1.0Kg，阻燃剂TCPP 3.0Kg，石墨20Kg，将其混合均匀制成A料；A料与MR-100 110 Kg混合高速搅拌25秒，发泡成为聚氨酯大泡块，塑化好的聚氨酯泡块进行切边、切片，制得汽车发动机隔音垫专用的软轻质PU板。
实施例3，准确地称取高分子量聚醚ZS-1406 、聚醚ZS-1618A、TEP-330N 84 Kg，多官能度聚醚G350 16Kg，硅油B8110 2.0Kg，胺类催化剂A-33、HP115 0.4Kg，发泡剂HCFC-141b 20Kg，开孔剂AK9955 2.0Kg，阻燃剂TCPP 8.0Kg ，石墨10Kg，将其混合均匀制成A料；将A料与M20S 100 Kg混合高速搅拌35秒，发泡成为聚氨酯大泡块，塑化好的聚氨酯泡块进行切边、切片，制得汽车发动机隔音垫专用的软轻质PU泡沫板。
实施例4，准确地称取高分子量聚醚ZS-1406和TEP-330N 80 Kg，多官能度聚醚G350 20 Kg，硅油AK7731、B8110 1.5Kg，胺类催化剂A-33、HP1056 0.8Kg，发泡剂水、HCFC-141b 16Kg，开孔剂AK9955 2.0Kg，阻燃剂TCPP 5.0Kg，石墨15Kg，将其混合均匀制成A料，A料与PM-200 105Kg混合高速搅拌30秒，发泡成为聚氨酯大泡块，塑化好的聚氨酯泡块进行切边、切片，制得汽车发动机隔音垫专用的软轻质PU泡沫板。
实施例5，准确地称取高分子量聚醚ZS-1406 88Kg，多官能度聚醚G350 12Kg，硅油Y-10366 1.0Kg，胺类催化剂HP1056 1.0Kg，发泡剂水 、HCFC-141b 17Kg ，开孔剂AK9955 1.3Kg，阻燃剂TCPP 7.0Kg，石墨14Kg，将其混合均匀制成A料，A料与M-200 120 Kg混合高速搅拌25秒，发泡成为聚氨酯大泡块，塑化好的聚氨酯泡块进行切边、切片，制得汽车发动机隔音垫专用的软轻质PU板。
上述实例所制得的软轻质PU泡沫板经检测，其主要性能指标：
吸声系数：0.60~0.85（GB/T18696.2）
开孔率 ≥80%
密度： 16~20kg/m3
燃烧性：≤5mm/min（GB8410）
断裂伸长率≥ 25%
压缩强度 ≥80kpa。
Claims (10)
1.一种汽车发动机隔音垫专用软轻质PU泡沫板，其特征在于它由下述重量配比的原料制成，高分子量聚醚多元醇80-90份、多官能度聚醚10-20份，硅油1-2份、胺类催化剂0.4-1.2份、发泡剂 10-20份、开孔剂1-2份、阻燃剂TCPP 3-8份、石墨10-20份，粗MDI 100-120份，所述的软轻质PU泡沫板具有弹性密度在：16~20kg/m3。
2.根据权利要求1所述的一种汽车发动机隔音垫专用软轻质PU泡沫板，其特征在于它由下述重量配比的原料制成，高分子量聚醚多元醇80份、多官能度聚醚多元醇20份、硅油1.5份、胺类催化剂0.8份、发泡剂16份、开孔剂2份、阻燃剂TCPP 5份、石墨15份，粗MDI 105份。
3.根据权利要求1或２所述的一种汽车发动机隔音垫专用软轻质PU泡沫板，其特征在于所述的高分子量聚醚多元醇的分子量为4500以上，高分子量聚醚多元醇为聚醚ZS-1618A、聚醚TEP-330N、聚醚TEP-3600、聚醚ZS-1406中的一种或两种以上混合。
4.根据权利要求1或２所述的一种汽车发动机隔音垫专用软轻质PU泡沫板，其特征在于所述的硅油为：AK7731、B8110 、Y-10366中的一种或两种混合。
5.根据权利要求1或２所述的一种汽车发动机隔音垫专用软轻质PU泡沫板，其特征在于所述的胺类催化剂为A-33、HP1056、HP115中的一种或两种的混合。
6.根据权利要求1或２所述的一种汽车发动机隔音垫专用软轻质PU泡沫板，其特征在于所述的发泡剂为水、HCFC-141b、HFC-245fa中的一种或两种混合。
7.根据权利要求1或２所述的一种汽车发动机隔音垫专用软轻质PU泡沫板，其特征在于所述的粗MDI为PM-200、M20S 、MR-100、M-200中的一种。
8.根据权利要求1或２所述的一种汽车发动机隔音垫专用软轻质PU泡沫板，其特征在于所述的开孔剂为AK9955表面活性剂。
9.根据权利要求1或２所述的一种汽车发动机隔音垫专用软轻质PU泡沫板，其特征在于所述的多官能度聚醚多元醇为聚醚G350，其官能度为5-7。
10.根据权利要求1或２所述的一种汽车发动机隔音垫专用软轻质PU泡沫板，其特征在于所述的石墨为80目的膨胀石墨。